Newkome-type dendron stabilized gold nanoparticles: Synthesis, reactivity, and stability.

ABSTRACT: We report the synthesis and evaluation of four Newkome-type dendrons, G1-COOH, G2-COOH, SH-G1-COOH, and TA-G1-COOH, and their respective gold-dendron conjugates, where GX represents the generation number. G1- and G2-COOH are 2-directional symmetric dendrons that have cystamine cores containing a disulfide group. SH-G1-COOH was prepared by treatment of G1-COOH with dithioerythritol to yield a free thiol group to replace the disulfide linkage. TA-G1-COOH has a thioctic acid moiety, which is a 5-member ring containing a disulfide group that cleaves to produce two anchoring thiols to bond with the gold surface. All dendrons have peripheral carboxylate groups to afford hydrophilicity and functionality. Gold nanoparticle conjugates were prepared by reaction of each dendron solution with a suspension of gold colloid (nominally 10 nm diameter) and purified by stirred cell ultrafiltration. Chemical structures were confirmed by (1)H and (13)C nuclear magnetic resonance spectroscopy and matrix assisted laser desorption/ionization time-of-flight mass spectrometry. Particle size and surface plasmon resonance of the conjugates were characterized by dynamic light scattering (DLS) and UV-Vis spectroscopy, respectively. X-ray photoelectron spectroscopy (XPS) was utilized to confirm covalent bonding between the thiols on the dendron and the gold surface. XPS also revealed changes in the S/Au intensity ratio as a function of the dendron chemical structure, suggesting steric effects play a role in the reaction and/or conformation of dendrons on the gold surface. The colloidal and chemical stability of the conjugates as a function of temperature, pH, and suspending medium, and with respect to chemical resistance toward KCN, was investigated using DLS and UV-Vis absorption.

SUBMITTER: Cho TJ

PROVIDER: S-EPMC3114632 | biostudies-literature | 2011 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Newkome-type dendron stabilized gold nanoparticles: Synthesis, reactivity, and stability.

Cho Tae Joon TJ Zangmeister Rebecca A RA Maccuspie Robert I RI Patri Anil K AK Hackley Vincent A VA

Chemistry of materials : a publication of the American Chemical Society 20110501 10

We report the synthesis and evaluation of four Newkome-type dendrons, G1-COOH, G2-COOH, SH-G1-COOH, and TA-G1-COOH, and their respective gold-dendron conjugates, where GX represents the generation number. G1- and G2-COOH are 2-directional symmetric dendrons that have cystamine cores containing a disulfide group. SH-G1-COOH was prepared by treatment of G1-COOH with dithioerythritol to yield a free thiol group to replace the disulfide linkage. TA-G1-COOH has a thioctic acid moiety, which is a 5-me ...[more]

PMID: 21686078

Similar Datasets

Project description:Confining Au nanoparticles (NPs) in a restricted space (e.g., zeolite micropores) is a promising way of overcoming their inherent thermal instability and susceptibility to aggregation, which limit catalytic applications. However, such approaches involve complex, multistep encapsulation processes. Here, we describe a successful strategy and its guiding principles for confining small (<2 nm) and monodisperse Au NPs within commercially available beta and MFI zeolites, which can oxidize CO at 40 °C and show size-selective catalysis. This protocol involves post-synthetic modification of the zeolite internal surface with thiol groups, which confines AuCl x species inside microporous frameworks during the activation process whereby Au precursors are converted into Au nanoparticles. The resulting beta and MFI zeolites contain uniformly dispersed Au NPs throughout the void space, indicating that the intrinsic stability of the framework promotes resistance to sintering. By contrast, in situ scanning transmission electron microscopy (STEM) studies evidenced that Au precursors in bare zeolites migrate from the matrix to the external surface during activation, thereby forming large and poorly dispersed agglomerates. Furthermore, the resistance of confined Au NPs against sintering is likely relevant to the intrinsic stability of the framework, supported by extended X-ray absorption fine structure (EXAFS), H2 chemisorption, and CO Fourier transform infrared (FT-IR) studies. The Au NPs supported on commercial MFI maintain their uniform dispersity to a large extent after treatment at 700 °C that sinters Au clusters on mesoporous silicas or beta zeolites. Low-temperature CO oxidation and size-selective reactions highlight that most gold NPs are present inside the zeolite matrix with a diameter smaller than 2 nm. These findings illustrate how confinement favors small, uniquely stable, and monodisperse NPs, even for metals such as Au susceptible to cluster growth under conditions often required for catalytic use. Moreover, this strategy may be readily adapted to other zeolite frameworks that can be functionalized by thiol groups.

Dataset Information

Newkome-type dendron stabilized gold nanoparticles: Synthesis, reactivity, and stability.

Publications

Newkome-type dendron stabilized gold nanoparticles: Synthesis, reactivity, and stability.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets