Structural and dynamical studies of acid-mediated conversion in amorphous-calcium-phosphate based dental composites.

ABSTRACT: OBJECTIVE:To investigate the complex structural and dynamical conversion process of the amorphous-calcium-phosphate (ACP)-to-apatite transition in ACP based dental composite materials. METHODS:Composite disks were prepared using zirconia hybridized ACP fillers (0.4 mass fraction) and photo-activated Bis-GMA/TEGDMA resin (0.6 mass fraction). We performed an investigation of the solution-mediated ACP-to-apatite conversion mechanism in controlled acidic aqueous environment with in situ ultra-small angle X-ray scattering based coherent X-ray photon correlation spectroscopy and ex situ X-ray diffraction, as well as other complementary techniques. RESULTS:We established that the ACP-to-apatite conversion in ACP composites is a two-step process, owing to the sensitivity to local structural changes provided by coherent X-rays. Initially, ACP undergoes a local microstructural rearrangement without losing its amorphous character. We established the catalytic role of the acid and found the time scale of this rearrangement strongly depends on the pH of the solution, which agrees with previous findings about ACP without the polymer matrix being present. In the second step, ACP is converted to an apatitic form with the crystallinity of the formed crystallites being poor. Separately, we also confirmed that in the regular Zr-modified ACP the rate of ACP conversion to hydroxyapatite is slowed significantly compared to unmodified ACP, which is beneficial for targeted slow release of functional calcium and phosphate ions from dental composite materials. SIGNIFICANCE:For the first time, we were able to follow the complete solution-mediated transition process from ACP to apatite in this class of dental composites in a controlled aqueous environment. A two-step process, suggested previously, was conclusively identified.

SUBMITTER: Zhang F

PROVIDER: S-EPMC4167569 | biostudies-literature | 2014 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Structural and dynamical studies of acid-mediated conversion in amorphous-calcium-phosphate based dental composites.

Zhang Fan F Allen Andrew J AJ Levine Lyle E LE Vaudin Mark D MD Skrtic Drago D Antonucci Joseph M JM Hoffman Kathleen M KM Giuseppetti Anthony A AA Ilavsky Jan J

Dental materials : official publication of the Academy of Dental Materials 20140728 10

<h4>Objective</h4>To investigate the complex structural and dynamical conversion process of the amorphous-calcium-phosphate (ACP)-to-apatite transition in ACP based dental composite materials.<h4>Methods</h4>Composite disks were prepared using zirconia hybridized ACP fillers (0.4 mass fraction) and photo-activated Bis-GMA/TEGDMA resin (0.6 mass fraction). We performed an investigation of the solution-mediated ACP-to-apatite conversion mechanism in controlled acidic aqueous environment with in si ...[more]

PMID: 25082155

Similar Datasets

Project description:Our studies of amorphous calcium phosphate (ACP)-based materials over the last decade have yielded bioactive polymeric composites capable of protecting teeth from demineralization or even regenerating lost tooth mineral. The anti-cariogenic/re-mineralizing potential of these ACP composites originates from their propensity, when exposed to the oral environment, to release in a sustained manner sufficient levels of mineral-forming calcium and phosphate ions to promote formation of stable apatitic tooth mineral. However, the less than optimal ACP filler/resin matrix cohesion, excessive polymerization shrinkage and water sorption of these experimental materials can adversely affect their physicochemical and mechanical properties, and, ultimately, limit their lifespan. This study demonstrates the effects of chemical structure and composition of the methacrylate monomers used to form the matrix phase of composites on degree of vinyl conversion (DVC) and water sorption of both copolymers and composites and the release of mineral ions from the composites. Modification of ACP surface via introducing cations and/or polymers ab initio during filler synthesis failed to yield mechanically improved composites. However, moderate improvement in composite's mechanical stability without compromising its remineralization potential was achieved by silanization and/or milling of ACP filler. Using ethoxylated bisphenol A dimethacrylate or urethane dimethacrylate as base monomers and adding moderate amounts of hydrophilic 2-hydroxyethyl methacrylate or its isomer ethyl-α-hydroxymethacrylate appears to be a promising route to maximize the remineralizing ability of the filler while maintaining high DVC. Exploration of the structure/composition/property relationships of ACP fillers and polymer matrices is complex but essential for achieving a better understanding of the fundamental mechanisms that govern dissolution/re-precipitation of bioactive ACP fillers, and, ultimately, the suitability of the composites for clinical evaluation.

Project description:PurposeThe aim was to assess monomer conversion, dimensional stability, flexural strength / modulus, surface apatite precipitation and wear of mono / tri calcium phosphate (CaP) and polylysine (PLS)-containing dental composites. These were formulated using a new, high molecular weight, fluid monomer phase that requires no polymerisation activator.Materials and methodsUrethane and Polypropylene Glycol Dimethacrylates were combined with low levels of an adhesion promoting monomer and a light activated initiator. This liquid was mixed with a hybrid glass containing either 10 wt% CaP and 1 wt% PLS (F1) or 20 wt% CaP and 2 wt% PLS (F2). Powder to liquid mass ratio was 5:1. Commercial controls included Gradia Direct Posterior (GD) and Filtek Z250 (FZ). Monomer conversion and polymerisation shrinkage were calculated using Fourier Transform Infrared (FTIR). Subsequent volume increases in water over 7 weeks were determined using gravimetric studies. Biaxial flexural strength (BFS) / modulus (BFM) reduction and surface apatite precipitation upon 1 and 4 weeks immersion in water versus simulated body fluid (SBF) were assessed using a mechanical testing frame and scanning electron microscope (SEM). Mass / volume loss and surface roughness (Ra) following 7 weeks water immersion and subsequent accelerated tooth-brush abrasion were examined using gravimetric studies and profilometer.ResultsF1 and F2 exhibited much higher monomer conversion (72%) than FZ (54%) and low calculated polymerization shrinkage (2.2 vol%). Final hygroscopic expansions decreased in the order; F2 (3.5 vol%) > F1 (1.8 vol%) ~ Z250 (1.6 vol%) > Gradia (1.0 vol%). BFS and BFM were unaffected by storage medium type. Average BFS / BFM upon 4 weeks immersion reduced from 144 MPa / 8 GPa to 107 MPa / 5 GPa for F1 and 105 MPa / 6 GPa to 82 MPa / 4 GPa for F2. Much of this change was observed in the first week of immersion when water sorption rate was high. Surface apatite layers were incomplete at 1 week, but around 2 and 15 micron thick for F1 and F2 respectively following 4 weeks in SBF. Mass and volume loss following wear were equal. Average results for F1 (0.5%), F2 (0.7%), and FZ (0.5%) were comparable but lower than that of GD (1%). Ra, however, decreased in the order; F1 (15 ?m) > F2 (11 ?m) > GD (9 ?m) > FZ (5 ?m).ConclusionsHigh monomer conversion in combination with large monomer size and lack of amine activator should improve cytocompatibility of the new composites. High monomer molecular weight and powder content enables low polymerisation shrinkage despite high conversion. Increasing active filler provides enhanced swelling to balance shrinkage, which, in combination with greater surface apatite precipitation, may help seal gaps and reduce bacterial microleakage. High monomer conversion also ensures competitive mechanical / wear characteristics despite enhanced water sorption. Furthermore, increased active filler could help reduce surface roughness upon wear.

Dataset Information

Structural and dynamical studies of acid-mediated conversion in amorphous-calcium-phosphate based dental composites.

Publications

Structural and dynamical studies of acid-mediated conversion in amorphous-calcium-phosphate based dental composites.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets