Culture on 3D Chitosan-Hyaluronic Acid Scaffolds Enhances Stem Cell Marker Expression and Drug Resistance in Human Glioblastoma Cancer Stem Cells.

ABSTRACT: The lack of in vitro models that support the growth of glioblastoma (GBM) stem cells (GSCs) that underlie clinical aggressiveness hinders developing new, effective therapies for GBM. While orthotopic patient-derived xenograft models of GBM best reflect in vivo tumor behavior, establishing xenografts is a time consuming, costly, and frequently unsuccessful endeavor. To address these limitations, a 3D porous scaffold composed of chitosan and hyaluronic acid (CHA) is synthesized. Growth and expression of the cancer stem cell (CSC) phenotype of the GSC GBM6 taken directly from fresh xenogratfs grown on scaffolds or as adherent monolayers is compared. While 2D adherent cultures grow as monolayers of flat epitheliod cells, GBM6 cells proliferate within pores of CHA scaffolds as clusters of self-adherent ovoid cells. Growth on scaffolds is accompanied by greater expression of genes that mediate epithelial-mesenchymal transition and maintain a primitive, undifferentiated phenotype, hallmarks of CSCs. Scaffold-grown cells also display higher expression of genes that promote resistance to hypoxia-induced oxidative stress. In accord, scaffold-grown cells show markedly greater resistance to clinically utilized alkylating agents compared to adherent cells. These findings suggest that our CHA scaffolds better mimic in vivo biological and clinical behavior and provide insights for developing novel individualized treatments.

SUBMITTER: Wang K

PROVIDER: S-EPMC5253135 | biostudies-literature | 2016 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Culture on 3D Chitosan-Hyaluronic Acid Scaffolds Enhances Stem Cell Marker Expression and Drug Resistance in Human Glioblastoma Cancer Stem Cells.

Wang Kui K Kievit Forrest M FM Erickson Ariane E AE Silber John R JR Ellenbogen Richard G RG Zhang Miqin M

Advanced healthcare materials 20161102 24

The lack of in vitro models that support the growth of glioblastoma (GBM) stem cells (GSCs) that underlie clinical aggressiveness hinders developing new, effective therapies for GBM. While orthotopic patient-derived xenograft models of GBM best reflect in vivo tumor behavior, establishing xenografts is a time consuming, costly, and frequently unsuccessful endeavor. To address these limitations, a 3D porous scaffold composed of chitosan and hyaluronic acid (CHA) is synthesized. Growth and express ...[more]

PMID: 27805789

Similar Datasets

Project description:IntroductionThe quality of cartilaginous tissue derived from bone marrow mesenchymal stromal stem cell (BMSC) transplantation has been correlated with clinical outcome. Therefore, culture conditions capable of modulating tissue phenotype, such as oxygen tension and scaffold composition, are under investigation. The objective of this study was to assess the effect of hypoxia on in vitro BMSC chondrogenesis within clinically approved porous scaffolds composed of collagen and hyaluronic acid (HA). It was hypothesized that hypoxic isolation/expansion and differentiation would improve BMSC chondrogenesis in each construct.MethodsOvine BMSCs were isolated and expanded to passage 2 under hypoxia (3% oxygen) or normoxia (21% oxygen). Cell proliferation and colony-forming characteristics were assessed. BMSCs were seeded at 10 million cells per cubic centimeter on cylindrical scaffolds composed of either collagen I sponge or esterified HA non-woven mesh. Chondrogenic differentiation was performed in a defined medium under hypoxia or normoxia for 14 days. Cultured constructs were assessed for gene expression, proteoglycan staining, glycosaminoglycan (GAG) quantity, and diameter change.ResultsIsolation/expansion under hypoxia resulted in faster BMSC population doublings per day (P <0.05), whereas cell and colony counts were not significantly different (P = 0.60 and 0.30, respectively). Collagen and HA scaffolds seeded with BMSCs that were isolated, expanded, and differentiated under hypoxia exhibited superior aggrecan and collagen II mRNA expressions (P <0.05), GAG quantity (P <0.05), and proteoglycan staining in comparison with normoxia. GAG/DNA was augmented with hypoxic isolation/expansion in all constructs (P <0.01). Comparison by scaffold composition indicated increased mRNA expressions of hyaline cartilage-associated collagen II, aggrecan, and SOX9 in collagen scaffolds, although expression of collagen X, which is related to hypertrophic cartilage, was also elevated (P <0.05). Proteoglycan deposition was not significantly improved in collagen scaffolds unless culture involved normoxic isolation/expansion followed by hypoxic differentiation. During chondrogenesis, collagen-based constructs progressively contracted to 60.1% ± 8.9% of the initial diameter after 14 days, whereas HA-based construct size was maintained (109.7% ± 4.2%).ConclusionsHypoxic isolation/expansion and differentiation enhance in vitro BMSC chondrogenesis within porous scaffolds. Although both collagen I and HA scaffolds support the creation of hyaline-like cartilaginous tissue, variations in gene expression, extracellular matrix formation, and construct size occur during chondrogenesis.

Project description:Chitosan is a natural polymer widely investigated and used due to its antibacterial activity, mucoadhesive, analgesic, and hemostatic properties. Its biocompatibility makes chitosan a favorable candidate for different applications in tissue engineering (TE), such as skin, bone, and cartilage tissue regeneration. Despite promising results obtained with chitosan 3D scaffolds, significant challenges persist in fabricating hydrogel structures with ordered architectures and biological properties to mimic native tissues. In this work, chitosan has been investigated aiming at designing and fabricating uniaxial scaffolds which can be proposed for the regeneration of anisotropic tissues (i.e., skin, skeletal muscle, myocardium) by 3D printing technology. Chitosan was blended with gelatin to form a polyelectrolyte complex in two different ratios, to improve printability and shape retention. After the optimization of the printing process parameters, different crosslinking conditions were investigated, and the 3D printed samples were characterized. Tripolyphosphate (TPP) was used as crosslinker for chitosan-based scaffolds. For the optimization of the printing temperature, the sol-gel temperature of the chitosan-gelatin blend was determined by rheological measurements and extrusion temperature was set to 20°C (i.e., below sol-gel temperature). The shape fidelity and surface morphology of the 3D printed scaffolds after crosslinking was dependent on crosslinking conditions. Interestingly, mechanical properties of the scaffolds were also significantly affected by the crosslinking conditions, nonetheless the stability of the scaffolds was strongly determined by the content of gelatin in the blend. Lastly, in vitro cytocompatibility test was performed to evaluate the interactions between L929 cells and the 3D printed samples. 2% w/v chitosan and 4% w/v gelatin hydrogel scaffolds crosslinked with 10% TPP, 30 min at 4°C following 30 min at 37°C have shown cytocompatible and stable characteristics, compared to all other tested conditions, showing suitable properties for the regeneration of anisotropic tissues.

Dataset Information

Culture on 3D Chitosan-Hyaluronic Acid Scaffolds Enhances Stem Cell Marker Expression and Drug Resistance in Human Glioblastoma Cancer Stem Cells.

Publications

Culture on 3D Chitosan-Hyaluronic Acid Scaffolds Enhances Stem Cell Marker Expression and Drug Resistance in Human Glioblastoma Cancer Stem Cells.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets