Atmospheric corrosion of metals in industrial city environment.

ABSTRACT: Atmospheric corrosion is a significant problem given destruction of various materials, especially metals. The corrosion investigation in the industrial city environment was carried out during one year exposure. Corrosion potential was determined using the potentiometric method. The highest effect of corrosion processes was observed during the winter season due to increased air pollution. Corrosion of samples pre-treated in tannic acid before the exposure was more difficult compared with the samples without pretreatment. The corrosion products determined with the SEM/EDS method prove that the most corrosive pollutants present in the industrial city air are SO2, CO2, chlorides and dust.

SUBMITTER: Kusmierek E

PROVIDER: S-EPMC4510135 | biostudies-literature | 2015 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Atmospheric corrosion of metals in industrial city environment.

Kusmierek Elzbieta E Chrzescijanska Ewa E

Data in brief 20150304

Atmospheric corrosion is a significant problem given destruction of various materials, especially metals. The corrosion investigation in the industrial city environment was carried out during one year exposure. Corrosion potential was determined using the potentiometric method. The highest effect of corrosion processes was observed during the winter season due to increased air pollution. Corrosion of samples pre-treated in tannic acid before the exposure was more difficult compared with the samp ...[more]

PMID: 26217736

Similar Datasets

Risk Assessment of Metals in Urban Soils from a Typical Industrial City, Suzhou, Eastern China.

Project description:Risk of metals in urban soils is less studied, compared to that in other types of soils, hindering accurate assessment of human exposure to metals. In this study, the concentrations of five metals (As, Cd, Cr, Pb, and Hg) were analyzed in 167 surface soil samples collected from Suzhou city and their potential ecological and human health risks were assessed. The mean concentrations of As, Cd, Pb, and Hg except Cr, were higher than the background values in Jiangsu Province. Metal concentrations varied among districts, where sites of high contamination showed a punctate distribution. Principal components and correlation analyses revealed that As, Pb, and Cd could originate from the same sources. The geo-accumulation (Igeo) and potential ecological risk indices (RI) were calculated and the relatively low values of Igeo (<0) and RI (<150) suggested generally low ecological risk. The noncarcinogenic risks of the metals were relatively low for Suzhou residents (i.e., average hazard index or HI: 0.1199 for adults and 0.5935 for children, <1), while the total carcinogenic risks (TCR) of Cr and As were acceptable (TCR in the range of 1.0 × 10-6 to 1.0 × 10-4). Children faced a higher threat than adults. Results of Monte-Carlo simulations were lower than those obtained from models using deterministic parameters. Of all the uncertain parameters, the ingestion rate and body weight were the most sensitive for adults and children, respectively, while As was an important factor for both. The results as well as the factors controlling risks of metals could help better understand the risks of metals in urban soils of industrial cities in China.

| S-EPMC5615562 | biostudies-literature

One dimensional wormhole corrosion in metals.

Project description:Corrosion is a ubiquitous failure mode of materials. Often, the progression of localized corrosion is accompanied by the evolution of porosity in materials previously reported to be either three-dimensional or two-dimensional. However, using new tools and analysis techniques, we have realized that a more localized form of corrosion, which we call 1D wormhole corrosion, has previously been miscategorized in some situations. Using electron tomography, we show multiple examples of this 1D and percolating morphology. To understand the origin of this mechanism in a Ni-Cr alloy corroded by molten salt, we combined energy-filtered four-dimensional scanning transmission electron microscopy and ab initio density functional theory calculations to develop a vacancy mapping method with nanometer-resolution, identifying a remarkably high vacancy concentration in the diffusion-induced grain boundary migration zone, up to 100 times the equilibrium value at the melting point. Deciphering the origins of 1D corrosion is an important step towards designing structural materials with enhanced corrosion resistance.

| S-EPMC9946947 | biostudies-literature

Corrosion Behavior of Silver-Plated Circuit Boards in a Simulated Marine Environment with Industrial Pollution.

Project description:The electrochemical corrosion behavior of a silver-plated circuit board (PCB-ImAg) in a polluted marine atmosphere environment (Qingdao in China) is studied through a simulated experiment. The morphologies of PCB-ImAg show some micropores on the surface that act as the corrosion-active points in the tests. Cl- mainly induces microporous corrosion, whereas SO₂ causes general corrosion. Notably, the silver color changes significantly under SO₂ influence. EIS results show that the initial charge transfer resistance in the test containing SO₂ and Cl- is 9.847 × 10³, while it is 3.701 × 10⁴ in the test containing Cl- only, which demonstrates that corrosion accelerates in a mixed atmosphere. Polarization curves further show that corrosion potential is lower in mixed solutions (between -0.397 V SCE and -0.214 V SCE) than it in the solution containing Cl- only (-0.168 V SCE), indicating that corrosion tendency increases with increased HSO₃- concentration.

| S-EPMC5551805 | biostudies-other

Distribution characteristics of microbial community structure in atmospheric particulates of the typical industrial city in Jiangsu province, China.

Project description:In this study, Xuzhou, a typical industrial city in the north of Jiangsu Province, was chosen to investigate the pollution level of atmospheric particulates. The proportion of fine particles (PM2.5) in PM10 is larger than that of coarse particles (about 58%). The physicochemical properties of PM2.5 were analyzed by SEM and EDS. DGGE was used to study the distribution characteristics of bacterial community structure on atmospheric particulates (TSP, PM2.5 and PM10) in different functional areas of Xuzhou city during the winter haze. It was found that the microbial populations of atmospheric particles were mainly divided into three groups: Proteobacteria, Bacteroidetes, and Pachytenella. The community structure of bacteria in fine particle size was more abundant than that in coarse particle size. When haze occurs, the concentration of all kinds of pathogens in fine particle size will increase. Therefore, it is necessary to focus on the monitoring and management of fine particles.

| S-EPMC8806265 | biostudies-literature

Risk Assessment of Heavy Metals in Soils from Four Different Industrial Plants in a Medium-Sized City in North China.

Project description:Laboratory experiments were carried out to analyze 39 soil samples collected from four industrial areas in Xuzhou City using inductively coupled plasma mass spectrometry and atomic fluorescence spectrometry. The descriptive statistics of heavy metals (HMs) in the soil profiles showed that the HM content at three depths was highly variable, and most coefficients of variation (CVs) showed moderate variability. The enrichment of Cd at all depths exceeded the risk screening value, and Cd pollution occurred in four plants. The enrichment of the other HMs at three depths was mainly concentrated in the pharmaceutical plant A and chemical plant C. It was found that the different HMs had different vertical distribution characteristics. For the different industrial plants, the raw materials and products not only made the spatial distribution characteristics of the HMs different, but also caused the HM types and contents to differ. The average single pollution indices of Cd in plant A, iron-steel plant B, and plant C indicated a slight pollution level. The other seven HMs in A, B, and C and all HMs in chemical plant D belonged to the safe category. The mean values of the Nemerow pollution index in the four industrial plants belonged to the warning category. The analysis showed that none of the HMs posed potential noncarcinogenic health risks, and only the carcinogenic health risks of Cr in plants A and C were unacceptable. The carcinogenic effect of Cr through the inhalation intake of resuspended soil particulates and that of Cd, Ni, and As via direct oral ingestion were the main exposure pathways.

| S-EPMC10059013 | biostudies-literature

Vibrational Spectroscopy in Studies of Atmospheric Corrosion.

Project description:Vibrational spectroscopy has been successfully used for decades in studies of the atmospheric corrosion processes, mainly to identify the nature of corrosion products but also to quantify their amounts. In this review article, a summary of the main achievements is presented with focus on how the techniques infrared spectroscopy, Raman spectroscopy, and vibrational sum frequency spectroscopy can be used in the field. Several different studies have been discussed where these instruments have been used to assess both the nature of corrosion products as well as the properties of corrosion inhibitors. Some of these techniques offer the valuable possibility to perform in-situ measurements in real time on ongoing corrosion processes, which allows the kinetics of formation of corrosion products to be studied, and also minimizes the risk of changing the surface properties which may occur during ex-situ experiments. Since corrosion processes often occur heterogeneously over a surface, it is of great importance to obtain a deeper knowledge about atmospheric corrosion phenomena on the nano scale, and this review also discusses novel vibrational microscopy techniques allowing spectra to be acquired with a spatial resolution of 20 nm.

| S-EPMC5507006 | biostudies-other

Pollution Characteristics and Human Health Risk Assessment of Heavy Metals in Street Dust from a Typical Industrial Zone in Wuhan City, Central China.

Project description:This study aimed to assess the pollution levels, sources, and human health risks of heavy metals in street dust from a typical industrial district in Wuhan City, Central China. In total, 47 street dust samples were collected from the major traffic arteries and streets around Wuhan Iron and Steel (Group) Company (WISC) in Qingshan District, Wuhan. The concentrations of heavy metals (Cr, Mn, Ni, Zn, Fe, Cu, and Cd) in street dust were determined by atomic absorption spectroscopy. Results indicated that the mean concentrations of Zn (249.71 mg/kg), Cu (51.15 mg/kg), and Cd (0.86 mg/kg) in street dust were higher than their corresponding soil background values in Hubei Province. Heavy metal enrichment is closely related to urban transportation and industrial production. The pollution level of heavy metals in street dust was assessed using the geo-accumulation method (Igeo) and potential ecological risk assessment (PERI). Based on the Igeo value, Cr, Mn, Fe, and Ni showed no pollution, Zn and Cu showed light to moderate contamination, and Cd showed moderate contamination. The PERI values of heavy metals in street dust ranged between 76.70 and 7027.28, which represents a medium to high potential ecological risk. Principal component analysis showed that the sources of heavy metals in street dust were mainly influenced by anthropogenic activities. Among the studied metals, Cu, Cr, Zn, Fe, and Mn mainly come from industrial processes, while Ni and Cd come from traffic exhaust. The non-carcinogenic risk indexes of heavy metals for children and adults are ranked as Cr > Cu > Ni > Cd > Zn. The health risks to children through the different exposure pathways are higher than those for adults. Hand-to-mouth intake is the riskiest exposure pathway for non-carcinogenic risk. In addition, Cr, Ni, and Cd do not pose a carcinogenic risk for the residents.

| S-EPMC9518381 | biostudies-literature

Marine Atmospheric Corrosion of Carbon Steel: A Review.

Project description:The atmospheric corrosion of carbon steel is an extensive topic that has been studied over the years by many researchers. However, until relatively recently, surprisingly little attention has been paid to the action of marine chlorides. Corrosion in coastal regions is a particularly relevant issue due the latter's great importance to human society. About half of the world's population lives in coastal regions and the industrialisation of developing countries tends to concentrate production plants close to the sea. Until the start of the 21st century, research on the basic mechanisms of rust formation in Cl--rich atmospheres was limited to just a small number of studies. However, in recent years, scientific understanding of marine atmospheric corrosion has advanced greatly, and in the authors' opinion a sufficient body of knowledge has been built up in published scientific papers to warrant an up-to-date review of the current state-of-the-art and to assess what issues still need to be addressed. That is the purpose of the present review. After a preliminary section devoted to basic concepts on atmospheric corrosion, the marine atmosphere, and experimentation on marine atmospheric corrosion, the paper addresses key aspects such as the most significant corrosion products, the characteristics of the rust layers formed, and the mechanisms of steel corrosion in marine atmospheres. Special attention is then paid to important matters such as coastal-industrial atmospheres and long-term behaviour of carbon steel exposed to marine atmospheres. The work ends with a section dedicated to issues pending, noting a series of questions in relation with which greater research efforts would seem to be necessary.

| S-EPMC5506973 | biostudies-other

Health Risks and Contamination Levels of Heavy Metals in Dusts from Parks and Squares of an Industrial City in Semi-Arid Area of China.

Project description:The contamination characteristics and health risk of barium (Ba), cobalt (Co), chromium (Cr), copper (Cu), manganese (Mn), nickel (Ni), lead (Pb), vanadium (V), zinc (Zn), arsenic (As), mercury (Hg), and cadmium (Cd) in samples of dust gathered from squares and parks of Baotou city, an industrial city situated in a semi-arid location of the northwest China were investigated. The contents of Ba, Co, Cr, Cu, Mn, Ni, V, Pb, and Zn in the collected dust samples were determined using X-ray fluorescence spectrometry, while the contents of As and Hg in the dust were investigated by use of the ICP-MS. Further, cadmium was quantified through the atomic absorption spectrometry. Levels of contamination of heavy metals analyzed in the dust samples were evaluated using the Geo-Accumulation index (Igeo) as well as through a Pollution Load Index (PLI). Their health risks to children and adults were evaluated based on the US EPA model of health risk. The findings portrayed that the mean concentrations of Ba, Co Cr, Cu, Pb, V, Cd, and Hg were elevated as compared with their local soil background values. Mean values of Igeo illustrate the order of Co > Cr> Cd > Hg > Pb > Cu > Ba > V > Ni > Mn > Zn > As. It was evident that dusts from the parks and squares were "unpolluted" to "moderately polluted". Assessment of health risk depicts that ingestion is the foremost route of exposure in regard to the heavy metals, then the dermal adsorption follows. Hg exposure from dust might also set impending health threats to children. Besides, the cancer risks of Co, Cr, Ni, Cd, and As are considered to be within the presently tolerable range.

| S-EPMC5580590 | biostudies-literature

Large private shareholders, industrial policies and industrial loans of city commercial banks: Evidence from China.

Project description:We show that large private shareholders have an information advantage about their industry; this can alleviate the information asymmetry suffered by banks, and consequently, increase bank lending to these shareholders' industry. Using a sample of Chinese city commercial banks, we show that an increase in the large private shareholders' shareholding of banks increases bank lending to these shareholders' industry. Importantly, using Chinese local government industrial policy as a moderator, we find that industrial policies have a positive and significant moderating effect on the relationship between large private shareholders and banks' industry-specific lending. This relationship strengthens when local industrial policy supports these shareholders' industry. This helps explain why banks prefer the industries to which their large private shareholders belong to and how industrial policy affects bank credit allocation.

| S-EPMC9731413 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data