Crucial differences in the hydrolytic degradation between industrial polylactide and laboratory-scale poly(L-lactide).

ABSTRACT: The rate of degradation of large-scale synthesized polylactide (PLA) of industrial origin was compared with that of laboratory-scale synthesized poly(L-lactide) (PLLA) of similar molar mass. The structural discrepancy between the two material types resulted in a significant difference in degradation rate. Although the hydrolysis of industrial PLA was substantially faster than that of PLLA, the PLA material became less brittle and fragmented to a lesser extent during degradation. In addition, a comprehensive picture of the degradation of industrial PLA was obtained by subjecting different PLA materials to hydrolytic degradation at various temperatures and pH's for up to 182 days. The surrounding environment had no effect on the degradation rate at physiological temperature, but the degradation was faster in water than in a phosphate buffer after prolonged degradation at temperatures above the T(g). The degree of crystallinity had a greater influence than the degradation environment on the rate of hydrolysis. For a future use of polylactide in applications where bulk plastics are generally used today, for example plastic packages, the appropriate PLA grade must be chosen based on the conditions prevailing in the degradation environment.

SUBMITTER: Hoglund A

PROVIDER: S-EPMC3359772 | biostudies-literature | 2012 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Crucial differences in the hydrolytic degradation between industrial polylactide and laboratory-scale poly(L-lactide).

Höglund Anders A Odelius Karin K Albertsson Ann-Christine AC

ACS applied materials & interfaces 20120514 5

The rate of degradation of large-scale synthesized polylactide (PLA) of industrial origin was compared with that of laboratory-scale synthesized poly(L-lactide) (PLLA) of similar molar mass. The structural discrepancy between the two material types resulted in a significant difference in degradation rate. Although the hydrolysis of industrial PLA was substantially faster than that of PLLA, the PLA material became less brittle and fragmented to a lesser extent during degradation. In addition, a c ...[more]

PMID: 22563747

Similar Datasets

Project description:This methodology permits to simulate the performance of different Poly(D,L-lactide-co-glycolide) copolymer formulations (PDLGA) in the human body, to identify the more influencing variables on hydrolytic degradation and, thus, to estimate biopolymer degradation level. The PDLGA characteristic degradation trends, caused by hydrolysis processes, have been studied to define their future biomedical applications as dental scaffolds. For this purpose, the mass loss, pH, glass transition temperature (Tg) and absorbed water mass of the different biopolymers have been obtained from samples into a phosphate-buffered saline solution (PBS) with initial pH of 7.4, at 37°C (human body conditions). The mass loss has been defined as the variable that characterize the biopolymer degradation level. Its dependence relationship with respect to time, pH and biopolymer formulation has been modelled using statistical learning tools. Namely, generalized additive models (GAM) and nonlinear mixed-effects regression with logistic and asymptotic functions have been applied. GAM model provides information about the relevant variables and the parametric functions that relate mass loss, pH and time. Mixed effects are introduced to model and estimate the degradation properties, and to compare the PDLGA biopolymer populations. The degradation path for each polymer formulation has been estimated and compared with respect to the others for helping to use the proper polymer for each specific medical application, performing selection criteria. It was found that the mass loss differences in PDLGA copolymers are strongly related with the way the pH decay versus time, due to carboxylic acid groups formation. This may occur in those environments in which the degradation products remain relatively confined with the non degraded mass. This is the case emulated with the present experimental procedure. The results show that PDLGA polymers degradation degree, in terms of half life and degradation rate, is increasing when acid termination is included, when DL-lactide molar ratio is reduced, decreasing the midpoint viscosity, or when glycolide is not included.

Dataset Information

Crucial differences in the hydrolytic degradation between industrial polylactide and laboratory-scale poly(L-lactide).

Publications

Crucial differences in the hydrolytic degradation between industrial polylactide and laboratory-scale poly(L-lactide).

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets