In Vitro-Activity of Er:YAG Laser in Comparison with other Treatment Modalities on Biofilm Ablation from Implant and Tooth Surfaces.

ABSTRACT:

Background and aim

Bacterial biofilms play a major role in the etiology of periodontal and peri-implant diseases. The aim of the study was to evaluate the removal of bacterial biofilms and attachment of epithelial cells (EC), gingival fibroblasts (GF) and osteoblast-like cells (OC) to dentin and titanium surfaces after Er:YAG laser (Er:YAG) in comparison with other treatment methods.

Material and methods

Multi-species bacterial biofilms were grown on standardized dentin and titanium specimens with a sand-blasted and acid etched (SLA) surface for 3.5 d. Thereafter, the specimens were placed into artificially-created pockets. The following methods for biofilm removal were used: 1) Gracey (dentin) or titanium curettes (CUR), 2) Er:YAG, 3) photodynamic therapy (PDT) and 4) CUR with adjunctive PDT (CUR/PDT). Colony forming units (CFUs) of the remaining biofilms and attachment of EC, GF and OC were determined. Statistical analysis was performed by means of ANOVA with post-hoc LSD.

Results

All treatment methods decreased statistically significantly (p<0.001) total CFUs in biofilms compared with untreated dentin and titanium surfaces respectively. On dentin, Er:YAG was equally efficient as CUR and PDT but inferior to CUR/PDT (p = 0.005). On titanium, surfaces, the use of Er:YAG resulted in statistically significantly superior biofilm removal compared to the 3 other treatments (each p<0.001). Counts of attached EC, GF and OC were the lowest on untreated contaminated dentin and titanium surfaces each. After CUR/PDT higher EC counts were found on dentin (p = 0.006). On titanium, all decontamination methods statistically significantly increased (p<0.001) the counts of attached EC without differences between groups. Statistically significantly higher counts of GF (p = 0.024) and OC (p<0.001) were observed after Er:YAG decontamination compared with untreated surfaces.

Conclusion

Ablation of subgingival biofilms and in particular decontamination of titanium implant surfaces with an Er:YAG laser seem to be a promising approach and warrants further investigations.

SUBMITTER: Eick S

PROVIDER: S-EPMC5268770 | biostudies-literature | 2017

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

In Vitro-Activity of Er:YAG Laser in Comparison with other Treatment Modalities on Biofilm Ablation from Implant and Tooth Surfaces.

Eick Sigrun S Meier Ivan I Spoerlé Florian F Bender Philip P Aoki Akira A Izumi Yuichi Y Salvi Giovanni E GE Sculean Anton A

PloS one 20170126 1

<h4>Background and aim</h4>Bacterial biofilms play a major role in the etiology of periodontal and peri-implant diseases. The aim of the study was to evaluate the removal of bacterial biofilms and attachment of epithelial cells (EC), gingival fibroblasts (GF) and osteoblast-like cells (OC) to dentin and titanium surfaces after Er:YAG laser (Er:YAG) in comparison with other treatment methods.<h4>Material and methods</h4>Multi-species bacterial biofilms were grown on standardized dentin and titani ...[more]

PMID: 28125700

Similar Datasets

Project description:(1) Background: The relatively high prevalence of peri-implantitis (PI) and the lack of a standard method for decontamination of the dental implant surface have pushed us to conduct further research in the field. Bacterial biofilms were found to play a primordial role in the etiology of PI. Therefore, the aim is to evaluate the efficacy of a laser-assisted elimination of biofilm protocol in the removal of a multi-species biofilm on titanium surfaces. (2) Methods: In total, 52 titanium discs (grade 4) were used. The study group consisted of 13 titanium disks contaminated with multi-species biofilms and subsequently irradiated with the laser (T + BF + L). The control groups consisted of the following types of titanium disks: 13 contaminated with multi-species biofilms (T + BF), 13 sterile and irradiated (T + L), 13 sterile and untreated (T). Q-Switch Nd:YAG laser Irradiation parameters were the following: energy density equal to 0.597 J/cm2 per pulse, power equal to 270 milliwatt per pulse, 2.4 mm of spot diameter, and 10 Hz repetition rate for pulse duration of six nanoseconds (ns). The laser irradiation was made during 2 s of total time in non-contact and at 0.5 mm away from the titanium disc surface. After treatment, presence of biofilms on the disks was evaluated by staining with crystal violet (CV), which was measured as optical density at six hundred thirty nm, and statistical analyses were done. (3) Results: the optical density values were 0.004 ± 0.004 for the study group T + BF + L, 0.120 ± 0.039 for group T + BF, 0.006 ± 0.003 for group T + L, and 0.007 ± 0.007 for group T. For the study group, laser treatment resulted in a total elimination of the biofilm, with mean values statistically significantly lower than those of contaminated titanium surfaces and similar to those of sterile titanium surfaces. (4) Conclusions: Our irradiation protocol provided a significant elimination of the multi-species biofilm on titanium surfaces. Laser treated titanium surfaces were biofilm-free, similar to the sterile ones.

Project description:We investigated the biofilm removal effects of laser activated irrigation (LAI) using a pig model, focusing on the impact of the fiber tip position, and used a high-speed camera to observe the occurrence and positioning of the cavitation associated with laser irradiation. A total of 16 roots of deciduous mandibular second premolars from 4 pigs were used. After a pulpectomy, the canals were left open for 2 weeks and sealed for 4 weeks to induce intraradicular biofilm. Root canal irrigation was then performed with Er:YAG laser activation. The fiber tip was inserted at two different positions, i.e., into the root canal in the intracanal LAI group and into the pulp chamber in the coronal LAI group. Intracanal needle irrigation with saline or 5% NaOCl was utilized in the positive control and conventional needle irrigation (CNI) groups. SEM and qPCR were carried out to evaluate treatment efficacy. Statistical analysis was performed using ANOVA and a Tukey-Kramer post-hoc test for qPCR and with a Steel-Dwass test to compare the SEM scores, with α = 0.05. A high-speed camera was used to observe the generation of cavitation bubbles and the movement of the induced bubbles after laser irradiation. The intracanal and coronal LAI groups showed significantly lower amounts of bacteria than either the positive control or CNI groups. There was no significant difference found between the intracanal and coronal LAI groups. SEM images revealed opened dentinal tubules with the destruction of biofilm in both LAI groups. High-speed camera images demonstrated cavitation bubble production inside the root canal after a single pulse irradiation pulse. The generated bubbles moved throughout the entire internal multi-rooted tooth space. Coronal LAI can generate cavitation in the root canal with a simply placed fiber inside the pulp chamber, leading to effective biofilm removal. This method could thus contribute to the future development of endodontic treatments for refractory apical periodontitis caused by intraradicular biofilm.

Project description:BACKGROUND:When implants are restored with cement-retained restorations, prosthetic retrievability can be difficult and often requires sectioning using rotary instruments. Sometimes repeated removals of a cement-retained implant crown are needed such as for treatment of peri-implantitis or immediate implant provisionalization. The purpose of this study was to evaluate the effect of erbium-doped yttrium aluminum garnet (Er:YAG) laser as a non-invasive treatment modality to remove lithium disilicate crowns from zirconia implant abutments following long-term cementation, repetitive debonding and re-cementation, and short-term retrieval. MATERIAL AND METHODS:Twenty identical lithium disilicate crowns were cemented onto zirconia prefabricated abutments using composite resin cement. Ten cemented crowns were removed at 48 hours after cementation as a short-term group (ST), while another 10 were removed 6 months after cementation as a long-term group (LT). To mimicking repetitive recementation and retrieval, the LT crowns were then recemented and removed after 48 hours as a long-term recemention (LTR) group. The LTR crowns were then again recemented and removed after 48 hours as a long-term repeated recemention (LTRR) group. Er:YAG laser was used to facilitate the retrieval of these crowns. recorded and analyzed using ANOVA and t-test. The surfaces of the crown and the abutment were further examined using light microscopy and scanning electron microscopy (SEM). Temperature changes of the abutment and crown upto 10 minutes were also measured and statistically analyzed (paired t-test). RESULTS:The average times of crown removal from zirconia abutments were 4 minutes (min) and 42 second (sec) in LT to 3 min 24 sec in LTR, and 3 min 12 sec in LTRR and ST groups. LTR took the longest time to remove, statistically (ANOVA and t-test, p < .001). No statistical differences were observed among the removal times of LTR, LTRR, and ST groups (t-test, p = .246, .246 and 1). SEM examination of the material surface showed no visual surface damaging from treatment with Er:YAG laser. The temperatures during irradiation ranged from 18.4°C to 20°C and 22.2°C to 24.5°C (Paired t-test, p < .0001) for the abutment and the crown during irradiation from 1 min to 10 mins. CONCLUSIONS:Long-term cementation can increase time in lithium disilicate crown removal from zirconia abutment using Er:YAG. Er:YAG laser is a non-invasive tool to remove cement-retained implant prostheses and should be considered as a viable alternative to rotary instruments.

Project description:IntroductionMicro- or nano-topography can both provide antimicrobial properties and improve osseointegration of dental implant titanium surfaces. Laser treatment is one of the best surface microtexturing techniques. The aim of this study was to evaluate in vitro and in situ biofilm formation on a laser-treated titanium surface, comparing it with two conventional surfaces, machined and grit-blasted.MethodsFor the in vitro experiment, an oral microcosm biofilm model was developed on the surface of titanium disks and reference human enamel using a bioreactor for 48 h. For the in situ experiment, titanium implants with laser-treated, machined and grit-blasted surfaces were mounted on intraoral trays and worn by ten volunteers for 48 h. Biofilm formation was quantitatively evaluated, and surfaces were analyzed using confocal laser scanning microscopy, scanning electron microscopy and energy-dispersive X-ray spectroscopy.Results–in vitro studyBiofilm structures with a prevalence of viable cells covered most of the machined, grit-blasted and human enamel surfaces, whereas less dense biofilm structures with non-confluent microcolonies were observed on the laser-treated titanium. Laser-treated titanium showed the lowest biofilm formation, where microorganisms colonized the edges of the laser-created pits, with very few or no biofilm formation observed inside the pits.Results–in situ studyThe biofilm formation pattern observed was similar to that in the in vitro experiment. Confocal laser scanning microscopy showed complete coverage of the implant threads, with mostly viable cells in grit-blasted and machined specimens. Unexpectedly, laser-treated specimens showed few dead microbial cells colonizing the bottom of the threads, while an intense colonization was found on the threading sides.ConclusionThis data suggests that laser-created microtopography can reduce biofilm formation, with a maximum effect when the surface is blasted orthogonally by the laser beam. In this sense the orientation of the laser beam seems to be relevant for the biological interaction with biofilms.

Project description:BackgroundGlaucoma is a leading cause of global blindness, especially preventable blindness. The increased prevalence of glaucoma has led to a growing demand for newer, safer, more rapid, and simpler treatments for the reduction of intraocular pressure (IOP). In this study, we evaluated the safety and feasibility of performing filtration glaucoma surgery with an Ab-Interno Er:YAG laser in rabbits.MethodsNine New Zealand White rabbits age 16 weeks were studied. After subconjunctival injection of mitomycin C (MMC), a novel Ab-Interno Er:YAG laser probe was inserted into the anterior chamber (AC) through a clear corneal 1 mm paracentesis and directed at the trabecular meshwork adjacent to the MMC injection area. A pulsed laser beam was applied to create a patent sclerostomy connecting the AC to the subconjuctival space, resulting in a filtering bleb. The laser system used was the Er:YAG laser system - LAS25-FCU, (Pantec Biosolutions AG, Liechtenstein). Parameters used: Wave lengh: 2940 nm, Pulse length: 100-400 μsec,frequency: 250 Hz. Average laser power in accordance to the fiber tip diameter: 0.85 W(range 0.8-0.92 W). Complete ocular exams, including IOP measurements, were performed on 1, 7, 14, and 23 days postoperatively. Three rabbits were sacrificed on days 1, 14, and 23, and histological examinations were performed on all nine eyes.ResultsAll procedures resulted in a functional medium-large superior bleb without significant complications. The bleb was sustained in all rabbits by day 14 and in one of the three rabbits that reached the last follow-up at 23 days. No cases of postoperative hypotony were observed. There was a transient significant reduction in mean IOP on postoperative days 5 and 7 (P = 0.028). Histopathological analysis revealed a patent full-thickness scleral tunnel with only a minor degree of surrounding coagulation necrosis.ConclusionsThe Ab-Interno laser sclerostomy procedure is potentially safe and effective based on initial experience in an in-vivo rabbit animal model.

Project description:The periocular region is challenging for cosmetic laser surgeons. Surgery and laser resurfacing have traditionally been used to correct periorbital lines and wrinkles. Although effective, the associated downtime with these methods has made many people reluctant to decide for such treatments. More recently, the non-ablative long-pulse 2940 nm Er:YAG laser is being used to improve the structure and function and hence the appearance of skin in the periorbital region. The objective of this study is to evaluate the safety and efficacy of long-pulse 2940 nm Er:YAG laser for non-ablative treatment of periorbital static wrinkles and skin laxity. This is a prospective analysis of 30 patients treated for periorbital rejuvenation using three sessions of non-ablative long-pulse Er:YAG laser over a 3-month period. All patients were assessed according to Fitzpatrick's classification of periorbital wrinkles to class I, II, or III and were treated with 2940 nm Er:YAG laser using a fluence of 3.75 J/cm2, a repetition rate of 1.7-2 Hz, and with the SMOOTH™ pulse mode (250 ms). The treatment sessions were performed on each patient, 4 weeks apart. Patient improvement was assessed before each laser session as well as at 12 months after the final treatment. Blind photographic evaluations were performed by three independent physicians using unlabeled before and after photos arranged in non-chronological order. Reviewers were asked to determine the before and after photos. Patients were asked to answer a questionnaire measuring satisfaction 4 weeks after each session, and to report any adverse reactions. There was statistically and clinically significant improvement in the Fitzpatrick classification of the periorbital wrinkles. Blinded evaluators correctly identified the before and after photos in all cases. All patients reported mild edema and erythema, which persisted for 1 to 2 days, and superficial peeling of the skin for 4 to 6 days after each laser treatment. No long-term adverse effects were reported. The non-ablative long-pulse 2940 nm Er:YAG laser seems to be a safe and effective treatment for periocular rejuvenation with minimal and tolerable adverse reaction. The improvement attained from the laser sessions was persisting after 1 year denoting the long-term efficacy of the procedure.

Dataset Information

In Vitro-Activity of Er:YAG Laser in Comparison with other Treatment Modalities on Biofilm Ablation from Implant and Tooth Surfaces.

Background and aim

Material and methods

Results

Conclusion

Publications

In Vitro-Activity of Er:YAG Laser in Comparison with other Treatment Modalities on Biofilm Ablation from Implant and Tooth Surfaces.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets