Mycosynthesis of silver nanoparticles bearing antibacterial activity.

ABSTRACT: Mycosynthesis of silver nanoparticles was achieved by endophytic Colletotrichum sp. ALF2-6 inhabiting Andrographis paniculata. Well dispersed nanoparticles were characterized using UV-Visible spectrometry with maximum absorption conferring at 420 nm. FTIR analysis revealed possible biomolecules reducing the metal salt and stabilization of nanoparticles. XRD analysis depicted the diffraction intensities exhibiting between 20 and 80 °C at 2theta angle thus conferring the crystalline nature of nanoparticles. Morphological characteristic using TEM revealed the polydispersity of nanoparticles with size ranging from 20 to 50 nm. Synthesized nanoparticles exhibited bactericidal activity against selected human pathogens. Nanoparticles mode of action was carried out to reveal DNA damage activity. Thus the present investigation reports facile fabrication of silver nanoparticles from endophytic fungi.

SUBMITTER: Azmath P

PROVIDER: S-EPMC4792906 | biostudies-literature | 2016 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Mycosynthesis of silver nanoparticles bearing antibacterial activity.

Azmath Pasha P Baker Syed S Rakshith Devaraju D Satish Sreedharamurthy S

Saudi pharmaceutical journal : SPJ : the official publication of the Saudi Pharmaceutical Society 20150121 2

Mycosynthesis of silver nanoparticles was achieved by endophytic Colletotrichum sp. ALF2-6 inhabiting Andrographis paniculata. Well dispersed nanoparticles were characterized using UV-Visible spectrometry with maximum absorption conferring at 420 nm. FTIR analysis revealed possible biomolecules reducing the metal salt and stabilization of nanoparticles. XRD analysis depicted the diffraction intensities exhibiting between 20 and 80 °C at 2theta angle thus conferring the crystalline nature of nano ...[more]

PMID: 27013906

Similar Datasets

Project description:BackgroundIt is generally accepted that antibacterial properties of Ag nanoparticles (AgNPs) are dictated by their dissolved fraction. However, dissolution-based concept alone does not fully explain the toxic potency of nanoparticulate silver compared to silver ions.Methodology/principal findingsHerein, we demonstrated that the direct contact between bacterial cell and AgNPs' surface enhanced the toxicity of nanosilver. More specifically, cell-NP contact increased the cellular uptake of particle-associated Ag ions - the single and ultimate cause of toxicity. To prove that, we evaluated the toxicity of three different AgNPs (uncoated, PVP-coated and protein-coated) to six bacterial strains: Gram-negative Escherichia coli, Pseudomonas fluorescens, P. putida and P. aeruginosa and Gram-positive Bacillus subtilis and Staphylococcus aureus. While the toxicity of AgNO3 to these bacteria varied only slightly (the 4-h EC50 ranged from 0.3 to 1.2 mg Ag/l), the 4-h EC50 values of protein-coated AgNPs for various bacterial strains differed remarkably, from 0.35 to 46 mg Ag/l. By systematically comparing the intracellular and extracellular free Ag(+) liberated from AgNPs, we demonstrated that not only extracellular dissolution in the bacterial test environment but also additional dissolution taking place at the particle-cell interface played an essential role in antibacterial action of AgNPs. The role of the NP-cell contact in dictating the antibacterial activity of Ag-NPs was additionally proven by the following observations: (i) separation of bacterial cells from AgNPs by particle-impermeable membrane (cut-off 20 kDa, ?4 nm) significantly reduced the toxicity of AgNPs and (ii) P. aeruginosa cells which tended to attach onto AgNPs, exhibited the highest sensitivity to all forms of nanoparticulate Ag.Conclusions/significanceOur findings provide new insights into the mode of antibacterial action of nanosilver and explain some discrepancies in this field, showing that "Ag-ion" and "particle-specific" mechanisms are not controversial but, rather, are two faces of the same coin.

Project description:The present study was carried out to reduce the size of silver nanoparticles (AgNPs) by optimizing physico-chemical conditions of the Aspergillus fumigatus BTCB10 growth based on central composite design (CCD) through response surface methodology (RSM). Variables such as a concentration of silver nitrate (mM), NaCl (%) and the wet weight of biomass (g) were controlled to produce spherical, monodispersed particles of 33.23 nm size, observing 78.7% reduction in size as compared to the initially obtained size that was equal to 356 nm. The obtained AgNPs exhibited negative zeta potential of -9.91 mV with a peak at 420 nm in the UV-Vis range whereas Fourier Transform Infrared (FT-IR) analysis identified O-H, C = C, C ≡ C, C-Br and C-Cl groups attached as capping agents. After conducting RSM experiments, a high nitrate reductase activity value of 179.15 nmol/h/ml was obtained; thus indicating a likely correlation between enzyme production and AgNPs synthesis. The F-value (significant at 3.91), non-significant lack of fit and determination coefficient (R2 = 0.7786) is representative of the good relation between the predicted values of response. We conclude that CCD is an effective tool in obtaining significant results of high quality and efficiency.The present study was carried out to reduce the size of silver nanoparticles (AgNPs) by optimizing physico-chemical conditions of the Aspergillus fumigatus BTCB10 growth based on central composite design (CCD) through response surface methodology (RSM). Variables such as a concentration of silver nitrate (mM), NaCl (%) and the wet weight of biomass (g) were controlled to produce spherical, monodispersed particles of 33.23 nm size, observing 78.7% reduction in size as compared to the initially obtained size that was equal to 356 nm. The obtained AgNPs exhibited negative zeta potential of –9.91 mV with a peak at 420 nm in the UV-Vis range whereas Fourier Transform Infrared (FT-IR) analysis identified O–H, C = C, C ≡ C, C–Br and C–Cl groups attached as capping agents. After conducting RSM experiments, a high nitrate reductase activity value of 179.15 nmol/h/ml was obtained; thus indicating a likely correlation between enzyme production and AgNPs synthesis. The F-value (significant at 3.91), non-significant lack of fit and determination coefficient (R2 = 0.7786) is representative of the good relation between the predicted values of response. We conclude that CCD is an effective tool in obtaining significant results of high quality and efficiency.

Dataset Information

Mycosynthesis of silver nanoparticles bearing antibacterial activity.

Publications

Mycosynthesis of silver nanoparticles bearing antibacterial activity.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure