A robust salt-tolerant superoleophobic alginate/graphene oxide aerogel for efficient oil/water separation in marine environments.

ABSTRACT: Marine pollution caused by frequent oil spill accidents has brought about tremendous damages to marine ecological environment. Therefore, the facile large-scale preparation of three-dimensional (3D) porous functional materials with special wettability is in urgent demand. In this study, we report a low-cost and salt-tolerant superoleophobic aerogel for efficient oil/seawater separation. The aerogel is prepared through incorporating graphene oxide (GO) into alginate (ALG) matrix by using a facile combined freeze-drying and ionic cross-linking method. The 3D structure interconnected by ALG and GO ensures the high mechanical strength and good flexibility of the developed aerogel. The rough microstructure combined with the hydrophilicity of the aerogel ensures its excellent underwater superoleophobic and antifouling properties. High-content polysaccharides contained in the aerogel guarantees its excellent salt-tolerant property. More impressively, the developed aerogel can retain its underwater superoleophobicity even after 30 days of immersion in seawater, indicating its good stability in marine environments. Furthermore, the aerogel could separate various oil/water mixtures with high separation efficiency (>99%) and good reusability (at least 40 cycles). The facile fabrication process combined with the excellent separation performance makes it promising for practical applications in marine environments.

SUBMITTER: Li Y

PROVIDER: S-EPMC5387746 | biostudies-literature | 2017 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

A robust salt-tolerant superoleophobic alginate/graphene oxide aerogel for efficient oil/water separation in marine environments.

Li Yuqi Y Zhang Hui H Fan Mizi M Zheng Peitao P Zhuang Jiandong J Chen Lihui L

Scientific reports 20170411

Marine pollution caused by frequent oil spill accidents has brought about tremendous damages to marine ecological environment. Therefore, the facile large-scale preparation of three-dimensional (3D) porous functional materials with special wettability is in urgent demand. In this study, we report a low-cost and salt-tolerant superoleophobic aerogel for efficient oil/seawater separation. The aerogel is prepared through incorporating graphene oxide (GO) into alginate (ALG) matrix by using a facile ...[more]

PMID: 28397862

Similar Datasets

Project description:The strong expansion potential of invasive plants is often attributed to fast adaptive responses to stress. However, the evolution of tolerance to one stressor may affect the responses to other stressors. Currently, it remains unclear what effect the evolution to one stressor might have on the responses to other single or combined stressors. Moreover, it is unknown how this might differ between invasive and native species.Invasive plants (Mikania micrantha and Bidens pilosa) and native plants (Merremia hederacea and Sida acuta) from low- and high-salinity habitats were grown under control and stressful conditions [salt stress, water stress (drought/waterlogging), and their combinations]. We explored the effects of evolved salt tolerance on the responses to water stress/combined stresses and the underlying trait mechanisms.The high-salinity populations of all species exhibited stronger salt tolerance than the low-salinity populations. As to the tolerance to other stressors, the high-salinity and low-salinity populations of the invasive species were similar, whereas the high-salinity populations of the native species exhibited stronger tolerance than the low-salinity populations under most stress treatments. However, the enhanced salt tolerance in native species was accompanied by reduced total biomass under control condition. The stress tolerance of native species correlated with leaf production rate and allocation to root, while the performance of native species under control condition correlated with leaf morphology and carbon assimilation rate. This suggests a trade-off between salt tolerance and performance in the native but not the invasive species, probably resulting from altered phenotypic/physiological traits.SynthesisOur work suggests that the evolution of tolerance to one stressor may have stronger effects on the tolerance to other stressors of the native compared with the invasive species. This may be a new paradigm to explain the greater advantage of invasive vs. native species in highly stressful habitats.

Project description:In this current study, facile, one-pot synthesis of functionalised nanocomposite coating with simultaneous hydrophilic and oleophobic properties was successfully achieved via the sol-gel technique. The synthesis of this nanocomposite coating aims to develop a highly efficient, simultaneously oleophobic-hydrophilic coating intended for polymer membranes to spontaneously separate oil-in-water emulsions, therefore, mitigating the fouling issue posed by an unmodified polymer membrane. The simultaneous hydrophilicity-oleophobicity of the nanocoating can be applied onto an existing membrane to improve their capability to spontaneously separate oil-in-water substances in the treatment of oily wastewater using little to no energy and being environmentally friendly. The synthesis of hybrid chitosan-silica (CTS-Si)/halloysite nanotube (HNT) nanocomposite coating using the sol-gel method was presented, and the resultant coating was characterised using FTIR, XPS, XRD, NMR, BET, Zeta Potential, and TGA. The wettability of the nanocomposite coating was evaluated in terms of water and oil contact angle, in which it was coated onto a polymer substrate. The coating was optimised in terms of oil and water contact angle using Response Surface Modification (RSM) with Central Composite Design (CCD) theory. The XPS results revealed the successful grafting of organosilanes groups of HNT onto the CTS-Si denoted by a wide band between 102.6-103.7 eV at Si2p. FTIR spectrum presented significant peaks at 3621 cm-1; 1013 cm-1 was attributed to chitosan, and 787 cm-1 signified the stretching of Si-O-Si on HNT. 29Si, 27Al, and 13H NMR spectroscopy confirmed the extensive modification of the particle's shells with chitosan-silica hybrid covalently linked to the halloysite nanotube domains. The morphological analysis via FESEM resulted in the surface morphology that indicates improved wettability of the nanocomposite. The resultant colloids have a high colloid stability of 19.3 mV and electrophoretic mobility of 0.1904 µmcm/Vs. The coating recorded high hydrophilicity with amplified oleophobic properties depicted by a low water contact angle (WCA) of 11° and high oil contact angle (OCA) of 171.3°. The optimisation results via RSM suggested that the optimised sol pH and nanoparticle loadings were pH 7.0 and 1.05 wt%, respectively, yielding 95% desirability for high oil contact angle and low water contact angle.

Dataset Information

A robust salt-tolerant superoleophobic alginate/graphene oxide aerogel for efficient oil/water separation in marine environments.

Publications

A robust salt-tolerant superoleophobic alginate/graphene oxide aerogel for efficient oil/water separation in marine environments.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets