Remineralization of enamel caries can decrease optical reflectivity.

ABSTRACT: The remineralization of enamel caries can lead to distinct optical changes within a lesion. We hypothesized that the restoration of mineral volume would result in a measurable decrease in the depth-resolved reflectivity of polarized light from the lesion. To test this hypothesis, we measured optical changes in artificial caries undergoing remineralization as a function of depth, using Polarization-sensitive Optical Coherence Tomography (PS-OCT). Lesions were imaged non-destructively before and after exposure to a remineralization regimen. After imaging, microradiographs of histological thin sections indicated that the significant reflectivity reduction measured by PS-OCT accurately represented the increase in mineral content within a larger repaired surface zone. Mineral volume changes arising from remineralization can be measured on the basis of the optical reflectivity of the lesion.

SUBMITTER: Jones RS

PROVIDER: S-EPMC2254215 | biostudies-literature | 2006 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Remineralization of enamel caries can decrease optical reflectivity.

Jones R S RS Fried D D

Journal of dental research 20060901 9

The remineralization of enamel caries can lead to distinct optical changes within a lesion. We hypothesized that the restoration of mineral volume would result in a measurable decrease in the depth-resolved reflectivity of polarized light from the lesion. To test this hypothesis, we measured optical changes in artificial caries undergoing remineralization as a function of depth, using Polarization-sensitive Optical Coherence Tomography (PS-OCT). Lesions were imaged non-destructively before and a ...[more]

PMID: 16931861

Similar Datasets

Remineralization of Artificial Dentin Caries Using Dentin and Enamel Matrix Proteins.

Project description:To assess the remineralizing potential of dentin matrix proteins and enamel matrix derivatives (DMPs and EMDs) after application on artificially induced dentin lesions, given the hypothesis that these materials increase the mineral uptake, binding, and mineralization. Forty-eight caries-free human premolars were used. Teeth were cut, polished, and embedded, leaving an open window on the root surface, of which one-third was covered with a flowable composite to preserve the healthy untreated dentin. Then, samples were demineralized in Buskes solution for 33 days. A micro-CT scan prior to treatment was performed. Next, the samples were randomly allocated into four groups: (A) An untreated negative control (CON), (B) application of porcine dentin matrix proteins (DMP), (C) treatment with enamel matrix derivatives (EMD, Emdogain, Straumann), and (D) amine fluoride application (AMF, Elmex fluid, GABA). All samples were placed in artificial saliva for 21 days. A second micro-CT scan was performed, after which the change in gray scaling within a defined region of interest (0.25 mm3) was analyzed. ANCOVA was applied to discover statistical differences between the different treatments. Both, treatment with AMF; (P = 0.011 versus CON) as well as with DMP (P = 0.043 versus CON) yielded a statistically significant difference compared to the control treatment. EMD treatment was not found to differ (P > 0.05). Mainly the top layer of the defects showed clear signs of remineralization, which was also evident in CON. This study was able to visually confirm the remineralization potential of demineralized dentin especially after DMP application, which, however, did not outperform AMF. Based on this, additional studies combining proteins and fluorides are now warranted and ongoing.

| S-EPMC6651374 | biostudies-literature

Application of fluoride disturbs plaque microecology and promotes remineralization of enamel initial caries

Project description:ABSTRACT Background The caries-preventive effect of topical fluoride application has been corroborated by a number of clinical studies. However, the effect of fluoride on oral microecology remains unclear. Objective To monitor the effect of fluoride on dental plaque microecology and demineralization/remineralization balance of enamel initial caries. Methods Three-year-old children were enrolled and treated with fluoride at baseline and 6 months. International Caries Detection and Assessment System II indices of 52 subjects were measured at baseline, 3, 6, and 12 months. Supragingival plaque samples of 12 subjects were collected at baseline, 3 and 14 days for 16S rRNA sequencing. Results Changes in microbial community structure were observed at 3 days after fluoridation. Significant changes in the relative abundance of microorganisms were observed after fluoride application, especially Capnocytophaga, unidentified Prevotellaceae and Rothia. Functional prediction revealed that cell movement, carbohydrate and energy metabolism were affected significantly after fluoride application. Fluoride significantly inhibited enamel demineralization and promoted remineralization of early demineralized caries enamel at 3 months. Conclusion Fluoride application significantly inhibited the progression of enamel initial caries and reversed the demineralization process, possibly by disturbing dental plaque microecology and modulating the physicochemical action of demineralization/remineralization. This deepened our understanding of caries-preventive effects and mechanisms of fluoride.

| S-EPMC9341347 | biostudies-literature

The remineralization effect of GERM CLEAN on early human enamel caries lesions in vitro.

Project description:This study aimed to evaluate the remineralization effect of GERM CLEAN, a novel antibacterial peptide, on early enamel caries. Thirty human enamel blocks from thirty teeth were randomly divided into three groups: double distilled water (DDW group), GERM CLEAN (GC group), and 1000 ppm fluoride (NaF group). Specimens were demineralized for 3 days (pH 4.6) followed by pH cycling twice daily for 14 days. For a pH cycle, specimens received corresponding treatments for 5 min, then were immersed in demineralizing solution for 1 h, received corresponding treatments again, and finally were immersed in remineralizing solution (pH 7.0) for approximately 11 h. Specimens were washed with DDW after each treatment. Microindentation tests, atomic force microscopy (AFM), and transverse micro-radiography (TMR) were conducted to analyze enamel blocks. GC demonstrated a lower percentage of surface microhardness recovery (SMHR%) (p < 0.0001), rougher surfaces (p < 0.0001), deeper lesion depth (p = 0.001), and more mineral loss (p = 0.001) than NaF, but showed higher SMHR% (p < 0.0001), smoother surfaces (p < 0.0001), shallower lesion depth (p = 0.049), and less mineral loss (p = 0.001) than DDW. As a result, GERM CLEAN has the potential to promote the remineralization of demineralized enamel.

| S-EPMC10011381 | biostudies-literature

Remineralization of enamel caries by an amelogenin-derived peptide and fluoride <i>in vitro</i>.

Project description:Dental caries is one of the most common oral diseases in the world. This study was tantamount to investigate the combinatory effects of an amelogenin-derived peptide (called QP5) and fluoride on the remineralization of artificial enamel caries. The peptide QP5 was synthesized and characterized, and the binding capability of the peptide on hydroxyapatite (HA) and demineralized tooth enamel surface was analysed. Then, the mineralization function of the peptide and fluoride was studied through the spontaneous mineralization testing and remineralization on enamel caries in vitro. First, the novel peptide QP5 could bind on the hydroxyapatite and demineralized tooth enamel surfaces. Second, QP5 can transitorily stabilize the formation of amorphous calcium phosphate and direct the transformation into hydroxyapatite crystals alone and in combination with fluoride. In addition, compared to blocks treated by peptide QP5 alone or fluoride, the sample blocks showed significantly higher surface microhardness, lower mineral loss and shallower lesion depth after treatment with a combination of QP5 and fluoride at high or low concentrations. The peptide QP5 could control the crystallization of hydroxyapatite, and combinatory application of peptide QP5 and fluoride had a potential synergistic effect on the remineralization of enamel caries.

| S-EPMC7266664 | biostudies-literature

A statherin-derived peptide promotes hydroxyapatite crystallization and <i>in situ</i> remineralization of artificial enamel caries.

Project description:In situ remineralization of hydroxyapatite on a human tooth enamel surface induced by anti-caries bioactive components is an alternative restorative strategy against dental caries. In this study, a novel biomimetic peptide DE-11, inspired by the salivary phosphoprotein statherin, was developed, and it showed beneficial potentials for the restoration of demineralized tooth enamel in vitro. The peptide DE-11 contained the initial six-peptide sequence of N-terminus of statherin extended by a mineralization hydrophilic tail composed of consecutive acidic amino acids capable of adsorbing calcium and phosphate ions. A strong adsorption capacity of DE-11 to hydroxyapatite was confirmed through Langmuir adsorption isotherm experiment and confocal laser scanning microscopy. Then, the nucleation and crystallization of hydroxyapatite due to DE-11 was characterized by scanning and transmission electron microscopy and selected-area electron diffraction. Moreover, the ability of DE-11 to promote the remineralization of initial enamel caries lesions was further evaluated. Initial lesions were created in bovine enamel blocks, which were then exposed to the peptide solution and finally immersed in artificial saliva. After 7 days, a higher percentage of surface microhardness recovery, a lower mineral loss, a shallower lesion depth, and a higher mineral content were found on the surface of the lesion body in the DE-11 group as compared to that in the negative group using surface microhardness testing, polarized light microscopy, and transverse microradiography; this indicated that DE-11 could induce in situ remineralization of hydroxyapatite on the demineralized enamel surface. Overall, these findings suggest that DE-11 is highly promising as a restorative biomaterial for enamel remineralization in the anti-caries applications.

| S-EPMC9077281 | biostudies-literature

HMU Fluorinze Mouthwash Enhances Enamel Remineralization: An In Vitro Study.

Project description:BACKGROUND:Fluoride therapy has long been used extensively to prevent dental caries. Fluoride appears in a variety of dental care products such as mouth rinses, dentifrices, gels, etc. HMU Fluorinze is the first mouthwash containing fluoride in Vietnam. AIM:This research was conducted to evaluate the efficacy of HMU Fluorinze mouthwash on remineralizing enamel in laboratory conditions. METHODS:20 third molar teeth were cleaned and covered with nail polish, except for a 3 x 3 mm square on their buccal surfaces. These teeth underwent two steps: demineralization using Coca-cola and remineralization for 20 daysusing standard calcifying solution (control group) and standard calcifying solution + HMU Fluorinze mouthwash 2 times/day (experimental group). The index measured of enamel structure after demineralization and remineralization was assessed by a DIAGNOdent pen 2190. RESULTS:The indices measured of the control group and experimental group at baseline were 3.65 ± 0.76 and 3.35 ± 0.64 respectively. After demineralization the control group measured 21.78 ± 4.48 and the experimental group, 20.25 ± 2.26. Following remineralization, the control group scores were 6.30 ± 1.03 and the experimental group, 3.90 ± 1.24, demonstrating statistical significance (p < 0.01) between the two groups. After 20 days, the results for the experimental group did not differ from the original results (p = 0.272), in contrast with the control group (p < 0.01). CONCLUSION:Results show that HMU Fluorinze mouthwash is better at remineralizing than standard calcifying solution.

| S-EPMC7084033 | biostudies-literature

Biomimetic remineralization of acid etched enamel using agarose hydrogel model.

Project description:Background: Minimally invasive dentistry aims to prevent progression of caries and treats non-cavitated lesions through non-invasive approaches to preserve the integrity of tooth structure. The aim of this research was to investigate the possible biomimetic effect of agarose hydrogel in remineralizing a human demineralized enamel model. Methods: Mandibular third molars were distributed into three groups (G1, G2 and G3) according to the follow up time (2, 4 and 6 days respectively). Caries like lesion was prepared by applying 37% phosphoric acid gel for 1 minute and then remineralization was performed through applying agarose hydrogel on the demineralized surfaces. The specimens were placed in phosphate solution at 37˚C for 2, 4 & 6 days. Scanning electron microscope (SEM), surface microhardness (SMH) and surface roughness analysis (SR) were performed to assess the regenerated tissue. Results: SEM revealed mineral depositions on the demineralized enamel surface that increased in density by time resulting in a relatively smooth surface in G3. SR and SMH analysis revealed significant differences between the remineralized enamel surfaces of different groups (p< 0.00001) with the highest SR in G1 and the highest SMH in G3. Conclusions: Agarose hydrogel application is a promising approach to treat early carious lesion. Further studies are needed to clarify the stability of agarose hydrogels in clinical application.

| S-EPMC6178904 | biostudies-literature

Remineralization of early enamel lesions with a novel prepared tricalcium silicate paste.

Project description:To evaluate the remineralization potential of prepared tricalcium silicate (TCS) paste compared to silver diamine fluoride-potassium iodide (SDF-KI) and casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) on artificial enamel lesions. Thirty permanent sound molars were collected for the study. After cleaning, root cutting, and applying acid-resistant nail varnish, leaving a 4 × 4 mm buccal window, the teeth were subjected to demineralization process. The teeth were divided into three treatment groups (n = 10). In each group, the teeth were sectioned buccolingually to obtain two halves (30 self-control and 30 experimental halves). The self-control halves were subjected to cross-sectional microhardness (CSMH), energy-dispersive X-ray spectroscopy at 50, 100, and 150 µm from the external enamel surface, and micromorphological analysis at the superficial enamel surface. The experimental halves were subjected to the same tests after 30 days of remineralization. Three-way analysis of variance (ANOVA) outcomes showed no significant difference in CSMH after treatment among the three different groups at the different levels (p > 0.05). Meanwhile, three-way ANOVA outcomes showed a significant difference in calcium/ phosphate ratio after treatment among the three different groups at the different levels. (p < 0.05). The tricalcium silicate paste used in this study showed potential remineralization in subsurface enamel lesions.

| S-EPMC9200717 | biostudies-literature

Three-dimensional observation and analysis of remineralization in dentinal caries lesions.

Project description:The remineralization mechanism in dental caries lesions is not completely understood. This study reports on ultrastructural and chemical changes observed within arrested caries lesions. Carious human teeth were observed using scanning electron microscopy (SEM) and focused-ion-beam (FIB)-SEM. The crystals detected in the caries lesions were characterized by transmission electron microscopy (TEM), along with chemical element mapping using energy-dispersive spectroscopy (EDS)-STEM. FIB-SEM 3D reconstructions revealed a severely damaged dentin surface abundantly covered by bacteria. Although the dentin tubules were clogged up to a depth of 100 ?m, bacterial invasion into dentin tubules was not observed. TEM crystal analysis and EDS-STEM revealed the presence of Ca and P, as well as of Mg within the HAp crystals deposited inside the dentin tubules. It was concluded that extensive remineralization with deposition of Mg-HAp crystals had occurred in dentin tubules of caries-arrested dentin. Understanding the natural remineralization process is thought to be helpful for developing clinical biomimetic remineralization protocols.

| S-EPMC7062784 | biostudies-literature

Engineered Biomaterials Trigger Remineralization and Antimicrobial Effects for Dental Caries Restoration.

Project description:Dental caries is the most prevalent chronic disease globally, significantly impacting individuals' quality of life. A key reason behind the failure of implanted restorations is their biological inactivity, meaning they are unable to form crosslinks with the surrounding tooth structures, thus making patients susceptible to implant loss and recurrent tooth decay. For the treatment of caries, antibacterial medicine and remineralization are effective means of treating the recurrence of caries. Owing to the rapid progression in the biomaterials field, several biomaterials have been reported to display antimicrobial properties and aid in dentin remineralization. Bioactive materials hold considerable potential in diminishing biofilm accumulation, inhibiting the process of demineralization, enabling dentin remineralization, and combating bacteria related to caries. Bioactive materials, such as fluoride, amorphous calcium phosphate, bioactive glass, collagen, and resin-based materials, have demonstrated their effectiveness in promoting dentin remineralization and exerting antibacterial effects on dental caries. However, the concentration of fluoride needs to be strictly controlled. Although amorphous calcium phosphate can provide the necessary calcium and phosphorus ions for remineralization, it falls short in delivering the mechanical strength required for oral mastication. Resin-based materials also offer different advantages due to the complexity of their design. In this review, we delve into the application of advanced bioactive materials for enhancing dentin remineralization and antibacterial properties. We eagerly anticipate future developments in bioactive materials for the treatment of dental caries.

| S-EPMC10489995 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data