Immobilization of amphiphilic polycations by catechol functionality for antimicrobial coatings.

ABSTRACT: A new strategy for preparing antimicrobial surfaces by a simple dip-coating procedure is reported. Amphiphilic polycations with different mole ratios of monomers containing dodecyl quaternary ammonium, methoxyethyl, and catechol groups were synthesized by free-radical polymerization. The polymer coatings were prepared by immersing glass slides into a polymer solution and subsequent drying and heating. The quaternary ammonium side chains endow the coatings with potent antibacterial activity, the methoxyethyl side chains enable tuning the hydrophobic/hydrophilic balance, and the catachol groups promote immobilization of the polymers into films. The polymer-coated surfaces displayed bactericidal activity against Escherichia coli and Staphylococcus aureus in a dynamic contact assay and prevented the accumulation of viable E. coli, S. aureus, and Acinetobacter baumannii for up to 96 h. Atomic force microscopy (AFM) images of coating surfaces indicated that the surfaces exhibit virtually the same smoothness for all polymers except the most hydrophobic. The hydrophobic polymer without methoxyethyl side chains showed clear structuring into polymer domains, causing high surface roughness. Sum-frequency generation (SFG) vibrational spectroscopy characterization of the surface structures demonstrated that the dodecyl chains are predominantly localized at the surface-air interface of the coatings. SFG also showed that the phenyl groups of the catechols are oriented on the substrate surface. These results support our hypothesis that the adhesive or cross-linking functionality of catechol groups discourages polymer leaching, allowing the tuning of the amphiphilic balance by incorporating hydrophilic components into the polymer chains to gain potent biocidal activity.

SUBMITTER: Han H

PROVIDER: S-EPMC3071020 | biostudies-literature | 2011 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Immobilization of amphiphilic polycations by catechol functionality for antimicrobial coatings.

Han Hua H Wu Jianfeng J Avery Christopher W CW Mizutani Masato M Jiang Xiaoming X Kamigaito Masami M Chen Zhan Z Xi Chuanwu C Kuroda Kenichi K

Langmuir : the ACS journal of surfaces and colloids 20110310 7

A new strategy for preparing antimicrobial surfaces by a simple dip-coating procedure is reported. Amphiphilic polycations with different mole ratios of monomers containing dodecyl quaternary ammonium, methoxyethyl, and catechol groups were synthesized by free-radical polymerization. The polymer coatings were prepared by immersing glass slides into a polymer solution and subsequent drying and heating. The quaternary ammonium side chains endow the coatings with potent antibacterial activity, the ...[more]

PMID: 21391641

Similar Datasets

Project description:BackgroundBiofilm formation on medical device surfaces is a persistent problem that shelters bacteria and encourages infections and implant rejection. One promising approach to tackle this problem is to coat the medical device with an antimicrobial material. In this work, for the first time, we impart antimicrobial functionality to Ti3Au intermetallic alloy thin film coatings, while maintaining their superior mechanical hardness and biocompatibility.MethodsA mosaic Ti sputtering target is developed to dope controlled amounts of antimicrobial elements of Ag and Cu into a Ti3Au coating matrix by precise control of individual target power levels. The resulting Ti3Au-Ag/Cu thin film coatings are then systematically characterised for their structural, chemical, morphological, mechanical, corrosion, biocompatibility-cytotoxicity and antimicrobial properties.ResultsX-ray diffraction patterns reveal the formation of a super hard β-Ti3Au phase, but the thin films undergo a transition in crystal orientation from (200) to (211) with increasing Ag concentration, whereas introduction of Cu brings no observable changes in crystal orientation. Scanning and transmission electron microscopy analysis show the polyhedral shape of the Ti3Au crystal but agglomeration of Ag particles between crystal grains begins at 1.2 at% Ag and develops into large granules with increasing Ag concentration up to 4.1 at%. The smallest doping concentration of 0.2 at% Ag raises the hardness of the thin film to 14.7 GPa, a 360% improvement compared to the ∼4 GPa hardness of the standard Ti6Al4V base alloy. On the other hand, addition of Cu brings a 315-330% improvement in mechanical hardness of films throughout the entire concentration range of 0.5-7.1 at%. The thin films also show good electrochemical corrosion resistance and a > tenfold reduction in wear rate compared to Ti6Al4V alloy. All thin film samples exhibit very safe cytotoxic profiles towards L929 mouse fibroblast cells when analysed with Alamar blue assay, with ion leaching concentrations lower than 0.2 ppm for Ag and 0.08 ppm for Cu and conductivity tests reveal the positive effect of increased conductivity on myogenic differentiation. Antimicrobial tests show a drastic reduction in microbial survival over a short test period of < 20 min for Ti3Au films doped with Ag or Cu concentrations as low as 0.2-0.5 at%.ConclusionTherefore, according to these results, this work presents a new antimicrobial Ti3Au-Ag/Cu coating material with excellent mechanical performance with the potential to develop wear resistant medical implant devices with resistance to biofilm formation and bacterial infection.

Project description:Immobilizing particles on beads, fibers, or filaments, when only one side is exposed to the reaction medium and therefore can be selectively functionalized, is a scalable and easy to control strategy for the fabrication of amphiphilic Janus particles. Here we describe a new, robust method for the fabrication of amphiphilic Janus particles based on immobilization of polymethylsilsesquioxane (PMSQ) particles on polycarbonate (PC), a high impact-resistance polymer with superior mechanical properties. The immobilization of the particles on the PC microspores is performed via inverse solvent displacement method. PMSQ particles are added to a PC solution in tetrahydrofuran (THF), a good solvent for PC. The solution is then precipitated by the introduction of aqueous surfactant solution (antisolvent for PC) under an ultrasonic field. It is important to note that THF and water are miscible and do not form emulsion. During precipitation, PMSQ particles are assembled onto the surface of the PC spherical precipitates/microspheres. The exposed hemispheres of the PMSQ particles are then selectively silanized by (3-Aminopropyl)triethoxysilane (APTES) to introduce amine groups on their surface. To increase the polarity of the functionalized hemispheres, the amine groups are further modified to introduce carboxyl groups. SEM characterization confirms the fine embedment of PMSQ particles onto the PC microspheres. Covalent attachment of silica nanoparticles (NPs) to the functionalized hemispheres of the resulting particles along with fluorescent confocal microscopy conclusively prove the successful fabrication of amphiphilic Janus particles. The immobilization of particles onto highly rigid polymeric microspheres such as PC may pave the way for the development of a robust fabrication procedure with high resistance to temperature fluctuations and harsh mixing conditions that can arise during preparation. This method can be implemented toward a large variety of other synthetic commercial polymers such as polyamide, polyether sulfones, Polyether, ether ketone, or similar.

Dataset Information

Immobilization of amphiphilic polycations by catechol functionality for antimicrobial coatings.

Publications

Immobilization of amphiphilic polycations by catechol functionality for antimicrobial coatings.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets