Polyhedral Palladium-Silver Alloy Nanocrystals as Highly Active and Stable Electrocatalysts for the Formic Acid Oxidation Reaction.

ABSTRACT: Polyhedral noble-metal nanocrystals have received much attention and wide applications as electrical and optical devices as well as catalysts. In this work, a straightforward and effective hydrothermal route for the controllable synthesis of the high-quality Pd-Ag alloy polyhedrons with uniform size is presented. The morphology, composition and structure of the Pd-Ag alloy polyhedrons are fully characterized by the various physical techniques, demonstrating the Pd-Ag alloy polyhedrons are highly alloying. The formation/growth mechanisms of the Pd-Ag alloy polyhedrons are explored and discussed based on the experimental observations and discussions. As a preliminary electrochemical application, the Pd-Ag alloy polyhedrons are applied in the formic acid oxidation reaction, which shows higher electrocatalytic activity and stability than commercially available Pd black due to the "synergistic effects" between Pd and Ag atoms.

SUBMITTER: Fu GT

PROVIDER: S-EPMC4556982 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Boosting activity and selectivity of glycerol oxidation over platinum-palladium-silver electrocatalysts <i>via</i> surface engineering.

Project description:A series of platinum-palladium-silver nanoparticles with tunable structures were synthesized for glycerol electro-oxidation in both alkaline and acidic solutions. Electrochemical results indicate that the catalysts show superior activity in alkaline solutions relative to acidic solutions. In alkaline solutions, the peak current densities of ammonia-etched samples are approximately twice those of saturated-NaCl-etched samples. Ammonia-etched platinum-palladium-silver (PtPd@Ag-NH3) exhibits a peak current density of 9.16 mA cm-2, which is 18.7 and 10 times those of the Pt/C and Pd/C, respectively. The product distribution was analyzed by high performance liquid chromatography. Seven products including oxalic acid, tartronic acid, glyoxylic acid, glyceric acid (GLA), glyceraldehyde (GALD), glycolic acid, and dihydroxyacetone (DHA) were detected. The NH3·H2O etched samples tend to generate more GALD, while the NaCl etched samples have a great potential to produce DHA. The addition of Pd atoms can facilitate glycerol oxidation pathway towards the direction of GALD generation. The Pt@Ag-NaCl possesses the largest DHA selectivity of 79.09% at 1.3 V, while the Pt@Ag-NH3 exhibits the largest GLA selectivity of 45.01% at 0.5 V. The PtPd@Ag-NH3 exhibits the largest C3/C2 ratio of 17.45. The selectivity and product distribution of glycerol electro-oxidation can be tuned by engineering the surface atoms of the as-synthesized catalysts.

| S-EPMC9419557 | biostudies-literature

How palladium inhibits CO poisoning during electrocatalytic formic acid oxidation and carbon dioxide reduction.

Project description:Development of reversible and stable catalysts for the electrochemical reduction of CO2 is of great interest. Here, we elucidate the atomistic details of how a palladium electrocatalyst inhibits CO poisoning during both formic acid oxidation to carbon dioxide and carbon dioxide reduction to formic acid. We compare results obtained with a platinum single-crystal electrode modified with and without a single monolayer of palladium. We combine (high-scan-rate) cyclic voltammetry with density functional theory to explain the absence of CO poisoning on the palladium-modified electrode. We show how the high formate coverage on the palladium-modified electrode protects the surface from poisoning during formic acid oxidation, and how the adsorption of CO precursor dictates the delayed poisoning during CO2 reduction. The nature of the hydrogen adsorbed on the palladium-modified electrode is considerably different from platinum, supporting a model to explain the reversibility of this reaction. Our results help in designing catalysts for which CO poisoning needs to be avoided.

| S-EPMC8748733 | biostudies-literature

Stable complete methane oxidation over palladium based zeolite catalysts.

Project description:Increasing the use of natural gas engines is an important step to reduce the carbon footprint of mobility and power generation sectors. To avoid emissions of unburnt methane and the associated severe greenhouse effect of lean-burn engines, the stability of methane oxidation catalysts against steam-induced sintering at low temperatures (<500?°C) needs to be improved. Here we demonstrate how the combination of catalyst development and improved process control yields a highly efficient solution for complete methane oxidation. We design a material based on palladium and hierarchical zeolite with fully sodium-exchanged acid sites, which improves the support stability and prevents steam-induced palladium sintering under reaction conditions by confining the metal within the zeolite. Repeated short reducing pulses enable the use of a highly active transient state of the catalyst, which in combination with its high stability provides excellent performance without deactivation for over 90?h in the presence of steam.

| S-EPMC6026177 | biostudies-literature

Palladium concave nanocrystals with high-index facets accelerate ascorbate oxidation in cancer treatment.

Project description:Intravenous pharmacological dose of ascorbate has been proposed as a potential antitumor therapy; however, its therapeutic efficacy is limited due to the slow autoxidation. Here, we report that palladium (Pd) nanocrystals, which possess intrinsic oxidase-like activity, accelerate the autoxidation of ascorbate, leading to the enhancement of its antitumor efficacy. The oxidase-like activity of Pd nanocrystals was facet-dependent, with the concave nanostructure enclosed by high-index facets catalyzing ascorbate autoxidation more efficiently than the planar nanostructure enclosed by low-index facets. Our first-principles calculations provide the underlying molecular mechanisms for the facet-dependent activation of O2 molecule and subsequent ascorbate oxidation. Further in vitro and in vivo assays demonstrate the enhancement of the antitumor efficacy of ascorbate with these Pd concave nanocubes. Our animal experiments also indicate the combined approach with both ascorbate and Pd concave nanocubes displays an even better efficacy than currently available clinical medicines, with no obvious cytotoxicity to normal cells.

| S-EPMC6243004 | biostudies-literature

Uniformly dispersed platinum-cobalt alloy nanoparticles with stable compositions on carbon substrates for methanol oxidation reaction.

Project description:Alloying platinum (Pt) with suitable transition metals is effective way to enhance their catalytic performance for methanol oxidation reaction, and reduce their cost at mean time. Herein, we report our investigation on the synthesis of bimetallic platinum-cobalt (PtCo) alloy nanoparticles, their activation, as well as the catalytic evaluation for methanol oxidation reaction. The strategy starts with the synthesis of PtCo alloy nanoparticles in an organic medium, followed by loading on carbon substrates. We then remove the capping agent by refluxing the carbon-supported PtCo particles in acetic acid before electrochemical measurements. We emphasize the change in composition of the alloys during refluxing process, and the initial PtCo alloys with Pt/Co ratio of 1/2 turns into stable alloys with Pt/Co ratio of 3/1. The final Pt3Co particles have uniform distribution on carbon substrates, and exhibit activity with 2.4 and 1.5 times of that for commercial Pt/C and PtRu/C for methanol oxidation reaction.

| S-EPMC5595832 | biostudies-other

Stable and Efficient PtRu Electrocatalysts Supported on Zn-BTC MOF Derived Microporous Carbon for Formic Acid Fuel Cells Application.

Project description:Highly efficient, well-dispersed PtRu alloy nanoparticles supported on high surface area microporous carbon (MPC) electrocatalysts, are prepared and tested for formic acid oxidation reaction (FAOR). The MPC is obtained by controlled carbonization of a zinc-benzenetricarboxylate metal-organic framework (Zn-BTC MOF) precursor at 950°C, and PtRu (30 wt.%) nanoparticles (NPs) are prepared and deposited via a polyol chemical reduction method. The structural and morphological characterization of the synthesized electrocatalysts is carried out using powder X-ray diffraction (PXRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), transmission electron microscopy (TEM), an energy dispersive X-ray (EDX) technique, and gas adsorption analysis (BET). The FAOR performance of the catalysts is investigated through cyclic voltammetry (CV), chronoamperometry (CA), and electrochemical impedance spectroscopy (EIS). A correlation between high electrochemical surface area (ECSA) and high FAOR performance of the catalysts is observed. Among the materials employed, Pt1Ru2/MPC 950 with a high electrochemical surface area (25.3 m2 g-1) consequently showed superior activity of the FAOR (I r = 9.50 mA cm-2 and J m = 2,403 mA mgPt-1 ) at room temperature, with improved tolerance and stability toward carbonaceous species. The superior electrochemical performance, and tolerance to CO-poisoning and long-term stability is attributed to the high surface area carbon support (1,455 m2 g-1) and high percentage loading of ruthenium (20 wt.%). The addition of Ru promotes the efficiency of electrocatalyst by offering FAOR via a bifunctional mechanism.

| S-EPMC7237749 | biostudies-literature

Convenient Synthesis of 3D Fluffy PtPd Nanocorals Loaded on 2D h-BN Supports as Highly Efficient and Stable Electrocatalysts for Alcohol Oxidation Reaction.

Project description:Fuel cells hold great promise for clean and sustainable energy, whereas their widespread commercialization strongly depends on the development of highly efficient and stable electrocatalysts. Herein, three-dimensional fluffy PtPd nanocorals (NCs) loaded on two-dimensional (2D) hexagonal boron nitride (h-BN) supports were successfully achieved by a simple one-step strategy based on ultraviolet (UV) laser-excited photochemical reaction. As for alcohol oxidation reaction, the h-BN/PtPd NCs with unique nanoporous surface provide more enhanced electrocatalytic performances than many previous nanocatalysts, owing to abundant active sites and plentiful charge-transfer channels formed on high electrode-electrolyte contact area. Especially, the mass activity of h-BN/PtPd NCs is about 962.8 mA mgPtPd -1 in methanol oxidation reaction in alkaline solution, which can be maintained at ∼274.9 mA mgPtPd -1 (28.6% of the initial one) even after a 5 × 104 s durability test. The present work not only offers an advanced electrocatalyst for long-term fuel cells but also provides a versatile route for construction of complex metallic nanocomposites on 2D supports, holding great potential for diverse energy-related applications.

| S-EPMC6648133 | biostudies-literature

Nanocomposite Concept for Electrochemical <i>In Situ</i> Preparation of Pt-Au Alloy Nanoparticles for Formic Acid Oxidation.

Project description:Herein, we report a straightforward approach for the in situ preparation of Pt-Au alloy nanoparticles from Pt + xAu/C nanocomposites using monometallic colloidal nanoparticles as starting blocks. Four different compositions with fixed Pt content and varying Pt to Au mass ratios from 1:1 up to 1:7 were prepared as formic acid oxidation reaction (FAOR) catalysts. The study was carried out in a gas diffusion electrode (GDE) setup. It is shown that the presence of Au in the nanocomposites substantially improves the FAOR activity with respect to pure Pt/C, which serves as a reference. The nanocomposite with a mass ratio of 1:5 between Pt and Au displays the best performance during potentiodynamic tests, with the electro-oxidation rates, overpotential, and poisoning resistance being improved simultaneously. By comparison, too low or too high Au contributions in the nanocomposites lead to an unbalanced performance in the FAOR. The combination of operando small-angle X-ray scattering (SAXS), scanning transmission electron microscopy (STEM) elemental mapping, and wide-angle X-ray scattering (WAXS) reveals that for the nanocomposite with a 1:5 mass ratio, a conversion between Pt and Au from separate nanoparticles to alloy nanoparticles occurs during continuous potential cycling in formic acid. By comparison, the nanocomposites with lower Au contents, for example, 1:2, exhibit less in situ alloying, and the concomitant performance improvement is less pronounced. On applying identical location transmission electron microscopy (IL-TEM), it is revealed that the in situ alloying is due to Pt dissolution and re-deposition onto Au as well as Pt migration and coalescence with Au nanoparticles.

| S-EPMC9327087 | biostudies-literature

Electrodeposition of Stable Noble-Metal-Free Co-P Electrocatalysts for Hydrogen Evolution Reaction.

Project description:Hydrogen production via water splitting has been extensively explored over the past few decades, and considerable effort has been directed toward finding more reactive and cost-effective electrocatalysts by engineering their compositions, shapes, and crystal structures. In this study, we developed hierarchical cobalt phosphide (Co-P) nanosphere assemblies as non-noble metal electrocatalysts via one-step electrodeposition. The morphologies of the Co-P nanostructures and their electrocatalytic activities towards the hydrogen evolution reactions (HER) were controlled by the applied potentials during electrodeposition. The physicochemical properties of the as-prepared Co-P nanostructures in this study were characterized by field-emission scanning electron microscopy, X-ray photoemission spectroscopy and X-ray diffraction. Linear sweep voltammetry revealed that the Co-P grown at -0.9 V showed the best HER performance exhibiting the highest electrochemical active surface area and lowest interfacial charge transfer resistance. The Co-P electrocatalysts showed superior long-term stability to electrodeposited Pt, indicating their potential benefits.

| S-EPMC9867289 | biostudies-literature

Facet-specific assembly of proteins on SrTiO? polyhedral nanocrystals.

Project description:Precisely controlling the protein-nanomaterial interactions at selective sites is crucial in engineering biomolecule composite architectures with tailored nanostructures and functions for a variety of biomedical applications. This strategy, however, is only beginning to be explored. Here, we demonstrate the facet-specific assembly of proteins, such as albumin, immunoglobulin and protamine, on {100} facets of SrTiO3 polyhedral nanocrystals, while none on {110} facets. Molecular dynamics simulations indicate the immobile surface hydration layer might play a barrier role to effectively prevent proteins adsorption on specific {110} facets. This work thus provides new insights into the fundamentally understanding of protein-nanomaterial interactions, and open a novel, general and facile route to control the selective adsorption of various proteins on various nanocrystals.

| S-EPMC4035585 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data