New benzisoxazole derivative: A potential corrosion inhibitor for mild steel in 0.5 M hydrochloric acid medium -insights from electrochemical and density functional theory studies
Ontology highlight
ABSTRACT:
SUBMITTER: P P
PROVIDER: S-EPMC10616339 | biostudies-literature | 2023 Oct
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:In the current study, 3,3',3''-((1,3,5-triazine-2,4,6-triyl)tris(azaneylylidene))tris(indolin-2-one) (MISB), which is the condensation product of melamine (triazine) and isatin, was investigated as a mild steel corrosion inhibitor in 0.5 M HCl. The ability of the synthesized tris-Schiff base to suppress corrosion was evaluated utilizing weight loss measurements, electrochemical techniques and theoretical computation. The maximum inhibition efficiency of 92.07%, 91.51% and 91.60% was achieved using 34.20 × 10-3 mM of MISB in weight loss measurements, polarization, and EIS tests, respectively. It was revealed that an increase in temperature decreased the inhibition performance of MISB, whereas an increase in the concentration of MISB increased it. The analysis demonstrated that the synthesized tris-Schiff base inhibitor followed the Langmuir adsorption isotherm and was an effective mixed-type inhibitor, but it exhibited dominant cathodic behavior. According to the electrochemical impedance measurements, the Rct values increased with an increase in the inhibitor concentration. The weight loss and electrochemical assessments were also supported by quantum calculations and surface characterization analysis, and the SEM images showed a smooth surface morphology.
| S-EPMC10291281 | biostudies-literature
Project description:In the present study the authors' main goal is to avoid the corrosive attack of the chloride ions of 3.5% NaCl solution in saline medium on the mild steel (MS), by addition of small amount of a new derivative of the hydrazide called ligand (HL), as a corrosion inhibitor. This study had been achieved by employing different electrochemical measurements such as, open circuit potential (OCP), electrochemical impedance spectroscopy (EIS) and potentio-dynamic polarization (PDP) methods. The results of the electrochemical test (OCP), showed that, the open circuit potential of the mild steel in saline solution, was guided to more positive direction in presence of the ligand (HL), at its ideal concentration (1 × 10-3 M), compared to the (OCP), of the mild steel in absence of (HL). The results of the electrochemical methods, EIS and PDP presented that, the ligand (HL), was acted as a good corrosion inhibitor for hindering the corrosion process of the mild steel in 3.5% sodium chloride, as it was recorded a good percentage of the inhibition efficiency (77.45%, 53.41%, by EIS and PDP techniques respectively), at its optimum concentration (1 × 10-3 M). Also, the corrosion rate of the mild steel in the saline medium without (HL), was listed about (0.0017 mm/year), while in existence of (HL), was decreased to a value about (0.00061 mm/year). As well, some of electrical properties of (HL), and its derivative [Pd(II), Cr(III), and Ru(III)], complexes were investigated such as; the activation energy (Ea(ac)), which recorded values in the range of 0.02-0.44 (eV) range and electrical conductivity which listed values at room temperature in the range of 10-5-10-8 S.cm-1. The results of the AC and DC electrical conductivity measurements for (HL), and its derivative [Pd(II), Cr(III) and Ru(III)] complexes indicate semiconducting nature which suggests that these compounds could be used in electronic devices. Also, the complexes exhibited higher conductivity values than (HL). Photophysical studies showed good florescence properties of HL that indicated that it can be used to determine most of the drugs with no fluorescence properties by quenching and calculating quantum yield. Moreover, the hydrazide ligand (HL), has shown selectivity as an active anticancer candidate drug for both breast and colon cancer in humans. Density function theory demonstrated that, the frontier molecular orbital HOMOs of the complexes have exhibited similar behavior and the charge density has localized in the metallic region of all the studied complexes. Also, the values of the energy gap of the ligand (HL), and its complexes Pd(II), Cr(III) and Ru(III), had been arranged in this order HL > Cr(III) > Ru(III) > Pd(II). All characterization using different spectroscopic techniques were reported to elucidate the proposed structures such as; thermal analysis, elemental analysis of C, H, and N atoms, spectral analysis using IR, UV, 1H NMR techniques, scanning electron microscopy and energy dispersive X-ray analyses.
| S-EPMC11387426 | biostudies-literature
Project description:A new curcumin derivative, i.e., (1E,4Z,6E)-5-chloro-1,7-bis(4-hydroxy-3-methoxyphenyl)hepta-1,4,6-trien-3-one (chlorocurcumin), was prepared starting with the natural compound curcumin. The newly synthesized compound was characterized by elemental analysis and spectral studies (IR, ¹H-NMR and 13C-NMR). The corrosion inhibition of mild steel in 1 M HCl by chlorocurcumin has been studied using potentiodynamic polarization (PDP) measurements and electrochemical impedance spectroscopy (EIS). The inhibition efficiency increases with the concentration of the inhibitor but decreases with increases in temperature. The potentiodynamic polarization reveals that chlorocurcumin is a mixed-type inhibitor. The kinetic parameters for mild steel corrosion were determined and discussed.
| S-EPMC5452761 | biostudies-other
Project description:Plant extracts have gained a lot of attention due to their ecofriendly nature for corrosion inhibition. In this study, we examined the inhibition performance of grape seed extract as an eco-environmental inhibitor for mild steel in hydrochloric acid medium. Electrochemical impedance spectroscopy, potentiodynamic polarization, and electrochemical noise techniques were employed to study mild steel's electrochemical behavior in the hydrochloric acid solutions containing grape seed extract. Results depicted that grape seed extract could successfully inhibit the corrosion of mild steel. Besides, water droplet contact angle, field-emission scanning electron microscopy coupled with energy dispersive spectroscopy, Fourier transform infrared spectroscopy, Raman spectroscopy, X-ray photoelectron spectroscopy, and atomic force microscopy were utilized to study the surface of mild steel specimens after dipping in acidic solutions. Electrochemical impedance results showed a corrosion efficiency of about 88% in 300 ppm of grape seed extract. Also, results revealed more compact corrosion products with improved integrity in the presence of grape seed, which confirmed electrochemical test results.
| S-EPMC8443659 | biostudies-literature
Project description:The corrosion mitigation efficiency of biotin drug for mild steel in 15% hydrochloric acid was thoroughly investigated by weight loss and electrochemical methods. The surface morphology was studied by the contact angle, scanning electrochemical microscopy, atomic force microscopy and scanning electron microscopy methods. Quantum chemical calculation and Fukui analysis were done to correlate the experimental and theoretical data. The influence of the concentration of inhibitor, immersion time, temperature, activation energy, enthalpy and entropy has been reported. The mitigation efficiency of biotin obtained by all methods was in good correlation with each other. Polarization studies revealed that biotin acted as a mixed inhibitor. The adsorption of biotin was found to obey the Langmuir adsorption isotherm. Surface studies showed the hydrophobic nature of the steel with inhibitor and vindicated the formation of a film on the metal surface that reduced the corrosion rate.
| S-EPMC5750002 | biostudies-literature
Project description:In this study, 1,5-diallyl-1H-pyrazolo [3,4-d] pyrimidin-4 (5H)-one (PPD) was evaluated as an anticorrosion agent for mild steel (MS) in 1 M HCl. The analysis was performed by weight loss (WL), potentiodynamic polarization measurement, and electrochemical impedance spectroscopy (EIS). The Tafel polarization showed that PPD is a mixed-type inhibitor and reaches 94% of the protective efficiency at 10-3 M. EIS results indicated that the resistance to charge transfer increases with increasing inhibitor concentration and the corrosion of MS is controlled by a charge transfer process. The inhibitor adsorption on the MS surface obeyed the Langmuir's adsorption isotherm. Thermodynamic parameters were calculated to elaborate the corrosion inhibition mechanism. The micrographic analysis revealed the existence of a barrier layer on the electrode surface with the presence of PPD. Theoretical examinations performed by electronic/atomic computer simulations confirmed that the obtained results were found to be consistent with experimental findings.
| S-EPMC9862199 | biostudies-literature
Project description:Turbinaria ornata (TO) extract was tested as green corrosion inhibitor on mild steel (MS) coupons in conc. HCl medium with an efficiency of 100% at 25 g l-1 during 5 min exposure. Antibacterial efficacy performed against 16 S rDNA identified marine biofilming bacteria (MBB) and human pathogenic bacteria (HPB). Maximum inhibition growth was 16 mm on MBB observed in Bacillus megaterium (MBF14 - AB894827) and 20 mm on HPB in Escherichia coli (B5 - NCIM 2931). Similarly, minimum of 10 mm on MBB witnessed in Pseudomonas sp., (MBF9 - AB894829). Toxicity studies proved 50.0% LC50 at 500 μg ml-1 in 24 hrs, whereas Balanus amphitrite resulted in 100% mortality within 12 hrs. Results including weight loss, potentiodynamic polarization and electrochemical impedance spectroscopy, FT-IR and GC-MS confirm 10-Octadecaonic acid as a major corrosion inhibitor from T. ornata and is discovered as a novel antifoulant. Anticorrosion formulation will become available soon.
| S-EPMC5805700 | biostudies-literature
Project description:Sonneratia caseolaris leaf extract was characterized for its mitigation of the electrochemical corrosion of steel in naturally aerated hydrochloric acid environments by electrochemical methods and surface analysis. The presence of S. caseolaris leaf extract (SCLE) in the hydrochloric acid medium ameliorated the corrosion resistance of steel via the adsorption of SCLE species to form a barrier layer. The improved inhibition effectiveness was demonstrated to be independent of the SCLE concentration and the corrosive environment. The highest inhibition performance of approximately 98% was reached for steel in a 1 M HCl medium containing 2500 ppm SCLE. The performance significantly decreased with a decrease in the HCl concentration from 1.00 to 0.01 M with the same SCLE concentration. In addition, severe corrosion occurred on the uninhibited steel surface but was significantly reduced on the inhibited steel surface. The analyzed results also indicated the existence of electronegative functional groups in SCLE, which could promote the adsorption process for the self-formation of the barrier layer on the steel surface. The work reported herein suggested a powerful strategy to mitigate electrochemical corrosion by adding an effective new inhibitor to achieve a green inhibitor system.
| S-EPMC8928340 | biostudies-literature
Project description:A new coumarin derivative, N,N'-((2E,2'E)-2,2'-(1,4-phenylenebis (methanylylidene))bis(hydrazinecarbonothioyl))bis(2-oxo-2H-chromene-3-carboxamide) PMBH, was synthesized and its chemical structure was elucidated and confirmed using spectroscopic techniques (Infrared spectroscopy IR, Proton nuclear magnetic resonance, 1H-NMR and carbon-13 nuclear magnetic resonance 13C-NMR). The corrosion inhibition effect of PMBH on mild steel in 1.0 M HCl was investigated using corrosion potential (ECORR), potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and electrochemical frequency modulation (EFM) measurements. The obtained results indicated that PMBH has promising inhibitive effects on the corrosion of mild steel in 1.0 M HCl across all of the conditions examined. Scanning electron microscopy (SEM) was used to investigate the morphology of the mild steel before and after immersion in 1.0 M HCl solution containing 0.5 mM of PMBH. Surface analysis revealed improvement of corrosion resistance in presence of PMBH.
| S-EPMC5455929 | biostudies-other
Project description:Halogen-substituted benzaldehyde thiosemicarbazone derivatives were synthesized and their inhibition performance for mild steel in hydrochloric acid solution were investigated systematically using weight loss measurements, electrochemical techniques, scanning electron microscopy and quantum chemical calculations. Results of weight loss measurements indicated that all these compounds exhibited excellent inhibition performance and the inhibition efficiency increased with increasing inhibitor concentrations. Polarization results revealed that the synthesized benzaldehyde thiosemicarbazone derivatives were mixed-type inhibitors. Adsorption of these compounds onto a mild steel surface was mainly chemisorption and complied with the Langmuir adsorption isotherms. Both theoretical calculations and experimental measurements suggested that the inhibition efficiency of these compounds followed the order of Br-BT > Cl-BT > F-BT > H-BT.
| S-EPMC9597289 | biostudies-literature