Dry gel spinning of fungal hydrogels for the development of renewable yarns from food waste
Ontology highlight
ABSTRACT:
SUBMITTER: Lindh A
PROVIDER: S-EPMC11295346 | biostudies-literature | 2024 Jan
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:A fungal biorefinery is presented to valorize food waste to fungal monofilaments with tunable properties for different textile applications. Rhizopus delemar is successfully grown on bread waste and the fibrous cell wall is isolated. A spinnable hydrogel is produced from cell wall by protonation of amino groups of chitosan followed by homogenization and concentration. Fungal hydrogel is wet spun to form fungal monofilaments which underwent post-treatments to tune the properties. The highest tensile strength of untreated monofilaments is 65 MPa (and 4% elongation at break). The overall highest tensile strength of 140.9 MPa, is achieved by water post-treatment. Moreover, post-treatment with 3% glycerol resulted in the highest elongation % at break, i.e., 14%. The uniformity of the monofilaments also increased after the post-treatments. The obtained monofilaments are compared with commercial fibers using Ashby's plots and potential applications are discussed. The wet spun monofilaments are located in the category of natural fibers in Ashby's plots. After water and glycerol treatments, the properties shifted toward metals and elastomers, respectively. The compatibility of the monofilaments with human skin cells is supported by a biocompatibility assay. These findings demonstrate fungal monofilaments with tunable properties fitting a wide range of sustainable textiles applications.
| S-EPMC10935878 | biostudies-literature
Project description:Food waste is an abundant and inexpensive resource for the production of renewable fuels. Biocrude yields obtained from hydrothermal liquefaction (HTL) of food waste can be boosted using hydroxyapatite (HAP) as an inexpensive and abundant catalyst. Combining HAP with an inexpensive homogeneous base increased biocrude yield from 14 ± 1 to 37 ± 3%, resulting in the recovery of 49 ± 2% of the energy contained in the food waste feed. Detailed product analysis revealed the importance of fatty-acid oligomerization during biocrude formation, highlighting the role of acid-base catalysts in promoting condensation reactions. Economic and environmental analysis found that the new technology has the potential to reduce US greenhouse gas emissions by 2.6% while producing renewable diesel with a minimum fuel selling price of $1.06/GGE. HAP can play a role in transforming food waste from a liability to a renewable fuel.
| S-EPMC9486744 | biostudies-literature
Project description:In ecosystem engineering research, the contribution of microbial cooperation to ecosystem function has been emphasized. Fungi are one of the predominant decomposers in composting, but thus far, less attention has been given to fungal than to bacterial cooperation. Therefore, network and cohesion analyses were combined to reveal the correlation between fungal cooperation and organic matter (OM) degradation in ten composting piles. Positive cohesion, reflecting the cooperation degree, was positively linked to the degradation rate of OM. From the community perspective, core species (i.e., Candida tropicalis, Issatchenkia orientails, Kazachstania exigua, and Dipodascus australiensis) with high occurrence frequency and abundance were the key in regulating positive cohesion. These species were highly relevant to functional genera associated with OM degradation in both fungal and bacterial domains. Therefore, focusing on these core fungal species might be an appropriate strategy for targeted regulation of functional microbes and promotion of degradation rates.
| S-EPMC9500350 | biostudies-literature
Project description:Wine industry generates a large amount of biowaste, such as grape marc and wine lees, which is considered in the Directive (EU) 2018/2001 as an adequate feedstock to produce advanced biofuels. Grapeseed oil fatty acid ethyl esters (FAEEs) can be obtained from oil extracted from grape marc and bioethanol distilled from wine lees or wine surplus. Although FAEE still has no specific standard, grapeseed oil FAEE would fulfill all of the properties set by the standard EN 14214, except oxidation stability. This work analyzes the effect of natural antioxidants on the oxidation stability of grapeseed oil FAEE, using grapeseed oil fatty acid methyl esters (FAMEs) as a reference for comparison. On the one hand, the biofuel, produced with conventional transesterification, was mixed with FAME and FAEE produced via in situ transesterification. On the other hand, antioxidants extracted from grapeseed or defatted grapeseed flour were added to the biofuel. The results show that (1) FAEE has worse oxidation stability than FAME, (2) in situ transesterification improves the oxidation stability, and (3) addition of natural antioxidants is hindered by their low solubility in alkyl esters. Finally, the concentration of antioxidants, measured by UV-vis spectroscopy, showed a correlation between the absorbance at 285 nm (characteristic of phenolic compounds) and the induction time (IT) of the samples.
| S-EPMC7364578 | biostudies-literature
Project description:A comprehensive characterization of various carbon nanotube (CNT) yarns provides insight for producing high-performance CNT yarns as well as a useful guide to select the proper yarn for a specific application. Herein we systematically investigate the correlations between the physical properties of six CNT yarns produced by three spinning methods, and their structures and the properties of the constituent CNTs. The electrical conductivity increases in all yarns regardless of the spinning method as the effective length of the constituent CNTs and the density of the yarns increase. On the other hand, the tensile strength shows a much stronger dependence on the packing density of the yarns than the CNT effective length, indicating the relative importance of the interfacial interaction. The contribution of each physical parameter to the yarn properties are quantitatively analyzed by partial least square regression.
| S-EPMC8880327 | biostudies-literature
Project description:In this report, we introduce a novel and commercially viable method to recover renewable hydrogen and carbon nanotubes from waste glycerol produced in the biodiesel process. Gas-phase catalytic reforming converts glycerol to clean hydrogen fuel and by replacing the problematical coke formed on the catalyst with high value carbon nanotubes, added value can be realised. Additional benefits of around 2.8 kg CNTs from the reforming of 1 tonne of glycerol and the production of 500 Nm(3) H2 could have a considerable impact on the economics of glycerol utilization. Thereby, the contribution of this research will be a significant step forward in solving a current major technical and economic challenge faced by the biofuels industry.
| S-EPMC3783054 | biostudies-literature
Project description:Amplicon sequencing of medical waste fungal communities
| PRJNA822104 | ENA
Project description:The potential applications of self-assembled supramolecular gels based on natural molecules encouraged the researchers to develop a versatile synthetic method for their structural analogues. Herein, we report a facile synthesis of glycolipid from renewable resources, cashew nut shell liquid,d and d-glucose in good yield. Gelation behavior of these glycolipids were studied in a wide range of solvents and oils. To our delight, compound 5b formed a hydrogel with Critical gelator concentration (CGC) of 0.29% w/v. Morphological analysis of the hydrogel depicts the formation of twisted fibers with an entangled network. Formation of a twisted fibrous structure was further identified by CD spectral studies with respect to temperature. The molecular self-assembly assisted by hydrogen bonding, hydrophobic, and π⁻π stacking interactions were identified by X-ray diffraction (XRD) and FTIR studies. Rheological analysis depicted the mechanical strength and stability of the hydrogel, which is crucial in predicting the practical applications of supramolecular soft materials.
| S-EPMC6318777 | biostudies-literature