Synthesis and Application of Ferroelectric Poly(Vinylidene Fluoride-co-Trifluoroethylene) Films using Electrophoretic Deposition.

ABSTRACT: In this study, we investigated the deposition kinetics of polyvinylidene fluoride copolymerized with trifluoroethylene (P(VDF-TrFE)) particles on stainless steel substrates during the electrophoretic deposition (EPD) process. The effect of applied voltage and deposition time on the structure and ferroelectric property of the P(VDF-TrFE) films was studied in detail. A method of repeated EPD and heat treatment above melting point were employed to fabricate crack-free P(VDF-TrFE) thick films. This method enabled us to fabricate P(VDF-TrFE) films with variable thicknesses. The morphology of the obtained films was investigated by scanning electron microscopy (SEM), and the formation of ?-phase was confirmed by X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy. P(VDF-TrFE) films prepared with various thicknesses showed remnant polarization (P_r) of around 4??C/cm². To demonstrate the applicability of our processing recipe to complex structures, we fabricated a spring-type energy harvester by depositing P(VDF-TrFE) films on stainless steel springs using EPD process. Our preliminary results show that an electrophoretic deposition can be applied to produce high-quality P(VDF-TrFE) films on planar as well as three-dimensional (3-D) substrates.

SUBMITTER: Ryu J

PROVIDER: S-EPMC5090457 | biostudies-literature | 2016 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Synthesis and Application of Ferroelectric Poly(Vinylidene Fluoride-co-Trifluoroethylene) Films using Electrophoretic Deposition.

Ryu Jeongjae J No Kwangsoo K Kim Yeontae Y Park Eugene E Hong Seungbum S

Scientific reports 20161102

In this study, we investigated the deposition kinetics of polyvinylidene fluoride copolymerized with trifluoroethylene (P(VDF-TrFE)) particles on stainless steel substrates during the electrophoretic deposition (EPD) process. The effect of applied voltage and deposition time on the structure and ferroelectric property of the P(VDF-TrFE) films was studied in detail. A method of repeated EPD and heat treatment above melting point were employed to fabricate crack-free P(VDF-TrFE) thick films. This ...[more]

PMID: 27805008

Similar Datasets

Project description:Nitric oxide (NO) releasing polymers have been widely applied as biomaterials for a variety of biomedical implants and devices. However, the chemical leaching of NO donors and their byproduct species is almost always observed during the application of polymers doped with NO donors, unless the donor is covalently linked to the polymer. Herein, we report the first NO releasing poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) fluorinated copolymer prepared by incorporating a fluorinated S-nitrosothiol as the NO donor. Under physiological conditions, the resulting polymeric films can release NO for 16?days. Importantly, due to both fluorine-fluorine and electrostatic charge interactions between the fluorinated NO donor and the PVDF-HFP copolymer, the total chemical leaching of the fluorinated NO donor and its disulfide product after 9?day was only 0.6% (mol%) of the initial amount of NO donor loaded into the film. These new NO release PVDF-HFP films exhibit antimicrobial and anti-biofilm activities against both Gram positive S. aureus and Gram negative P. aeruginosa strains. The NO-releasing PVDF-HFP polymer can also be coated on Teflon tubing to release NO under physiological conditions for extended time periods. This NO-releasing PVDF-HFP copolymer with greatly reduced chemical leaching could help enhance the biocompatibility and antimicrobial activity of various biomedical devices. STATEMENT OF SIGNIFICANCE: Fluoropolymers have been widely used in creating various biomedical implants and devices. However, nitric oxide (NO) release fluoropolymers have not been well studied to date. Additionally, in the application of biomaterials doped with NO donors, a significant amount of NO donors and their byproducts almost always leach into aqueous environment. We now report an NO releasing poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) fluoropolymer by incorporating a new fluorinated S-nitrosothiol. The NO release can last for 16?days under physiological conditions. The total chemical leaching was determined to be only 0.6?mol% of the initial S-nitrosothiol loaded. As expected, significant antimicrobial/anti-biofilm activities of the NO release PVDF-HFP film were observed against Gram positive S. aureus and Gram negative P. aeruginosa bacterial strains.

Dataset Information

Synthesis and Application of Ferroelectric Poly(Vinylidene Fluoride-co-Trifluoroethylene) Films using Electrophoretic Deposition.

Publications

Synthesis and Application of Ferroelectric Poly(Vinylidene Fluoride-co-Trifluoroethylene) Films using Electrophoretic Deposition.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets