Modification of Ni-Rich FCG NMC and NCA Cathodes by Atomic Layer Deposition: Preventing Surface Phase Transitions for High-Voltage Lithium-Ion Batteries.

ABSTRACT: The energy density of current lithium-ion batteries (LIBs) based on layered LiMO2 cathodes (M = Ni, Mn, Co: NMC; M = Ni, Co, Al: NCA) needs to be improved significantly in order to compete with internal combustion engines and allow for widespread implementation of electric vehicles (EVs). In this report, we show that atomic layer deposition (ALD) of titania (TiO2) and alumina (Al2O3) on Ni-rich FCG NMC and NCA active material particles could substantially improve LIB performance and allow for increased upper cutoff voltage (UCV) during charging, which delivers significantly increased specific energy utilization. Our results show that Al2O3 coating improved the NMC cycling performance by 40% and the NCA cycling performance by 34% at 1 C/-1 C with respectively 4.35 V and 4.4 V UCV in 2 Ah pouch cells. High resolution TEM/SAED structural characterization revealed that Al2O3 coatings prevented surface-initiated layered-to-spinel phase transitions in coated materials which were prevalent in uncoated materials. EIS confirmed that Al2O3-coated materials had significantly lower increase in the charge transfer component of impedance during cycling. The ability to mitigate degradation mechanisms for Ni-rich NMC and NCA illustrated in this report provides insight into a method to enable the performance of high-voltage LIBs.

SUBMITTER: Mohanty D

PROVIDER: S-EPMC4880920 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Nanoscale morphological and chemical changes of high voltage lithium-manganese rich NMC composite cathodes with cycling.

Project description:Understanding the evolution of chemical composition and morphology of battery materials during electrochemical cycling is fundamental to extending battery cycle life and ensuring safety. This is particularly true for the much debated high energy density (high voltage) lithium-manganese rich cathode material of composition Li(1 + x)M(1 - x)O2 (M = Mn, Co, Ni). In this study we combine full-field transmission X-ray microscopy (TXM) with X-ray absorption near edge structure (XANES) to spatially resolve changes in chemical phase, oxidation state, and morphology within a high voltage cathode having nominal composition Li1.2Mn0.525Ni0.175Co0.1O2. Nanoscale microscopy with chemical/elemental sensitivity provides direct quantitative visualization of the cathode, and insights into failure. Single-pixel (? 30 nm) TXM XANES revealed changes in Mn chemistry with cycling, possibly to a spinel conformation and likely including some Mn(II), starting at the particle surface and proceeding inward. Morphological analysis of the particles revealed, with high resolution and statistical sampling, that the majority of particles adopted nonspherical shapes after 200 cycles. Multiple-energy tomography showed a more homogeneous association of transition metals in the pristine particle, which segregate significantly with cycling. Depletion of transition metals at the cathode surface occurs after just one cycle, likely driven by electrochemical reactions at the surface.

| S-EPMC4134180 | biostudies-other

Graphene collage on Ni-rich layered oxide cathodes for advanced lithium-ion batteries.

Project description:The energy storage performance of lithium-ion batteries (LIBs) depends on the electrode capacity and electrode/cell design parameters, which have previously been addressed separately, leading to a failure in practical implementation. Here, we show how conformal graphene (Gr) coating on Ni-rich oxides enables the fabrication of highly packed cathodes containing a high content of active material (~99 wt%) without conventional conducting agents. With 99 wt% LiNi0.8Co0.15Al0.05O2 (NCA) and electrode density of ~4.3 g cm-3, the Gr-coated NCA cathode delivers a high areal capacity, ~5.4 mAh cm-2 (~38% increase) and high volumetric capacity, ~863 mAh cm-3 (~34% increase) at a current rate of 0.2 C (~1.1 mA cm-2); this surpasses the bare electrode approaching a commercial level of electrode setting (96 wt% NCA; ~3.3 g cm-3). Our findings offer a combinatorial avenue for materials engineering and electrode design toward advanced LIB cathodes.

| S-EPMC8035182 | biostudies-literature

Size controllable single-crystalline Ni-rich cathodes for high-energy lithium-ion batteries

Project description:ABSTRACT A single-crystalline Ni-rich (SCNR) cathode with a large particle size can achieve higher energy density, and is safer, than polycrystalline counterparts. However, synthesizing large SCNR cathodes (>5 μm) without compromising electrochemical performance is very challenging due to the incompatibility between Ni-rich cathodes and high temperature calcination. Herein, we introduce Vegard's Slope as a guide for rationally selecting sintering aids, and we successfully synthesize size-controlled SCNR cathodes, the largest of which can be up to 10 μm. Comprehensive theoretical calculation and experimental characterization show that sintering aids continuously migrate to the particle surface, suppress sublattice oxygen release and reduce the surface energy of the typically exposed facets, which promotes grain boundary migration and elevates calcination critical temperature. The dense SCNR cathodes, fabricated by packing of different-sized SCNR cathode particles, achieve a highest electrode press density of 3.9 g cm−3 and a highest volumetric energy density of 3000 Wh L−1. The pouch cell demonstrates a high energy density of 303 Wh kg−1, 730 Wh L−1 and 76% capacity retention after 1200 cycles. SCNR cathodes with an optimized particle size distribution can meet the requirements for both electric vehicles and portable devices. Furthermore, the principle for controlling the growth of SCNR particles can be widely applied when synthesizing other materials for Li-ion, Na-ion and K-ion batteries. Controllable grain sizes in a wide range enable the single-crystalline Ni-rich cathode to break through the bottleneck of volumetric energy density, which makes it qualified to replace LiCoO2 and alleviate the cobalt crisis.

| S-EPMC9935991 | biostudies-literature

Enhancing the Electrochemical Performance of Ni-Rich LiNi0.88Co0.09Al0.03O2 Cathodes through Tungsten-Doping for Lithium-Ion Batteries.

Project description:The tungsten-doped (0.5 and 1.0 mol%) LiNi0.88Co0.09Al0.03O2 (NCA) cathode materials are manufactured to systematically examine the stabilizing effect of W-doping. The 1.0 mol% W-doped LiNi0.88Co0.09Al0.03O2 (W1.0-NCA) cathodes deliver 173.5 mAh g-1 even after 100 cycles at 1 C, which is 95.2% of the initial capacity. While the capacity retention of NCA cathodes cycled in identical conditions is 86.3%. The optimal performances of the W1.0-NCA could be ascribed to the suppression of impendence increase and the decrease in anisotropic volume change, as well as preventing the collapse of structures during cycling. These findings demonstrate that the W-doping considerably enhances the electrochemical performance of NCA, which has potential applications in the development of Ni-rich layered cathode materials that can display high capacity with superior cycling stability.

| S-EPMC8912114 | biostudies-literature

High Energy Density Single-Crystal NMC/Li6PS5Cl Cathodes for All-Solid-State Lithium-Metal Batteries.

Project description:To match the high capacity of metallic anodes, all-solid-state batteries require high energy density, long-lasting composite cathodes such as Ni-Mn-Co (NMC)-based lithium oxides mixed with a solid-state electrolyte (SSE). However in practice, cathode capacity typically fades due to NMC cracking and increasing NMC/SSE interface debonding because of NMC pulverization, which is only partially mitigated by the application of a high cell pressure during cycling. Using smart processing protocols, we report a single-crystal particulate LiNi0.83Mn0.06Co0.11O2 and Li6PS5Cl SSE composite cathode with outstanding discharge capacity of 210 mA h g-1 at 30 °C. A first cycle coulombic efficiency of >85, and >99% thereafter, was achieved despite a 5.5% volume change during cycling. A near-practical discharge capacity at a high areal capacity of 8.7 mA h cm-2 was obtained using an asymmetric anode/cathode cycling pressure of only 2.5 MPa/0.2 MPa.

| S-EPMC8397257 | biostudies-literature

Biobased Acrylic Latexes/Sodium Carboxymethyl Cellulose Aqueous Binders for Lithium-Ion NMC 811 Cathodes.

Project description:The increasing demands for sustainable energy storage technologies have prompted extensive research in the development of eco-friendly materials for lithium-ion batteries (LIBs). This research article presents the design of biobased latexes, which are fluorine-free and rely on renewable resources, based on isobornyl methacrylate (IBOMA) and 2-octyl acrylate (2OA) to be used as binders in batteries. Three different compositions of latexes were investigated, varying the ratio of IBOMA and 2OA: (1) Poly2OA homopolymer, (2) Poly(2OA0,6-co-IBOMA0,4) random copolymer, and (3) PolyIBOMA homopolymer. The combination of the two monomers provided a balance between rigidity from the hard monomer (IBOMA) and flexibility from the soft one (2OA). The study evaluated the performance of the biobased latexes using sodium carboxymethyl cellulose (CMC) as a thickener and cobinder by fabricating LiNi0.8Mn0.1Co0.1O2 (NMC 811) cathodes. Also, to compare with the state of the art, organic processed PVDF electrodes were prepared. Among aqueous slurries, rheological analysis showed that the CMC + Poly(2OA0,6-co-IBOMA0,4) binder system resulted in the most stable and well-dispersed slurries. Also, the electrodes prepared with this latex demonstrated enhanced adhesion (210 ± 9 N m-1) and reduced cracks compared to other aqueous compositions. Electrochemical characterization revealed that the aqueous processed cathodes using the CMC + Poly(2OA0,6-co-IBOMA0,4) biobased latex displayed higher specific capacities than the control with no latex at high C-rates (100.3 ± 2.1 vs 64.5 ± 0.8 mAh g-1 at 5C) and increased capacity retention after 90 cycles at 0.5C (84% vs 81% for CMC with no latex). Overall, the findings of this study suggest that biobased latexes, specifically the CMC + Poly(2OA0,6-co-IBOMA0,4) composition, are promising as environmentally friendly binders for NMC 811 cathodes, contributing to the broader goal of achieving sustainable energy storage systems.

| S-EPMC10825816 | biostudies-literature

Surface Coupling between Mechanical and Electric Fields Empowering Ni-Rich Cathodes with Superior Cyclabilities for Lithium-Ion Batteries.

Project description:Ni-rich cathodes with high energy densities are considered as promising candidates for advanced lithium-ion batteries, whereas their commercial application is in dilemma due to dramatic capacity decay and poor structure stability stemmed from interfacial instability, structural degradation, and stress-strain accumulation, as well as intergranular cracks. Herein, a piezoelectric LiTaO3 (LTO) layer is facilely deposited onto Li[Nix Coy Mn1- x - y ]O2 (x = 0.6, 0.8) cathodes to induce surface polarized electric fields via the intrinsic stress-strain of Ni-rich active materials, thus modulating interfacial Li+ kinetics upon cycling. Various characterizations indicate that the electrochemical performances of LTO-modified cathodes are obviously enhanced even under large current density and elevated temperature. Intensive explorations from in situ X-ray diffraction technique, finite element analysis, and first-principle calculation manifest that the improvement mechanism of LTO decoration can be attributed to the enhanced structural stability of bulk material, suppressed stress accumulation, and regulated ion transportation. These findings provide deep insight into surface coupling strategy between mechanical and electric fields to regulate the interfacial Li+ kinetics behavior and enhance structure stability for Ni-rich cathodes, which will also arouse great interest from scientists and engineers in multifunctional surface engineering for electrochemical systems.

| S-EPMC9218785 | biostudies-literature

Reclaimed and Up-Cycled Cathodes for Lithium-Ion Batteries.

Project description:As electric vehicles become more widely used, there is a higher demand for lithium-ion batteries (LIBs) and hence a greater incentive to find better ways to recycle these at their end-of-life (EOL). This work focuses on the process of reclamation and re-use of cathode material from LIBs. Black mass containing mixed LiMn2O4 and Ni0.8Co0.15Al0.05O2 from a Nissan Leaf pouch cell are recovered via two different recycling routes, shredding or disassembly. The waste material stream purity is compared for both processes, less aluminium and copper impurities are present in the disassembled waste stream. The reclaimed black mass is further treated to reclaim the transition metals in a salt solution, Ni, Mn, Co ratios are adjusted in order to synthesize an upcycled cathode, LiNi0.6Mn0.2Co0.2O2 via a co-precipitation method. The two reclamation processes (disassembly and shredding) are evaluated based on the purity of the reclaimed material, the performance of the remanufactured cell, and the energy required for the complete process. The electrochemical performance of recycled material is comparable to that of as-manufactured cathode material, indicating no detrimental effect of purified recycled transition metal content. This research represents an important step toward scalable approaches to the recycling of EOL cathode material in LIBs.

| S-EPMC9749079 | biostudies-literature

Construction of Uniform LiF Coating Layers for Stable High-Voltage LiCoO2 Cathodes in Lithium-Ion Batteries.

Project description:Stabilizing LiCoO2 (LCO) at 4.5 V rather than the common 4.2 V is important for the high specific capacity. In this study, we developed a simple and efficient way to improve the stability of LiCoO2 at high voltages. After a simple sol-gel method, we introduced trifluoroacetic acid (TA) to the surface of LCO via an afterwards calcination. Meanwhile, the TA reacted with residual lithium on the surface of LCO, further leading to the formation of uniform LiF nanoshells. The LiF nanoshells could effectively restrict the interfacial side reaction, hinder the transition metal dissolution and thus achieve a stable cathode-electrolyte interface at high working-voltages. As a result, the LCO@LiF demonstrated a much superior cycling stability with a capacity retention ratio of 83.54% after 100 cycles compared with the bare ones (43.3% for capacity retention), as well as high rate performances. Notably, LiF coating layers endow LCO with excellent high-temperature performances and outstanding full-cell performances. This work provides a simple and effective way to prepare stable LCO materials working at a high voltage.

| S-EPMC10974255 | biostudies-literature

LFP-Based Gravure Printed Cathodes for Lithium-Ion Printed Batteries.

Project description:Printed batteries have undergone increased investigation in recent years because of the growing daily use of small electronic devices. With this in mind, industrial gravure printing has emerged as a suitable production technology due to its high speed and quality, and its capability to produce any shape of image. The technique is one of the most appealing for the production of functional layers for many different purposes, but it has not been highly investigated. In this study, we propose a LiFePO4 (LFP)-based gravure printed cathode for lithium-ion rechargeable printed batteries and investigate the possibility of employing this printing technique in battery manufacture.

| S-EPMC6631390 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data