Top-down fabrication of sub-nanometre semiconducting nanoribbons derived from molybdenum disulfide sheets.

ABSTRACT: Developments in semiconductor technology are propelling the dimensions of devices down to 10 nm, but facing great challenges in manufacture at the sub-10 nm scale. Nanotechnology can fabricate nanoribbons from two-dimensional atomic crystals, such as graphene, with widths below the 10 nm threshold, but their geometries and properties have been hard to control at this scale. Here we find that robust ultrafine molybdenum-sulfide ribbons with a uniform width of 0.35 nm can be widely formed between holes created in a MoS2 sheet under electron irradiation. In situ high-resolution transmission electron microscope characterization, combined with first-principles calculations, identifies the sub-1 nm ribbon as a Mo5S4 crystal derived from MoS2, through a spontaneous phase transition. Further first-principles investigations show that the Mo5S4 ribbon has a band gap of 0.77 eV, a Young's modulus of 300GPa and can demonstrate 9% tensile strain before fracture. The results show a novel top-down route for controllable fabrication of functional building blocks for sub-nanometre electronics.

SUBMITTER: Liu X

PROVIDER: S-EPMC3644098 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Top-down Fabrication and Enhanced Active Area Electronic Characteristics of Amorphous Oxide Nanoribbons for Flexible Electronics.

Project description:Inorganic amorphous oxide semiconductor (AOS) materials such as amorphous InGaZnO (a-IGZO) possess mechanical flexibility and outstanding electrical properties, and have generated great interest for use in flexible and transparent electronic devices. In the past, however, AOS devices required higher activation energies, and hence higher processing temperatures, than organic ones to neutralize defects. It is well known that one-dimensional nanowires tend to have better carrier mobility and mechanical strength along with fewer defects than the corresponding two-dimensional films, but until now it has been difficult, costly, and impractical to fabricate such nanowires in proper alignments by either "bottom-up" growth techniques or by "top-down" e-beam lithography. Here we show a top-down, cost-effective, and scalable approach for the fabrication of parallel, laterally oriented AOS nanoribbons based on lift-off and nano-imprinting. High mobility (132?cm2/Vs), electrical stability, and transparency are obtained in a-IGZO nanoribbons, compared to the planar films of the same a-IGZO semiconductor.

| S-EPMC5516029 | biostudies-literature

Nickel particle-enabled width-controlled growth of bilayer molybdenum disulfide nanoribbons.

Project description:[Figure: see text].

| S-EPMC8664269 | biostudies-literature

Top-down synthesis of polyoxometalate-like sub-nanometer molybdenum-oxo clusters as high-performance electrocatalysts.

Project description:The top-down fabrication of catalytically active molecular metal oxide anions, or polyoxometalates, is virtually unexplored, although these materials offer unique possibilities, for catalysis, energy conversion and storage. Here, we report a novel top-down route, which enables the scalable synthesis and deposition of sub-nanometer molybdenum-oxo clusters on electrically conductive mesoporous carbon. The new approach uses a unique redox-cycling process to convert crystalline MoIVO2 particles into sub-nanometer molecular molybdenum-oxo clusters with a nuclearity of ∼1-20. The resulting molybdenum-oxo cluster/carbon composite shows outstanding, stable electrocatalytic performance for the oxygen reduction reaction with catalyst characteristics comparable to those of commercial Pt/C. This new material design could give access to a new class of highly reactive polyoxometalate-like metal oxo clusters as high-performance, earth abundant (electro-)catalysts.

| S-EPMC8146420 | biostudies-literature

Electrochemistry-assisted top-down characterization of disulfide-containing proteins.

Project description:Covalent disulfide bond linkage in a protein represents an important challenge for mass spectrometry (MS)-based top-down protein structure analysis as it reduces the backbone cleavage efficiency for MS/MS dissociation. This study presents a strategy for solving this critical issue via integrating electrochemistry (EC) online with a top-down MS approach. In this approach, proteins undergo electrolytic reduction in an electrochemical cell to break disulfide bonds and then undergo online ionization into gaseous ions for analysis by electron-capture dissociation (ECD) and collision-induced dissociation (CID). The electrochemical reduction of proteins allows one to remove disulfide bond constraints and also leads to increased charge numbers of the resulting protein ions. As a result, sequence coverage was significantly enhanced, as exemplified by β-lactoglobulin A (24 vs 75 backbone cleavages before and after electrolytic reduction, respectively) and lysozyme (5 vs 66 backbone cleavages before and after electrolytic reduction, respectively). This methodology is fast and does not need chemical reductants, which would have an important impact in high-throughput proteomics research.

| S-EPMC3661022 | biostudies-literature

Fabrication of Large-Area Molybdenum Disulfide Device Arrays Using Graphene/Ti Contacts.

Project description:Two-dimensional (2D) molybdenum disulfide (MoS2) is the most mature material in 2D material fields owing to its relatively high mobility and scalability. Such noticeable properties enable it to realize practical electronic and optoelectronic applications. However, contact engineering for large-area MoS2 films has not yet been established, although contact property is directly associated to the device performance. Herein, we introduce graphene-interlayered Ti contacts (graphene/Ti) into large-area MoS2 device arrays using a wet-transfer method. We achieve MoS2 devices with superior electrical and photoelectrical properties using graphene/Ti contacts, with a field-effect mobility of 18.3 cm2/V∙s, on/off current ratio of 3 × 107, responsivity of 850 A/W, and detectivity of 2 × 1012 Jones. This outstanding performance is attributable to a reduction in the Schottky barrier height of the resultant devices, which arises from the decreased work function of graphene induced by the charge transfer from Ti. Our research offers a direction toward large-scale electronic and optoelectronic applications based on 2D materials.

| S-EPMC8348625 | biostudies-literature

Correlation of Fabrication Methods and Enhanced Wear Performance in Nanoporous Anodic Aluminum Oxide with Incorporated Molybdenum Disulfide (MoS<sub>2</sub>) Nanomaterials.

Project description:Wear performance is integral to component longevity, minimizing industrial waste and excess energy costs in a wide variety of applications. Anodized aluminum oxide (AAO) has many beneficial properties leading to its wide use across industries as a surface treatment for many aluminum components, but the wear properties of the coating could be improved significantly. Here, we used an electrochemical method to incorporate molybdenum disulfide (MoS2), a nanomaterial used as a dry lubricant, to modify alloys of aluminum during AAO preparation. Using Raman spectroscopy and tribological scratch measurements, we thoroughly characterized the structure and wear behavior of the films. The MoS2 deposition procedure was optimal on aluminum 5052 anodized in higher acid concentrations, with friction coefficients at around 0.05 (~10× better than unmodified AAO). Changing anodization conditions to produce harder films with smaller pores led to worsened wear properties, likely because of lower MoS2 content. Studying a commercial MoS2/AAO film of a different Al alloy (7075) showed that a heat treatment step intended to fully convert all deposited MoSx species to MoS2 can adversely affect wear in some alloys. While Al 6061 and 1100 produced films with worse wear performance compared to Al 5052 or 7075, our results show evidence that acid cleaning after initial anodization likely removes residual alloying elements, affecting MoS2 incorporation. This study demonstrates a nanomaterial modified AAO film with superior wear characteristics to unmodified AAO and relates fabrication procedure, film structure, and practical performance.

| S-EPMC10934346 | biostudies-literature

Sensing the electrical activity of single ion channels with top-down silicon nanoribbons.

Project description:Using top-down fabricated silicon nanoribbons, we measure the opening and closing of ion channels alamethicin and gramicidin A. A capacitive model of the system is proposed to demonstrate that the geometric capacitance of the nanoribbon is charged by ion channel currents. The integration of top-down nanoribbons with electrophysiology holds promise for integration of electrically active living systems with artificial electronics.

| S-EPMC6390970 | biostudies-literature

Fabrication of MoSe<sub>2</sub> nanoribbons via an unusual morphological phase transition.

Project description:Transition metal dichalcogenides (TMDs) are a family of van der Waals layered materials exhibiting unique electronic, optical, magnetic and transport properties. Their technological potentials hinge critically on the ability to achieve controlled fabrication of desirable nanostructures, such as nanoribbons and nanodots. To date, nanodots/nanoislands have been regularly observed, while controlled fabrication of TMD nanoribbons remains challenging. Here we report a bottom-up fabrication of MoSe2 nanoribbons using molecular beam epitaxy, via an unexpected temperature-induced morphological phase transition from the nanodot to nanoribbon regime. Such nanoribbons are of zigzag nature, characterized by distinct chemical and electronic properties along the edges. The phase space for nanoribbon growth is narrowly defined by proper Se:Mo ratios, as corroborated experimentally using different Se fluxes, and supported theoretically using first-principles calculations that establish the crucial role of the morphological reconstruction of the bare Mo-terminated edge. The growth mechanism revealed should be applicable to other TMD systems.

| S-EPMC5418606 | biostudies-literature

Magnetism in semiconducting molybdenum dichalcogenides.

Project description:Transition metal dichalcogenides (TMDs) are interesting for understanding the fundamental physics of two-dimensional (2D) materials as well as for applications to many emerging technologies, including spin electronics. Here, we report the discovery of long-range magnetic order below T M = 40 and 100 K in bulk semiconducting TMDs 2H-MoTe2 and 2H-MoSe2, respectively, by means of muon spin rotation (?SR), scanning tunneling microscopy (STM), and density functional theory (DFT) calculations. The ?SR measurements show the presence of large and homogeneous internal magnetic fields at low temperatures in both compounds indicative of long-range magnetic order. DFT calculations show that this magnetism is promoted by the presence of defects in the crystal. The STM measurements show that the vast majority of defects in these materials are metal vacancies and chalcogen-metal antisites, which are randomly distributed in the lattice at the subpercent level. DFT indicates that the antisite defects are magnetic with a magnetic moment in the range of 0.9 to 2.8 ?B. Further, we find that the magnetic order stabilized in 2H-MoTe2 and 2H-MoSe2 is highly sensitive to hydrostatic pressure. These observations establish 2H-MoTe2 and 2H-MoSe2 as a new class of magnetic semiconductors and open a path to studying the interplay of 2D physics and magnetism in these interesting semiconductors.

| S-EPMC6303124 | biostudies-literature

Large-Scale Production of Large-Size Atomically Thin Semiconducting Molybdenum Dichalcogenide Sheets in Water and Its Application for Supercapacitor.

Project description:To progress from laboratory research to commercial applications, it is necessary to develop an effective method to prepare large quantities and high-quality of the large-size atomically thin molybdenum dichalcogenides (MoS2). Aqueous-phase processes provide a viable method for producing thin MoS2 sheets using organolithium-assisted exfoliation; unfortunately, this method is hindered by changing pristine semiconducting 2H phase to distorted metallic 1T phase. Recovery of the intrinsic 2H phase typically involves heating of the 1T MoS2 sheets on solid substrates at high temperature. This has restricted and hindered the utilization of 2H phase MoS2 sheets suspensions. Here, we demonstrate that the synergistic effect of the rigid planar structure and charged nature of organic salt such as imidazole (ImH) can be successfully used to produce atomically thin 2H-MoS2 sheets suspension in water. Moreover, lateral size and area of the exfoliated sheet can be up to 50??m and 1000??m(2), respectively. According to the XPS measurements, nearly 100% of the 2H-MoS2 sheets was successfully prepared. A composite paper supercapacitor using the exfoliated 2H-MoS2 and carbon nanotubes delivered a superior volumetric capacitance of ~410?F/cm(3). Therefore, the organic salts-assisted liquid-phase exfoliation has great potential for large-scale production of 2H-MoS2 suspensions for supercapacitor application.

| S-EPMC4881041 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data