Copolymerization and terpolymerization of carbon dioxide/propylene oxide/phthalic anhydride using a (salen)Co(III) complex tethering four quaternary ammonium salts.

ABSTRACT: The (salen)Co(III) complex 1 tethering four quaternary ammonium salts, which is a highly active catalyst in CO2/epoxide copolymerizations, shows high activity for propylene oxide/phthalic anhydride (PO/PA) copolymerizations and PO/CO2/PA terpolymerizations. In the PO/PA copolymerizations, full conversion of PA was achieved within 5 h, and strictly alternating copolymers of poly(1,2-propylene phthalate)s were afforded without any formation of ether linkages. In the PO/CO2/PA terpolymerizations, full conversion of PA was also achieved within 4 h. The resulting polymers were gradient poly(1,2-propylene carbonate-co-phthalate)s because of the drift in the PA concentration during the terpolymerization. Both polymerizations showed immortal polymerization character; therefore, the molecular weights were determined by the activity (g/mol-1) and the number of chain-growing sites per 1 [anions in 1 (5) + water (present as impurity) + ethanol (deliberately fed)], and the molecular weight distributions were narrow (M w/M n, 1.05-1.5). Because of the extremely high activity of 1, high-molecular-weight polymers were generated (M n up to 170,000 and 350,000 for the PO/PA copolymerization and PO/CO2/PA terpolymerization, respectively). The terpolymers bearing a substantial number of PA units (f PA, 0.23) showed a higher glass-transition temperature (48 °C) than the CO2/PO alternating copolymer (40 °C).

SUBMITTER: Jeon JY

PROVIDER: S-EPMC4142976 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Zinc Amido-Oxazolinate Catalyzed Ring Opening Copolymerization and Terpolymerization of Maleic Anhydride and Epoxides.

Project description:Ring opening copolymerization (ROCOP) of epoxides and cyclic anhydrides has become an attractive approach for the synthesis of biodegradable polyesters with various compositions. Encouraged by the efficiency and versatility of a series of amido-oxazolinate zinc complexes, in this study they were shown to be active catalysts for the synthesis of unsaturated polyesters via ROCOP of maleic anhydride and various epoxides. The relative activity of epoxides in these reactions was observed to be styrene oxide > cyclohexene oxide > phenyl glycidyl ether, which could be correlated with the electronic and steric features of the substrate. To provide more structural possibilities for the polyesters, the difference in epoxide reactivity was exploited in an attempt to prepare block terpolymers from one anhydride and two epoxides. Terpolymerization was carried out in one or two steps in a single pot. The thermal characterization by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) techniques suggested that the resulting materials were mostly random terpolymers.

| S-EPMC7570669 | biostudies-literature

Copolymerization of Phthalic Anhydride with Epoxides Catalyzed by Amine-Bis(Phenolate) Chromium(III) Complexes.

Project description:The effect of ligand structure on the catalytic activity of amine-bis(phenolate) chromium(III) complexes in the ring-opening copolymerization of phthalic anhydride and a series epoxides was studied. Eight complexes differing in the donor-pendant group (R1) and substituents (R2) in phenolate units were examined as catalysts of the model reaction between phthalic anhydride and cyclohexane oxide in toluene. They were used individually or as a part of the binary catalytic systems with nucleophilic co-catalysts. The co-catalyst was selected from the following organic bases: PPh3, DMAP, 1-butylimidazole, or DBU. The binary catalytic systems turned out to be more active than the complexes used individually, and DMAP proved to be the best choice as a co-catalyst. When the molar ratio of [PA]:[epoxide]:[Cr]:[DMAP] = 250:250:1:1 was applied, the most active complex (R1-X = CH2NMe2, R2 = F) allowed to copolymerize phthalic anhydride with differently substituted epoxides (cyclohexene oxide, 4-vinylcyclohexene oxide, styrene oxide, phenyl glycidyl ether, propylene oxide, butylene oxide, and epichlorohydrin) within 240 min at 110 °C. The resulting polyesters were characterized by Mn up to 20.6 kg mol-1 and narrow dispersity, and they did not contain polyether units.

| S-EPMC8197922 | biostudies-literature

An Investigation of the Organoborane/Lewis Base Pairs on the Copolymerization of Propylene Oxide with Succinic Anhydride.

Project description:The copolymerization of biorenewable succinic anhydride (SA) with propylene oxide (PO) is a promising way to synthesize biodegradable aliphatic polyesters. However, the catalytic systems for this reaction still deserve to be explored because the catalytic activity of the reported catalysts and the molecular weights of produced polyesters are unsatisfied. Herein, we investigate the copolymerization of SA with PO catalyzed by the organoborane/base pairs. The types of Lewis bases, organoboranes, and their loadings all have a large impact on the activity and selectivity of the copolymerization. High ester content of >99% was achieved when performed the PO/SA copolymerization using triethyl borane (TEB)/phosphazene base P1-t-Bu (t-BuP1) pair with a molar ratio of 1/1 at 30-80 °C. Using TEB/t-BuP1 pair with the molar ratio of 4/1 at 80 °C, the turnover of frequency (TOF) was up to 128 h-1 and clearly higher than the known TOF values (0.5-34 h-1) of the PO/SA copolymerization by previously reported catalysts. The number-average molecular weights (Mns) of the resultant polyesters reached up to 20.4 kg/mol when copolymerization was carried out using TEB/t-BuP1 (1/1, in molar ratio) at 30 °C.

| S-EPMC7024261 | biostudies-literature

Hydrogenation of Alkynes and Olefins Catalyzed by Quaternary Ammonium Salts.

Project description:Catalytic hydrogenation of unsaturated hydrocarbons to alkenes and alkanes using molecular hydrogen is one of the most fundamental transformations in organic synthesis. While methodologies involving transition metals as catalysts in homogeneous and heterogeneous processes have been well developed, metal-free catalytic hydrogenation offers an ideal approach for future chemistry. Herein, the common and inexpensive quaternary ammonium salts are first introduced as catalysts in the catalytic hydrogenation system for the transformations from alkynes or olefins into the corresponding olefins or alkanes. Interestingly, the hydrogenation process of alkynes can be controlled to selectively produce alkenes or alkanes under different conditions. Moreover, the possible mechanism is discussed in new insights into the catalytic behavior of quaternary ammonium salts.

| S-EPMC10870019 | biostudies-literature

Synthesis and Antimicrobial Evaluation of Bis-morpholine Triazine Quaternary Ammonium Salts.

Project description:Efficient, environmentally and economically sustainable, and nontoxic antibacterial products are of global relevance in the fight against microorganism contamination. In this work, an easy and straightforward method for the synthesis of bis-morpholino triazine quaternary ammonium salts (bis-mTQAS) is reported, starting from 2,4,6-trichloro-1,3,5-triazine or 2,4-dichloro-6-methoxy-1,3,5-triazine and various N-alkylmorpholines. Bis-mTQAS were tested as antimicrobials against Gram-negative and Gram-positive bacterial strains. The best-performing bis-mTQAS were found to achieve total disinfection against Staphylococcus aureus ATCC 25923 and Escherichia coli ATCC 25922 at 50 and 400 μg/mL, respectively. Distinctively, bis-mTQAS with the highest antimicrobial efficiency had lowest cytotoxicity.

| S-EPMC8596621 | biostudies-literature

Synthesis, physiochemical property and antimicrobial activity of novel quaternary ammonium salts.

Project description:Twenty-four novel 5-phenyl-1,3,4-oxadiazole-2-thiol (POT) analogues, benzo[d]oxazole-2-thiol, benzo[d]thiazole-2-thiol and 5-methyl-1,3,4-thiadiazole-2-thiol-substituted N,N-bis(2-hydroxyethyl) quaternary ammonium salts (QAS) (5a-d, 6a-d, 7a-d, 10a-d, 13a-d, 16a-d) were prepared and characterised by FTIR, NMR and elemental analysis. Part of target compounds (5d, 6d, 7d, 10d, 13d, 16d) displayed potent antimicrobial effect against ten common pathogens (S. aureus, α-H-tococcus, β-H-tococcus, E. coli, P. aeruginosa, Proteus vulgaris, Canidia Albicans, Cytospora mandshurica, Physalospora piricola, Aspergillus niger) and had relatively low cytotoxity against two human cell lines (HaCat and LO2). TEM and SEM images of E. coli and S. aureus morphologies treated with 7d showed that the antibacterial mechanism might be the QAS fixing on cell wall surfaces and puncturing to result in the release of bacterial cytoplasm. This study provides new information of QAS, which could be used to design novel antimicrobial agents applied in clinic or agriculture.

| S-EPMC6010013 | biostudies-literature

Enhanced Poly(propylene carbonate) with Thermoplastic Networks: A Cross-Linking Role of Maleic Anhydride Oligomer in CO2/PO Copolymerization.

Project description:Cross-linking is an effective way to enhance biodegradable poly(propylene carbonate) (PPC) from CO2 and propylene oxide (PO). Cross-linked PPC can be prepared by one-step terpolymerization of multifunctional third monomers with CO2 and PO. However, few such third monomers are available. Each molecule of maleic anhydride oligomer (MAO) contains more than two cyclic anhydride groups. Here, we use it to synthesize PPC with cross-linked networks by adding a small quantity of MAO (0.625-5 wt% of PO) in CO2/PO copolymerization that was catalyzed by zinc glutarate. The formation of networks in the prepared copolymers was confirmed by the presence of gel in copolymers combined Fourier transform infrared spectroscopy (FT-IR), 1H NMR, and the improved mechanical properties. The 5% weight-loss degradation temperatures and maximum weight-loss degradation temperatures greatly increase up to 289.8 °C and 308.8 °C, respectively, which are remarkably high when compared to those of PPC. The minimum permanent deformation of the copolymers closes to 0, while that of PPC is 173%. The maximum tensile strength of the copolymers is 25.5 MPa higher than that of PPC, reaching 38.4 MPa, and it still has some toughness with the elongation at break of 25%. The above phenomena indicate that MAO that was inserted in PPC chains play a cross-linking role, which results in enhanced thermal stability, dimensional stability, and mechanical strength, comprehensively.

| S-EPMC6780336 | biostudies-literature

Cross-Linked Networks in Poly(propylene carbonate) by Incorporating (Maleic Anhydride/<i>cis</i>-1,2,3,6-Tetrahydrophthalic Anhydride) Oligomer in CO<sub>2</sub>/Propylene Oxide Copolymerization: Improving and Tailoring Thermal, Mechanical, and Dimensional Properties.

Project description:Poly(propylene carbonate) (PPC) from CO2 and propylene oxide (PO) has wide potential applications as a degradable "plastic". However, the thermal stability and mechanical properties of PPC cannot meet most of the application requirements. Herein, we focus on improving these properties. A (maleic anhydride/cis-1,2,3,6-tetrahydrophthalic anhydride) (MA/THPA) oligomer containing several cyclocarboxylic anhydride groups, which can copolymerize with PO, has been readily synthesized and used as the third comonomer to prepare PPC with cross-linked networks. The gel contents increase from 16 to 42% with increasing MA/THPA oligomer feed contents from 0.5 to 4 wt % of PO. The formation of cross-linked networks in PPC greatly improves the thermal, mechanical, and dimensional properties. The 5% weight-loss degradation temperature increases from 217 °C to nearly 290 °C before and after cross-linking, which ensures that PPC does not decompose in melt processing. The tensile strength of the copolymer is in the range of 22.2-44.3 MPa with elongation at break of 11-312%. The maximum tensile strength is improved by 143% compared to that of PPC. When the MA/THPA oligomer feed is above 3 wt % of PO, the hot-set elongation of the copolymer at 65 °C decreases more than 10 times when compared with that of PPC, and the permanent deformation is close to 0, while it is 145% for PPC. The dimensional stability is improved sharply. It can overcome the cold flow phenomenon of PPC. The improvement of the above comprehensive properties is of great significance to the practical application of PPC in various fields.

| S-EPMC7379107 | biostudies-literature

Crystal structures of three new N-halo-methyl-ated quaternary ammonium salts.

Project description:In the crystals of the title N-halo-methyl-ated quaternary ammonium salts, C19H23IN(+)·I(-), (I) [systematic name: N-(4,4-di-phenyl-but-3-en-1-yl)-N-iodo-methyl-N,N-di-methyl-ammonium iodide], C20H25IN(+)·I(-), (II) [systematic name: N-(5,5-di-phenyl-pent-4-en-1-yl)-N-iodo-methyl-N,N-di-methyl-ammonium iodide], and C21H27IN(+)·I(-), (III) [systematic name: N-(6,6-di-phenyl-hex-5-en-1-yl)-N-iodo-methyl-N,N-di-methyl-ammonium iodide], there are short I⋯I(-) inter-actions of 3.564 (4), 3.506 (1) and 3.557 (1) Å for compounds (I), (II) and (III), respectively. Compound (I) crystallizes in the Sohncke group P21 as an 'enanti-opure' compound and is therefore a potential material for NLO properties. In the crystal of compound (I), mol-ecules are linked by C-H⋯I(-) and C-H⋯π inter-actions which, together with the I⋯I(-) inter-actions, lead to the formation of ribbons along [100]. In (II), there are only C-H⋯I(-) inter-actions which, together with the I⋯I(-) inter-actions, lead to the formation of helices along [010]. In (III), apart from the I⋯I(-) inter-actions, there are no significant inter-molecular inter-actions present.

| S-EPMC4647383 | biostudies-literature

Quaternary ammonium salts based on (-)-borneol as effective inhibitors of influenza virus.

Project description:A series of compounds containing a 1,7,7-trimethylbicyclo[2.2.1]heptane fragment were evaluated for their antiviral activity against influenza A virus strain A/Puerto Rico/8/34 (H1N1) in vitro. The most potent antiviral compound proved to be a quaternary ammonium salt based on (-)-borneol, 10a. In in vitro experiments, compound 10a inhibited influenza A viruses (H1, H1pdm09, and H3 subtypes), with an IC50 value of 2.4-16.8 µM (depending on the virus), and demonstrated low toxicity (CC50 = 1311 µM). Mechanism-of-action studies for compound 10a revealed it to be most effective when added at the early stages of the viral life cycle. In direct haemolysis inhibition tests, compound 10a was shown to decrease the membrane-disrupting activity of influenza A virus strain A/Puerto Rico/8/34. According to molecular modelling results, the lead compound 10a can bind to different sites in the stem region of the viral hemagglutinin.

| S-EPMC8116641 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data