Controlling exchange bias in Fe3O4/FeO composite particles prepared by pulsed laser irradiation.

ABSTRACT: Spherical iron oxide nanocomposite particles composed of magnetite and wustite have been successfully synthesized using a novel method of pulsed laser irradiation in ethyl acetate. Both the size and the composition of nanocomposite particles are controlled by laser irradiation condition. Through tuning the laser fluence, the Fe3O4/FeO phase ratio can be precisely controlled, and the magnetic properties of final products can also be regulated. This work presents a successful example of the fabrication of ferro (ferri) (FM)/antiferromagnetic (AFM) systems with high chemical stability. The results show this novel simple method as widely extendable to various FM/AFM nanocomposite systems.

SUBMITTER: Swiatkowska-Warkocka Z

PROVIDER: S-EPMC3211284 | biostudies-literature | 2011 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Controlling exchange bias in Fe3O4/FeO composite particles prepared by pulsed laser irradiation.

Swiatkowska-Warkocka Zaneta Z Kawaguchi Kenji K Wang Hongqiang H Katou Yukiko Y Koshizaki Naoto N

Nanoscale research letters 20110316 1

Spherical iron oxide nanocomposite particles composed of magnetite and wustite have been successfully synthesized using a novel method of pulsed laser irradiation in ethyl acetate. Both the size and the composition of nanocomposite particles are controlled by laser irradiation condition. Through tuning the laser fluence, the Fe3O4/FeO phase ratio can be precisely controlled, and the magnetic properties of final products can also be regulated. This work presents a successful example of the fabric ...[more]

PMID: 21711758

Similar Datasets

Project description:This work thoroughly investigates chemical solvent-particles interactions during the formation of composite particles by pulsed laser melting of α-Fe2O3. Two solvents, with different dielectric constants, such as ethyl acetate (εr = 6) and ethanol (εr = 24.6), were examined in terms of their effect on the morphology, size, and phase composition of iron oxide composites. We calculated the laser fluence curves using the heating-melting-evaporation approach to identify the critical particle size that undergoes the phase changes first. We assessed the temperature of the particles irradiated with 390 mJ/pulse.cm2 in both solvents, including the heat dissipation between the particles and the liquid. The phase diagram of the Fe-O-C-H system was calculated to determine the temperature-pressure relationship of the system in equilibrium. We also employed an in situ GC-MS analysis to identify the volatile products during irradiation. Based on our experimental results, we concluded that the final diameter of the composites increases from 400 to 600 nm, along with the decreasing dielectric constant of the solvent, which is related to the different polarization of the organic liquid and the degree of particle agglomeration. The reduction of hematite in ethanol proceeded much faster, ending up with Fe/FeCx, while in ethyl acetate, it ended up with Fe3O4. Among all the particles, those with a diameter of 200 nm have the highest temperature and undergo the phase transition first. The temperature of a 200 nm composite particle in ethanol is slightly lower than in ethyl acetate, i.e. 1870 K as compared to 1902 K. Phase equilibrium diagrams proved the existence of Fe, FeO, and Fe3O4 as the preferred phases at about 1900 K. Our research provides a new insight into the process of submicron particle formation during pulsed laser irradiation and allows proposing a mechanism for the growth of particles of different size and phase composition depending on the solvent.

Project description:Therapeutic proteins and peptides are clinically important, offering potency while reducing the potential for off-target effects. Research interest in developing therapeutic polypeptides has grown significantly during the last four decades. However, despite the growing research effort, maintaining the stability of polypeptides throughout their life cycle remains a challenge. Electrohydrodynamic (EHD) techniques have been widely explored for encapsulation and delivery of many biopharmaceuticals. In this work, we explored monoaxial electrospraying for encapsulation of bovine liver catalase, investigating the effects of the different components of the electrospraying solution on the integrity and bioactivity of the enzyme. The catalase was successfully encapsulated within polymeric particles made of polyvinylpyrrolidone (PVP), dextran, and polysucrose. The polysorbate 20 content within the electrospraying solution (50 mM citrate buffer, pH 5.4) affected the catalase loading-increasing the polysorbate 20 concentration to 500 μg/mL resulted in full protein encapsulation but did not prevent loss in activity. The addition of ethanol (20% v/v) to a fully aqueous solution improves the electrospraying process by reducing surface tension, without loss of catalase activity. The polymer type was shown to have the greatest impact on preserving catalase activity within the electrosprayed particles. When PVP was the carrier there was no loss in activity compared with fresh aqueous solutions of catalase. The optimum particles were obtained from a 20% w/v PVP or 30% w/v PVP-trehalose (1:1 w/w) solution. The addition of trehalose confers stability advantages to the catalase particles. When trehalose-PVP particles were stored at 5 °C, enzymatic activity was maintained over 3 months, whereas for the PVP-only analogue a 50% reduction in activity was seen. This demonstrates that processing catalase by monoaxial electrospraying can, under optimised conditions, result in stable polymeric particles with no loss of activity.

Dataset Information

Controlling exchange bias in Fe3O4/FeO composite particles prepared by pulsed laser irradiation.

Publications

Controlling exchange bias in Fe3O4/FeO composite particles prepared by pulsed laser irradiation.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets