Desulphurization characteristics of bamboo charcoal from sulfur solution.

ABSTRACT: Sulfur powder and sulfur dioxide (SO₂) often floated in air, produced acid rain and algal blooms, and could cause diseases. Bamboo charcoal could have adsorption and filtration properties. In order to figure out the optimal adsorption condition and the intrinsic change of the bamboo charcoal, five chemicals were adsorbed by bamboo charcoal and were analyzed by FT-IR. Fe₂(SO₄)₃'s, Na₂SO₄'s, Na₂S₂O₈'s, S's, and Na₂SO₃'s optimal adsorption condition was the concentration of 19 g/1000 g and stir time of 20 min, 21 g/1000 g and stir time of 60 min, 7 g/1000 g and stir time of 120 min, 11 g/1000 g and stir time of 120 min, 21 g/1000 g and stir time of 60 min, respectively. FT-IR spectra showed that for FT-IR spectra of Fe₂(SO₄)₃, the transmissivity of the peaks at 3435 cm^-1 and 2925 cm^-1 achieved the maximum for 60 min and the concentration was 19 g/1000 g, the transmissivity of the peaks at 1630 cm^-1, 1060 cm^-1 and 660 cm^-1 achieved the maximum for 60 min and the concentration was 7 g/1000 g. For FT-IR spectra of Na₂SO₄, the transmissivity of the peaks at 1630 cm^-1, 1060 cm^-1 and 660 cm^-1 achieved the maximum for 20 min and the concentration was 13 g/1000 g. For FT-IR spectra of Na₂S₂O₈, the transmissivity of the peaks at 3435 cm^-1, 2925 cm^-1, 1630 cm^-1 and 1060 cm^-1 achieved the maximum for 120 min and the concentration was 19 g/1000 g. For FT-IR spectra of S, the transmissivity of the peaks at 3435 cm^-1, 2925 cm^-1, 1630 cm^-1 and 1060 cm^-1 achieved the maximum for 20 min and the concentration was 11 g/1000 g, 17 g/1000 g and 21 g/1000 g. For FT-IR spectra of Na₂SO₃, the transmissivity of the peaks at 3435 cm^-1 achieved the maximum for 120 min and the concentration was 5 g/1000 g, the transmissivity of the peaks at 2925 cm^-1, 1630 cm^-1 and 1060 cm^-1 achieved the maximum for 120 min and the concentration was 11 g/1000 g. In these states, the number of the transmissivity of the maximum peaks is the largest.

SUBMITTER: Ge S

PROVIDER: S-EPMC5198999 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Bamboo leaf extract solution (BLES) and sodium copper chlorophyllin solution (SCCS) are known for their anti-oxidant activities. Oral malodor is often related with periodontal pathogens. The present study was undertaken to investigate the anti-bacterial effect of both BLES and SCCS on anaerobic periodontal bacteria producing oral malodorous volatile sulfur compounds (VSC).Porphyromonas gingivalis W83 (PG), Prevotella intermidai TDC19B (PI), Fusobacterium nucleatum ATCC25586 (FN) and Prevotella nigrescence ATCC33563 (PN) were investigated as oral isolated bacteria. VSC production ability of the oral strains was investigated by gas chromatography. With serial dilution of BLES or SCCS, the strains PG, PI, FN or PN were cultured anaerobically with AnaeroPack at 37 ℃ for 3 days. For the determination of anti-bacterial action of BLES or SCCS, the inoculum was cultured with original concentrations of BLES 0.16% (w/v) or SCCS 0.25% (w/v).Gas chromatography exhibited that all strains, PG, PI, FN and PN were responsible for producing a high range of H2S and a moderate range of CH3SH. Anti-bacterial effect of BLES or SCCS on the strains was observed. Inhibition of BLES or SCCS on the strains was revealed as concentration dependent. BLES or SCCS inhibited bacterial proliferation at higher concentrations (PG; 0.04% BLES or 0.03% SCCS, PI; 0.002% BLES or 0.03% SCCS, FN; 0.005% BLES or 0.01% SCCS, PN; 0.01% BLES or 0.015% SCCS). No viable bacterial colony observed at original concentration of BLES 0.16% or SCCS 0.25%. Strain growth was eliminated from inhibition at lower concentrations (PG; 0.02% BLES or 0.015% SCCS, PI; 0.001% BLES or 0.015% SCCS, FN; 0.002% BLES or 0.007% SCCS, PN; 0.005% BLES or 0.007% SCCS).High concentrations of both BLES (0.16%) and SCCS (0.25%) show superior inhibiting capability on all four oral malodor associated periodontal anaerobes during testing, suggesting that these compounds might have a beneficial effect on oral health care.

Project description:Nano bamboo charcoal is being widely used as sustained release carrier for chemicals for its high specific surface area, sound biocompatibility, and nontoxicity; however, there have been no reports on nano bamboo charcoal as sustained release carrier for traditional Chinese medicine (TCM).To study the effect of nano bamboo charcoal in absorbing and sustained releasing Eucommia ulmoides extract (EUE) and to verify the in vitro anticancer effect of the sustained release liquid, so as to provide a theoretical basis for the development and utilization of nano bamboo charcoal as TCM sustained-release preparation.The adsorption capacity for the nano bamboo charcoal on EUE was measured by Langmuir model, and the release experiment was carried out under intestinal fluid condition. Characteristic changes for the nano bamboo charcoal nano-drug delivery system with and without adsorption of E. ulmoides were evaluated by scanning electron microscopy, Fourier transform infrared spectroscopy, thermogravimetric analysis, and specific surface area. In addition, the anticancer effect from this novel bamboo charcoal E. ulmoides delivery system was evaluated against a human colon cancer cell line (HCT116).It was found that nano bamboo charcoal exhibits good adsorption capacity (up to 462.96 mg/g at 37°C). The cumulative release rate for EUE from this nano bamboo charcoal delivery system was 70.67%, and specific surface area for the nano bamboo charcoal decreased from 820.32 m2/g to 443.80 m2/g after EUE was loaded. An in vitro anticancer study showed that the inhibition rate for E. ulmoides against HCT116 cancer cells was 23.07%, for this novel bamboo charcoal nano-drug delivery system.This study provides a novel strategy for the delivery of traditional Chinese medicine using bamboo charcoal nano-drug delivery system.The adsorption equilibrium was reached after 30 min of ultrasonic treatmentThe saturated adsorption capacity of Eucommia ulmoides extract by nano bamboo charcoal under ultrosonic condition was 462. 96 mg/gThe cumulative release rate of E. ulmoides extract from the nano bamboo charcoal delivery system in artificial intestinal juice was 70.67%The inhibition ratio of HCT116 cancer cells by sustained release liquid was 23.07%. Abbreviation used: EUE: Eucommia ulmoides extract.

Project description:The ability of bamboo charcoal to reduce the negative effects of high dietary selenium (Se) concentrations was assessed by feeding juvenile blunt snout bream (Megalobrama amblycephala) one of five Se-rich diets (1.5 mg/kg Se; 36% protein, 8.7% lipid) containing graded levels (0-4 g/kg) of bamboo charcoal powder for eight weeks. There were four tanks (350 L) of fish (initial weight 16.0 ± 0.5 g) for each treatment, and the fish were fed to satiation four times each day. At the end of the feeding trial, all of the fish from each tank were weighed to calculate the growth performance. Blood samples were firstly obtained to collect plasma for the biochemical indexes determination. Liver tissues were then collected to determine the antioxidant enzyme activities and gene expression. Dorsal muscles were also collected to determine the nutrient composition. The results show that when the bamboo charcoal content in the Se-rich feed ranged between 0 and 3 g/kg, the weight growth rate (WGR) and specific growth rate (SGR) values increased with the higher dietary bamboo charcoal content, and the maximum WGR and SGR values were achieved when the bamboo charcoal content in the Se-rich feed was 2-3 g/kg (p < 0.05). The Se content in muscle tissues decreased significantly with the increased bamboo charcoal content (p < 0.05) in the Se-rich feed, which ranged from 0 to 4 g/kg. When the bamboo charcoal content in the Se-rich feed was 2-3 g/kg, the levels of glucose (GLU) and albumin (ALB) in plasma reached a maximum (p < 0.05), whereas the level of alkaline phosphatase (ALP) reached a minimum (p < 0.05). Additionally, the activities of catalase (CAT), total superoxide dismutase (T-SOD), total antioxidative capacity (T-AOC), and glutathione peroxidase (GSH-Px) were significantly enhanced (p < 0.05) when the bamboo charcoal content was 3 g/kg. In contrast, the malondialdehyde (MDA) level increased sharply when the bamboo charcoal content in the Se-rich feed was 1 g/kg, compared to the control group and the groups supplemented with 2-3 g/kg bamboo charcoal (p < 0.05). Regarding mRNA-level gene expression, the results show that dietary supplementation with 0 to 3 g/kg of bamboo charcoal increased the expression of keap1 and nrf2, whereas nfkb expression was inhibited (p < 0.05). The mRNA expression of the antioxidant enzymes cat, gpx, and mn-sod was consistently enhanced in the group fed with the 3 g/kg bamboo charcoal diet (p < 0.05). The expression of the pro-inflammatory cytokines tnfα and tgfβ was inhibited in the groups supplemented with 2-3 g/kg bamboo charcoal, whereas the expression of anti-inflammatory cytokines (il10) increased in the bamboo charcoal supplementation groups compared to the control group (p < 0.05). Generally, supplementation with 2-3 g/kg of bamboo charcoal in Se-rich feed improved the growth performance, physiological status, and antioxidant enzyme activities of blunt snout bream. Moreover, bamboo charcoal supplementation in Se-rich diets stimulated the antioxidant system and inhibited the inflammatory response by activating Nrf2-Keap1 and suppressing NF-κB.

Dataset Information

Desulphurization characteristics of bamboo charcoal from sulfur solution.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets