Cranial bone regeneration according to different particle sizes and densities of demineralized dentin matrix in the rabbit model.
Ontology highlight
ABSTRACT: Background
The objective of this study was to place bone graft materials in cranial defects in a rabbit model and compare their bone regenerating ability according to the size and density of demineralized dentin matrix (DDM).Methods
We selected nine healthy male rabbits that were raised under the same conditions and that weighed about 3 kg. Two circular defects 8 mm in diameter were created in each side of the cranium. The defects were grafted with DDM using four different particle sizes and densities: 0.1 mL of 0.25- to 1.0-mm particles (group 1); 0.2 mL of 0.25- to 1.0-mm particles (group 2); 0.1 mL of 1.0- to 2.0-mm particles (group 3); and 0.2 mL of 1.0- to 2.0-mm particles (group 4). After 2, 4, and 8 weeks, the rabbits were sacrificed, and bone samples were evaluated by means of histologic, histomorphometric, and quantitative RT-PCR analysis.Results
In group 1, osteoblast activity and bone formation were greater than in the other three groups on histological examination. In groups 2, 3, and 4, dense connective tissue was seen around original bone even after 8 weeks. Histomorphometric analysis of representative sections in group 1 showed a higher rate of new bone formation, but the difference from the other groups was not statistically significant. RT-PCR analysis indicated a correlation between bone formation and protein (osteonectin and osteopontin) expression.Conclusions
DDM with a space between particles of 200 μm was effective in bone formation, suggesting that materials with a small particle size could reasonably be used for bone grafting.
SUBMITTER: Nam JW
PROVIDER: S-EPMC4932123 | biostudies-literature |
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:Demineralized dentin matrix (DDM)-based materials have been actively developed and are well-known for their excellent performance in dental tissue regeneration. However, DDM-based bio-ink suitable for fabrication of engineered dental tissues that are patient-specific in terms of shape and size, has not yet been developed. In this study, we developed a DDM particle-based bio-ink (DDMp bio-ink) with enhanced three-dimensional (3D) printability. The bio-ink was prepared by mixing DDM particles and a fibrinogen-gelatin mixture homogeneously. The effects of DDMp concentration on the 3D printability of the bio-ink and dental cell compatibility were investigated. As the DDMp concentration increased, the viscosity and shear thinning behavior of the bio-ink improved gradually, which led to the improvement of the ink's 3D printability. The higher the DDMp content, the better were the printing resolution and stacking ability of the 3D printing. The printable minimum line width of 10% w/v DDMp bio-ink was approximately 252 μm, whereas the fibrinogen-gelatin mixture was approximately 363 μm. The ink's cytocompatibility test with dental pulp stem cells (DPSCs) exhibited greater than 95% cell viability. In addition, as the DDMp concentration increased, odontogenic differentiation of DPSCs was significantly enhanced. Finally, we demonstrated that cellular constructs with 3D patient-specific shapes and clinically relevant sizes could be fabricated through co-printing of polycaprolactone and DPSC-laden DDMp bio-ink.
| S-EPMC8071469 | biostudies-literature
Project description:BackgroundDentin is a permeable tubular composite and complex structure, and in weight, it is composed of 20% organic matrix, 10% water, and 70% hydroxyapatite crystalline matrix. Demineralization of dentin with gradient concentrations of ethylene diamine tetraacetic acid, 0.6 N hydrochloric acid, or 2% nitric acid removes a major part of the crystalline apatite and maintains a majority of collagen type I and non-collagenous proteins, which creates an osteoinductive scaffold containing numerous matrix elements and growth factors. Therefore, demineralized dentin should be considered as an excellent naturally-derived bioactive material to enhance dental and alveolar bone tissues regeneration.MethodThe PubMed and Midline databases were searched in October 2021 for the relevant articles on treated dentin matrix (TDM)/demineralized dentin matrix (DDM) and their potential roles in tissue regeneration.ResultsSeveral studies with different study designs evaluating the effect of TDM/DDM on dental and bone tissues regeneration were found. TDM/DDM was obtained from human or animal sources and processed in different forms (particles, liquid extract, hydrogel, and paste) and different shapes (sheets, slices, disc-shaped, root-shaped, and barrier membranes), with variable sizes measured in micrometers or millimeters, demineralized with different protocols regarding the concentration of demineralizing agents and exposure time, and then sterilized and preserved with different techniques. In the act of biomimetic acellular material, TDM/DDM was used for the regeneration of the dentin-pulp complex through direct pulp capping technique, and it was found to possess the ability to activate the odontogenic differentiation of stem cells resident in the pulp tissues and induce reparative dentin formation. TDM/DDM was also considered for alveolar ridge and maxillary sinus floor augmentations, socket preservation, furcation perforation repair, guided bone, and bioroot regenerations as well as bone and cartilage healing.ConclusionTo our knowledge, there are no standard procedures to adopt a specific form for a specific purpose; therefore, future studies are required to come up with a well-characterized TDM/DDM for each specific application. Likely as decellularized dermal matrix and prospectively, if the TDM/DDM is supplied in proper consistency, forms, and in different sizes with good biological properties, it can be used efficiently instead of some widely-used regenerative biomaterials.
| S-EPMC9294090 | biostudies-literature
Project description:ObjectivesThis study aimed to examine the influence of particle size and extent of demineralization of dentin matrix on bone regeneration.Materials and methodsExtracted human teeth were pulverized and divided into 3 groups according to particle size; 200, 500, and 1000 μm. Each group was divided into 3 groups depending on the extent of demineralization; undemineralized dentin (UDD), partially demineralized dentin matrix (PDDM), and completely demineralized dentin matrix (CDDM). The dentin sample was implanted into rat calvarial bone defects. After 4 and 8 weeks, the bone regeneration was evaluated with micro-CT images, histomorphometric and immunohistochemical analyses. Osteoblasts were cultured on UDD and DDM to evaluate the cell attachment using electron microscope.ResultsMicro-CT images and histological observation revealed that CDDM had largely resorbed but UDD had not, and both of them induced little bone formation, whereas all particle sizes of PDDM induced more new bone, especially the 1000 μm. Electron microscopic observation showed osteoblasts attached to DDM but not to UDD.ConclusionsPDDM with larger particle size induced prominent bone regeneration, probably because PDDM possessed a suitable surface for cell attachment. There might be an exquisite balance between its resorption and bone formation on it. PDDM could be considered as a potential bone substitute.
| S-EPMC4721666 | biostudies-literature
Project description:ObjectivesDentin, the bulk material of the tooth, resemble the bone's chemical composition and is considered a valuable bone substitute. In the current study, we assessed the cytotoxicity and osteogenic potential of demineralized dentin matrix (DDM) in comparison to HA nanoparticles (n-HA) on bone marrow mesenchymal stem cells (BMMSCs) using a hydrogel formulation.Materials and methodsHuman extracted teeth were minced into particles and treated via chemical demineralization using ethylene diamine tetra-acetic acid solution (EDTA) to produce DDM particles. DDM and n-HA particles were added to the sodium alginate then, the combination was dripped into a 5% (w/v) calcium chloride solution to obtain DDM hydrogel (DDMH) or nano-hydroxyapatite hydrogel (NHH). The particles were evaluated by dynamic light scattering (DLS) and the hydrogels were evaluated via scanning electron microscope (SEM). BMMSCs were treated with different hydrogel concentrations (25%, 50%, 75% and neat/100%) and cell viability was evaluated using MTT assay after 72 h of culture. Collagen-I (COL-I) gene expression was studied with real-time quantitative polymerase chain reaction (RT-qPCR) after 3 weeks of culture and alkaline phosphatase (ALP) activity was assessed using enzyme-linked immune sorbent assay (ELISA) over 7th, 10th, 14th and 21st days of culture. BMMSCs seeded in a complete culture medium were used as controls. One-way ANOVA was utilized to measure the significant differences in the tested groups.ResultsDLS measurements revealed that DDM and n-HA particles had negative values of zeta potential. SEM micrographs showed a porous microstructure of the tested hydrogels. The viability results revealed that 100% concentrations of either DDMH or NHH were cytotoxic to BMMSCs after 72 h of culture. However, the cytotoxicity of 25% and 50% concentrations of DDMH were not statistically significant compared to the control group. RT-qPCR showed that COL-I gene expression was significantly upregulated in BMMSCs cultured with 50% DDMH compared to all other treated or control groups (P < 0.01). ELISA analysis revealed that ALP level was significantly increased in the groups treated with 50% DDMH compared to 50% NHH after 21 days in culture (P < 0.001).ConclusionThe injectable hydrogel containing demineralized dentin matrix was successfully formulated. DDMH has a porous structure and has been shown to provide a supporting matrix for the viability and differentiation of BMMSCs. A 50% concentration of DDMH was revealed to be not cytotoxic to BMMSCs and may have a great potential to promote bone formation ability.
| S-EPMC10148431 | biostudies-literature
Project description:While proanthocyanidins (PA) are effective in improving collagen's resistance to collagenolytic degradation, the direct incorporation of PA into an adhesive system is detrimental to the light-curing thereof. Conversely, the use of PA as a primer could circumvent this issue, but little is known about the efficacy of PA in stabilizing collagen when applied in a clinically relevant manner. This study investigated the pre- and post-digestion morphology of an acid-etched dentin collagen layer that underwent PA treatment for time periods on a scale of seconds. The null hypothesis, that there is no difference between the PA-treated and untreated control group, had to be rejected, since it was revealed that the untreated control could not survive 1 hr of exogenous collagenase digestion, while the PA-treated collagen could sustain at least 16 hrs of digestion with no perceptible changes in collagen structure. In addition, the stabilizing effect of the gold-standard cross-linker glutaraldehyde at comparable experimental conditions was found to be almost non-existent within the 5, 15, or 30 sec of cross-linking permitted. Therefore, PA have been proven to be extraordinarily efficient in stabilizing demineralized dentin collagen against enzymatic challenges in a clinically relevant setting, likely due to the non-covalent nature of their interaction with collagen molecules.
| S-EPMC3711569 | biostudies-literature
Project description:Demineralized dentin matrix (DDM) treated with gamma irradiation (GR) has shown promising results as an allograft without any adverse effects in in vivo and clinical studies. The purpose of this study was to evaluate the effects of 15 and 25 kGy GR on the osteoinductive properties of DDM at extra-skeletal sites. As a control group, non-irradiated DDM powder was implanted into the right subcutaneous tissues of the dorsal thigh muscles of 20 nude mice. DDM powder irradiated with 15 and 25 kGy was implanted into the left side. After two and four weeks, the bone mineral density (BMD) was measured with dual-energy X-ray absorptiometry. After confirming osteoblast- and osteoclast-specific activities by alkaline phosphatase (ALP) and tartrate-resistant acid phosphatase (TRAP) staining, a histological analysis was performed to measure the new bone formation and the number of osteoblasts and osteoclast-like cells on the surface of the DDMs. Histomorphometry was used to calculate the new bone formation area on the surface of the DDM particles (DDMs). The BMD in all the groups increased from two and four weeks without statistically significant differences. The osteoblasts were dominantly activated on DDM without GR, and DDM treated with 25 kGy compared to DDM treated with 15 kGy. Among the groups, new bone formation was identified in all the groups at each time point. In conclusion, GR at doses of 15 and 25 kGy does not affect the osteoinductive properties of DDM powder.
| S-EPMC8883982 | biostudies-literature
Project description:ObjectiveThe purpose of this study was to prospectively evaluate the efficacy of a demineralized dentin matrix (DDM) in decreasing the initial inflammatory response of the gingiva and facilitating the repair and regeneration of soft tissue in alveolar ridge preservation.MethodsThis clinical study employed a split-mouth design. Fourteen patients with a total of forty-four sites underwent extraction and alveolar ridge preservation (ARP) procedures. A Bilaterally symmetrical extraction operation were conducted on the premolars of each patient. The experimental group received DDM as a graft material for ARP, while the control group underwent natural healing. Within the first month postoperatively, the pain condition, color, and swelling status of the extraction sites were initially assessed at different time points Subsequently, measurements were taken for buccal gingival margin height, buccal-lingual width, extraction socket contour, and the extraction socket area and healing rate were digitally measured. Additionally, Alcian Blue staining was used for histological evaluation of the content during alveolar socket healing.ResultsBoth groups experienced uneventful healing, with no adverse reactions observed at any of the extraction sites. The differences in VAS pain scores between the two groups postoperatively were not statistically significant. In the early stage of gingival tissue healing (3 days postoperatively), there were statistically significant differences in gingival condition and buccal gingival margin height between the two groups. In the later stage of gingival tissue healing (7, 14, and 30 days postoperatively), there were statistically significant differences in buccal-lingual width, extraction socket healing area, and healing rate between the two groups. Furthermore, the histological results from Alcian Blue staining suggested that the experimental group may play a significant role in promoting gingival tissue healing, possibly by regulating inflammatory responses when compared to the control group.ConclusionThe application of DDM in alveolar ridge preservation has been found to diminish initial gingival inflammation after tooth extraction. Additionally, it has shown the ability to accelerate early gingival soft tissue healing and preserve its anatomical contour.Clinical trial registrationchictr.org.cn, identifier ChiCTR2100050650.
| S-EPMC10622762 | biostudies-literature
Project description:Background/purposeDemineralized dentin matrix (DDM) is used as a tissue regeneration scaffold. Effective preservation of DDM benefits clinical applications. Cryopreservation and freeze-drying may be effective methods to retain DDM mechanical properties and biological activity.Materials and methodsHuman periodontal ligament stem cells (hPDLSCs) isolated using enzymatic dissociation were identified by multidirectional differentiation and flow cytometry. DDM was prepared with EDTA and divided into four groups: fresh DDM (fDDM), room temperature-preserved DDM (rtDDM), cryopreserved DDM (cDDM) and freeze-dried DDM (fdDDM). The DDM surface morphology was observed, and microhardness was detected. Transforming growth factor-β1 (TGF-β1), fibroblast growth factor (FGF) and collagen-Ⅰ (COL-Ⅰ) concentrations in DDM liquid extracts were detected by enzyme-linked immunosorbent assay (ELISA). The hPDLSCs were cultured with DDM liquid extracts. The effect of DDM on cells proliferation was examined by CCK-8 assay. The effect of DDM on hPDLSC secreted phosphoprotein-1 (SPP1), periostin (POSTN) and COL-Ⅰ gene expression was examined by real-time qPCR.ResultscDDM dentinal tubules were larger than those of the other groups. The three storage conditions had no significant effect on DDM microhardness and COL-Ⅰ concentration. However, TGF-β1 and FGF concentrations decreased after storage, with the greatest change in rtDDM, followed by fdDDM and cDDM. The liquid extracts of fDDM, cDDM and fdDDM slightly inhibited hPDLSCs proliferation, but those of rtDDM had no significant effect. The hPDLSCs cultured with fDDM, cDDM and fdDDM liquid extracts showed increased SPP1, POSTN and COL-Ⅰ gene expression.ConclusionCryopreservation and freeze-drying better maintain the mechanical properties and biological activity of DDM.
| S-EPMC9236943 | biostudies-literature
Project description:We aimed to evaluate the efficacy of demineralized dentin matrix (DDM) fixed with recombinant human bone morphogenetic protein-2 (rhBMP-2) through an experimental and a clinical study. Unilateral upper second and third premolars of eight beagles were extracted. A mucoperiosteal flap was elevated around the extraction socket, and a bone defect was made using a surgical drill. Each DDM was fixed with rhBMP-2, and autogenous bone was grafted at the bone defect area with a collagenous membrane. The beagles were euthanized at two, four, eight, and 12 weeks after receiving the bone graft. Block specimens involving grafted bone and surrounding natural bone were extracted. A total of 23 patients who received bone grafts using human DDM fixed with rhBMP-2 (AutoBT BMP) with implant placements (36 implants; maxilla: 14, mandible: 22) were selected. The implant stability, marginal bone loss, and clinical outcome were evaluated. Three trephine cores were harvested fourmonths after bone grafting, and histologic examination was performed. In the histological evaluation performed four weeks after the bone graft, autogenous bone showed 52% new bone formation and DDM fixed with rhBMP-2 showed 33% new bone formation. Twelve weeks after the bone graft, autogenous bone showed 75% new bone formation and DDM fixed with rhBMP-2 showed 48% new bone formation. In the clinical study, favorable osseointegration was obtained in 35 out of 36 implant sites (one case of osseointegration failure). In all cases, severe complications were not observed. Histomorphometrically, new bone formation was observed in 14.98% of the cases. The residual DDM particles were 6.22%. AutoBT BMP provides good osteoinductive and osteoconductive potential and clinical efficacy.
| S-EPMC5615704 | biostudies-literature
Project description:This study aimed to evaluate the bonding strength and thermal properties of demineralized dentin with and without EDC treatment. Sound human molars were randomly divided into seven treatment groups (n = 20): control, 80% ethanol, and five EDC ethanol solutions (0.01-1.0 M). In each group, 16 samples were used for bond strength assessment and 4 samples were used for scanning electron microscopy (SEM) analysis. A further 70 intact molars were used to obtain a fine demineralized dentin powder, treated with the same solutions and were evaluated the crosslink degree by ninhydrin test and denaturation temperature (Td) by differential scanning calorimetry. EDC-treated specimens (<1.0 M) had a higher bond strength, especially 0.3 and 0.5 M group, than the control counterpart. There was a significant drop in bond strength of 1.0 M EDC group. SEM revealed a homogeneous and regular interface under all treatments. EDC treatment significantly increased the demineralized dentin cross-link degree and Td compared with the control and ethanol treatments. The 0.3 and 0.5 M treatments showed the highest cross-link degree and Td. In terms of mechnical and theramal properties consideration, 0.3 and 0.5 M EDC solutions may be favorable for when applied with etch-and-rinse adhesives, but it is still needed further long-term study.
| S-EPMC5457252 | biostudies-other