Preparation of Pd supported on La(Sr)-Mn-O Perovskite by microwave Irradiation Method and Its Catalytic Performances for the Methane Combustion.

ABSTRACT: In this work, a series of palladium supported on the La0.8Sr0.2MnO3.15 perovskite catalysts (Pd/LSM-x) with different Pd loading were prepared by microwave irradiation processing plus incipient wetness impregnation method and characterized by XRD, TEM, H2-TPR and XPS. These catalysts were evaluated on the lean CH4 combustion. The results show that the Pd/LSM-x samples prepared by microwave irradiation processing possess relative higher surface areas than LSM catalyst. The addition of Pd to the LSM leads to the increase in the oxygen vacancy content and the enhancement in the mobility of lattice oxygen which play an important role on the methane combustion. The Pd/LSM-3 catalysts with 4.2wt% Pd loading exhibited the best performance for CH4 combustion that temperature for 10% and 90% of CH4 conversion is 315 and 520 °C.

SUBMITTER: Wang W

PROVIDER: S-EPMC4726093 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Water electrolysis on La(1-x)Sr(x)CoO(3-?) perovskite electrocatalysts.

Project description:Perovskite oxides are attractive candidates as catalysts for the electrolysis of water in alkaline energy storage and conversion systems. However, the rational design of active catalysts has been hampered by the lack of understanding of the mechanism of water electrolysis on perovskite surfaces. Key parameters that have been overlooked include the role of oxygen vacancies, B-O bond covalency, and redox activity of lattice oxygen species. Here we present a series of cobaltite perovskites where the covalency of the Co-O bond and the concentration of oxygen vacancies are controlled through Sr(2+) substitution into La(1-x)Sr(x)CoO(3-?) . We attempt to rationalize the high activities of La(1-x)Sr(x)CoO(3-?) through the electronic structure and participation of lattice oxygen in the mechanism of water electrolysis as revealed through ab initio modelling. Using this approach, we report a material, SrCoO2.7, with a high, room temperature-specific activity and mass activity towards alkaline water electrolysis.

| S-EPMC4814573 | biostudies-literature

Catalytic Performance of Palladium Supported on Sheaf-Like Ceria in the Lean Methane Combustion.

Project description:Sheaf-like CeO2 (CeO2-S) in microscale was prepared by the hydrothermal method, and then etched with KOH aiming to obtain an imperfect fluorite structure (CeO2-SK) with high content of oxygen vacancies and oxygen mobility. With CeO2-S and CeO2-SK as supports respectively, a modified colloidal deposition method was employed to obtain Pd/CeO2 catalysts for being used in lean methane combustion. According to the inductively coupled plasma (ICP), N2 physisorption and scanning electron microscopy (SEM) results, the Pd supported catalysts are very similar in their Pd loading, surface area and morphologies. SEM and transmission electron microscopy (TEM) results revealed various nanorods exposed CeO2 (110) and (100) facets on Pd/CeO2-SK surface after KOH etching. Raman spectra and H2-temperature programmed reduction (H2-TPR) results indicated that Pd/CeO2-SK catalyst has a much higher content of catalytic active PdO species than Pd/CeO2-S catalyst. It was also found that the catalytic performance of Pd/CeO2 in lean methane combustion depends greatly upon the exposing crystal planes and oxygen vacancies content of sheaf-like CeO2, and Pd/CeO2-SK exhibits higher activity than Pd/CeO2-S. The larger amount of CeO2 (110) and (100) planes on Pd/CeO2-SK surface can enhance the formation of oxygen vacancies, active Pd species and migration of lattice oxygen, which all evidently improve the redox ability and catalytic activity of the Pd/CeO2-SK catalysts in lean methane combustion.

| S-EPMC7022713 | biostudies-literature

AMnO3 (A = Sr, La, Ca, Y) Perovskite Oxides as Oxygen Reduction Electrocatalysts.

Project description:A series of perovskite-type manganites AMnO3 (A = Sr, La, Ca and Y) particles were investigated as electrocatalysts for the oxygen reduction reaction. AMnO3 materials were synthesized by means of an ionic-liquid method, yielding phase pure particles at different temperatures. Depending on the calcination temperature, particles with mean diameter between 20 and 150 nm were obtained. Bulk versus surface composition and structure are probed by X-ray photoelectron spectroscopy and extended X-ray absorption fine structure. Electrochemical studies were performed on composite carbon-oxide electrodes in alkaline environment. The electrocatalytic activity is discussed in terms of the effective Mn oxidation state, A:Mn particle surface ratio and the Mn-O distances.

| S-EPMC6413806 | biostudies-literature

Enhanced Microwave Absorption Properties of Intrinsically Core/shell Structured La(0.6)Sr(0.4)MnO(3) Nanoparticles.

Project description:The intrinsically core/shell structured La(0.6)Sr(0.4)MnO(3) nanoparticles with amorphous shells and ferromagnetic cores have been prepared. The magnetic, dielectric and microwave absorption properties are investigated in the frequency range from 1 to 12 GHz. An optimal reflection loss of -41.1 dB is reached at 8.2 GHz with a matching thickness of 2.2 mm, the bandwidth with a reflection loss less than -10 dB is obtained in the 5.5-11.3 GHz range for absorber thicknesses of 1.5-2.5 mm. The excellent microwave absorption properties are a consequence of the better electromagnetic matching due to the existence of the protective amorphous shells, the ferromagnetic cores, as well as the particular core/shell microstructure. As a result, the La(0.6)Sr(0.4)MnO(3) nanoparticles with amorphous shells and ferromagnetic cores may become attractive candidates for the new types of electromagnetic wave absorption materials. ELECTRONIC SUPPLEMENTARY MATERIAL: The online version of this article (doi:10.1007/s11671-009-9374-y) contains supplementary material, which is available to authorized users.

| S-EPMC2894104 | biostudies-literature

Selective electrochemical decomposition of outgrowths and nanopatterning in La 0.7 Sr 0.3 MnO3 perovskite thin films.

Project description:The outgrowth formation in inorganic thin films is a dramatic problem that has limited the technological impact of many techniques and materials. Outgrowths are often themselves part of the films, but are detrimental for vertical junctions since they cause short-circuits or work as defects, compromising the reproducibility and in some cases the operation of the corresponding devices. The problem of outgrowth is particularly relevant in ablation-based methods and in some complex oxides, but is present in a large variety of systems and techniques. Here we propose an efficient local electrochemical method to selectively decompose the outgrowths of conductive oxide thin films by electrochemical decomposition, without altering the properties of the background film. The process is carried out using the same set-up as for local oxidation nanolithography, except for the sign of the voltage bias and it works at the nanoscale both as serial method using a scanning probe and as parallel method using conductive stamps. We demonstrated our process using La 0.7 Sr 0.3 MnO3 perovskite as a representative material but in principle it can be extended to many other conductive systems.

| S-EPMC4261174 | biostudies-literature

Onset of High Methane Combustion Rates over Supported Palladium Catalysts: From Isolated Pd Cations to PdO Nanoparticles.

Project description:Industrial low-temperature methane combustion catalyst Pd/Al2O3 suffers from H2O-induced deactivation. It is imperative to design Pd catalysts free from this deactivation and with high atomic efficiency. Using a small-pore zeolite SSZ-13 as support, herein we report well-defined Pd catalysts with dominant active species as finely dispersed Pd cations, uniform PdO particles embedded inside the zeolite framework, or PdO particles decorating the zeolite external surface. Through detailed reaction kinetics and spectroscopic and microscopic studies, we show that finely dispersed sites are much less active than PdO nanoparticles. We further demonstrate that H2O-induced deactivation can be readily circumvented by using zeolite supports with high Si/Al ratios. Finally, we provide a few rational catalyst design suggestions for methane oxidation based on the new knowledge learned in this study.

| S-EPMC8395651 | biostudies-literature

Probing the temperature of supported platinum nanoparticles under microwave irradiation by in situ and operando XAFS.

Project description:Microwave irradiation can cause high local temperatures at supported metal nanoparticles, which can enhance reaction rates. Here we discuss the temperature of platinum nanoparticles on γ-Al2O3 and SiO2 supports under microwave irradiation using the Debye-Waller factor obtained from in situ extended X-ray absorption fine structure (EXAFS) measurements. Microwave irradiation exhibits considerably smaller Deby-Waller factors than conventional heating, indicating the high local temperature at the nanoparticles. The difference in the average temperatures between the platinum nanoparticles and the bulk under microwaves reaches 26 K and 132 K for Pt/Al2O3 and Pt/SiO2, respectively. As a result, Pt/SiO2 exhibits considerably more reaction acceleration for the catalytic dehydrogenation of 2-propanol under microwave irradiation than Pt/Al2O3. We also find microwaves enhance the reduction of PtOx nanoparticles by using operando X-ray absorption near edge structure (XANES) spectroscopy. The present results indicate that significant local heating of platinum nanoparticles by microwaves is effective for the acceleration of catalytic reactions.

| S-EPMC9814256 | biostudies-literature

Structurally distorted perovskite La0.8Sr0.2Mn0.5Co0.5O3-δ by graphene nanoplatelet and their composite for supercapacitors with enhanced stability.

Project description:Supercapacitors are promising energy storage devices with high charging/discharging speeds and power densities. To improve their poor stability, we fabricated electrodes by integrating perovskite materials (La0.8Sr0.2Mn0.5Co0.5O3-δ, LSMCO) possessing redox reaction ability with graphene nanoplatelets exhibiting good electronic properties. One of the resultant composites (L25G70) demonstrated high capacitance and excellent capacitance retention (95% after 5000 cycles). These results are superior to other electrodes (L50G45 and L75G20) containing a larger ratio of LSMCO, even L75G20 did not exhibit supercapacitor behavior after 3000 cycles. GN can induce structural distortion in LSMCO, thereby the high amount of adsorbed oxygen per lattice oxygen can explain the best electrochemical performance of L25G70, while structural collapse rationalized the failure of L75G20. The findings of this study demonstrated that the use of LSMCO can improve the cycling stability of supercapacitors.

| S-EPMC9203535 | biostudies-literature

Enhancement of Uranium Recycling from Tailings Caused by the Microwave Irradiation-Induced Composite Oxidation of the Fe–Mn Binary System

Project description:The extraction of

| S-EPMC9301716 | biostudies-literature

Mn-inlaid antiphase boundaries in perovskite structure.

Project description:Improvements in the polarization of environmentally-friendly perovskite ferroelectrics have proved to be a challenging task in order to replace the toxic Pb-based counterparts. In contrast to common methods by complex chemical composition designs, we have formed Mn-inlaid antiphase boundaries in Mn-doped (K,Na)NbO3 thin films using pulsed laser deposition method. Here, we observed that mono- or bi-atomic layer of Mn has been identified to inlay along the antiphase boundaries to balance the charges originated from the deficiency of alkali ions and to induce the strain in the KNN films. Thus, rectangular saturated polarization-electric field hysteresis loops have been achieved, with a significantly improved twice remanent polarization of 114 μC/cm2 with an applied electric field of 606 kV/cm, which can be comparable to that of the typical Pb-based thin films. Moreover, we directly see the Mn occupation at the A-site of KNN perovskite structure using atomic-scale microstructure and composition analysis. The Mn-inlaid antiphase boundary can further enrich the understanding of perovskite crystal structure and give more possibilities for the design and optimization of perovskite materials.

| S-EPMC11306794 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data