Controlled synthesis and visible light photocatalytic activity of Bi12GeO20 uniform microcrystals.

ABSTRACT: We successfully synthesized uniform Bi12GeO20 microspheres and microtetrahedrons enclosed by four {111} facets using a controlled hydrothermal method for the first time. The photocatalytic activity of these regular-shaped products was further investigated by the degradation of RhB and gaseous formaldehyde under visible light irradiation (λ>420 nm). The Bi12GeO20 microtetrahedrons (s) exhibited enhanced photocatalytic activity and stability which is closely related to the high capacity of exposed {111} facets for uptake of O2. The formation mechanism studies indicate that the Bi12GeO20 seeds were directed to grow into truncated microcubes, truncated microtetrahedrons, and then microtetrahedrons when the NaOH concentration was 5 M. The same batch of seeds only evolved into microspheres when the NaOH concentration was switched to 3 M. The difference in Bi12GeO20 morphology could be attributed to the rates of both crystal nucleation and crystal growth.

SUBMITTER: Wan Z

PROVIDER: S-EPMC4158326 | biostudies-literature | 2014 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Controlled synthesis and visible light photocatalytic activity of Bi12GeO20 uniform microcrystals.

Wan Zhen Z Zhang Gaoke G

Scientific reports 20140909

We successfully synthesized uniform Bi12GeO20 microspheres and microtetrahedrons enclosed by four {111} facets using a controlled hydrothermal method for the first time. The photocatalytic activity of these regular-shaped products was further investigated by the degradation of RhB and gaseous formaldehyde under visible light irradiation (λ>420 nm). The Bi12GeO20 microtetrahedrons (s) exhibited enhanced photocatalytic activity and stability which is closely related to the high capacity of exposed ...[more]

PMID: 25199641

Similar Datasets

Solvothermal Synthesis of Cu2ZnSnSe4 Nanoparticles and Their Visible-Light-Driven Photocatalytic Activity

Project description: Not available

| S-EPMC11243532 | biostudies-literature

Hydrothermal Synthesis of Bismuth Ferrite Hollow Spheres with Enhanced Visible-Light Photocatalytic Activity.

Project description:In recent years, semiconductor hollow spheres have gained much attention due to their unique combination of morphological, chemical, and physico-chemical properties. In this work, we report for the first time the synthesis of BiFeO3 hollow spheres by a facile hydrothermal treatment method. The mechanism of formation of pure phase BiFeO3 hollow spheres is investigated systematically by variation of synthetic parameters such as temperature and time, ratio and amount of precursors, pressure, and calcination procedures. The samples were characterized by X-ray powder diffraction, scanning electron microscopy, energy dispersive X-ray spectroscopy, and UV-vis diffuse reflectance spectroscopy. We observe that the purity and morphology of the synthesized materials are very sensitive to synthesis parameters. In general, the chemically and morphologically very robust hollow spheres have diameters in the range of 200 nm to 2 μm and a wall thickness of 50-200 nm. The synthesized BiFeO3 hollow spheres were applied as catalysts in the photodegradation of the model pollutant Rhodamine B under visible-light irradiation. Notably, the photocatalyst demonstrated exceptionally high removal efficiencies leading to complete degradation of the dye in less than 150 min at neutral pH. The superior efficiencies of the synthesized material are attributed to the unique features of hollow spheres. The active species in the photocatalytic process have been identified by trapping experiments.

| S-EPMC10343919 | biostudies-literature

Facile Green Synthesis of BiOBr Nanostructures with Superior Visible-Light-Driven Photocatalytic Activity.

Project description:Novel green bismuth oxybromide (BiOBr-G) nanoflowers were successfully synthesized via facile hydrolysis route using an Azadirachta indica (Neem plant) leaf extract and concurrently, without the leaf extract (BiOBr-C). The Azadirachta indica leaf extract was employed as a sensitizer and stabilizer for BiOBr-G, which significantly expanded the optical window and boosted the formation of photogenerated charge carriers and transfer over the BiOBr-G surface. The photocatalytic performance of both samples was investigated for the degradation of methyl orange (MO) and phenol (Ph) under the irradiation of visible light. The leaf extract mediated BiOBr-G photocatalyst displayed significantly higher photocatalytic activity when compared to BiOBr-C for the degradation of both pollutants. The degradation rate of MO and Ph by BiOBr-G was found to be nearly 23% and 16% more when compared to BiOBr-C under visible light irradiation, respectively. The substantial increase in the photocatalytic performance of BiOBr-G was ascribed to the multiple synergistic effects between the efficient solar energy harvesting, narrower band gap, high specific surface area, porosity, and effective charge separation. Furthermore, BiOBr-G displayed high stability for five cycles of photocatalytic activity, which endows its practical application as a green photocatalyst in the long run.

| S-EPMC6117687 | biostudies-literature

Nanocasting synthesis of BiFeO<sub>3</sub> nanoparticles with enhanced visible-light photocatalytic activity.

Project description:In this work, monodisperse BiFeO3 nanoparticles with a particle diameter of 5.5 nm were synthesized by a nanocasting technique using mesoporous silica SBA-15 as a hard template and pre-fabricated metal carboxylates as metal precursors. To the best of our knowledge, the synthesized particles are the smallest BiFeO3 particles ever prepared by any method. The samples were characterized by X-ray powder diffraction, transmission electron microscopy and UV-vis diffuse reflectance spectroscopy. The phase purity of the product depends on the type of carboxylic acid used in the synthesis of the metal precursors, the type of solvent in the wet impregnation process, and the calcination procedure. By using tartaric acid in the synthesis of the metal precursors, acidified 2-methoxyethanol in the wet impregnation process and a calcination procedure with intermediate plateaus, monodisperse 5.5 nm BiFeO3 nanoparticles were successfully obtained. Furthermore, the nanoparticles were applied in photodegradation reactions of rhodamine B in aqueous solution under visible-light irradiation. Notably, the cast BiFeO3 nanoparticles demonstrated very high efficiencies and stability under visible-light irradiation, much higher than those of BiFeO3 nanoparticles synthesized by other synthetic methods. The possible mechanism in the photodegradation process has been deeply discussed on the basis of radical trapping experiments.

| S-EPMC7736686 | biostudies-literature

Synthesis, Characterization and Visible-Light Photocatalytic Activity of Solid and TiO2-Supported Uranium Oxycompounds.

Project description:In this study, various solid uranium oxycompounds and TiO2-supported materials based on nanocrystalline anatase TiO2 are synthesized using uranyl nitrate hexahydrate as a precursor. All uranium-contained samples are characterized using N2 adsorption, XRD, UV-vis, Raman, TEM, XPS and tested in the oxidation of a volatile organic compound under visible light of the blue region to find correlations between their physicochemical characteristics and photocatalytic activity. Both uranium oxycompounds and TiO2-supported materials are photocatalytically active and are able to completely oxidize gaseous organic compounds under visible light. If compared to the commercial visible-light TiO2 KRONOS® vlp 7000 photocatalyst used as a benchmark, solid uranium oxycompounds exhibit lower or comparable photocatalytic activity under blue light. At the same time, uranium compounds contained uranyl ion with a uranium charge state of 6+, exhibiting much higher activity than other compounds with a lower charge state of uranium. Immobilization of uranyl ions on the surface of nanocrystalline anatase TiO2 allows for substantial increase in visible-light activity. The photonic efficiency of reaction over uranyl-grafted TiO2, 12.2%, is 17 times higher than the efficiency for commercial vlp 7000 photocatalyst. Uranyl-grafted TiO2 has the potential as a visible-light photocatalyst for special areas of application where there is no strict control for use of uranium compounds (e.g., in spaceships or submarines).

| S-EPMC8073566 | biostudies-literature

Facile Synthesis of SrCO₃-Sr(OH)₂/PPy Nanocomposite with Enhanced Photocatalytic Activity under Visible Light.

Project description:Pyrrole monomer was chemically polymerized onto SrCO₃-Sr(OH)₂ powders to obtain SrCO₃-Sr(OH)₂/polypyrrole nanocomposite to be used as a candidate for photocatalytic degradation of methylene blue dye (MB). The material was characterized by Fourier transform infrared (FTIR) spectroscopy, UV/Vis spectroscopy, and X-ray diffraction (XRD). It was observed from transmission electronic microscopy (TEM) analysis that the reported synthesis route allows the production of SrCO₃-Sr(OH)₂ nanoparticles with particle size below 100 nm which were embedded within a semiconducting polypyrrole matrix (PPy). The SrCO₃-Sr(OH)₂ and SrCO₃-Sr(OH)₂/PPy nanocomposites were tested in the photodegradation of MB dye under visible light irradiation. Also, the effects of MB dye initial concentration and the catalyst load on photodegradation efficiency were studied and discussed. Under the same conditions, the efficiency of photodegradation of MB employing the SrCO₃-Sr(OH)₂/PPy nanocomposite increases as compared with that obtained employing the SrCO₃-Sr(OH)₂ nanocomposite.

| S-EPMC5456521 | biostudies-literature

Biofabricated BiOI with enhanced photocatalytic activity under visible light irradiation.

Project description:In the recent past, there has been a large-scale utilization of plant extracts for the synthesis of various photocatalysts. The biofabrication technology eliminates the usage of harmful chemicals and serves as an eco-friendly approach for environmental remediation. Herein, a comparative analysis between bismuth oxyiodide synthesized via Azadirachta indica (neem) leaf extract (BiOI-G) and without leaf extract (BiOI-C) has been envisaged. The BiOI-G and BiOI-C samples were characterized by spectral and microscopic techniques, which revealed that the Azadirachta indica assisted BiOI-G attained enhanced features over BiOI-C such as narrower band gap, large surface area, porosity, increased absorption range of visible light and effectual splitting of the photogenerated e--h+ pairs. Benefiting from these enhanced features, BiOI-G degraded methyl orange (MO), rhodamine B (RhB), and benzotriazole (BT) at a significantly higher rate in comparison to BiOI-C. The degradation rate of MO, RhB and BT by BiOI-G was observed to be 1.3, 1.25 and 1.29 times higher in comparison to BiOI-C. Moreover, BiOI-G displayed high stability upto five cycles of the photocatalytic activity, which endow its effectiveness as a highly-efficient green photocatalyst.

| S-EPMC9084558 | biostudies-literature

Visible-Light-Driven Photocatalytic Activity of Magnetic BiOBr/SrFe12O19 Nanosheets.

Project description:Magnetic BiOBr/SrFe12O19 nanosheets were successfully synthesized using the hydrothermal method. The as-prepared samples were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), and UV-visible diffused reflectance spectra (UV-DRS), and the magnetic properties were tested using a vibration sample magnetometer (VSM). The as-produced composite with an irregular flaky-shaped aggregate possesses a good anti-demagnetization ability (Hc = 861.04 G) and a high photocatalytic efficiency. Under visible light (λ > 420 nm) and UV light-emitting diode (LED) irradiation, the photodegradation rates of Rhodamine B (RhB) using BiOBr/SrFe12O19 (5 wt %) (BOB/SFO-5) after 30 min of reaction were 97% and 98%, respectively, which were higher than that using BiOBr (87%). The degradation rate of RhB using the recovered BiOBr/5 wt % SrFe12O19 (marked as BOB/SFO-5) was still more than 85% in the fifth cycle, indicating the high stability of the composite catalyst. Meanwhile, after five cycles, the magnetic properties were still as stable as before. The radical-capture experiments proved that superoxide radicals and holes were main active species in the photocatalytic degradation of RhB.

| S-EPMC6567020 | biostudies-literature

Facile synthesis of a ZnO-BiOI p-n nano-heterojunction with excellent visible-light photocatalytic activity.

Project description:In this paper, an efficient method to produce a ZnO/BiOI nano-heterojunction is developed by a facile solution method followed by calcination. By tuning the ratio of Zn/Bi, the morphology varies from nanoplates, flowers to nanoparticles. The heterojunction formed between ZnO and BiOI decreases the recombination rate of photogenerated carriers and enhances the photocatalytic activity of ZnO/BiOI composites. The obtained ZnO/BiOI heterostructured nanocomposites exhibit a significant improvement in the photodegradation of rhodamine B under visible light (? ? 420 nm) irradiation as compared to single-phase ZnO and BiOI. A sample with a Zn/Bi ratio of 3:1 showed the highest photocatalytic activity (?99.3% after 100 min irradiation). The photodegradation tests indicated that the ZnO/BiOI heterostructured nanocomposites not only exhibit remarkably enhanced and sustainable photocatalytic activity, but also show good recyclability. The excellent photocatalytic activity could be attributed to the high separation efficiency of the photoinduced electron-hole pairs as well as the high specific area.

| S-EPMC5852526 | biostudies-literature

Visible-light active conducting polymer nanostructures with superior photocatalytic activity.

Project description:The development of visible-light responsive photocatalysts would permit more efficient use of solar energy, and thus would bring sustainable solutions to many environmental issues. Conductive polymers appear as a new class of very active photocatalysts under visible light. Among them poly(3,4-ethylenedioxythiophene) (PEDOT) is one of the most promising conjugated polymer with a wide range of applications. PEDOT nanostructures synthesized in soft templates via chemical oxidative polymerization demonstrate unprecedented photocatalytic activities for water treatment without the assistance of sacrificial reagents or noble metal co-catalysts and turn out to be better than TiO2 as benchmark catalyst. The PEDOT nanostructures exhibit a narrow band gap (E?=?1.69?eV) and are characterized by excellent ability to absorb light in visible and near infrared region. The novel PEDOT-based photocatalysts are very stable with cycling and can be reused without appreciable loss of activity. Interestingly, hollow micrometric vesicular structures of PEDOT are not effective photocatalysts as compared to nanometric spindles suggesting size and shape dependent photocatalytic properties. The visible-light active photocatalytic properties of the polymer nanostructures present promising applications in solar light harvesting and broader fields.

| S-EPMC4676008 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data