Apparent interfacial fracture toughness of resin/ceramic systems.

ABSTRACT: We suggest that the apparent interfacial fracture toughness (K(A)) may be estimated by fracture mechanics and fractography. This study tested the hypothesis that the K(A) of the adhesion zone of resin/ceramic systems is affected by the ceramic microstructure. Lithia disilicate-based (Empress2-E2) and leucite-based (Empress-E1) ceramics were surface-treated with hydrofluoric acid (HF) and/or silane (S), followed by an adhesive resin. Microtensile test specimens (n = 30; area of 1 +/- 0.01 mm(2)) were indented (9.8 N) at the interface and loaded to failure in tension. We used tensile strength (sigma) and the critical crack size (c) to calculate K(A) (K(A) = Ysigmac(1/2)) (Y = 1.65). ANOVA and Weibull analyses were used for statistical analyses. Mean K(A) (MPa.m(1/2)) values were: (E1HF) 0.26 +/- 0.06; (E1S) 0.23 +/- 0.06; (E1HFS) 0.30 +/- 0.06; (E2HF) 0.31 +/- 0.06; (E2S) 0.13 +/- 0.05; and (E2HFS) 0.41 +/- 0.07. All fractures originated from indentation sites. Estimation of interfacial toughness was feasible by fracture mechanics and fractography. The K(A) for the systems tested was affected by the ceramic microstructure and surface treatment.

SUBMITTER: Della Bona A

PROVIDER: S-EPMC2244791 | biostudies-literature | 2006 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Apparent interfacial fracture toughness of resin/ceramic systems.

Della Bona A A Anusavice K J KJ Mecholsky J J JJ

Journal of dental research 20061101 11

We suggest that the apparent interfacial fracture toughness (K(A)) may be estimated by fracture mechanics and fractography. This study tested the hypothesis that the K(A) of the adhesion zone of resin/ceramic systems is affected by the ceramic microstructure. Lithia disilicate-based (Empress2-E2) and leucite-based (Empress-E1) ceramics were surface-treated with hydrofluoric acid (HF) and/or silane (S), followed by an adhesive resin. Microtensile test specimens (n = 30; area of 1 +/- 0.01 mm(2)) ...[more]

PMID: 17062746

Similar Datasets

Project description:Fracture risk does not solely depend on strength but also on fracture toughness; ie, the ability of bone material to resist crack initiation and propagation. Because resistance to crack growth largely depends on bone properties at the tissue level, including collagen characteristics, current X-ray based assessment tools may not be suitable to identify age-related, disease-related, or treatment-related changes in fracture toughness. To identify useful clinical surrogates that could improve the assessment of fracture resistance, we investigated the potential of (1)H nuclear magnetic resonance spectroscopy (NMR) and reference point indentation (RPI) to explain age-related variance in fracture toughness. Harvested from cadaveric femurs (62 human donors), single-edge notched beam (SENB) specimens of cortical bone underwent fracture toughness testing (R-curve method). NMR-derived bound water showed the strongest correlation with fracture toughness properties (r = 0.63 for crack initiation, r = 0.35 for crack growth, and r = 0.45 for overall fracture toughness; p < 0.01). Multivariate analyses indicated that the age-related decrease in different fracture toughness properties were best explained by a combination of NMR properties including pore water and RPI-derived tissue stiffness with age as a significant covariate (adjusted R(2) = 53.3%, 23.9%, and 35.2% for crack initiation, crack growth, and overall toughness, respectively; p < 0.001). These findings reflect the existence of many contributors to fracture toughness and emphasize the utility of a multimodal assessment of fracture resistance. Exploring the mechanistic origin of fracture toughness, glycation-mediated nonenzymatic collagen crosslinks and intracortical porosity are possible determinants of bone fracture toughness and could explain the sensitivity of NMR to changes in fracture toughness. Assuming fracture toughness is clinically important to the ability of bone to resist fracture, our results suggest that improvements in fracture risk assessment could potentially be achieved by accounting for water distribution (quantitative ultrashort echo time magnetic resonance imaging) and by a local measure of tissue resistance to indentation, RPI.

Dataset Information

Apparent interfacial fracture toughness of resin/ceramic systems.

Publications

Apparent interfacial fracture toughness of resin/ceramic systems.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets