Methanol steam reforming promoted by molten salt-modified platinum on alumina catalysts.

ABSTRACT: We herein describe a straight forward procedure to increase the performance of platinum-on-alumina catalysts in methanol steam reforming by applying an alkali hydroxide coating according to the "solid catalyst with ionic liquid layer" (SCILL) approach. We demonstrate by diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) and temperature-programmed desorption (TPD) studies that potassium doping plays an important role in the catalyst activation. Moreover, the hygroscopic nature and the basicity of the salt modification contribute to the considerable enhancement in catalytic performance. During reaction, a partly liquid film of alkali hydroxides/carbonates forms on the catalyst/alumina surface, thus significantly enhancing the availability of water at the catalytically active sites. Too high catalyst pore fillings with salt introduce a considerable mass transfer barrier into the system as indicated by kinetic studies. Thus, the optimum interplay between beneficial catalyst modification and detrimental mass transfer effects had to be identified and was found on the applied platinum-on-alumina catalyst at KOH loadings around 7.5?mass%.

SUBMITTER: Kusche M

PROVIDER: S-EPMC4641462 | biostudies-literature | 2014 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Hydrogen Production from Methanol Steam Reforming over Fe-Modified Cu/CeO2 Catalysts.

Project description:Fe-modified Cu catalysts with CeO2 support, prepared by the impregnation method, were subjected to physicochemical analysis and catalytic tests in the steam reforming of methanol (SRM). Physicochemical studies of the catalysts were carried out using the XRF, TEM, STEM-EDS, XRD, TPR and nitrogen adsorption/desorption methods. XRD, TEM studies and catalytic tests of the catalysts were carried out at two reduction temperatures, 260 °C and 400 °C, to determine the relationship between the form and oxidation state of the active phase of the catalysts and the catalytic properties of these systems in the SRM. Additionally, the catalysts after the reaction were analysed for the changes in the structure and morphology using TEM methods. The presented results show that the composition of the catalysts, morphology, structure, form and oxidation state of the Cu and Fe active metals in the catalysts and the reaction temperature significantly impact their activity, selectivity and stability in the SRM process. The gradual deactivation of the studied catalysts under SRM conditions could result from the forming of carbon deposits and/or the gradual oxidation of the copper and iron phases under the reaction conditions.

| S-EPMC11357062 | biostudies-literature

Effects of P:Ni Ratio on Methanol Steam Reforming on Nickel Phosphide Catalysts.

Project description:This study investigates the influence of the phosphorus-to-nickel (P:Ni) ratio on methanol steam reforming (MSR) over nickel phosphide catalysts using density functional theory (DFT) calculations. The catalytic behavior of Ni(111) and Ni12P5(001) surfaces was explored and contrasted to our previous results from research on Ni2P(001). The DFT-predicted barriers reveal that Ni(111) predominantly favors the methanol decomposition route, where methanol is converted into carbon monoxide through a stepwise pathway involving CH3OH* → CH3O* → CH2O* → CHO* → CO*. On the other hand, Ni12P5 with a P:Ni atomic ratio of 0.42 (5:12) exhibits a substantial increase in selectivity towards methanol steam reforming (MSR) relative to methanol decomposition. In this pathway, formaldehyde is transformed into CO2 through a sequence of reactions involving CH2O*→ H2COOH* → HCOOH* → HCOO* → CO2. The introduction of phosphorus into the catalyst alters the surface morphology and electronic structure, favoring the MSR pathway. However, with a further increase in the P:Ni atomic ratio to 0.5 (1:2) on Ni2P catalysts, the selectivity towards MSR decreases, resulting in a more balanced competition between methanol decomposition and MSR. These results highlight the significance of tuning the P:Ni atomic ratio in designing efficient catalysts for the selective production of CO2 through the MSR route, offering valuable insights into optimizing nickel phosphide catalysts for desired chemical transformations.

| S-EPMC10459788 | biostudies-literature

Properties of Bulk In-Pt Intermetallic Compounds in Methanol Steam Reforming.

Project description:Heterogeneous catalysts are often complex materials containing different compounds. While this can lead to highly beneficial interfaces, it is difficult to identify the role of single components. In methanol steam reforming (MSR), the interplay between intermetallic compounds, supporting oxides and redox reactions leads to highly active and CO2 -selective materials. Herein, the intrinsic catalytic properties of unsupported In3 Pt2 , In2 Pt, and In7 Pt3 as model systems for Pt/In2 O3 -based catalytic materials in MSR are addressed. In2 Pt was identified as the essential compound responsible for the reported excellent CO2 -selectivity of 99.5 % at 300 °C in supported systems, showing a CO2 -selectivity above 99 % even at 400 °C. Additionally, the partial oxidation of In7 Pt3 revealed that too much In2 O3 is detrimental for the catalytic properties. The study highlights the crucial role of intermetallic In-Pt compounds in Pt/In2 O3 materials with excellent CO2 -selectivity.

| S-EPMC9311744 | biostudies-literature

Hydrogen Production by Steam Reforming of Ethanol over Nickel Catalysts Supported on Sol Gel Made Alumina: Influence of Calcination Temperature on Supports.

Project description:Selecting a proper support in the catalyst system plays an important role in hydrogen production via ethanol steam reforming. In this study, sol gel made alumina supports prepared for nickel (Ni) catalysts were calcined at different temperatures. A series of (Ni/AlS.G.) catalysts were synthesized by an impregnation procedure. The influence of varying the calcination temperature of the sol gel made supports on catalyst activity was tested in ethanol reforming reaction. The characteristics of the sol gel alumina supports and Ni catalysts were affected by the calcination temperature of the supports. The structure of the sol gel made alumina supports was transformed in the order of γ → (γ + θ) → θ-alumina as the calcination temperature of the supports increased from 600 °C to 1000 °C. Both hydrogen yield and ethanol conversion presented a volcano-shaped behavior with maximum values of 4.3 mol/mol ethanol fed and 99.5%, respectively. The optimum values were exhibited over Ni/AlS.G800 (Ni catalyst supported on sol gel made alumina calcined at 800 °C). The high performance of the Ni/AlS.G800 catalyst may be attributed to the strong interaction of Ni species and sol gel made alumina which lead to high nickel dispersion and small particle size.

| S-EPMC5458952 | biostudies-other

Interplay of Support Chemistry and Reaction Conditions on Copper Catalyzed Methanol Steam Reforming.

Project description:A series of Cu catalysts supported on SiO2, Al2O3-SiO2, TiO2 rutile, and Cu/TiO2 anatase metal oxides has been studied for methanol reforming in the vapor phase. The highest activity was obtained on Cu/SiO2 catalysts (5493 ?mol H2 min-1·gcat -1) followed by Cu/TiO2 rutile, Cu/Al2O3-SiO2, and anatase. XRD and HRTEM characterization after reaction revealed that on Cu/SiO2 significant sintering occurred during reaction. In contrast, the particle size growth on Cu/TiO2 rutile and anatase was less pronounced, which could be associated with the interaction between Cu clusters and TiO2. Characterization by TGA showed that on Cu/Al2O3-SiO2 the main cause of deactivation was coke deposition.

| S-EPMC6251558 | biostudies-literature

Role of Fe Species of Ni-Based Catalysts for Efficient Low-Temperature Ethanol Steam Reforming.

Project description:The suppression of methane and coke formation over Ni-based catalysts for low temperature ethanol steam reforming remains challenging. This paper describes the structural evolution of Fe-modified Ni/MgAl2O4 catalysts and the influence of iron species on methane and coke suppression for low temperature ethanol steam reforming. Ni-Fe alloy catalysts are gradually oxidized by water to generate Ni-rich alloy and γ-Fe2O3 species at steam-to-carbon ratio of 4. The electron transfer from iron to nickel within Ni-Fe alloy weakens the CO adsorption and effectively alleviates the CO/CO2 methanation. The oxidation capacity of γ-Fe2O3 species promotes the transformation of ethoxy to acetate groups to avoid methane formation and the elimination of carbon deposits for anticoking. Ni10Fe10/MgAl2O4 shows a superior performance with a highest H2 yield of 4.6 mol/mol ethanol at 400 °C for 15 h. This research could potentially provide instructions for the design of Ni-based catalysts for low-temperature ethanol steam reforming.

| S-EPMC8479767 | biostudies-literature

The sol-gel autocombustion as a route towards highly CO2-selective, active and long-term stable Cu/ZrO2 methanol steam reforming catalysts.

Project description:The adaption of the sol-gel autocombustion method to the Cu/ZrO2 system opens new pathways for the specific optimisation of the activity, long-term stability and CO2 selectivity of methanol steam reforming (MSR) catalysts. Calcination of the same post-combustion precursor at 400 °C, 600 °C or 800 °C allows accessing Cu/ZrO2 interfaces of metallic Cu with either amorphous, tetragonal or monoclinic ZrO2, influencing the CO2 selectivity and the MSR activity distinctly different. While the CO2 selectivity is less affected, the impact of the post-combustion calcination temperature on the Cu and ZrO2 catalyst morphology is more pronounced. A porous and largely amorphous ZrO2 structure in the sample, characteristic for sol-gel autocombustion processes, is obtained at 400 °C. This directly translates into superior activity and long-term stability in MSR compared to Cu/tetragonal ZrO2 and Cu/monoclinic ZrO2 obtained by calcination at 600 °C and 800 °C. The morphology of the latter Cu/ZrO2 catalysts consists of much larger, agglomerated and non-porous crystalline particles. Based on aberration-corrected electron microscopy, we attribute the beneficial catalytic properties of the Cu/amorphous ZrO2 material partially to the enhanced sintering resistance of copper particles provided by the porous support morphology.

| S-EPMC8238116 | biostudies-literature

Propane Steam Reforming over Catalysts Derived from Noble Metal (Ru, Rh)-Substituted LaNiO3 and La0.8Sr0.2NiO3 Perovskite Precursors.

Project description:The propane steam reforming (PSR) reaction was investigated over catalysts derived from LaNiO3 (LN), La0.8Sr0.2NiO3 (LSN), and noble metal-substituted LNMx and LSNMx (M = Ru, Rh; x = 0.01, 0.1) perovskites. The incorporation of foreign cations in the A and/or B sites of the perovskite structure resulted in an increase in the specific surface area, a shift of XRD lines toward lower diffraction angles, and a decrease of the mean primary crystallite size of the parent material. Exposure of the as-prepared samples to reaction conditions resulted in the in situ development of new phases including metallic Ni and La2O2CO3, which participate actively in the PSR reaction. The LN-derived catalyst exhibited higher activity compared to LSN, and its performance for the title reaction did not change appreciably following partial substitution of Ru for Ni. In contrast, incorporation of Ru and, especially, Rh in the LSN perovskite matrix resulted in the development of catalysts with significantly enhanced catalytic performance, which improved by increasing the noble metal content. The best results were obtained for the LSNRh0.1-derived sample, which exhibited excellent long-term stability for 40 hours on stream as well as high propane conversion (XC3H8 = 92%) and H2 selectivity (SH2 = 97%) at 600 °C.

| S-EPMC8401020 | biostudies-literature

Hydrogen Production from Gadolinium-Promoted Yttrium-Zirconium-Supported Ni Catalysts through Dry Methane Reforming

Project description:Hydrogen production from dry reforming of methane (DRM)

| S-EPMC10286284 | biostudies-literature

CO(2)-selective methanol steam reforming on In-doped Pd studied by in situ X-ray photoelectron spectroscopy.

Project description:In situ X-ray photoelectron spectroscopy (in situ XPS) was used to study the structural and catalytic properties of Pd-In near-surface intermetallic phases in correlation with previously studied PdZn and PdGa.Room temperature deposition of ∼4 monolayer equivalents (MLEs) of In metal on Pd foil and subsequent annealing to 453 K in vacuum yields a ∼1:1 Pd/In near-surface multilayer intermetallic phase. This Pd(1)In(1) phase exhibits a similar "Cu-like" electronic structure and indium depth distribution as its methanol steam reforming (MSR)-selective multilayer Pd(1)Zn(1) counterpart.Catalytic characterization of the multilayer Pd(1)In(1) phase in MSR yielded a CO(2)-selectivity of almost 100% between 493 and 550 K. In contrast to previously studied In(2)O(3)-supported PdIn nanoparticles and pure In(2)O(3), intermediate formaldehyde is only partially converted to CO(2) using this Pd(1)In(1) phase. Strongly correlated with PdZn, on an In-diluted PdIn intermetallic phase with "Pd-like" electronic structure, prepared by thermal annealing at 623 K, methanol steam reforming is suppressed and enhanced CO formation via full methanol dehydrogenation is observed.To achieve CO(2)-TOF values on the isolated Pd(1)In(1) intermetallic phase as high as on supported PdIn/In(2)O(3), at least 593 K reaction temperature is required. A bimetal-oxide synergism, with both bimetallic and oxide synergistically contributing to the observed catalytic activity and selectivity, manifests itself by accelerated formaldehyde-to-CO(2) conversion at markedly lowered temperatures as compared to separate oxide and bimetal. Combination of suppression of full methanol dehydrogenation to CO on Pd(1)In(1) inhibited inverse water-gas-shift reaction on In(2)O(3) and fast water activation/conversion of formaldehyde is the key to the low-temperature activity and high CO(2)-selectivity of the supported catalyst.

| S-EPMC3485566 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data