Endodontic release system for apexification with calcium hydroxide microspheres.

ABSTRACT: The use of calcium hydroxide (CH) as an intracanal medicament for apexification is widespread. However, because of a short residence time in the root canal, the CH must be refreshed frequently, increasing the number of appointments required and leading to patient non-compliance. We hypothesized that a core-/shell-structured CH microsphere system would lead to sustained slow release of calcium and hydroxide ions of CH for long periods of time, eliminating the need for multiple visits for apexification. In this study, calcium hydroxide microspheres (CHMSs) with a core/shell structure were prepared by an emulsion method. The CHMS shell was composed of alginate, which was crosslinked by the Ca(2+) released from the CH in the CHMSs. Therefore, this system provides a unique feedback loop that controls the release of ions from the CHMSs. The in vitro experiments from the root canals of extracted human teeth showed that the CHMSs had a sustained, slow release of Ca(2+), at a constant rate of approximately 2 to 3% per month from day one to the six-month endpoint of the experiment. After 6 months, 72.1 ± 5.8% of the total CH from the CHMSs remained in the root canals of the teeth, while only 46.9 ± 10.9% and 36.8 ± 7.5% remained from a commercial product (UltraCal(®)XS) and CH powder alone, respectively (p < 0.01). The pH of all of the formulations (CHMS, UltraCal(®) XS, and CH powder) in the extracted teeth never rose above 9 during the release period, indicating a buffering effect of the teeth. The core-/shell-structured CHMSs are, therefore, a promising delivery vehicle for the sustained slow release of Ca(2+) and OH(-) in the root canal.

SUBMITTER: Strom TA

PROVIDER: S-EPMC3525129 | biostudies-literature | 2012 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Endodontic release system for apexification with calcium hydroxide microspheres.

Strom T A TA Arora A A Osborn B B Karim N N Komabayashi T T Liu X X

Journal of dental research 20120822 11

The use of calcium hydroxide (CH) as an intracanal medicament for apexification is widespread. However, because of a short residence time in the root canal, the CH must be refreshed frequently, increasing the number of appointments required and leading to patient non-compliance. We hypothesized that a core-/shell-structured CH microsphere system would lead to sustained slow release of calcium and hydroxide ions of CH for long periods of time, eliminating the need for multiple visits for apexific ...[more]

PMID: 22914537

Similar Datasets

Project description:Calcium silicate-based materials are used to block the communication between the root canal and the periodontal ligament space. This brings the materials into contact with tissues and the potential for local and systemic elemental release and movement. The aim of the study was to evaluate the elemental release of bismuth from ProRoot MTA in contact with connective tissues after 30 and 180 days as well as any accumulation in peripheral organs using an animal model. Tricalcium silicate and hydroxyapatite containing 20% bismuth oxide (HAp-Bi) were used as controls. The null hypothesis was that bismuth migrates from tricalcium silicate-based materials when associated with silicon. The materials were examined using scanning electron microscopy, energy dispersive spectroscopy (SEM/EDS) and X-ray diffraction prior to implantation as well as using SEM/EDS, micro X-ray fluorescence and Raman spectroscopy after implantation to assess elemental presence in surrounding tissues. Histological analysis was used to evaluate the changes in tissue architecture and inductively coupled plasma mass spectrometry (ICP-MS) was used to investigate the elemental deposition. For the systemic investigation, routine blood analysis was performed and organs were obtained to evaluate the presence of bismuth and silicon using ICP-MS after acid digestion. In the histological analysis of the implantation sites, macrophages and multinucleated giant cells could be observed after 30 days which after 180 days became a chronic infiltrate; although, no major differences were identified in red and white blood cell analyses and biochemical tests. Implantation altered the materials as observed in the Raman analysis and bismuth was detected both locally and within kidney samples after both periods of analysis, indicating the potential for accumulation of bismuth in this organ. Smaller amounts of bismuth than observed in the kidney were also detected in blood, liver and brain for the ProRoot MTA and HAp-Bi after 180 days. Bismuth was released from the ProRoot MTA locally and was detected systemically and in samples without silicon; thus, the null hypothesis was rejected. The bismuth release demonstrated that this element accumulated both locally and systemically, mainly in the kidneys in comparison with brain and liver regardless of the material base.

Dataset Information

Endodontic release system for apexification with calcium hydroxide microspheres.

Publications

Endodontic release system for apexification with calcium hydroxide microspheres.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets