Chemical Recycling of PET Using Catalysts from Layered Double Hydroxides: Effect of Synthesis Method and Mg-Fe Biocompatible Metals.

ABSTRACT: The chemical recycling of poly(ethylene terephthalate) (PET) residues was performed via glycolysis with ethylene glycol (EG) over Mg-Fe and Mg-Al oxide catalysts derived from layered double hydroxides. Catalysts prepared using the high supersaturation method (h.s.c.) presented a higher surface area and larger particles, but this represented less PET conversion than those prepared by the low supersaturation method (l.s.c.). This difference was attributed to the smaller mass transfer limitations inside the (l.s.c.) catalysts. An artificial neural network model well fitted the PET conversion and bis(2-hydroxyethyl) terephthalate (BHET) yield. The influence of Fe in place of Al resulted in a higher PET conversion of the Mg-Fe-h.s.c. catalyst (~95.8%) than of Mg-Al-h.s.c. (~63%). Mg-Fe catalysts could be reused four to five times with final conversions of up to 97% with reaction conditions of EG: PET = 5:1 and catalyst: PET = 0.5%. These results confirm the Mg-Fe oxides as a biocompatible novel catalyst for the chemical recycling of PET residues to obtain non-toxic BHET for further polymerization, and use in food and beverage packaging.

SUBMITTER: Arcanjo AP

PROVIDER: S-EPMC10422272 | biostudies-literature | 2023 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Chemical Recycling of PET Using Catalysts from Layered Double Hydroxides: Effect of Synthesis Method and Mg-Fe Biocompatible Metals.

Arcanjo Ana P AP Liborio Denisson O DO Arias Santiago S Carvalho Florival R FR Silva Josivan P JP Ribeiro Bernardo D BD Dias Marcos L ML Castro Aline M AM Fréty Roger R Barbosa Celmy M B M CMBM Pacheco Jose Geraldo A JGA

Polymers 20230802 15

The chemical recycling of poly(ethylene terephthalate) (PET) residues was performed via glycolysis with ethylene glycol (EG) over Mg-Fe and Mg-Al oxide catalysts derived from layered double hydroxides. Catalysts prepared using the high supersaturation method (h.s.c.) presented a higher surface area and larger particles, but this represented less PET conversion than those prepared by the low supersaturation method (l.s.c.). This difference was attributed to the smaller mass transfer limitations i ...[more]

PMID: 37571167

Similar Datasets

Project description:Layered double hydroxides (LDHs) are an ideal platform to host catalytic metal centers for water oxidation (WO) owing to the high accessibility of water to the interlayer region, which makes all centers potentially reachable and activated. Herein, we report the syntheses of three iridium-doped zinc-aluminum LDHs (Ir-LDHs) nanomaterials (1-3, with about 80 nm of planar size and a thickness of 8 nm as derived by field emission scanning electron microscopy and powder X-ray diffraction studies, respectively), carried out in the confined aqueous environment of reverse micelles, through a very simple and versatile procedure. These materials exhibit excellent catalytic performances in WO driven by NaIO4 at neutral pH and 25 °C, with an iridium content as low as 0.5 mol % (∼0.8 wt %), leading to quantitative oxygen yields (based on utilized NaIO4, turnover number up to ∼10,000). Nanomaterials 1-3 display the highest ever reported turnover frequency values (up to 402 min-1) for any heterogeneous and heterogenized catalyst, comparable only to those of the most efficient molecular iridium catalysts, tested under similar reaction conditions. The boost in activity can be traced to the increased surface area and pore volume (>5 times and 1 order of magnitude, respectively, higher than those of micrometric materials of size 0.3-1 μm) estimated for the nanosized particles, which guarantee higher noble metal accessibility. X-ray absorption spectroscopy (XAS) studies suggest that 1-3 nanomaterials, as-prepared and after catalysis, contain a mixture of isolated, single octahedral Ir(III) sites, with no evidence of Ir-Ir scattering from second-nearest neighbors, excluding the presence of IrO2 nanoparticles. The combination of the results obtained from XAS, elemental analysis, and ionic chromatography strongly suggests that iridium is embedded in the brucite-like structure of LDHs, having four hydroxyls and two chlorides as first neighbors. These results demonstrate that nanometric LDHs can be successfully exploited to engineer efficient WOCs, minimizing the amount of iridium used, consistent with the principle of the noble-metal atom economy.

Dataset Information

Chemical Recycling of PET Using Catalysts from Layered Double Hydroxides: Effect of Synthesis Method and Mg-Fe Biocompatible Metals.

Publications

Chemical Recycling of PET Using Catalysts from Layered Double Hydroxides: Effect of Synthesis Method and Mg-Fe Biocompatible Metals.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets