Dataset from the uniaxial tensile testing of human curly hair fibers under different conditions.

ABSTRACT: Individual human hair fibers exhibiting a curly morphology were procured from a female donor within her early thirties (30s). The selected hair fibers donor had refrained from undergoing any form of chemical treatment, including dyeing, relaxing, and bleaching, for a minimum period of six (6) months prior to specimen collection. The isolated single fibers were subjected to uniaxial tensile testing at various strain rates (10⁰.s^-1,10^-2. s^-1 10^-3. & 10^-4.s^-1). Furthermore, the specimens underwent testing under dry conditions at a temperature of 25°C, as well as full immersion in a saline solution at both 25°C and 35°C. The ensuing mechanical attributes, encompassing engineering was analyzed following the tensile testing.

SUBMITTER: Mathebela L

PROVIDER: S-EPMC10733091 | biostudies-literature | 2024 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Dataset from the uniaxial tensile testing of human curly hair fibers under different conditions.

Mathebela Lebogang L Sigwadi Rudzani R Lekwana Tetelo T Ngwangwa Harry H Pandelani Thanyani T Nemavhola Fulufhelo F

Data in brief 20231212

Individual human hair fibers exhibiting a curly morphology were procured from a female donor within her early thirties (30s). The selected hair fibers donor had refrained from undergoing any form of chemical treatment, including dyeing, relaxing, and bleaching, for a minimum period of six (6) months prior to specimen collection. The isolated single fibers were subjected to uniaxial tensile testing at various strain rates (100.s-1,10-2. s-1 10-3</s ...[more]

PMID: 38125370

Similar Datasets

A dataset of synthetic face centered cubic 3D polycrystalline microstructures, grain-wise microstructural descriptors and grain averaged stress fields under uniaxial tensile deformation.

Project description:This data article presents a data set comprised of 36 synthetic 3D equiaxed polycrystalline microstructures, the microstructural descriptors for each grain, and the stress and strain fields resulting from crystal plasticity simulations mimicking uniaxial tensile deformation to a total strain of 4%. This is related to the research article entitled "Applied Machine Learning to predict stress hotspots I: Face Centered Cubic Materials" (Mangal and Holm, 2018) [1]. The microstructures were created using an open source Dream.3D software tool, and the crystal plasticity simulations were carried out using the elasto-viscoplastic fast Fourier transform (EVPFFT) method. Six different kinds of FCC textures are represented with six stochastically different microstructures with varying texture intensity for each texture kind. This dataset is freely available in a Mendeley Data archive "A dataset of synthetic face centered cubic 3D polycrystalline microstructures, grain-wise microstructural descriptors and grain averaged stress fields under uniaxial tensile deformation" located at 〈http://dx.doi.org/10.17632/ss75fdg5dg.1〉 for any academic, educational, or research purposes.

| S-EPMC6141364 | biostudies-literature

Infarcted rat myocardium: Data from biaxial tensile and uniaxial compressive testing and analysis of collagen fibre orientation.

Project description:Myocardial infarction was experimentally induced in rat hearts and harvested immediately, 7, 14 and 28 days after the infarction induction. Anterior wall infarct samples underwent biaxial tensile and uniaxial compressive testing. Orientation of collagen fibres was analysed following mechanical testing. In this paper, we present the tensile and compressive stress-strain raw data, the calculated tensile and compressive moduli and the measured angles of collagen orientation. The presented data is associated with the research article titled "Characterisation of the mechanical properties of infarcted myocardium in the rat under biaxial tension and uniaxial compression" (Sirry et al., 2016) [1].

| S-EPMC4992040 | biostudies-literature

A fine resolution dataset of accessibility under different traffic conditions in European cities.

Project description:Urban accessibility and congestion indicators allow us to benchmark cities. If these indicators are also available at a fine resolution, we can compare different neighbourhoods within a city. We present a dataset of different accessibility indicators for all urban areas with more than 250 thousand people in the EU27, the UK, Switzerland and Norway. Each city is analysed by means of a population grid of 500?m by 500?m and represented by a wider area covering both the densely populated urban centre and the commuting zone. To capture congestion, we measure accessibility for each grid cell at different times of the day that correspond to different traffic conditions using the detailed network and congestion information provided by TomTom.

| S-EPMC7447804 | biostudies-literature

A dataset of synthetic hexagonal close packed 3D polycrystalline microstructures, grain-wise microstructural descriptors and grain averaged stress fields under uniaxial tensile deformation for two sets of constitutive parameters.

Project description:This data article presents a data set comprised of 54 synthetic 3D equiaxed polycrystalline microstructures, the microstructural descriptors for each grain and the stress fields resulting from two sets of crystal plasticity simulations mimicking uniaxial tensile deformation to a total strain of 2%. This is related to the research article entitled "Applied Machine Learning to predict stress hotspots II: Hexagonal Close Packed Materials" (Mangal and Holm, 2018). The microstructures were created using an open source Dream.3D software tool and the crystal plasticity simulations were carried out using elasto-viscoplastic fast Fourier transform (EVPFFT) method. Eight different kinds of HCP textures are represented with stochastically different microstructures with varying texture intensity for each texture kind. For each texture kind, between six and nine stochastically different microstructures with varying texture intensity (measured by multiples of random density (MRD)) are created. This dataset is freely available in two Mendeley Data archives "Synthetic HCP 3D polycrystalline microstructures with grain-wise microstructural descriptors and stress fields under uniaxial tensile deformation: Part One" and "Synthetic HCP 3D polycrystalline microstructures with grain-wise microstructural descriptors and stress fields under uniaxial tensile deformation: Part Two" located at http://dx.doi.org/10.17632/kt8hfg4t2p.1 and http://dx.doi.org/10.17632/nsfn6tw295.1 respectively for any academic, educational, or research purposes.

| S-EPMC6260324 | biostudies-literature

Experimental vibration dataset collected of a beam reinforced with masses under different health conditions.

Project description:Vibration signals extracted from structures across diverse health conditions have become indispensable for monitoring structural integrity. These datasets represent a resource for real-time condition monitoring, enabling the precise detection and diagnosis of system anomalies. This paper aims to enrich the scientific community's database on structural dynamics and experimental methodologies pertinent to system modelling. Leveraging experimental measurements obtained from mass-reinforced beams, these datasets validate numerical models, refine identification techniques, quantify uncertainties, and continuously foster machine learning algorithms' evolution to monitor structural integrity. Furthermore, the beam dataset is data-driven and can be used to develop and test innovative structural health monitoring strategies, specifically identifying damages and anomalies within intricate structural frameworks. Supplemental datasets like Mass-position and damage index introduce parametric uncertainty into experimental and damage identification metrics. Thereby offering valuable insights to elevate the efficacy of monitoring and control techniques. These comprehensive tests also encapsulate paramedic uncertainty, providing robust support for applications in uncertainty quantification, stochastic modelling, and supervised and unsupervised machine learning methodologies.

| S-EPMC10828560 | biostudies-literature

Dataset for time-lapse ultrasonic tomography of a granite slab under uniaxial compression test.

Project description:This data article includes raw data for time-lapse ultrasonic tomography measurements during a uniaxial compression test. Two sets of experimental data are included: first, the ultrasonic tomography (UT) observation (i.e., waveform) data at each 20 MPa axial stress step during the uniaxial loading test; and second, the stress-strain curve of the uniaxial compression test. A numerical model based on the combined finite-discrete element method (FDEM) was used to improve the understanding of the experimental results. The model file and the simulated acoustic emission (AE) data extracted from the simulation results are also included in this article. Data sets presented in this article help to improve understanding of the progressive rock failure process at microscopic and macroscopic scales.

| S-EPMC6128094 | biostudies-literature

Dataset of the phospholipidome and transcriptome of Campylobacter jejuni under different growth conditions.

Project description:The membrane phospholipid composition is not a stable bacterial characteristic but can change in response to altered environmental conditions. Here we provide the dataset of the phospholipidome and transcriptome of the microaerophilic human pathogen Campylobacter jejuni under different environmental conditions. These data have been used in Cao (2020), The unique phospholipidome of the enteric pathogen C. jejuni: Lysolipids are required for motility at low oxygen availability. Here the abundance of each phospholipid is shown during the growth of C. jejuni for 0-108 h under low and high oxygen conditions (0.3 vs 10% O2). The phospholipid data were obtained by applying high performance liquid chromatography tandem-mass spectrometry (LC-MS/MS). The transcriptomic data obtained by RNA-seq show the differential expressed genes between logarithmic and stationary grown bacteria. In addition, our data might serve as a reference information for further in-depth investigation to understand the relation between specific phospholipids and the activity of membrane associated proteins.

| S-EPMC7548934 | biostudies-literature

Study on Ultrasonic Nondestructive Testing of Self-Compacting Concrete under Uniaxial Compression Test.

Project description:To study the variation law of ultrasonic parameters of self-compacting concrete before and after damage under uniaxial compression test conditions, the C30 self-compacting concrete blocks stored for 7 days and 28 days were subjected to ultrasonic nondestructive testing, and the variation law of the sound time, amplitude, and sound velocity before and after the damage of self-compacting concrete blocks was emphatically analyzed. The concrete acoustic detection software was introduced to judge and analyze the abnormal values of the parameters of each measuring point, and the defect distribution map of each test block was obtained. The results showed that after curing the self-compacting concrete test block for 7 days and 28 days, the average value of sound time before and after the failure of each measuring point of the test block is small, and the average value of sound time before the failure is less than that after; the average amplitude after failure is smaller than that before failure, and the amplitude of some measuring points will be smaller than that before. The average sound velocity after failure is less than that before failure, and the internal defects appear and the structure is not dense. This study provides a theoretical basis for the application of ultrasonic detection technology in the field of self-compacting concrete and also provides a practical basis for the stability monitoring and failure warning of self-compacting concrete.

| S-EPMC9267734 | biostudies-literature

The what, why and how of curly hair: a review.

Project description:An attempt to understand and explain a peculiarity that was observed for curly fibres during experimentation revealed disparate literature reporting on several key issues. The phenotypical nature of curly fibres is only accurately understood within the larger scope of hair fibres, which are highly complex biological structures. A brief literature search produced thousands of research items. Besides the large amount of information on the topic, there was also great variability in research focus. From our review, it appeared that the complexity of hair biology, combined with the variety of research subtopics, often results in uncertainty when relating different aspects of investigation. During the literature investigation, we systematically categorized elements of curly hair research into three basic topics: essentially asking why fibres curl, what the curly fibre looks like and how the curly fibre behaves. These categories were subsequently formalized into a curvature fibre model that is composed of successive but distinctive tiers comprising the elements in curly hair research. The purpose of this paper is twofold: namely to present (i) a literature review that explores the different aspects of curly human scalp hair and (ii) the curvature fibre model as a systemized approach to investigating curly hair.

| S-EPMC6894537 | biostudies-literature

Microstructural Origin of the Double Yield Points of the Metallocene Linear Low-Density Polyethylene (mLLDPE) Precursor Film under Uniaxial Tensile Deformation.

Project description:The microstructural origin of the double yield points of metallocene linear low-density polyethylene (mLLDPE) precursor films has been studied with the assistance of the synchrotron radiation small- and wide-angle X-ray scattering (SAXS/WAXS). It has been shown that the microstructural origin of the double yield points is highly related to the initial orientation of the original precursor film. For less oriented mLLDPE precursor films, the rearrangement of lamellae and the appearance of the monoclinic phase are the microstructural origins of the first yield point. In comparison, for the highly-oriented mLLDPE precursor film, only the orthorhombic-monoclinic phase transition appears at the first yield point. The melting-recrystallization and the formation of the fibrillary structure happen beyond the second yield point for all studied mLLDPE precursor films. Finally, the detailed microstructural evolution roadmaps of mLLDPE precursor films under uniaxial tensile deformation have been established, which might serve as a guide for processing high-performance polymer films by post-stretching.

| S-EPMC7794766 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data