Thermosensitive multilayer hydrogels of poly(N-vinylcaprolactam) as nanothin films and shaped capsules.

ABSTRACT: We report on nanothin multilayer hydrogels of cross-linked poly(N-vinylcaprolactam) (PVCL) that exhibit distinctive and reversible thermoresponsive behavior. The single-component PVCL hydrogels were produced by selective cross-linking of PVCL in layer-by-layer films of PVCL-NH(2) copolymers assembled with poly(methacrylic acid) (PMAA) via hydrogen bonding. The degree of the PVCL hydrogel film shrinkage, defined as the ratio of wet thicknesses at 25°C to 50°C, was demonstrated to be 1.9±0.1 and 1.3±0.1 for the films made from PVCL-NH(2)-7 and PVCL-NH(2)-14 copolymers, respectively. No temperature-responsive behavior was observed for non-cross-linked two-component films due to the presence of PMAA. We also demonstrated that temperature-sensitive PVCL capsules of cubical and spherical shapes could be fabricated as hollow hydrogel replicas of inorganic templates. The cubical (PVCL)(7) capsules retained their cubical shape when temperature was elevated from 25°C to 50°C exhibiting 21±1% decrease in the capsule size. Spherical hydrogel capsules demonstrated similar shrinkage of 23±1%. The temperature-triggered capsule size changes were completely reversible. Our work opens new prospects for developing biocompatible and nanothin hydrogel-based coatings and containers for temperate-regulating drug delivery, cellular uptake, sensing, and transport behavior in microfluidic devices.

SUBMITTER: Liang X

PROVIDER: S-EPMC3472452 | biostudies-literature | 2012 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Thermosensitive multilayer hydrogels of poly(N-vinylcaprolactam) as nanothin films and shaped capsules.

Liang Xing X Kozlovskaya Veronika V Chen Yi Y Zavgorodnya Oleksandra O Kharlampieva Eugenia E

Chemistry of materials : a publication of the American Chemical Society 20120801 19

We report on nanothin multilayer hydrogels of cross-linked poly(N-vinylcaprolactam) (PVCL) that exhibit distinctive and reversible thermoresponsive behavior. The single-component PVCL hydrogels were produced by selective cross-linking of PVCL in layer-by-layer films of PVCL-NH(2) copolymers assembled with poly(methacrylic acid) (PMAA) via hydrogen bonding. The degree of the PVCL hydrogel film shrinkage, defined as the ratio of wet thicknesses at 25°C to 50°C, was demonstrated to be 1.9±0.1 and 1 ...[more]

PMID: 23087543

Similar Datasets

Project description:Endophthalmitis is a rare, but serious, intravitreal inflammatory disorder that can arise after cataract surgery. The intracameral injection of 1 mg cefuroxime (CEF) followed by three-times daily antibiotic topical administration for a week is generally recognized as the routine method of prophylaxis after cataract surgery. This procedure is controversial because of both the low efficacy and the low adherence to therapy by elderly patients. A unique slow release antibiotic intravitreal injection could solve these problems. The objective of the present study was to design ophthalmic nanocomposite delivery systems based on in situ gelling formulations that undergo sol-to-gel transition upon change in temperature to prolong the effect of CEF. Oil in water (O/W) microemulsion (µE) and solid lipid nanoparticles (SLN), obtained with an innovative formulation technology called cold microemulsion dilution, were evaluated as ocular drug delivery systems for CEF. Drug entrapment efficiency up to 80% was possible by esterifying CEF with 1-dodecanol to obtain dodecyl-CEF (dCEF). Both dCEF-loaded SLN and µE were then added with Pluronic®F127 (20% w/v) to obtain a nanocomposite hydrogel-based long acting system. The prepared thermosensitive formulations were evaluated for their physical appearance, drug content, gelation temperature, injectability and rheological properties, in vitro release studies and stability studies. Moreover, cell proliferation assays on human retinal pigment epithelial ARPE-19 cells were performed to evaluate the influence of this innovative system on the cellular viability. In addition, minimal inhibitory concentration (MIC) was assessed for both CEF and dCEF, revealing the need of dCEF hydrolysis for the antimicrobial activity. Although further experimental investigations are required, the physico-chemical characterization of the nanocomposite hydrogels and the preliminary in vitro release studies highlighted the potential of these systems for the sustained release of CEF.

Project description:Soft nanoparticles are interesting materials due to their size, deformability, and ability to host guest molecules. Surface properties play an essential role in determining the fate of the particles in biological medium, and coating of the nanoparticles (and polymers) with carbohydrates has been found to be an efficient strategy for increasing their biocompatibility and fine-tuning other important properties such as aqueous solubility. In this work, soft nanogels of poly(N-vinylcaprolactam), PNVCL, were surface-functionalized with different glucose and maltose ligands, and the colloidal properties of the gels were analyzed. The PNVCL nanogels were first prepared via semibatch precipitation polymerization, where a comonomer, propargyl acrylate (PA), was added after preparticle formation. The aim was to synthesize "clickable" nanogels with alkyne groups on their surfaces. The nanogels were then functionalized with two separate azido-glucosides and azido-maltosides (containing different linkers) through a copper-catalyzed azide-alkyne cycloaddition (CuAAc) click reaction. The glucose and maltose bearing nanogels were thermoresponsive and shrank upon heating. Compared to the PNVCL-PA nanogel, the carbohydrate bearing ones were larger, more hydrophilic, had volume phase transitions at higher temperatures, and were more stable against salt-induced precipitation. In addition to investigating the colloidal properties of the nanogels, the carbohydrate recognition was addressed by studying the interactions with a model lectin, concanavalin A (Con A). The binding efficiency was not affected by the temperature, which indicates that the carbohydrate moieties are located on the gel surfaces, and are capable of interacting with other biomolecules independent of temperature. Thus, the synthesis produces nanogels, which have surface functions capable of biorelevant interactions and a thermoresponsive structure. These types of particles can be used for drug delivery.

Dataset Information

Thermosensitive multilayer hydrogels of poly(N-vinylcaprolactam) as nanothin films and shaped capsules.

Publications

Thermosensitive multilayer hydrogels of poly(N-vinylcaprolactam) as nanothin films and shaped capsules.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure