Adsorption of lead over graphite oxide.

ABSTRACT: The adsorption efficiency and kinetics of removal of lead in presence of graphite oxide (GO) was determined using the Atomic Absorption Spectrophotometer (AAS). The GO was prepared by the chemical oxidation of graphite and characterized using FTIR, SEM, TGA and XRD. The adsorption efficiency of GO for the solution containing 50, 100 and 150 ppm of Pb(2+) was found to be 98%, 91% and 71% respectively. The adsorption ability of GO was found to be higher than graphite. Therefore, the oxidation of activated carbon in removal of heavy metals may be a viable option to reduce pollution in portable water.

SUBMITTER: Olanipekun O

PROVIDER: S-EPMC4123955 | biostudies-literature | 2014 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Adsorption of lead over graphite oxide.

Olanipekun Opeyemi O Oyefusi Adebola A Neelgund Gururaj M GM Oki Aderemi A

Spectrochimica acta. Part A, Molecular and biomolecular spectroscopy 20131007

The adsorption efficiency and kinetics of removal of lead in presence of graphite oxide (GO) was determined using the Atomic Absorption Spectrophotometer (AAS). The GO was prepared by the chemical oxidation of graphite and characterized using FTIR, SEM, TGA and XRD. The adsorption efficiency of GO for the solution containing 50, 100 and 150 ppm of Pb(2+) was found to be 98%, 91% and 71% respectively. The adsorption ability of GO was found to be higher than graphite. Therefore, the oxidation of a ...[more]

PMID: 24152870

Similar Datasets

Synthesis and characterization of reduced graphite oxide-polymer composites and their application in adsorption of lead.

Project description:Herein, we report the in situ polymerization of 1,5-diaminonaphthalene (15DAN) and 1,4-diaminoanthraquinone (14DAA) on the surface of reduced graphite oxide (RGO). Synthesized RGO-P15DAN and RGO-P14DAA were characterized by FTIR, Raman, SEM, TGA and XRD. The adsorption capacity and adsorptivity of the synthesized composites were investigated by Atomic Absorption Spectroscopy (AAS) using 100 ppm aqueous solution of Pb(2+) ions. Further, we compared the results of the composites with those of poly 1,5-(diaminonaphthalene) (P15DAN), poly 1,4-(diaminoanthraquinone) (P14DAA), RGO, graphite oxide (GO) and graphite. Among the tested adsorbents, RGO-P15DAN demonstrated the high adsorptivity.

| S-EPMC4710513 | biostudies-literature

Albumin (BSA) adsorption onto graphite stepped surfaces.

Project description:Nanomaterials are good candidates for the design of novel components with biomedical applications. For example, nano-patterned substrates may be used to immobilize protein molecules in order to integrate them in biosensing units. Here, we perform long MD simulations (up to 200 ns) using an explicit solvent and physiological ion concentrations to characterize the adsorption of bovine serum albumin (BSA) onto a nano-patterned graphite substrate. We have studied the effect of the orientation and step size on the protein adsorption and final conformation. Our results show that the protein is stable, with small changes in the protein secondary structure that are confined to the contact area and reveal the influence of nano-structuring on the spontaneous adsorption, protein-surface binding energies, and protein mobility. Although van der Waals (vdW) interactions play a dominant role, our simulations reveal the important role played by the hydrophobic lipid-binding sites of the BSA molecule in the adsorption process. The complex structure of these sites, that incorporate residues with different hydrophobic character, and their flexibility are crucial to understand the influence of the ion concentration and protein orientation in the different steps of the adsorption process. Our study provides useful information for the molecular engineering of components that require the immobilization of biomolecules and the preservation of their biological activity.

| S-EPMC5457296 | biostudies-literature

Graphite Oxide Improves Adhesion and Water Resistance of Canola Protein-Graphite Oxide Hybrid Adhesive.

Project description:Protein derived adhesives are extensively explored as a replacement for synthetic ones, but suffers from weak adhesion and water resistance. Graphite oxide (GO) has been extensively used in nanocomposites, but not in adhesives applications. The objectives of this study were to prepare functionally improved protein adhesive by exfoliating GO with different oxidation levels, and to determine the effect of GO on adhesion mechanism. GO were prepared by oxidizing graphite for 0.5, 2, and 4?h (GO-A, GO-B and GO-C, respectively). Increasing oxidation time decreased C/O ratio; while the relative proportion of C-OH, and C?=?O groups initially increased up to 2?h of oxidation, but reduced upon further oxidation. Canola protein-GO hybrid adhesive (CPA-GO) was prepared by exfoliating GO at a level of 1% (w/w). GO significantly increased (p?<?0.05) adhesion; where GO-B addition showed the highest dry, and wet strength of 11.67?±?1.00, and 4.85?±?0.61?MPa, respectively. The improvements in adhesion was due to the improved exfoliation of GO, improved adhesive and cohesive interactions, increased hydrogen bonding, increased hydrophobic interactions and thermal stability of CPA-GO. GO, as we proposed for the first time is easier to process and cost-effective in preparing protein-based adhesives with significantly improved functionalities.

| S-EPMC5599558 | biostudies-literature

Understanding adsorption geometry of organometallic molecules on graphite.

Project description:To comprehensively investigate the adsorption geometries of organometallic molecules on graphene, Cp*Ru+ fragments as an organometallic molecule is bound on highly oriented pyrolytic graphite and imaged at atomic resolution using scanning tunneling microscopy (STM) (Cp* = pentamethylcyclopentadienyl). Atomic resolution imaging through STM shows that the Cp*Ru+ fragments are localized above the hollow position of the hexagonal structure, and that the first graphene layer adsorbed with the fragments on the graphite redeveloped morphologically to minimize its geometric energy. For a better understanding of the adsorption site and molecular geometry, experimental results are compared with computed calculations for the graphene surface with Cp*Ru+ fragments. These calculations show the adsorption geometries of the fragment on the graphene surface and the relationship between the geometric energy and molecular configuration. Our results provide the chemical anchoring geometry of molecules on the graphene surface, thereby imparting the theoretical background necessary for controlling the various properties of graphene in the future.

| S-EPMC8446079 | biostudies-literature

Sulfuric acid intercalated graphite oxide for graphene preparation.

Project description:Graphene has shown enormous potential for innovation in various research fields. The current chemical approaches based on exfoliation of graphite via graphite oxide (GO) are potential for large-scale synthesis of graphene but suffer from high cost, great operation difficulties, and serious waste discharge. We report a facile preparation of graphene by rapid reduction and expansion exfoliation of sulfuric acid intercalated graphite oxide (SIGO) at temperature just above 100°C in ambient atmosphere, noting that SIGO is easily available as the immediate oxidation descendent of graphite in sulfuric acid. The oxygenic and hydric groups in SIGO are mainly removed through dehydration as catalyzed by the intercalated sulfuric acid (ISA). The resultant consists of mostly single layer graphene sheets with a mean diameter of 1.07??m after dispersion in DMF. This SIGO process is reductant free, easy operation, low-energy, environmental friendly and generates graphene with low oxygen content, less defect and high conductivity. The provided synthesis route from graphite to graphene via SIGO is compact and readily scalable.

| S-EPMC3853688 | biostudies-literature

Nitrated Graphene Oxide Derived from Graphite Oxide: A Promising Energetic Two-Dimensional Material.

Project description:In order to synthesize a novel two-dimensional energetic material, nitrated graphene oxide (NGO) was prepared by the nitrification of graphite oxide to make a functional modification. Based on the morphological characterization, the NGO has a greater degree of curl and more wrinkles on the surface. The structure characterization and density functional theory calculation prove that epoxy and hydroxyl groups on the edge of graphite oxide have reacted with nitronium cation (NO2+) to produce nitro and nitrate groups. Hydrophobicity of NGO implied higher stability in storage than graphene oxide. Synchronous simultaneous analysis was used to explore the decomposition mechanism of NGO preliminarily. The decomposition enthalpy of NGO is 662.0 J·g-1 and the activation energy is 166.5 kJ·mol-1. The thermal stability is similar to that of general nitrate energetic materials. The hygroscopicity, thermal stability and flammability of NGO prove that it is a novel two-dimensional material with potential applications as energetic additives in the catalyst, electrode materials and energetic devices.

| S-EPMC7823779 | biostudies-literature

Characterization of Graphite Oxide and Reduced Graphene Oxide Obtained from Different Graphite Precursors and Oxidized by Different Methods Using Raman Spectroscopy Statistical Analysis.

Project description:In this paper, various graphite oxide (GO) and reduced graphene oxide (rGO) preparation methods are analyzed. The obtained materials differed in their properties, including (among others) their oxygen contents. The chemical and structural properties of graphite, graphite oxides, and reduced graphene oxides were previously investigated using Raman spectroscopy (RS), X-ray photoelectron spectroscopy (XPS), and X-ray diffraction (XRD). In this paper, hierarchical clustering analysis (HCA) and analysis of variance (ANOVA) were used to trace the directions of changes of the selected parameters relative to a preparation method of such oxides. We showed that the oxidation methods affected the physicochemical properties of the final products. The aim of the research was the statistical analysis of the selected properties in order to use this information to design graphene oxide materials with properties relevant for specific applications (i.e., in gas sensors).

| S-EPMC7914510 | biostudies-literature

Graphene oxide and H2 production from bioelectrochemical graphite oxidation.

Project description:Graphene oxide (GO) is an emerging material for energy and environmental applications, but it has been primarily produced using chemical processes involving high energy consumption and hazardous chemicals. In this study, we reported a new bioelectrochemical method to produce GO from graphite under ambient conditions without chemical amendments, value-added organic compounds and high rate H2 were also produced. Compared with abiotic electrochemical electrolysis control, the microbial assisted graphite oxidation produced high rate of graphite oxide and graphene oxide (BEGO) sheets, CO2, and current at lower applied voltage. The resultant electrons are transferred to a biocathode, where H2 and organic compounds are produced by microbial reduction of protons and CO2, respectively, a process known as microbial electrosynthesis (MES). Pseudomonas is the dominant population on the anode, while abundant anaerobic solvent-producing bacteria Clostridium carboxidivorans is likely responsible for electrosynthesis on the cathode. Oxygen production through water electrolysis was not detected on the anode due to the presence of facultative and aerobic bacteria as O2 sinkers. This new method provides a sustainable route for producing graphene materials and renewable H2 at low cost, and it may stimulate a new area of research in MES.

| S-EPMC4647224 | biostudies-literature

Observation of second sound in graphite over 200 K.

Project description:Second sound refers to the phenomenon of heat propagation as temperature waves in the phonon hydrodynamic transport regime. We directly observe second sound in graphite at temperatures of over 200 K using a sub-picosecond transient grating technique. The experimentally determined dispersion relation of the thermal-wave velocity increases with decreasing grating period, consistent with first-principles-based solution of the Peierls-Boltzmann transport equation. Through simulation, we reveal this increase as a result of thermal zero sound-the thermal waves due to ballistic phonons. Our experimental findings are well explained with the interplay among three groups of phonons: ballistic, diffusive, and hydrodynamic phonons. Our ab initio calculations further predict a large isotope effect on the properties of thermal waves and the existence of second sound at room temperature in isotopically pure graphite.

| S-EPMC8755757 | biostudies-literature

A General Route for Growing Metal Sulfides onto Graphene Oxide and Exfoliated Graphite Oxide.

Project description:Graphene-based materials are elective materials for a number of technologies due to their unique properties. Also, semiconductor nanocrystals have been extensively explored due to their size-dependent properties that make them useful for several applications. By coupling both types of materials, new applications are envisaged that explore the synergistic properties in such hybrid nanostructures. This research reports a general wet chemistry method to prepare graphene oxide (GO) sheets decorated with nanophases of semiconductor metal sulfides. This method allows the in situ growth of metal sulfides onto GO by using metal dialkyldithiocarbamate complexes as single-molecule precursors. In particular, the role of GO as heterogeneous substrate for the growth of semiconductor nanocrystals was investigated by using Raman spectroscopic and imaging methods. The method was further extended to other graphene-based materials, which are easily prepared in a larger scale, such as exfoliated graphite oxide (EGO).

| S-EPMC5618356 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data