Solvothermal synthesis of uniform bismuth nanospheres using poly(N-vinyl-2-pyrrolidone) as a reducing agent.

ABSTRACT: Uniform bismuth nanospheres were successfully prepared from bismuth nitrate in the presence of poly(N-vinyl-2-pyrrolidone) (PVP) by solvothermal process. The product was characterized by powder X-ray diffraction, scanning electron microscopy, transmission electron microscopy, selected area electron diffraction, and energy-dispersive X-ray. PVP plays a critical role both as a reducing agent and a capping agent in the formation of bismuth nanospheres. Shape and size of bismuth nanospheres could be tuned by changing the employed PVP/bismuth salt ratio. It was also found the solvent had an effect on the morphologies of bismuth nanomaterials. The possible formation and growth mechanism of bismuth nanospheres were also discussed and proposed to explain the reduction step.

SUBMITTER: Wu J

PROVIDER: S-EPMC3212213 | biostudies-literature | 2011 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Solvothermal synthesis of uniform bismuth nanospheres using poly(N-vinyl-2-pyrrolidone) as a reducing agent.

Wu Jiliang J Qin Fan F Lu Zhong Z Yang Hai-Jian HJ Chen Rong R

Nanoscale research letters 20110112 1

Uniform bismuth nanospheres were successfully prepared from bismuth nitrate in the presence of poly(N-vinyl-2-pyrrolidone) (PVP) by solvothermal process. The product was characterized by powder X-ray diffraction, scanning electron microscopy, transmission electron microscopy, selected area electron diffraction, and energy-dispersive X-ray. PVP plays a critical role both as a reducing agent and a capping agent in the formation of bismuth nanospheres. Shape and size of bismuth nanospheres could be ...[more]

PMID: 21711606

Similar Datasets

Synthesis and physico-chemical properties of poly(N-vinyl pyrrolidone)-based hydrogels with titania nanoparticles.

Project description:Poly(N-vinyl pyrrolidone) (PVP)-based hydrogels with titania nanoparticles (TN) were synthesized by the sol-gel method for the first time and were characterized in different states (native, freeze-dried, air-dried to constant weight and ground to powder, or swollen to constant weight in H2O or D2O) by various methods such as wide-angle and small-angle X-ray and neutron scattering, neutron spin-echo (NSE) spectroscopy, and scanning electron microscopy. The static (static polymer-polymer correlation length (mesh size), associates of cross-links and PVP microchains) and dynamic (polymer chain relaxation rate, hydrodynamic polymer-polymer correlation length) structural elements were determined. The incorporation of titania nanoparticles into PVP hydrogel slightly increases the size of structural inhomogeneities (an increase in the static and dynamic polymer-polymer correlation length, the formation of associates of cross-links and PVP chains). Titania nanoparticles have an impact on the microstructure of the composite hydrogel and form associates with sizes from 0.5 to 2 µm attached to PVP hydrogel pore walls. The PVP and TN/PVP hydrogels show a high degree of water swelling. Moreover, the presence of titania nanoparticles in TN/PVP increases the number of water adsorption cycles compared to PVP hydrogel. The high swelling degree, bacteria-resistant and antimicrobial properties against Staphylococcus aureus allow considering NT/PVP hydrogels for medical applications as wound coatings.

| S-EPMC7222127 | biostudies-literature

Oxidation-Responsive Emulsions Stabilized with Poly(Vinyl Pyrrolidone-co-allyl Phenyl Sulfide).

Project description:Oxidation-responsive emulsions were obtained by stabilizing mineral oil droplets using amphiphilic poly(vinyl pyrrolidone-co-allyl phenyl sulfide) (P(VP-APS)). 1H nuclear magnetic resonance (NMR) spectroscopy revealed that P(VP-APS) whose APS content was 0%, 3.28%, 3.43% and 4.58% were successfully prepared by free radical reaction and the sulfide of APS was oxidized by H2O2 treatment. X-ray Photoelectron Spectroscopy (XPS) also disclosed that the sulfide of APS was oxidized to sulfone by the oxidizing agent. The optical density of copolymer solutions and the interfacial activity of the copolymers markedly decreased by H2O2 treatment possibly because the sulfide of APS was oxidized and the amphiphilicity of the copolymers were weakened. The increase rate of the oil droplet diameter of the emulsions was outstandingly promoted when H2O2 solution (10%, v/v) was used as an aqueous phase. The phase separation of the emulsions was also expedited by the oxidizing agent. The oxidation of APS and the weakened interfacial activity were thought to be a main reason for the demulsification of P(VP-APS)-stabilized emulsions.

| S-EPMC7077715 | biostudies-literature

Preparation and Properties of Electrospun Poly (Vinyl Pyrrolidone)/Cellulose Nanocrystal/Silver Nanoparticle Composite Fibers.

Project description:Poly (vinyl pyrrolidone) (PVP)/cellulose nanocrystal (CNC)/silver nanoparticle composite fibers were prepared via electrospinning using N,N'-dimethylformamide (DMF) as a solvent. Rheology, morphology, thermal properties, mechanical properties, and antimicrobial activity of nanocomposites were characterized as a function of material composition. The PVP/CNC/Ag electrospun suspensions exhibited higher conductivity and better rheological properties compared with those of the pure PVP solution. The average diameter of the PVP electrospun fibers decreased with the increase in the amount of CNCs and Ag nanoparticles. Thermal stability of electrospun composite fibers was decreased with the addition of CNCs. The CNCs help increase the composite tensile strength, while the elongation at break decreased. The composite fibers included Ag nanoparticles showed improved antimicrobial activity against both the Gram-negative bacterium Escherichia coli (E. coli) and the Gram-positive bacterium Staphylococcus aureus (S. aureus). The enhanced strength and antimicrobial performances of PVP/CNC/Ag electrospun composite fibers make the mat material an attractive candidate for application in the biomedical field.

| S-EPMC5456859 | biostudies-literature

Binary Graft of Poly(acrylic acid) and Poly(vinyl pyrrolidone) onto PDMS Films for Load and Release of Ciprofloxacin.

Project description:Polymers are versatile compounds which physical and chemical properties can be taken advantage of in wide applications. Particularly, in the biomedical field, polydimethylsiloxane (PDMS) is one of the most used for its high biocompatibility, easy manipulation, thermal, and chemical stability. Nonetheless, its hydrophobic nature makes it susceptible to bacterial pollution, which represents a disadvantage in this field. A potential solution to this is through the graft of stimuli-sensitive polymers that, besides providing hydrophilicity, allow the creation of a drug delivery system. In this research, PDMS was grafted with acrylic acid (AAc) and vinyl pyrrolidone (VP) in two steps using gamma radiation. The resulting material was analyzed by several characterization techniques such as infrared spectroscopy (FTIR), swelling, contact angle, critical pH, and thermogravimetric analysis (TGA), demonstrating the presence of both polymers onto PDMS films and showing hydrophilic and pH-response properties. Among the performed methods to graft, the loading and release of ciprofloxacin were successful in those samples obtained by direct irradiation method. Furthermore, the antimicrobial assays showed zones of inhibition for microorganisms such as Staphylococcus aureus and Escherichia coli.

| S-EPMC9861813 | biostudies-literature

One Step e-Beam Radiation Cross-Linking of Quaternary Hydrogels Dressings Based on Chitosan-Poly(Vinyl-Pyrrolidone)-Poly(Ethylene Glycol)-Poly(Acrylic Acid).

Project description:We report on the successful preparation of wet dressings hydrogels based on Chitosan-Poly(N-Vinyl-Pyrrolidone)-Poly(ethylene glycol)-Poly(acrylic acid) and Poly(ethylene oxide) by e-beam cross-linking in weakly acidic media, to be used for rapid healing and pain release of infected skin wounds. The structure and compositions of hydrogels investigated according to sol-gel and swelling studies, network parameters, as well as FTIR and XPS analyses showed the efficient interaction of the hydrogel components upon irradiation, maintaining the bonding environment while the cross-linking degree increasing with the irradiation dose and the formation of a structure with the mesh size in the range 11-67 nm. Hydrogels with gel fraction above 85% and the best swelling properties in different pH solutions were obtained for hydrogels produced with 15 kGy. The hydrogels are stable in the simulated physiological condition of an infected wound and show appropriate moisture retention capability and the water vapor transmission rate up to 272.67 g m-2 day-1, to ensure fast healing. The hydrogels proved to have a significant loading capacity of ibuprofen (IBU), being able to incorporate a therapeutic dose for the treatment of severe pains. Simultaneously, IBU was released up to 25% in the first 2h, having a release maximum after 8 h.

| S-EPMC7731230 | biostudies-literature

Exfoliation and Noncovalent Functionalization of Graphene Surface with Poly-N-Vinyl-2-Pyrrolidone by In Situ Polymerization.

Project description:Heteroatom functionalization on a graphene surface can endow the physical and structural properties of graphene. Here, a one-step in situ polymerization method was used for the noncovalent functionalization of a graphene surface with poly-N-vinyl-2-pyrrolidone (PNVP) and the exfoliation of graphite into graphene sheets. The obtained graphene/poly-N-vinyl pyrrolidone (GPNVP) composite was thoroughly characterized. The surface morphology of GPNVP was observed using field emission scanning electron microscopy and high-resolution transmission electron microscopy. Raman spectroscopy and X-ray diffraction studies were carried out to check for the exfoliation of graphite into graphene sheets. Thermogravimetric analysis was performed to calculate the amount of PNVP on the graphene surface in the GPNVP composite. The successful formation of the GPNVP composite and functionalization of the graphene surface was confirmed by various studies. The cyclic voltammetry measurement at different scan rates (5-500 mV/s) and electrochemical impedance spectroscopy study of the GPNVP composite were performed in the typical three-electrode system. The GPNVP composite has excellent rate capability with the capacitive property. This study demonstrates the one-pot preparation of exfoliation and functionalization of a graphene surface with the heterocyclic polymer PNVP; the resulting GPNVP composite will be an ideal candidate for various electrochemical applications.

| S-EPMC7999643 | biostudies-literature

Pressure-assisted solvent- and catalyst-free production of well-defined poly(1-vinyl-2-pyrrolidone) for biomedical applications.

Project description:In this work, we developed a fast, highly efficient, and environmentally friendly catalytic system for classical free-radical polymerization (FRP) utilizing a high-pressure (HP) approach. The application of HP for thermally-induced, bulk FRP of 1-vinyl-2-pyrrolidone (VP) allowed to eliminate the current limitation of ambient-pressure polymerization of 'less-activated' monomer (LAM), characterized by the lack of temporal control yielding polymers of unacceptably large disperisites and poor result reproducibility. By a simple manipulation of thermodynamic conditions (p = 125-500 MPa, T = 323-333 K) and reaction composition (two-component system: monomer and low content of thermoinitiator) well-defined poly(1-vinyl-2-pyrrolidone)s (PVP) in a wide range of molecular weights and low/moderate dispersities (M n = 16.2-280.5 kg mol-1, Đ = 1.27-1.45) have been produced. We have found that HP can act as an 'external' controlling factor that warrants the first-order polymerization kinetics for classical FRP, something that was possible so far only for reversible deactivation radical polymerization (RDRP) systems. Importantly, our synthetic strategy adopted for VP FRP enabled us to obtain polymers of very high M n in a very short time-frame (0.5 h). It has also been confirmed that VP bulk polymerization yields polymers with significantly lower glass transition temperatures (T g) and different solubility properties in comparison to macromolecules obtained during the solvent-assisted reaction.

| S-EPMC9054399 | biostudies-literature

Replacement of Poly(vinyl pyrrolidone) by Thiols: A Systematic Study of Ag Nanocube Functionalization by Surface-Enhanced Raman Scattering.

Project description:In this work, we used surface-enhanced Raman scattering (SERS) to monitor the replacement of poly(vinyl pyrrolidone) (PVP) on Ag nanocubes by cysteamine, thiol-terminated PEG, and benzenedithiol. PVP is widely used as a colloidal stabilizer and capping agent to control the shape of Ag (as well as many other noble metals) nanocrystals during synthesis, and to stabilize the final colloidal suspension. However, the surface chemistry of Ag nanocrystals often needs to be tailored for specific applications, so the PVP coating must be removed and/or replaced by other ligands. By monitoring the signature peak from the carbonyl groups of PVP, we show, for the first time, that the PVP adsorbed on the surface of Ag nanocubes was completely replaced by the thiol molecules at room temperature over the course of a few hours. We observed the same trend no matter if the Ag nanocubes were suspended in an aqueous solution of the thiol or supported on a silicon substrate and then immersed in the thiol solution.

| S-EPMC3279944 | biostudies-literature

Photopolymerized poly(l-lactide-<i>b-N</i>-vinyl-2-pyrrolidone) network resists cell adhesion <i>in situ</i>.

Project description:A three-armed star-shaped poly(l-lactide) (PLLA) oligomer was synthesized using glycerol to ring-opening and polymerize l-lactide. The resultant oligomer introduced photoreactive groups at the terminal of PLLA chains by a coupling reaction with monoethyl fumarate (FAME). Photopolymerizable resin has been prepared by mixing PLLA 3-FAME, N-vinyl-2-pyrrolidone (NVP) as a reactive diluent and Irgacure 2959 as a photoinitiator. The PLLA 3-FAME/NVP cross-linked network could be formed by UV curing and was characterized through mechanical property tests, cytotoxicity experiments and cell adhesion experiments. In the dry state, Young's modulus and tensile strength of the network were significantly higher than those of pure PLLA formed by fused deposition modeling (FDM) printing, due to the formation of the cross-linked net. In the wet state, however, Young's modulus and tensile strength of the network were reduced by less than those of PLLA since the water-absorbed NVP content was easy to stretch. Moreover, the resultant network not only exhibited no obvious cytotoxicity but also resisted the adhesion of L929 fibroblasts. Combined with Digital Light Processing (DLP) technology, the poly(l-lactide-b-N-vinyl-2-pyrrolidone) network may be widely used in the field of anti-adhesion barrier materials and/or biological anti-fouling materials with customization requirements.

| S-EPMC9034047 | biostudies-literature

Mutual Effects of Hydrogen Bonding and Polymer Hydrophobicity on Ibuprofen Crystal Inhibition in Solid Dispersions with Poly(N-vinyl pyrrolidone) and Poly(2-oxazolines).

Project description:Poly(N-vinyl pyrrolidone) (PVP), poly(2-methyl-2-oxazoline) (PMOZ), poly(2-ethyl-2-oxazoline) (PEOZ), poly(2-n-propyl-2-oxazoline) (PnPOZ), and poly(2-isopropyl-2-oxazoline) (PiPOZ) were used to prepare solid dispersions with ibuprofen (IB), a model poorly-water soluble drug. Dispersions, prepared by solvent evaporation, were investigated using powder X-ray diffractometry, differential scanning calorimetry, and FTIR spectroscopy; hydrogen bonds formed between IB and all polymers in solid dispersions. PMOZ, the most hydrophilic polymer, showed the poorest ability to reduce or inhibit the crystallinity of IB. In contrast, the more hydrophobic polymers PVP, PEOZ, PnPOZ, and PiPOZ provided greater but similar abilities to reduce IB crystallinity, despite the differing polymer hydrophobicity and that PiPOZ is semi-crystalline. These results indicate that crystallinity disruption is predominantly due to hydrogen bonding between the drug molecules and the polymer. However, carrier properties affected drug dissolution, where PnPOZ exhibited lower critical solution temperature that inhibited the release of IB, whereas drug release from other systems was consistent with the degree of ibuprofen crystallinity within the dispersions.

| S-EPMC8148000 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data