Stability of a Benzyl Amine Based CO₂ Capture Adsorbent in View of Regeneration Strategies.

ABSTRACT: In this work, the chemical and thermal stability of a primary amine-functionalized ion-exchange resin (Lewatit VP OC 1065) is studied in view of the potential options of regenerating this sorbent in a CO₂ removal application. The adsorbent was treated continuously in the presence of air, different O₂/CO₂/N₂ mixtures, concentrated CO₂, and steam, and then the remaining CO₂ adsorption capacity was measured. Elemental analysis, BET/BJH analysis, Fourier transform infrared spectroscopy, and thermogravimetric analysis were applied to characterize adsorbent properties. This material was found to be thermally and hydrothermally stable at high temperatures. However, significant oxidative degradation occurred already at moderate temperatures (above 70 °C). Temperatures above 120 °C lead to degradation in concentrated dry CO₂. Adding moisture to the concentrated CO₂ stream improves the CO₂-induced stability. Adsorbent regeneration with nitrogen stripping is studied with various parameters, focusing on minimizing the moles of purge gas required per mole of CO₂ desorbed.

SUBMITTER: Yu Q

PROVIDER: S-EPMC5384483 | biostudies-literature | 2017 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Stability of a Benzyl Amine Based CO2 Capture Adsorbent in View of Regeneration Strategies.

Yu Qian Q Delgado Jorge de la P JP Veneman Rens R Brilman Derk W F DW

Industrial & engineering chemistry research 20170302 12

In this work, the chemical and thermal stability of a primary amine-functionalized ion-exchange resin (Lewatit VP OC 1065) is studied in view of the potential options of regenerating this sorbent in a CO2 removal application. The adsorbent was treated continuously in the presence of air, different O2/CO2/N2 mixtures, concentrated CO2, and steam, and then the remaining CO2 adsorption capacity was measured. Elemental analysis, BET/B ...[more]

PMID: 28405055

Similar Datasets

Project description:Rising CO2 emissions are responsible for increasing global temperatures causing climate change. Significant efforts are underway to develop amine-based sorbents to directly capture CO2 from air (called direct air capture (DAC)) to combat the effects of climate change. However, the sorbents' performances have usually been evaluated at ambient temperatures (25 °C) or higher, most often under dry conditions. A significant portion of the natural environment where DAC plants can be deployed experiences temperatures below 25 °C, and ambient air always contains some humidity. In this study, we assess the CO2 adsorption behavior of amine (poly(ethyleneimine) (PEI) and tetraethylenepentamine (TEPA)) impregnated into porous alumina at ambient (25 °C) and cold temperatures (-20 °C) under dry and humid conditions. CO2 adsorption capacities at 25 °C and 400 ppm CO2 are highest for 40 wt% TEPA-incorporated γ-Al2O3 samples (1.8 mmol CO2/g sorbent), while 40 wt % PEI-impregnated γ-Al2O3 samples exhibit moderate uptakes (0.9 mmol g-1). CO2 capacities for both PEI- and TEPA-incorporated γ-Al2O3 samples decrease with decreasing amine content and temperatures. The 40 and 20 wt % TEPA sorbents show the best performance at -20 °C under dry conditions (1.6 and 1.1 mmol g-1, respectively). Both the TEPA samples also exhibit stable and high working capacities (0.9 and 1.2 mmol g-1) across 10 cycles of adsorption-desorption (adsorption at -20 °C and desorption conducted at 60 °C). Introducing moisture (70% RH at -20 and 25 °C) improves the CO2 capacity of the amine-impregnated sorbents at both temperatures. The 40 wt% PEI, 40 wt % TEPA, and 20 wt% TEPA samples show good CO2 uptakes at both temperatures. The results presented here indicate that γ-Al2O3 impregnated with PEI and TEPA are potential materials for DAC at ambient and cold conditions, with further opportunities to optimize these materials for the scalable deployment of DAC plants at different environmental conditions.

Project description:Aminopolymer-based sorbents are preferred materials for extraction of CO2 from ambient air [direct air capture (DAC) of CO2] owing to their high CO2 adsorption capacity and selectivity at ultra-dilute conditions. While those adsorptive properties are important, the stability of a sorbent is a key element in developing high-performing, cost-effective, and long-lasting sorbents that can be deployed at scale. Along with process upsets, environmental components such as CO2, O2, and H2O may contribute to long-term sorbent instability. As such, unraveling the complex effects of such atmospheric components on the sorbent lifetime as they appear in the environment is a critical step to understanding sorbent deactivation mechanisms and designing more effective sorbents and processes. Here, a poly(ethylenimine) (PEI)/Al2O3 sorbent is assessed over continuous and cyclic dry and humid conditions to determine the effect of the copresence of CO2 and O2 on stability at an intermediate temperature of 70 °C. Thermogravimetric and elemental analyses in combination with in situ horizontal attenuated total reflection infrared (HATR-IR) spectroscopy are performed to measure the extent of deactivation, elemental content, and molecular level changes in the sorbent due to deactivation. The thermal/thermogravimetric analysis results reveal that incorporating CO2 with O2 accelerates sorbent deactivation using these sorbents in dry and humid conditions compared to that using CO2-free air in similar conditions. The in situ HATR-IR spectroscopy results of PEI/Al2O3 sorbent deactivation under a CO2-air environment show the formation of primary amine species in higher quantity (compared to that in conditions without O2 or CO2), which arises due to the C-N bond cleavage at secondary amines due to oxidative degradation. We hypothesize that the formation of bound CO2 species such as carbamic acids catalyzes C-N cleavage reactions in the oxidative degradation pathway by shuttling protons, resulting in a low activation energy barrier for degradation, as probed by metadynamics simulations. In the cyclic experiment after 30 cycles, results show a gradual loss in stability (dry: 29%, humid: 52%) under CO2-containing air (0.04% CO2/21% O2 balance N2). However, the loss in capacity during cyclic studies is significantly less than that during continuous deactivation, as expected.

Project description:Zeolites, silica-supported amines, and metal-organic frameworks (MOFs) have been demonstrated as promising adsorbents for direct air CO2 capture (DAC), but the shaping and structuring of these materials into sorbent modules for practical processes have been inadequately investigated compared to the extensive research on powder materials. Furthermore, there have been relatively few studies reporting the DAC performance of sorbent contactors under cold, subambient conditions (temperatures below 20 °C). In this work, we demonstrate the successful fabrication of adsorbent monoliths composed of cellulose acetate (CA) and adsorbent particles such as zeolite 13X and MOF MIL-101(Cr) by a 3D printing technique: solution-based additive manufacturing (SBAM). These monoliths feature interpenetrated macroporous polymeric frameworks in which microcrystals of zeolite 13X or MIL-101(Cr) are evenly distributed, highlighting the versatility of SBAM in fabricating monoliths containing sorbents with different particle sizes and density. Branched poly(ethylenimine) (PEI) is successfully loaded into the CA/MIL-101(Cr) monoliths to impart CO2 uptakes of 1.05 mmol gmonolith-1 at -20 °C and 400 ppm of CO2. Kinetic analysis shows that the CO2 sorption kinetics of PEI-loaded MIL-101(Cr) sorbents are not compromised in the monoliths compared to the powder sorbents. Importantly, these monoliths exhibit promising working capacities (0.95 mmol gmonolith-1) over 14 temperature swing cycles with a moderate regeneration temperature of 60 °C. Dynamic breakthrough experiments at 25 °C under dry conditions reveal a CO2 uptake capacity of 0.60 mmol gmonolith-1, which further increases to 1.05 and 1.43 mmol gmonolith-1 at -20 °C under dry and humid (70% relative humidity) conditions, respectively. Our work showcases the successful implementation of SBAM in making DAC sorbent monoliths with notable CO2 capture performance over a wide range of sorption temperatures, suggesting that SBAM can enable the preparation of efficient sorbent contactors in various form factors for other important chemical separations.

Project description:An excessive amount of CO2 is the leading cause of climate change, and hence, its reduction in the Earth's atmosphere is critical to stop further degradation of the environment. Although a large body of work has been carried out for post-combustion low-temperature CO2 capture, there are very few high temperature pre-combustion CO2 capture processes. Lithium silicate (Li4SiO4), one of the best known high-temperature CO2 capture sorbents, has two main challenges, moderate capture kinetics and poor sorbent stability. In this work, we have designed and synthesized lithium silicate nanosheets (LSNs), which showed high CO2 capture capacity (35.3 wt% CO2 capture using 60% CO2 feed gas, close to the theoretical value) with ultra-fast kinetics and enhanced stability at 650 °C. Due to the nanosheet morphology of the LSNs, they provided a good external surface for CO2 adsorption at every Li-site, yielding excellent CO2 capture capacity. The nanosheet morphology of the LSNs allowed efficient CO2 diffusion to ensure reaction with the entire sheet as well as providing extremely fast CO2 capture kinetics (0.22 g g-1 min-1). Conventional lithium silicates are known to rapidly lose their capture capacity and kinetics within the first few cycles due to thick carbonate shell formation and also due to the sintering of sorbent particles; however, the LSNs were stable for at least 200 cycles without any loss in their capture capacity or kinetics. The LSNs neither formed a carbonate shell nor underwent sintering, allowing efficient adsorption-desorption cycling. We also proposed a new mechanism, a mixed-phase model, to explain the unique CO2 capture behavior of the LSNs, using detailed (i) kinetics experiments for both adsorption and desorption steps, (ii) in situ diffuse reflectance infrared Fourier transform (DRIFT) spectroscopy measurements, (iii) depth-profiling X-ray photoelectron spectroscopy (XPS) of the sorbent after CO2 capture and (iv) theoretical investigation through systematic electronic structure calculations within the framework of density functional theory (DFT) formalism.

Dataset Information

Stability of a Benzyl Amine Based CO₂ Capture Adsorbent in View of Regeneration Strategies.

Publications

Stability of a Benzyl Amine Based CO<sub>2</sub> Capture Adsorbent in View of Regeneration Strategies.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets