Orientation and conformation of osteocalcin adsorbed onto calcium phosphate and silica surfaces.

ABSTRACT: Adsorption isotherms, circular dichroism (CD) spectroscopy, x-ray photoelectron spectroscopy (XPS), and time-of-flight secondary ion mass spectrometry (ToF-SIMS) were used to investigate the adsorption of human osteocalcin (hOC) and decarboxylated (i.e., Gla converted back to Glu) hOC (dhOC) onto various calcium phosphate surfaces as well as silica surfaces. The adsorption isotherms and XPS nitrogen signals were used to track the amount of adsorbed hOC and dhOC. The intensities of key ToF-SIMS amino acid fragments were used to assess changes in the structure of adsorbed hOC and dhOC. CD spectra were used to investigate the secondary structure of OC. The largest differences were observed when the proteins were adsorbed onto silica versus calcium phosphate surfaces. Similar amounts (3-4 at. % N) of hOC and dhOC were adsorbed onto the silica surface. Higher amounts of hOC and dhOC were adsorbed on all the calcium phosphate surfaces. The ToF-SIMS data showed that the intensity of the Cys amino acid fragment, normalized to intensity of all amino acid fragments, was significantly higher (?×10) when the proteins were adsorbed onto silica. Since in the native OC structure the cysteines are located in the center of three ?-helices, this indicates both hOC and dhOC are more denatured on the silica surface. As hOC and dhOC denature upon adsorption to the silica surface, the cysteines become more exposed and are more readily detected by ToF-SIMS. No significant differences were detected between hOC and dhOC adsorbed onto the silica surface, but small differences were observed between hOC and dhOC adsorbed onto the calcium phosphate surfaces. In the OC structure, the ?-3 helix is located above the ?-1 and ?-2 helices. Small differences in the ToF-SIMS intensities from amino acid fragments characteristic of each helical unit (Asn for ?-1; His for ?-2; and Phe for ?-3) suggests either slight changes in the orientation or a slight uncovering of the ?-1 and ?-2 for adsorbed dhOC. XPS showed that similar amounts of hOC and dhOC were absorbed onto hydroxyapaptite and octacalcium phosphate surfaces, but ToF-SIMS detected some small differences in the amino acid fragment intensities on these surfaces for adsorbed hOC and dhOC.

SUBMITTER: Scudeller LA

PROVIDER: S-EPMC5436982 | biostudies-literature | 2017 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Orientation and conformation of osteocalcin adsorbed onto calcium phosphate and silica surfaces.

Scudeller Luisa A LA Srinivasan Selvi S Rossi Alexandre M AM Stayton Patrick S PS Drobny Gary P GP Castner David G DG

Biointerphases 20170518 2

Adsorption isotherms, circular dichroism (CD) spectroscopy, x-ray photoelectron spectroscopy (XPS), and time-of-flight secondary ion mass spectrometry (ToF-SIMS) were used to investigate the adsorption of human osteocalcin (hOC) and decarboxylated (i.e., Gla converted back to Glu) hOC (dhOC) onto various calcium phosphate surfaces as well as silica surfaces. The adsorption isotherms and XPS nitrogen signals were used to track the amount of adsorbed hOC and dhOC. The intensities of key ToF-SIMS a ...[more]

PMID: 28521505

Similar Datasets

Project description:Silicon (Si) is suggested to be an important/essential nutrient for bone and connective tissue health. Silicon-substituted hydroxyapatite (Si-HA) has silicate ions incorporated into its lattice structure and was developed to improve attachment to bone and increase new bone formation. Here we investigated the direct adsorption of silicate species onto an HA coated surface as a cost effective method of incorporating silicon on to HA surfaces for improved implant osseointegration, and determined changes in surface characteristics and osteoblast cell adhesion. Plasma-sprayed HA-coated stainless steel discs were incubated in silica dispersions of different concentrations (0-42 mM Si), at neutral pH for 12 h. Adsorbed Si was confirmed by XPS analysis and quantified by ICP-OES analysis following release from the HA surface. Changes in surface characteristics were determined by AFM and measurement of surface wettability. Osteoblast cell adhesion was determined by vinculin plaque staining. Maximum Si adsorption to the HA coated disc occurred after incubation in the 6 mM silica dispersion and decreased progressively with higher silica concentrations, while no adsorption was observed with dispersions below 6 mM Si. Comparison of the Si dispersions that produced the highest and lowest Si adsorption to the HA surface, by TEM-based analysis, revealed an abundance of small amorphous nanosilica species (NSP) of ~1.5 nm in diameter in the 6 mM Si dispersion, with much fewer and larger NSP in the 42 mM Si dispersions. 29Si-NMR confirmed that the NSPs in the 6 mM silica dispersion were polymeric and similar in composition to the larger NSPs in the 42 mM Si dispersion, suggesting that the latter were aggregates of the former. Amorphous NSP adsorbed from the 6 mM dispersion on to a HA-coated disc surface increased the surface's water contact angle by 53°, whereas that adsorbed from the 42 mM dispersion decreased the contact angle by 18°, indicating increased and decreased hydrophobicity, respectively. AFM showed an increase in surface roughness of the 6 mM Si treated surface, which correlated well with an increase in number of vinculin plaques. These findings suggest that NSP of the right size (relative to charge) adsorb readily to the HA surface, changing the surface characteristics and, thus, improving osteoblast cell adhesion. This treatment provides a simple way to modify plasma-coated HA surfaces that may enable improved osseointegration of bone implants.

Dataset Information

Orientation and conformation of osteocalcin adsorbed onto calcium phosphate and silica surfaces.

Publications

Orientation and conformation of osteocalcin adsorbed onto calcium phosphate and silica surfaces.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets