K(0.53)Mn(2.37)Fe(1.24)(PO(4))(3).

ABSTRACT: During an attempt to crystallize potassium manganese diiron phosphate KMnFe(2)(PO(4))(3) by the flux method, a new phase, potassium dimanganese iron triphosphate, K(0.53)Mn(2.37)Fe(1.24)(PO(4))(3), was isolated. This phase, whose composition was confirmed by ICP analysis, is isotypic with the alluaudite-like phosphates, thus it exhibits the (A2)(A'2)(A1)(A'1)(A''1)(M1)(M2)(2)(PO(4))(3) general formula. The site occupancies led to the following cation distribution: 0.53?K on A'2 (site symmetry 2), 0.31 Mn on A''1, 1.0 Mn on M1 (site symmetry 2) and (0.62 Fe + 0.38 Mn) on M2. The structure is built up from infinite chains of edge-sharing M1O(6) and M2O(6) octa-hedra. These chains run along [10] and are connected by two different PO(4) tetrahedra, one of which exhibits 2 symmetry. The resulting three-dimensional framework delimits large tunnels parallel to [001], which are partially occupied by the K(+) and Mn(2+) cations.

SUBMITTER: Hidouri M

PROVIDER: S-EPMC3050314 | biostudies-literature | 2010 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

K(0.53)Mn(2.37)Fe(1.24)(PO(4))(3).

Hidouri Mourad M Ben Amara Mongi M

Acta crystallographica. Section E, Structure reports online 20101211 Pt 1

During an attempt to crystallize potassium manganese diiron phosphate KMnFe(2)(PO(4))(3) by the flux method, a new phase, potassium dimanganese iron triphosphate, K(0.53)Mn(2.37)Fe(1.24)(PO(4))(3), was isolated. This phase, whose composition was confirmed by ICP analysis, is isotypic with the alluaudite-like phosphates, thus it exhibits the (A2)(A'2)(A1)(A'1)(A''1)(M1)(M2)(2)(PO(4))(3) general formula. The site occupancies led to the following cation distribution: 0.53 K on A'2 (site symmetry 2) ...[more]

PMID: 21522509

Similar Datasets

NASICON-related Na?.?Mn?.?Fe?.?(PO?)?.

Project description:The solid solution, sodium [iron(III)/manganese(II)] tris-(orthophosphate), Na?.?Mn?.?Fe?.?(PO?)?, was obtained using a flux method. Its crystal structure is related to that of NASICON-type compounds. The [(Mn/Fe)?(PO?)?] framework is built up from an (Mn/Fe)O?octa-hedron (site symmetry 3.), with a mixed Mn/Fe occupancy, and a PO? tetra-hedron (site symmetry .2). The Na? cations are distributed over two partially occupied sites in the cavities of the framework. One Na? cation (site symmetry -3.) is surrounded by six O atoms, whereas the other Na? cation (site symmetry .2) is surrounded by eight O atoms.

| S-EPMC3393140 | biostudies-literature

KMg(0.09)Fe(1.91)(PO(4))(2).

Project description:KMg(0.09)Fe(1.91)(PO(4))(2), potassium [iron(II)/magnesium] iron(III) bis(orthophosphate), is a solid solution derived from compounds with general formula KM(II)Fe(PO(4))(2) (M(II) = Fe, Cu), in which the Mg atoms substitute Fe atoms only in the octa-hedrally surrounded sites. The framework of the structure is built up from [FeO(5)] trigonal bipyramids and [MO(6)] (M = (Fe, Mg) octa-hedra sharing corners and edges and connected by two types of bridging PO(4) tetra-hedra. The K(+) cations are nine-coordinated and are situated in channels running along [101].

| S-EPMC3379059 | biostudies-literature

Root shotgun proteomics from Fe- and Mn-deficient and Mn-toxic tomato plants

Project description:The aim of this work was to study the effects of Fe and Mn deficiencies and Mn toxicity on the protein profile of the root of tomato (Solanum lycopersicum), with the aim of elucidating plant response mechanisms to these nutritional stresses. Tomato was chosen as a model plant because the tomato genome has been published. The high-throughput shotgun analysis has permitted to identify and quantitate a large number of low abundance proteins in the tomato root. Protein identification was carried out using the Mascot search engine and the non-redundant databases NCBInr and ITAG v2.3.

2018-08-06 | PXD008326 | Pride

Xylem sap shotgun proteomics from Fe- and Mn-deficient and Mn-toxic tomato plants

Project description:The aim of this work was to study the effects of Fe and Mn deficiencies and Mn toxicity on the protein profile of the xylem sap of tomato (Solanum lycopersicum), with the aim of elucidating plant response mechanisms to these nutritional stresses. Tomato was chosen as a model plant because the tomato genome has been published and this plant species has adequate root pressure and turgid stems that permit xylem sap sampling in sufficient amounts by de-topping. The high-throughput shotgun analysis has permitted to identify and quantitate a large number of low abundance proteins in the tomato xylem sap.

2017-11-30 | PXD007517 | Pride

Is Mn(I) More Promising Than Fe(II)-A Comparison of Mn vs Fe Complexes for Olefin Metathesis.

Project description:Olefin metathesis is one of the most significant transformations in organic chemistry and is an excellent example for efficient homogeneous catalysis. Although most currently used catalysts are primarily based on 4d and 5d metals, cycloaddition and cycloreversion reactions can also be attributed to first-row transition metals, such as Fe. Surprisingly, the potential of Mn(I)-based catalysts for olefin metathesis has been unexplored despite their prominence in homogeneous catalysis and their diagonal relationship to Ru(II). In the present study, we have investigated the prospective capabilities of Mn complexes for cycloaddition and reversion reactions using density functional theory. Therefore, we have initially compared the literature known iron model systems and their isoelectronic Mn counterparts regarding their reactivity and electronic structure. Next, we constructed potential Mn complexes derived from synthetically accessible species, including carbonyl ligands and obeying octahedral geometry. Based on thermodynamic parameters and the calculation of electronic descriptors, we were able to validate the isodiagonal relationship. Our study serves as guidance for the experimental chemist.

| S-EPMC10900517 | biostudies-literature

Effect of Mn and Fe on the Formation of Fe- and Mn-Rich Intermetallics in Al-5Mg-Mn Alloys Solidified Under Near-Rapid Cooling.

Project description:Mn was an important alloying element used in Al-Mg-Mn alloys. However, it had to be limited to a low level (<1.0 wt %) to avoid the formation of coarse intermetallics. In order to take full advantage of the benefits of Mn, research was carried out to investigate the possibility of increasing the content of Mn by studying the effect of cooling rate on the formation of Fe- and Mn-rich intermetallics at different content levels of Mn and Fe. The results indicated that in Al-5Mg-Mn alloy with low Fe content (<0.1 wt %), intermetallic Al₆(Fe,Mn) was small in size and amount. With increasing Mn content, intermetallic Al₆(Fe,Mn) increased, but in limited amount. In high-Fe-containing Al-5Mg-Mn alloys (0.5 wt % Fe), intermetallic Al₆(Fe,Mn) became the dominant phase, even in the alloy with low Mn content (0.39 wt %). Cooling rate played a critical role in the refinement of the intermetallics. Under near-rapid cooling, intermetallic Al₆(Fe,Mn) was extremely refined. Even in the high Mn and/or high-Fe-containing alloys, it still demonstrated fine Chinese script structures. However, once the alloy composition passed beyond the eutectic point, the primary intermetallic Al₆(Fe,Mn) phase displayed extremely coarse platelet-like morphology. Increasing the content of Fe caused intermetallic Al₆(Fe,Mn) to become the primary phase at a lower Mn content.

| S-EPMC5456489 | biostudies-other

Spontaneous Formation of an Fe/Mn Diamond Core: Models for the Fe/Mn Sites in Class 1c Ribonucleotide Reductases.

Project description:A handful of oxygen-activating enzymes has recently been found to contain Fe/Mn active sites, like Class 1c ribonucleotide reductases and R2-like ligand-binding oxidase, which are closely related to their better characterized diiron cousins. These enzymes are proposed to form high-valent intermediates with Fe-O-Mn cores. Herein, we report the first examples of synthetic Fe/Mn complexes that mimic doubly bridged intermediates proposed for enzymatic oxygen activation. Fe K-edge extended X-ray absorption fine structure (EXAFS) analysis has been used to characterize the structures of each of these compounds. Linear compounds accurately model the Fe···Mn distances found in Fe/Mn proteins in their resting states, and doubly bridged diamond core compounds accurately model the distances found in high-valent biological intermediates. Unlike their diiron analogues, the paramagnetic nature of Fe/Mn compounds can be analyzed by EPR, revealing S = 1/2 signals that reflect antiferromagnetic coupling between the high-spin Fe(III) and Mn(III) units of heterobimetallic centers. These compounds undergo electron transfer with various ferrocenes, linear compounds being capable of oxidizing diacetyl ferrocene, a weak reductant, and diamond core compounds being capable of oxidizing acetyl ferrocene. Diamond core compounds can also perform HAT reactions from substrates with X-H bonds with bond dissociation free energies (BDFEs) up to 75 kcal/mol and are capable of oxidizing TEMPO-H at rates of 0.32-0.37 M-1 s-1, which are comparable to those reported for some mononuclear FeIII-OH and MnIII-OH compounds. However, such reactivity is not observed for the corresponding diiron compounds, a difference that Nature may have taken advantage of in evolving enzymes with heterobimetallic active sites.

| S-EPMC8997264 | biostudies-literature

Unsymmetrical bimetallic complexes with M(II)-(?-OH)-M(III) cores (M(II)M(III) = Fe(II)Fe(III), Mn(II)Fe(III), Mn(II)Mn(III)): structural, magnetic, and redox properties.

Project description:Heterobimetallic cores are important units within the active sites of metalloproteins but are often difficult to duplicate in synthetic systems. We have developed a synthetic approach for the preparation of a complex with a Mn(II)-(?-OH)-Fe(III) core, in which the metal centers have different coordination environments. Structural and physical data support the assignment of this complex as a heterobimetallic system. A comparison with analogous homobimetallic complexes, Mn(II)-(?-OH)-Mn(III) and Fe(II)-(?-OH)-Fe(III) cores, further supports this assignment.

| S-EPMC3826960 | biostudies-other

Improving the radiopacity of Fe-Mn biodegradable metals by magnetron-sputtered W-Fe-Mn-C coatings: Application for thinner stents.

Project description:In this exploratory work, micrometric radiopaque W-Fe-Mn-C coatings were produced by magnetron sputtering plasma deposition, for the first time, with the aim to make very thin Fe-Mn stents trackable by fluoroscopy. The power of Fe-13Mn-1.2C target was kept constant at 400 W while that of W target varied from 100 to 400 W producing three different coatings referred to as P100, P200, P400. The effect of the increased W power on coatings thickness, roughness, structure, corrosion behavior and radiopacity was investigated. The coatings showed a power-dependent thickness and W concentration, different roughness values while a similar and uniform columnar structure. An amorphous phase was detected for both P100 and P200 coatings while γ-Fe, bcc-W and W3C phases found for P400. Moreover, P200 and P400 showed a significantly higher corrosion rate (CR) compared to P100. The presence of W, W3C as well as the Fe amount variation determined two different micro-galvanic corrosion mechanisms significantly changing the CR of coatings, 0.26 ± 0.02, 59.68 ± 1.21 and 59.06 ± 1.16 μm/year for P100, P200 and P400, respectively. Sample P200 with its most uniform morphology, lowest roughness (RMS = 3.9 ± 0.4 nm) and good radiopacity (∼6%) appeared the most suitable radiopaque biodegradable coating investigated in this study.

| S-EPMC8777240 | biostudies-literature

Superplasticity in a lean Fe-Mn-Al steel.

Project description:Superplastic alloys exhibit extremely high ductility (>300%) without cracks when tensile-strained at temperatures above half of their melting point. Superplasticity, which resembles the flow behavior of honey, is caused by grain boundary sliding in metals. Although several non-ferrous and ferrous superplastic alloys are reported, their practical applications are limited due to high material cost, low strength after forming, high deformation temperature, and complicated fabrication process. Here we introduce a new compositionally lean (Fe-6.6Mn-2.3Al, wt.%) superplastic medium Mn steel that resolves these limitations. The medium Mn steel is characterized by ultrafine grains, low material costs, simple fabrication, i.e., conventional hot and cold rolling, low deformation temperature (ca. 650?°C) and superior ductility above 1300% at 850?°C. We suggest that this ultrafine-grained medium Mn steel may accelerate the commercialization of superplastic ferrous alloys.Research in new alloy compositions and treatments may allow the increased strength of mass-produced, intricately shaped parts. Here authors introduce a superplastic medium manganese steel which has an inexpensive lean chemical composition and which is suited for conventional manufacturing processes.

| S-EPMC5622104 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data