Tailoring the degradation rates of thermally responsive hydrogels designed for soft tissue injection by varying the autocatalytic potential.

ABSTRACT: The ability to modulate the degradation properties of biomaterials such as thermally responsive hydrogels is desirable when exploring new therapeutic strategies that rely on the temporary presence of a placed scaffold or gel. Here we report a method of manipulating the absorption rate of a poly(N-isopropylacrylamide) ((poly(NIPAAm)) based hydrogel across a wide range (from 1 d to 5 mo) by small alterations in the composition. Relying upon the autocatalytic effect, the degradation of poly(NIPAAm-co-HEMA-co-MAPLA), (HEMA = 2-hydroxyethyl methacrylate; MAPLA = methacrylate-polylactide) was greatly accelerated by adding a fourth monomer methacrylic acid (MAA) at no more than 2 mol% to obtain poly(NIPAAm-co-HEMA-co-MAPLA-co-MAA) (pNHMMj) where j reflects the MAA molar % in the reactant mixture. MAA residue introduction decreased the pH inside the hydrogels and in surrounding buffered solutions. Accelerated degradation positively correlated with MAA content in pNHMMj polymers, putatively by the accelerated cleavage of MAPLA residues to raise the transition temperature of the polymer above body temperature. Physical properties including thermal transition behavior and initial mechanical strength did not vary significantly with MAA content. A rat hindlimb injection model generally reflected the in vitro observation that higher MAA content resulted in more rapid degradation and cellular infiltration. The strategy of tuning the degradation of thermally responsive hydrogels where degradation or solubilization is determined by their polyester components might be applied to other tissue engineering and regenerative medicine applications where designed biomaterial degradation behavior is needed.

SUBMITTER: Zhu Y

PROVIDER: S-EPMC4405660 | biostudies-literature | 2015

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Tailoring the degradation rates of thermally responsive hydrogels designed for soft tissue injection by varying the autocatalytic potential.

Zhu Yang Y Jiang Hongbin H Ye Sang-Ho SH Yoshizumi Tomo T Wagner William R WR

Biomaterials 20150320

The ability to modulate the degradation properties of biomaterials such as thermally responsive hydrogels is desirable when exploring new therapeutic strategies that rely on the temporary presence of a placed scaffold or gel. Here we report a method of manipulating the absorption rate of a poly(N-isopropylacrylamide) ((poly(NIPAAm)) based hydrogel across a wide range (from 1 d to 5 mo) by small alterations in the composition. Relying upon the autocatalytic effect, the degradation of poly(NIPAAm- ...[more]

PMID: 25890745

Similar Datasets

Project description:The ability to assess changes in smooth muscle contractility and pharmacological responsiveness in normal or pathological-relevant vascular tissue environments is critical to enable vascular drug discovery. However, major challenges remain in both capturing the complexity of in vivo vascular remodeling and evaluating cell contractility in complex, tissue-like environments. Herein, we developed a biomimetic fibrous hydrogel with tunable structure, stiffness, and composition to resemble the native vascular tissue environment. This hydrogel platform was further combined with the combinatory protein array technology as well as advanced approaches to measure cell mechanics and contractility, thus permitting evaluation of smooth muscle functions in a variety of tissue-like microenvironments. Our results demonstrated that biomimetic fibrous structure played a dominant role in smooth muscle function, while the presentation of adhesion proteins co-regulated it to various degrees. Specifically, fibre networks enabled cell infiltration and upregulated expression of actomyosin proteins in contrast to flat hydrogels. Remarkably, fibrous structure and physiologically relevant stiffness of hydrogels cooperatively enhanced smooth muscle contractility and pharmacological responses to vasoactive drugs at both the single cell and intact tissue levels. Together, this study is the first to demonstrate alterations of human vascular smooth muscle contractility and pharmacological responsiveness in biomimetic soft, fibrous environments with a cellular array platform. The integrated platform produced here could enable investigations for pathobiology and pharmacological interventions by developing a broad range of patho-physiologically relevant in vitro tissue models. STATEMENT OF SIGNIFICANCE:Engineering functional smooth muscle in vitro holds the great potential for diseased tissue replacement and drug testing. A central challenge is recapitulating the smooth muscle contractility and pharmacological responses given its significant phenotypic plasticity in response to changes in environment. We present a biomimetic fibrous hydrogel with tunable structure, stiffness, and composition that enables the creation of functional smooth muscle tissues in the native-like vascular tissue microenvironment. Such fibrous hydrogel is further combined with the combinatory protein array technology to construct a cellular array for evaluation of smooth muscle phenotype, contraction, and cell mechanics. The integrated platform produced here could be promising for developing a broad range of normal or diseased in vitro tissue models.

Project description:Liquid perfluorocarbon nanodroplets (NDs) are an attractive alternative to microbubbles (MBs) for ultrasound-mediated therapeutic and diagnostic applications. ND size and size distribution have a strong influence on their behaviour in vivo, including extravasation efficiency, circulation time, and response to ultrasound stimulation. Thus, it is desirable to identify ways to tailor the ND size and size distribution during manufacturing. In this study phospholipid-coated NDs, comprising a perfluoro-n-pentane (PFP) core stabilised by a DSPC/PEG40s (1,2-distearoyl-sn-glycero-3-phosphocholine and polyoxyethylene(40)stearate, 9:1 molar ratio) shell, were produced in phosphate-buffered saline (PBS) by sonication. The effect of the following production-related parameters on ND size was investigated: PFP concentration, power and duration of sonication, and incorporation of a lipophilic fluorescent dye. ND stability was also assessed at both 4 °C and 37 °C. When a sonication pulse of 6 s and 15% duty cycle was employed, increasing the volumetric concentration of PFP from 5% to 15% v/v in PBS resulted in an increase in ND diameter from 215.8 ± 16.8 nm to 408.9 ± 171.2 nm. An increase in the intensity of sonication from 48 to 72 W (with 10% PFP v/v in PBS) led to a decrease in ND size from 354.6 ± 127.2 nm to 315.0 ± 100.5 nm. Increasing the sonication time from 20 s to 40 s (using a pulsed sonication with 30% duty cycle) did not result in a significant change in ND size (in the range 278-314 nm); however, when it was increased to 60 s, the average ND diameter reduced to 249.7 ± 9.7 nm, which also presented a significantly lower standard deviation compared to the other experimental conditions investigated (i.e., 9.7 nm vs. > 49.4 nm). The addition of the fluorescent dye DiI at different molar ratios did not affect the ND size distribution. NDs were stable at 4 °C for up to 6 days and at 37 °C for up to 110 min; however, some evidence of ND-to-MB phase transition was observed after 40 min at 37 °C. Finally, phase transition of NDs into MBs was demonstrated using a tissue-mimicking flow phantom under therapeutic ultrasound exposure conditions (ultrasound frequency: 0.5 MHz, acoustic pressure: 2-4 MPa, and pulse repetition frequency: 100 Hz).

Dataset Information

Tailoring the degradation rates of thermally responsive hydrogels designed for soft tissue injection by varying the autocatalytic potential.

Publications

Tailoring the degradation rates of thermally responsive hydrogels designed for soft tissue injection by varying the autocatalytic potential.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets