Dual-porosity hollow nanoparticles for the immunoprotection and delivery of nonhuman enzymes.

ABSTRACT: Although enzymes of nonhuman origin have been studied for a variety of therapeutic and diagnostic applications, their use has been limited by the immune responses generated against them. The described dual-porosity hollow nanoparticle platform obviates immune attack on nonhuman enzymes paving the way to in vivo applications including enzyme-prodrug therapies and enzymatic depletion of tumor nutrients. This platform is manufactured with a versatile, scalable, and robust fabrication method. It efficiently encapsulates macromolecular cargos filled through mesopores into a hollow interior, shielding them from antibodies and proteases once the mesopores are sealed with nanoporous material. The nanoporous shell allows small molecule diffusion allowing interaction with the large macromolecular payload in the hollow center. The approach has been validated in vivo using l-asparaginase to achieve l-asparagine depletion in the presence of neutralizing antibodies.

SUBMITTER: Ortac I

PROVIDER: S-EPMC4059531 | biostudies-literature | 2014 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Dual-porosity hollow nanoparticles for the immunoprotection and delivery of nonhuman enzymes.

Ortac Inanc I Simberg Dmitri D Yeh Ya-san YS Yang Jian J Messmer Bradley B Trogler William C WC Tsien Roger Y RY Esener Sadik S

Nano letters 20140206 6

Although enzymes of nonhuman origin have been studied for a variety of therapeutic and diagnostic applications, their use has been limited by the immune responses generated against them. The described dual-porosity hollow nanoparticle platform obviates immune attack on nonhuman enzymes paving the way to in vivo applications including enzyme-prodrug therapies and enzymatic depletion of tumor nutrients. This platform is manufactured with a versatile, scalable, and robust fabrication method. It eff ...[more]

PMID: 24471767

Similar Datasets

Project description:Tunable glutathione (GSH)-sensitive hollow mesoporous silica nanoparticles (HMSiO2 NPs) were developed using a structural difference-based selective etching strategy. These organosilica hollow nanoparticles contained disulfide linkages (S-S) in the outer shell which were degraded by GSH. The particles were compared with their nonGSH-sensitive tetraethyl orthosilicate (TEOS) HMSiO2 counterparts in terms of their synthesis method, characterization, doxorubicin (DOX) release profile, and in vitro cytotoxicity in MCF-7 breast cancer cells. Transmission electron microscopy (TEM) of the particles indicated that the fabricated HMSiO2 NPs had an average diameter of 130?±?5?nm. Thermogravimetric analysis (TGA) revealed that GSH-sensitive particles had approximately 5.3% more weight loss than TEOS HMSiO2 NPs. Zeta potential of these redox-responsive particles was -23?±?1?mV at pH?6 in deionized (DI) water. Nitrogen adsorption-desorption isotherm revealed that the surface area of the hollow mesoporous nanoreservoirs was roughly 446?±?6?m2?g-1 and the average diameter of the pores was 2.3?±?0.5?nm. TEM images suggest that the nanoparticles started to lose mass integrity from Day 1. The particles showed a high loading capacity for DOX (8.9?±?0.5%) as a model drug, due to the large voids existing in the hollow structures. Approximately 58% of the incorporated DOX released within 14?days in phosphate buffered saline (PBS) at pH?6 and in the presence of 10?mM of GSH, mimicking intracellular tumor microenvironment while release from TEOS HMSiO2 NPs was only c.a. 18%. The uptake of these hollow nanospheres by MCF-7 cells and RAW 264.7 macrophages was evaluated using TEM and confocal microscopy. The nanospheres were shown to accumulate in the endolysosomal compartments after incubation for 24?h with the maximum uptake of c.a. 2.1?±?0.3% and 5.2?±?0.4%, respectively. Cytotoxicity of the nanospheres was investigated using CCK-8 assay. Results indicate that intact hollow particles (both GSH-sensitive and TEOS HMSiO2 NPs) were nontoxic to MCF-7 cells after incubation for 24?h within the concentration range of 0-1000??g?ml-1. DOX-loaded GSH-sensitive nanospheres containing 6??g?ml-1 of DOX killed c.a. 51% of MCF-7 cells after 24?h while TEOS HMSiO2 NPs killed c.a. 20% with the difference being statistically significant. Finally, cytotoxicity data in RAW 264.7 macrophages and NIH 3?T3 fibroblasts shows that intact GSH-sensitive HMSiO2 NPs did not show any toxic effects on these cells with the concentrations equal or <125??g?ml-1.

Dataset Information

Dual-porosity hollow nanoparticles for the immunoprotection and delivery of nonhuman enzymes.

Publications

Dual-porosity hollow nanoparticles for the immunoprotection and delivery of nonhuman enzymes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets