Cross-linked cationic diblock copolymer worms are superflocculants for micrometer-sized silica particles.

ABSTRACT: A series of linear cationic diblock copolymer nanoparticles are prepared by polymerization-induced self-assembly (PISA) via reversible addition-fragmentation chain transfer (RAFT) aqueous dispersion polymerization of 2-hydroxypropyl methacrylate (HPMA) using a binary mixture of non-ionic and cationic macromolecular RAFT agents, namely poly(ethylene oxide) (PEO₁₁₃, M_n = 4400 g mol^-1; M_w/M_n = 1.08) and poly([2-(methacryloyloxy)ethyl]trimethylammonium chloride) (PQDMA₁₂₅, M_n = 31?800 g mol^-1, M_w/M_n = 1.19). A detailed phase diagram was constructed to determine the maximum amount of PQDMA₁₂₅ stabilizer block that could be incorporated while still allowing access to a pure worm copolymer morphology. Aqueous electrophoresis studies indicated that zeta potentials of +35 mV could be achieved for such cationic worms over a wide pH range. Core cross-linked worms were prepared via statistical copolymerization of glycidyl methacrylate (GlyMA) with HPMA using a slightly modified PISA formulation, followed by reacting the epoxy groups of the GlyMA residues located within the worm cores with 3-aminopropyl triethoxysilane (APTES), and concomitant hydrolysis/condensation of the pendent silanol groups with the secondary alcohol on the HPMA residues. TEM and DLS studies confirmed that such core cross-linked cationic worms remained colloidally stable when challenged with either excess methanol or a cationic surfactant. These cross-linked cationic worms are shown to be much more effective bridging flocculants for 1.0 ?m silica particles at pH 9 than the corresponding linear cationic worms (and also various commercial high molecular weight water-soluble polymers.). Laser diffraction studies indicated silica aggregates of around 25-28 ?m diameter when using the former worms but only 3-5 ?m diameter when employing the latter worms. Moreover, SEM studies confirmed that the cross-linked worms remained intact after their adsorption onto the silica particles, whereas the much more delicate linear worms underwent fragmentation under the same conditions. Similar results were obtained with 4 ?m silica particles.

SUBMITTER: Penfold NJW

PROVIDER: S-EPMC5450592 | biostudies-literature | 2016 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Cross-linked cationic diblock copolymer worms are superflocculants for micrometer-sized silica particles.

Penfold Nicholas J W NJW Ning Yin Y Verstraete Pierre P Smets Johan J Armes Steven P SP

Chemical science 20160913 12

A series of linear cationic diblock copolymer nanoparticles are prepared by polymerization-induced self-assembly (PISA) via reversible addition-fragmentation chain transfer (RAFT) aqueous dispersion polymerization of 2-hydroxypropyl methacrylate (HPMA) using a binary mixture of non-ionic and cationic macromolecular RAFT agents, namely poly(ethylene oxide) (PEO113, Mn = 4400 g mol-1; Mw/Mn = 1.08) and poly([2-(meth ...[more]

PMID: 28567260

Similar Datasets

Project description:Well-defined sterically stabilized diblock copolymer nanoparticles of 29 nm diameter are prepared by RAFT aqueous emulsion polymerization of methyl methacrylate using a dithiobenzoate-capped poly(glycerol monomethacrylate) precursor. These nanoparticles are evaluated as a dispersant for the preparation of organic crystalline microparticles via ball milling. This is exemplified for azoxystrobin, which is a broad-spectrum fungicide that is widely used to protect various food crops. Laser diffraction and optical microscopy studies indicate the formation of azoxystrobin microparticles of approximately 2 μm diameter after ball milling for 10 min at 400 rpm. Nanoparticle adsorption at the surface of these azoxystrobin microparticles is confirmed by electron microscopy studies. The extent of nanoparticle adsorption on the azoxystrobin microparticles can be quantified using a supernatant assay based on solution densitometry. This technique indicates an adsorbed amount of approximately 5.5 mg m-2, which is sufficient to significantly reduce the negative zeta potential exhibited by azoxystrobin. Moreover, this adsorbed amount appears to be essentially independent of the nature of the core-forming block, with similar data being obtained for both poly(methyl methacrylate)- and poly(2,2,2-trifluoroethyl methacrylate)-based nanoparticles. Finally, X-ray photoelectron spectroscopy studies confirm attenuation of the underlying N1s signal arising from the azoxystrobin microparticles by the former adsorbed nanoparticles, suggesting a fractional surface coverage of approximately 0.24. This value is consistent with a theoretical surface coverage of 0.25 calculated from the adsorption isotherm data. Overall, this study suggests that sterically stabilized diblock copolymer nanoparticles may offer a useful alternative approach to traditional soluble copolymer dispersants for the preparation of suspension concentrates affecting the context of agrochemical applications.

Project description:Cationic non-viral vectors show great potential to introduce genetic material into cells, due to their ability to transport large amounts of genetic material and their high synthetic versatility. However, designing materials that are effective without showing toxic effects or undergoing non-specific interactions when applied systemically remains a challenge. The introduction of shielding polymers such as polyethylene glycol (PEG) can enhance biocompatibility and circulation time, however, often impairs transfection efficiency. Herein, a multicomponent polymer system is introduced, based on cationic and hydrophobic particles (P(nBMA46-co-MMA47-co-DMAEMA90), (PBMD)) with high delivery performance and a pH-responsive block copolymer (poly((N-acryloylmorpholine)-b-(2-(carboxy)ethyl acrylamide)) (P(NAM72-b-CEAm74), PNC)) as shielding system, with PNAM as alternative to PEG. The pH-sensitive polymer design promotes biocompatibility and excellent stability at extracellular conditions (pH 7.4) and also allows endosomal escape and thus high transfection efficiency under acidic conditions. PNC shielded particles are below 200 nm in diameter and showed stable pDNA complexation. Further, interaction with human erythrocytes at extracellular conditions (pH 7.4) was prevented, while acidic conditions (pH 6) enabled membrane leakage. The particles demonstrate transfection in adherent (HEK293T) as well as difficult-to-transfect suspension cells (K-562), with comparable or superior efficiency compared to commercial linear poly(ethylenimine) (LPEI). Besides, the toxicity of PNC-shielded particles was significantly minimized, in particular in K-562 cells and erythrocytes. In addition, a pilot in vivo experiment on bone marrow blood cells of mice that were injected with PNC-shielded particles, revealed slightly enhanced cell transfection in comparison to naked pDNA. This study demonstrates the applicability of cationic hydrophobic polymers for transfection of adherent and suspension cells in culture as well as in vivo by co-formulation with pH-responsive shielding polymers, without substantially compromising transfection performance.

Dataset Information

Cross-linked cationic diblock copolymer worms are superflocculants for micrometer-sized silica particles.

Publications

Cross-linked cationic diblock copolymer worms are superflocculants for micrometer-sized silica particles.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets