Symmetric pH-dependent swelling and antibacterial properties of chitosan brushes.

ABSTRACT: Charged polymer brushes grafted to surfaces are of great interest for antibacterial, biosensor, nanofluidic, and drug delivery applications. In this paper, chitosans with quaternary ammonium salts, CH-Q, were immobilized on silicon oxide and characterized by in situ quartz-crystal microbalance with dissipation, QCM-D, and in situ spectroscopic ellipsometry, SE. Both methods showed that the hydrated film exhibited a minimum thickness of ~40 nm near pH 5 that increased strongly (up to ~80 nm) at lower and higher pH. This symmetric swelling is surprising because CH-Q is a cationic polymer. The CH-Q grafted layer was stable for pH values from 3 to 8 and exhibited rapid, reversible swelling and contraction upon varying pH. The CH-Q layer also reduced S. aureus colonization by a factor of ~30× compared to bare silicon oxide and an amine terminated silane grafted to silicon oxide. This antibacterial characteristic of CH-Q is attributed to the quaternary ammonium salts and the flexible polymer brush.

SUBMITTER: Lee HS

PROVIDER: S-EPMC3191253 | biostudies-literature | 2011 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Symmetric pH-dependent swelling and antibacterial properties of chitosan brushes.

Lee Hyun-Su HS Eckmann David M DM Lee Daeyeon D Hickok Noreen J NJ Composto Russell J RJ

Langmuir : the ACS journal of surfaces and colloids 20110922 20

Charged polymer brushes grafted to surfaces are of great interest for antibacterial, biosensor, nanofluidic, and drug delivery applications. In this paper, chitosans with quaternary ammonium salts, CH-Q, were immobilized on silicon oxide and characterized by in situ quartz-crystal microbalance with dissipation, QCM-D, and in situ spectroscopic ellipsometry, SE. Both methods showed that the hydrated film exhibited a minimum thickness of ~40 nm near pH 5 that increased strongly (up to ~80 nm) at l ...[more]

PMID: 21894981

Similar Datasets

Project description:This study investigates the swelling of grafted polycationic brushes as a function of pH and anion type. The brushes are chitosan (CH) and chitosans with 27% and 51% degree of substitution (DS) of quaternary ammonium salt, denoted as CH-Q(25) and CH-Q(50), respectively. The water content and swelling behaviors are monitored using in situ quartz-crystal microbalance with dissipation (QCM-D). The pH varies from ~3.5 to 8.5, and the counter anion types include chloride, acetate, and citrate. At fixed pH, the water content and brush swelling increase as the DS increases. Whereas the CH-Q(50) brush layer shows symmetric swelling with a minimum near pH = 4.5, the swelling of CH and CH-Q(25) is relatively constant as pH decreases from 8.2 to 5.5, and then begins to increase near pH 4. These studies indicate that the symmetric swelling of CH-Q(50) is likely attributed to increasing protonation of primary amines for pH values below pH 6.5 and the quaternary ammonium salts above pH 6.5. At pH 4, the swelling of the CH brush increases upon exchanging the smaller chloridewith a bulkier acetate anion, which is less effective at screening intra/inter molecular repulsion. In contrast, upon exchanging the acetate with trifunctional citrate, CH and CH-Q(25) brushes collapse by 53 and 42%, respectively, because the citrate forms ionic cross-links. To test antibacterial properties, silicon oxide, CH and CH-Q(50) brush layers are exposed to 10(7)-10(8) cfu/ml of S. aureus for two days at 37 °C and exposed to stepped shear stresses in 2 min intervals. Whereas an S. aureus biofilm adheres strongly to silicon oxide and CH for stresses up to 12 dyne/cm(2), biofilms on CH-Q(50) detach at a relatively low shear stress, 1.5 dyne/cm(2). Due to their high degree of swelling that can be tuned via pH, counterion size and type, chitosan and quaternary modified chitosans have potential as responsive coatings for applications including MEMS/NEMS devices and drug eluting implants.

Dataset Information

Symmetric pH-dependent swelling and antibacterial properties of chitosan brushes.

Publications

Symmetric pH-dependent swelling and antibacterial properties of chitosan brushes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets