γ irradiation induced effects on bismuth active centres and related photoluminescence properties of Bi/Er co-doped optical fibres.

ABSTRACT: We investigate the effects of γ irradiation on bismuth active centres (BACs) and related photoluminescence properties of bismuth/erbium co-doped silica fibre (BEDF), [Si] ~28, [Ge] ~1.60, [Al] ~0.10, [Er] ~ <0.10 and [Bi] ~0.10 atom%, fabricated by in-situ solution doping and Modified Chemical Vapor Deposition (MCVD). The samples were irradiated at 1 kGy, 5 kGy, 15 kGy, 30 kGy and 50 kGy doses, and dose rate of 5.5 kGy/h, at room temperature. The optical properties of BEDF samples are tested before and after γ irradiation. We found that high dose γ irradiation could significantly influence the formation and composition of BACs and their photoluminescence performance, as important changes in absorption and emission properties associated with the 830 nm pump produces the direct evidence of γ irradiation effects on BAC-Si. We notice that the saturable to unsaturable absorption ratio at pump wavelength could be increased with high dose γ irradiation, indicating that emission and pump efficiency could be increased by γ irradiation. Our experimental results also reveal good radiation survivability of the BEDF under low and moderate γ irradiation. Our investigation suggests the existence of irradiation related processing available for tailoring the photoluminescence properties and performance of bismuth doped/co-doped fibres.

SUBMITTER: Sporea D

PROVIDER: S-EPMC4954960 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Laser restructuring and photoluminescence of glass-clad GaSb/Si-core optical fibres.

Project description:Semiconductor-core optical fibres have potential applications in photonics and optoelectronics due to large nonlinear optical coefficients and an extended transparency window. Laser processing can impose large temperature gradients, an ability that has been used to improve the uniformity of unary fibre cores, and to inscribe compositional variations in alloy systems. Interest in an integrated light-emitting element suggests a move from Group IV to III-V materials, or a core that contains both. This paper describes the fabrication of GaSb/Si core fibres, and a subsequent CO2 laser treatment that aggregates large regions of GaSb without suppressing room temperature photoluminescence. The ability to isolate a large III-V crystalline region within the Si core is an important step towards embedding semiconductor light sources within infrared light-transmitting silicon optical fibre.

| S-EPMC6470204 | biostudies-literature

Enhanced Photoluminescence and Photocatalytic Efficiency of La-Doped Bismuth Molybdate: Its Preparation and Characterization.

Project description:Herein, a systematic study of the enhanced physicochemical properties of lanthanide doped (La-doped) bismuth molybdate (Bi2MoO6) is performed. For this purpose, Bi2MoO6 and La-doped Bi2MoO6 were prepared by the sol-gel method. BiCl3, Na2MoO4·2H2O, and LaCl3·7H2O were taken as the main precursors while sodium dodecyl sulfate was used as a surfactant. Both Bi2MoO6 and La-doped Bi2MoO6 were calcined at 650 °C for 2 h. These prepared materials were characterized by spectroscopic techniques such as UV-VIS, FT-IR, XRD, photoluminescence, XPS, along with other techniques such as SEM, TEM, TGA, etc. The investigation of luminescence behavior revealed that the La-doped Bi2MoO6 nanocomposite exhibited much greater luminescence compared to the undoped Bi2MoO6. The photocatalytic behavior of the prepared materials was explored by studying the degradation of methylene blue (MB) at room temperature. The degradation of MB with Bi2MoO6 and La-doped bismuth molybdate were observed to be 68% and 75% @ 45 s, respectively, indicating an enhancement of catalytic performance due to the La doping.

| S-EPMC6981540 | biostudies-literature

Lanthanide-doped bismuth-based nanophosphors for ratiometric upconversion optical thermometry.

Project description:Nanothermometry could realize stable, efficient, and noninvasive temperature detection at the nanoscale. Unfortunately, most applications of nanothermometers are still limited due to their intricate synthetic process and low-temperature sensitivity. Herein, we reported a kind of novel bismuth-based upconversion nanomaterial with a fast and facile preparation strategy. The bismuth-based upconversion luminophore was synthesized by the co-precipitation method within 1 minute. By optimizing the doping ratio of the sensitizer Yb ion and the activator Er ion and adjusting the synthetic solvent strategy, the crystallinity of the nanomaterials was increased and the upconversion luminescence intensity was improved. Ratiometric upconversion optical measurements of temperature in the range of 278 K to 358 K can be achieved by ratiometric characteristic emission peaks of thermally sensitive Er ion. This method of rapidly constructing nanometer temperature probes provides a feasible strategy for the construction of novel fluorescent temperature probes.

| S-EPMC8985227 | biostudies-literature

Quantitatively Analyzing Pressure Induced Phase Transformation by Photoluminescence Spectra in Eu3+-doped Sodium Potassium Bismuth Titanate.

Project description:(Na0.8,K0.2)0.5Bi0.497Eu0.003TiO3 (NKBET20) piezoelectric ceramic powders were prepared by the solid-reaction method. The phase structures of the NKBET20 powders under various pressures were investigated by photoluminescence (PL) spectra and X-ray diffraction (XRD). The PL spectra of the doped Eu3+ ions suggest a pressure induced transformation from the tetragonal to rhombohedral phase (R phase), and the phase transformations were confirmed by XRD analyses. Furthermore, the fluorescence intensity ratio of the D 0 5 ? F 2 7 transition to the D 0 5 ? F 1 7 transition (FIR21) could be utilized for the quantitative analyses of the phase transformation. The results from the PL method show that as the pressure increases from 0 to 500 MPa, the fractions of the R phase of the NKBET20 powders increase from about 11% to 58%, while the fractions of the tetragonal phase (T phase) decrease from about 89% to 42%, which are consistent with the XRD Rietveld refinement. Unlike the ceramic bulks, the pressure induced phase transformation in the ceramic powders shows no obvious trigger point and is much gentler. This work suggests a different viewpoint to study the pressure induced phase transformation qualitatively and quantitatively, which can be used for more phase analyses.

| S-EPMC7079660 | biostudies-literature

Solar Photocatalytic Degradation of Trace Organic Pollutants in Water by Bi(0)-Doped Bismuth Oxyhalide Thin Films.

Project description:Herein, we demonstrate the fabrication of Bi(0)-doped bismuth oxyhalide solid solution films for the removal of trace organic pollutants (TrOPs) in water. With the advantage of a viscous AlOOH sol, very high loadings (75 wt %) of bismuth oxyhalides were embedded within the thin films and calcined at 500 °C to develop porous alumina composite coatings. Various concentrations of Bi(0) doping were tested for their photocatalytic activity. Seven TrOPs including iopromide (IPRM), iohexol (IHX), iopamidol (IPMD), sulfamethoxazole (SMX), carbamazepine, venlafaxine, and bezafibrate (BZF) were selected for this study based on their occurrence and detection in effluents and surface waters worldwide. In all tests, with the exception of IPRM, 3% Bi(0)-doped BiOCl0.875Br0.125 showed highest activity, which can be attributed to its unique, highly organized, and compact morphology besides its well-matched energy band positions. Although IPMD, IHX, IPRM, and SMX are susceptible to photolysis, still the photocatalytic activity significantly augmented the removal of all tested compounds. In addition, analysis of the surface charge excluded electrostatic interactions and confirmed the ion-exchange adsorption mechanism for the high degradation rate of BZF in the presence of bismuth oxyhalides.

| S-EPMC6645048 | biostudies-literature

Photoluminescence of monovalent indium centres in phosphate glass

Project description:Valence control of polyvalent cations is important for functionalization of various kinds of materials. Indium oxides have been used in various applications, such as indium tin oxide in transparent electrical conduction films. However, although metastable In+ (5 s2 configuration) species exhibit photoluminescence (PL), they have attracted little attention. Valence control of In+ cations in these materials will be important for further functionalization. Here, we describe In+ species using PL and X-ray absorption fine structure (XAFS) analysis. Three absorption bands in the UV region are attributed to the In+ centre: two weak forbidden bands (1S0 → 3P1,1S0 → 3P2) and a strong allowed band (1S0 → 1P1). The strongest PL excitation band cannot be attributed to the conventional allowed transition to the singlet excited state. Emission decay of the order of microseconds suggests that radiative relaxation occurs from the triplet excitation state. The XAFS analysis suggests that these In+ species have shorter In–O distances with lower coordination numbers than in In2O3. These results clearly demonstrate that In+ exists in a metastable amorphous network, which is the origin of the observed luminescent properties.

| S-EPMC4555169 | biostudies-literature

Enhanced Activation of Persulfate by Co-Doped Bismuth Ferrite Nanocomposites for Degradation of Levofloxacin Under Visible Light Irradiation.

Project description:In this study, magnetic visible light driven photocatalysts (bismuth ferrite, Bi2Fe4O9, BFO and Co-doped bismuth ferrite, Co-BFO) were successfully prepared by the facile hydrothermal method. The catalyst was used in the application of heterogeneous persulfate (PS) system under visible LED light irradiation for the degradation of levofloxacin (LFX), proving to be an excellent photocatalyst when evaluated by various characterization methods. The effect of Co-doping in the BFO structure was investigated that the decrease of band gap width and the generated photoelectrons and holes would effectively reduce the recombination of photogenerated electron-hole pairs, leading to the enhancement photocatalytic activity. The results demonstrated that Co-BFO catalyst had a high photodegradation efficiency over a wide pH range of 3.0-9.0 and the Co-BFO-2 composite displayed the optimal catalytic performance. It was found that the degradation rate of LFX by Co-BFO-2 catalyst was 3.52 times higher than that of pure BFO catalyst under visible light condition. The free radical trapping experiments and EPR tests demonstrated that superoxide, photogenerated holes and sulfate radicals were the main active species in the photocatalytic degradation of LFX. And a possible photocatalytic degradation mechanism of LFX was proposed in the Vis/Co-BFO/PS process. These findings provided new insight of the mechanism of heterogeneous activation of persulfate by Co-BFO under visible light irradiation.

| S-EPMC6927001 | biostudies-literature

Structural, electrical, and magnetic study of La-, Eu-, and Er- doped bismuth ferrite nanomaterials obtained by solution combustion synthesis.

Project description:In this work, the multiferroic bismuth ferrite materials Bi0.9RE0.1FeO3 doped by rare-earth (RE = La, Eu, and Er) elements were obtained by the solution combustion synthesis. Structure, electrical, and magnetic properties of prepared samples were investigated by X-ray photoelectron spectroscopy, Mössbauer spectroscopy, electrical hysteresis measurement, broadband dielectric spectroscopy, and SQUID magnetometry. All obtained nanomaterials are characterized by spontaneous electrical polarization, which confirmed their ferroelectric properties. Investigation of magnetic properties at 300.0 K and 2.0 K showed that all investigated Bi0.9RE0.1FeO3 ferrites possess significantly higher magnetization in comparison to bismuth ferrites obtained by different methods. The highest saturation magnetisation of 5.161 emu/g at 300.0 K was observed for the BLaFO sample, while at 2.0 K it was 12.07 emu/g for the BErFO sample. Several possible reasons for these phenomena were proposed and discussed.

| S-EPMC8610975 | biostudies-literature

Metabolism of bismuth subsalicylate and intracellular accumulation of bismuth by Fusarium sp. strain BI.

Project description:Enrichment cultures were conducted using bismuth subsalicylate as the sole source of carbon and activated sludge as the inoculum. A pure culture was obtained and identified as a Fusarium sp. based on spore morphology and partial sequences of 18S rRNA, translation elongation factor 1-alpha, and beta-tubulin genes. The isolate, named Fusarium sp. strain BI, grew to equivalent densities when using salicylate or bismuth subsalicylate as carbon sources. Bismuth nitrate at concentrations of up to 200 muM did not limit growth of this organism on glucose. The concentration of soluble bismuth in suspensions of bismuth subsalicylate decreased during growth of Fusarium sp. strain BI. Transmission electron microscopy and energy-dispersive spectroscopy revealed that the accumulated bismuth was localized in phosphorus-rich granules distributed in the cytoplasm and vacuoles. Long-chain polyphosphates were extracted from fresh biomass grown on bismuth subsalicylate, and inductively coupled plasma optical emission spectrometry showed that these fractions also contained high concentrations of bismuth. Enzyme activity assays of crude extracts of Fusarium sp. strain BI showed that salicylate hydroxylase and catechol 1,2-dioxygenase were induced during growth on salicylate, indicating that this organism degrades salicylate by conversion of salicylate to catechol, followed by ortho cleavage of the aromatic ring. Catechol 2,3-dioxygenase activity was not detected. Fusarium sp. strain BI grew with several other aromatic acids as carbon sources: benzoate, 3-hydroxybenzoate, 4-hydroxybenzoate, gentisate, d-mandelate, l-phenylalanine, l-tyrosine, phenylacetate, 3-hydroxyphenylacetate, 4-hydroxyphenylacetate, and phenylpropionate.

| S-EPMC546758 | biostudies-literature

Ce(3+)/Yb(3+)/Er(3+) triply doped bismuth borosilicate glass: a potential fiber material for broadband near-infrared fiber amplifiers.

Project description:Erbium doped bismuth borosilicate (BBS) glasses, possessing the broadest 1.55??m near infrared (NIR) emission band among oxide glasses, stand out as excellent fiber material for optical fiber amplifiers. In this work, we demonstrate that both broadened and enhanced NIR emission of Er(3+) can be obtained by sensibly combining the effects such as mixed glass former effect, phonon-assisted energy transfer (PAET) and de-excitation effect induced by codopant. Specially, by codoping CeO2 in a controlled manner, it leads to not only much improved optical quality of the glasses, enhanced NIR emission, but also significantly suppressed energy transfer up-conversion (ETU) luminescence which is detrimental to the NIR emission. Cerium incorporated in the glasses exists overwhelmingly as the trivalent oxidation state Ce(3+) and its effects on the luminescence properties of Er(3+) are discussed. Judd-Ofelt analysis is used to evaluate gain amplification of the glasses. The result indicates that Ce(3+)/Yb(3+)/Er(3+) triply doped BBS glasses are promising candidate for erbium doped fiber amplifiers. The strategy described here can be readily extended to other rare-earth ions (REs) to improve the performance of REs doped fiber lasers and amplifiers.

| S-EPMC5028740 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data