Metal leakage from orthodontic appliances chemically alters enamel surface during experimental in vitro simulated treatment.

ABSTRACT: Human enamel is composed mainly of apatite. This mineral of sorption properties is susceptible to chemical changes, which in turn affect its resistance to dissolution. This study aimed to investigate whether metal leakage from orthodontic appliances chemically alters the enamel surface during an in vitro simulated orthodontic treatment. Totally 107 human enamel samples were subjected to the simulation involving metal appliances and cyclic pH fluctuations over a period of 12 months in four complimentary experiments. The average concentrations and distribution of Fe, Cr, Ni, Ti and Cu within the enamel before and after the experiments were examined using ICP‒MS and LA‒ICP‒MS techniques. The samples exposed to the interaction with metal appliances exhibited a significant increase in average Fe, Cr and Ni (Kruskal-Wallis, p < 0.002) content in comparison to the control group. The outer layer, narrow fissures and points of contact with the metal components showed increased concentrations of Fe, Ti, Ni and Cr after simulated treatment, conversely to the enamel sealed with an adhesive system. It has been concluded that metal leakage from orthodontic appliances chemically alters enamel surface and microlesions during experimental in vitro simulated treatment.

SUBMITTER: Topolska JM

PROVIDER: S-EPMC10914722 | biostudies-literature | 2024 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Metal leakage from orthodontic appliances chemically alters enamel surface during experimental in vitro simulated treatment.

Topolska Justyna M JM Jagielska Agata A Motyl Sylwia S Kozub-Budzyń Gabriela A GA Kępa Luiza L Wagner Barbara B Wątor Katarzyna K

Scientific reports 20240305 1

Human enamel is composed mainly of apatite. This mineral of sorption properties is susceptible to chemical changes, which in turn affect its resistance to dissolution. This study aimed to investigate whether metal leakage from orthodontic appliances chemically alters the enamel surface during an in vitro simulated orthodontic treatment. Totally 107 human enamel samples were subjected to the simulation involving metal appliances and cyclic pH fluctuations over a period of 12 months in four compli ...[more]

PMID: 38443566

Similar Datasets

Project description:ObjectiveThis study aimed to evaluate enamel surface integrity and time consumed during residual cement removal after bracket debonding using different adhesive removal burs with and without a dental loupe.Material and methodsSixty human-extracted premolars were collected, cleaned, mounted, and prepared for orthodontic bracket bonding. Teeth were randomly divided into three main groups (n = 20) based on the adhesive removal method: tungsten carbide system (TC), sof-lex discs system (SD), and diamond system (DB) groups. Then, each group was subdivided into two subgroups (naked eye and magnifying loupe subgroups). The brackets were bonded and then debonded after 24 h, and the Adhesive Remnant Index (ARI) was assessed. The adhesive remnants were removed by different systems, and the final polishing was performed by Silicone OneGloss. The enamel surface roughness was evaluated before bracketing (T0), after residual cement removal (T1), and finally after polishing (T2) using surface Mitutoyo SJ-210 profilometry and Scanning Electron Microscopy (SEM) to determine the Enamel Damage Index (EDI) score. The time consumed for adhesive removal was recorded in seconds.ResultsThe Kruskal Wallis test showed a statistically significant difference in roughness values at T1 compared to T2 between subgroups (p < 0.001). When comparing EDI at T1 and T2, the Kruskal-Wallis H-test showed statistically significant differences in all subgroups. The pairwise comparisons revealed that EDI scores showed a statistically significant difference at T1 and T2 between DB vs. TC and SD (p = 0.015) but not between TC vs. SD (p = 1.000), indicating the highest roughness value observed in the DB group. The time for cement removal was significantly shorter in the magnifying loupe group than in the naked eye group and was shortest with the TC group, whereas the time was the longest with the DB group (p < 0.05).ConclusionAll three systems were clinically satisfactory for residual orthodontic adhesive removal. However, TC system produced the lowest enamel roughness, while the DB system created the greatest. The polishing step created smoother surfaces regardless of the systems used for resin removal.

Dataset Information

Metal leakage from orthodontic appliances chemically alters enamel surface during experimental in vitro simulated treatment.

Publications

Metal leakage from orthodontic appliances chemically alters enamel surface during experimental in vitro simulated treatment.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets