Scheelite-type NaDy(WO(4))(2).
Ontology highlight
ABSTRACT:
SUBMITTER: Zhao D
PROVIDER: S-EPMC2980022 | biostudies-literature | 2009 Dec
REPOSITORIES: biostudies-literature
Publications
Scheelite-type NaDy(WO(4))(2).
Zhao Dan D Li Feifei F Cheng Wendan W Zhang Hao H
Acta crystallographica. Section E, Structure reports online 20091212 Pt 1
The title compound sodium dysprosium(III) bis-[tungs-tate(VI)], NaDy(WO(4))(2), has been synthesized under high temperature solution growth (HTSG) conditions in air. The compound crystallizes with the scheelite structure and is composed of isolated WO(4) tetra-hedra ( symmetry) with one set of bond lengths and distorted [(Na/Dy)O(8)] dodeca-hedra ( symmetry; occupancy ratio Na:Dy = 1:1) with two sets of bond lengths. ...[more]
Similar Datasets
Project description:Explorations of the A(1+)-RE(3+)-Mo(6+)-O(2-) (A(1+) is an alkali metal cation, RE(3+) is a rare-earth metal cation) quaternary systems prepared by the high-temperature solution growth method led to the title structure, sodium erbium bis-(molyb-date), NaEr(MoO(4))(2). It is isostructural to the scheelite structure (CaWO(4)) and is composed of [MoO(4)](2-) tetra-hedra with symmetry and [(Na/Er)O(8)](14-) polyhedra. The [(Na/Er)O(8)](14-) polyhedron is a distorted tetra-gonal anti-prism, also with symmetry, with statistically mixed Na/Er atoms at its centre. There are two sets of Na/Er-O bond lengths [2.420?(4) and 2.435?(3)?Å], but just one set of Mo-O bond lengths [1.774?(4)?Å].
| S-EPMC2979262 | biostudies-literature
Project description:Scheelite-type NaNd[MoO(4)](2) contains one crystallographic position (site symmetry [Formula: see text]) for the large cations, which is mixed-occupied by Na(+) and Nd(3+) cations in a 1:1 molar ratio. Thus, both are surrounded by eight O atoms in the shape of a trigonal dodeca-hedron. Furthermore, the structure consists of crystallographically unique [MoO(4)](2-) units (site symmetry [Formula: see text]) surrounded by eight sodium and neodymium cations, which are all vertex-attached. The polyhedra around the Na(+)/Nd(3+) cations are connected to four others via common edges, building up a three-dimensional network in whose tetra-hedral voids of O atoms the Mo(6+) cations reside.
| S-EPMC3238578 | biostudies-literature
Project description:In scheelite-type La(0.667)[MoO(4)], one crystallographically unique position with site symmetry -4.. and an occupancy of 2/3 is found for the La(3+) cation. The cation is surrounded by eight O atoms in the shape of a trigonal dodeca-hedron. The structure also contains one [MoO(4)](2-) anion (site symmetry -4..), which is surrounded by eight vertex-attached La(3+) cations. The polyhedra around the La(3+) cations are inter-connected via common edges, building up a three-dimensional network, in the tetra-hedral voids of which the Mo(6+) cations reside.
| S-EPMC3569171 | biostudies-other
Project description:New polycrystalline SrMo1-xMxO4-δ (M = Fe and Cr) scheelite oxides have been prepared by topotactical oxidation, by annealing in air at 500 °C, from precursor perovskites with the stoichiometry SrMo1-xMxO3-δ (M = Fe and Cr). An excellent reversibility between the oxidized Sr(Mo,M)O4-δ scheelite and the reduced Sr(Mo,M)O3-δ perovskite phase accounts for the excellent behavior of the latter as anode material in solid-oxide fuel cells. A characterization by X-ray powder diffraction (XRD) and neutron powder diffraction (NPD) has been carried out to determine the crystal structure features. The scheelite oxides are tetragonal, space group I41/a (No. 88). The Rietveld-refinement from NPD data at room temperature shows evidence of oxygen vacancies in the structure, due to the introduction of Fe3+/Cr4+ cations in the tetrahedrally-coordinated B sublattice, where Mo is hexavalent. A thermal analysis of the reduced perovskite (SrMo1-xMxO3-δ) in oxidizing conditions confirms the oxygen stoichiometry obtained by NPD data; the stability range of the doped oxides, below 400-450 °C, is lower than that for the parent SrMoO3 oxide. The presence of a Mo4+/Mo5+ mixed valence in the reduced SrMo1-xMxO3-δ perovskite oxides confers greater instability against oxidation compared with the parent oxide. Finally, an XPS study confirms the surface oxidation states of Mo, Fe, and Cr in the oxidized samples SrMo0.9Fe0.1O4-δ and SrMo0.8Cr0.2O4-δ.
| S-EPMC7578960 | biostudies-literature
Project description:A set of new triple molybdates, LixNa1-xCaGd0.5(MoO4)3:Ho3+0.05/Yb3+0.45, was successfully manufactured by the microwave-accompanied sol-gel-based process (MAS). Yellow molybdate phosphors LixNa1-xCaGd0.5(MoO4)3:Ho3+0.05/Yb3+0.45 with variation of the LixNa1-x (x = 0, 0.05, 0.1, 0.2, 0.3) ratio under constant doping amounts of Ho3+ = 0.05 and Yb3+ = 0.45 were obtained, and the effect of Li+ on their spectroscopic features was investigated. The crystal structures of LixNa1-xCaGd0.5(MoO4)3:Ho3+0.05/Yb3+0.45 (x = 0, 0.05, 0.1, 0.2, 0.3) at room temperature were determined in space group I41/a by Rietveld analysis. Pure NaCaGd0.5Ho0.05Yb0.45(MoO4)3 has a scheelite-type structure with cell parameters a = 5.2077 (2) and c = 11.3657 (5) Å, V = 308.24 (3) Å3, Z = 4. In Li-doped samples, big cation sites are occupied by a mixture of (Li,Na,Gd,Ho,Yb) ions, and this provides a linear cell volume decrease with increasing Li doping level. The evaluated upconversion (UC) behavior and Raman spectroscopic results of the phosphors are discussed in detail. Under excitation at 980 nm, the phosphors provide yellow color emission based on the 5S2/5F4 → 5I8 green emission and the 5F5 → 5I8 red emission. The incorporated Li+ ions gave rise to local symmetry distortion (LSD) around the cations in the substituted crystalline structure by the Ho3+ and Yb3+ ions, and they further affected the UC transition probabilities in triple molybdates LixNa1-xCaGd0.5(MoO4)3:Ho3+0.05/Yb3+0.45. The complex UC intensity dependence on the Li content is explained by the specificity of unit cell distortion in a disordered large ion system within the scheelite crystal structure. The Raman spectra of LixNa1-xCaGd0.5(MoO4)3 doped with Ho3+ and Yb3+ ions were totally superimposed with the luminescence signal of Ho3+ ions in the range of Mo-O stretching vibrations, and increasing the Li+ content resulted in a change in the Ho3+ multiplet intensity. The individual chromaticity points (ICP) for the LiNaCaGd(MoO4)3:Ho3+,Yb3+ phosphors correspond to the equal-energy point in the standard CIE (Commission Internationale de L'Eclairage) coordinates.
| S-EPMC8659099 | biostudies-literature
Project description:Previous studies have shown that Pb-BHA complexes (lead complexes of benzohydroxamic acid) have better collecting ability and can be used in flotation experiments with BHA acting as a collector and lead ions acting as activators. However, the structures of Pb-BHA complexes adsorbed on a mineral surface remain unclear. In this work, the adsorption behavior of Pb-BHA complexes on the scheelite surface was studied by flotation experiments and adsorption capacity measurements, and the structures of the adsorbed Pb-BHA complexes were determined using X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (TOF-SIMS). The adsorption capacity results showed that more BHA was adsorbed on the scheelite surface in Pb-BHA flotation, and the XPS and TOF-SIMS analysis showed that the species of Pb-BHA complexes adsorbed on the scheelite surface were similar in activation flotation and Pb-BHA flotation. Therefore, the different contents of the complexes on the scheelite surface were responsible for the flotation behavior. XPS and TOF-SIMS showed that BHA combined with lead ions to form complexes with different structures, such as five- and four-membered ring structures. Structure fragment inference based on the measurements indicated that lead ions formed monomer complexes with two BHAs, and that lead hydroxide polymers with a certain degree of polymerization bonded with oxygen atoms in the complexes. The Pb-BHA complexes combine with oxygen atoms on the scheelite surface to form an adsorbate, rendering the surface hydrophobic.
| S-EPMC6798039 | biostudies-literature
Project description:A traditional semiconductor (WO₃) was synthesized from different precursors via hydrothermal crystallization targeting the achievement of three different crystal shapes (nanoplates, nanorods and nanostars). The obtained WO₃ microcrystals were analyzed by the means of X-ray diffraction (XRD), scanning electron microscopy (SEM) and diffuse reflectance spectroscopy (DRS). These methods contributed to the detailed analysis of the crystal morphology and structural features. The synthesized bare WO₃ photocatalysts were totally inactive, while the P25/WO₃ composites were efficient under UV light radiation. Furthermore, the maximum achieved activity was even higher than the bare P25's photocatalytic performance. A correlation was established between the shape of the WO₃ crystallites and the observed photocatalytic activity registered during the degradation of different substrates by using P25/WO₃ composites.
| S-EPMC5502922 | biostudies-other
Project description:The primary purpose of this study is to investigate the effects of hydrodynamic and acoustic cavitation (HAC) on the leaching efficiency of tungsten. The aim is to reduce energy use and to improve the recovery rate. The goal is also to carry out a leaching process at a much lower temperature than in an autoclave process that is currently used in the industry. Energy-efficient initiation and collapse of cavitation bubbles require optimization of (i) vibro-acoustic response of the reactor structure, (ii) multiple excitation frequencies adapted to the optimized reactor geometry, and (iii) hydrodynamic cavitation with respect to orifice geometry and flow conditions. The objective is to modify and apply a previously in house developed high power cavitation reactor in order to recover tungsten by leaching of the dissolution of scheelite in sodium hydroxide. In this process, various experimental conditions like dual-frequency excitation, different orifice geometry have been investigated. The numerically optimized reactor concept was excited by two frequencies 23 kHz and 39-43 kHz in various flow conditions. The effects of leaching time, leaching temperature, ultrasonic power and geometry of orifice plates have been studied.The leaching temperature was varied from 40 °C to 80 °C. The concentration of leaching reagent sodium hydroxide (NaOH) was 10 mol/L.The results were compared to conventional chemical leaching. Energy supplement with acoustic cavitation of 130 kWh/kg concentrate resulted in a leaching recovery of tungsten (WO3) of 71.5%, compared to 36.7% obtained in absence of ultrasound. The results confirm that the method developed is energy efficient and gives a recovery rate potentially better than current autoclave technology.
| S-EPMC7786575 | biostudies-literature
Project description:The title compound, dineodymium(III) tris-[tungstate(VI)], is a member of the Eu(2)(WO(4))(3) structure family and crystallizes isotypically with other rare earth tungstates and molybdates of this formula type. The structure is a derivative of the scheelite (CaWO(4)) structure and can be considered as an ordered defect variant with a threefold scheelite supercell and one rare earth (RE) site unoccupied. The Nd(3+) cations are coordinated by eight O atoms in form of a distorted bicapped trigonal prism. The two unique W cations are tetra-hedrally surrounded by O atoms. One WO(4) tetra-hedron has 2 symmetry and is relatively undistorted whereas the other tetra-hedron differs considerably from an ideal geometry. This is caused by an additional remote O atom at a distance of 2.149?(4)?Å. The resulting WO(4 + 1) polyhedra form W(2)O(8) dimers through edge-sharing. Together with the WO(4) and NdO(8) units, the three-dimensional set-up is accomplished.
| S-EPMC2969527 | biostudies-literature
Project description:Dicaesium bis-muth(III) phosphate(V) tungstate(VI), Cs(2)Bi(PO(4))(WO(4)), has been synthesized during complex investigation in a molten pseudo-quaternary Cs(2)O-Bi(2)O(3)-P(2)O(5)-WO(3) system. It is isotypic with K(2)Bi(PO(4))(WO(4)). The three-dimensional framework is built up from [Bi(PO(4))(WO(4))] nets, which are organized by adhesion of [BiPO(4)] layers and [WO(4)] tetra-hedra above and below of those layers. The inter-stitial space is occupied by Cs atoms. Bi, W and P atoms lie on crystallographic twofold axes.
| S-EPMC2970136 | biostudies-other