Ba2Gd2(Si4O13): a silicate with finite Si4O13 chains.

ABSTRACT: The title compound, dibarium digadolinium(III) tetrasilicate, crystallized from a molybdate-based flux. It represents a new structure type and contains finite zigzag-shaped C(2)-symmetric Si(4)O(13) chains and Gd(2)O(12) dimers built of edge-sharing GdO(7) polyhedra. The [9+1]-coordinated Ba atoms are located in voids in the atomic arrangement. All atoms are in general positions except for one O atom, which lies on a twofold axis. The structure is compared with those of the few other known tetrasilicates.

SUBMITTER: Wierzbicka-Wieczorek M

PROVIDER: S-EPMC2855576 | biostudies-literature | 2010 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Ba2Gd2(Si4O13): a silicate with finite Si4O13 chains.

Wierzbicka-Wieczorek Maria M Kolitsch Uwe U Tillmanns Ekkehart E

Acta crystallographica. Section C, Crystal structure communications 20100203 Pt 3

The title compound, dibarium digadolinium(III) tetrasilicate, crystallized from a molybdate-based flux. It represents a new structure type and contains finite zigzag-shaped C(2)-symmetric Si(4)O(13) chains and Gd(2)O(12) dimers built of edge-sharing GdO(7) polyhedra. The [9+1]-coordinated Ba atoms are located in voids in the atomic arrangement. All atoms are in general positions except for one O atom, which lies on a twofold axis. The structure is compared with those of the few other known tetra ...[more]

PMID: 20203391

Similar Datasets

Project description:The purpose of this study was to comparatively investigate the behavior of silicate and sol-silicate coatings non-modified or modified with an organosilane on wood and on wood pre-coated with silica-mineralized primers. Adhesion strength, morphology, and water permeability and related damages were studied to evaluate the possibility of utilizing such inorganic-based coating systems for durable protection of wood without or with relatively cheap and water-borne primers. Potassium silicate and potassium methylsiliconate aqueous solutions and a colloidal silica were used for the preparation of the coatings. The white coating paints were brushed on beech wood substrates at a rate of 220 g·m-2. The coatings exhibited good coverage ability. The pull-off adhesion strength values appeared to be related to pH following a polynomial law. The adhesion strength for the silicate coatings were adequate (above 3 MPa and up to 5 MPa) for wood, whereas the values for the sol-silicates were too low for practical applications. The adhesion values were in general higher for the samples cured in a climate room (23 ± 3 °C and 75 ± 2% relative humidity) than the samples cured in the ambient atmosphere of the laboratory (23 ± 3 °C and 25 ± 5% relative humidity). The presence of microdefects (cracks, holes) was revealed in the coating layers by optical and scanning electron microscopy. The surface roughness parameters assessed by confocal scanning laser microscopy were dependent on the magnification applied for their measurement. The arithmetic average roughness Sa was between 5 µm and 10 µm at magnification 5× and between 2.5 μm and 10 µm at magnification 20×. The maximum peak-to-valley height Sz confirmed the presence of open pores emerging through the coatings. The open pores constitute free pathways for water ingress through the coatings, and could explain the high water absorption of the coatings including the methysiliconate-containing silicate coating and despite the relatively high water contact angle and low wettability exhibited by this sample. The post-application of a hydrophobizing solution containing hexadecyltrimethoxysilane and dimethyloctadecyl[3-(trimethoxysilyl)propyl]ammonium chloride considerably reduced the water permeability, while application of nanosilica-containing organic primers increased the adhesion for the coatings. Silicate coatings with adhesion great enough and resistance against water damages can be generated on wood even without a primer using low silica-to-alkali ratio binders and an organosilane additive. The sol-silicate coatings appear to be applicable only with a primer. The improvement of the paint formulations to control the formation of microcracks and open pores could be useful to reduce the liquid water permeability and increase durability. Otherwise, the application of a hydrophobizing treatment can be used for this purpose.

Dataset Information

Ba2Gd2(Si4O13): a silicate with finite Si4O13 chains.

Publications

Ba2Gd2(Si4O13): a silicate with finite Si4O13 chains.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets