Gas-Phase Deposition of Ultrathin Aluminium Oxide Films on Nanoparticles at Ambient Conditions.

ABSTRACT: We have deposited aluminium oxide films by atomic layer deposition on titanium oxide nanoparticles in a fluidized bed reactor at 27 ± 3 °C and atmospheric pressure. Working at room temperature allows coating heat-sensitive materials, while working at atmospheric pressure would simplify the scale-up of this process. We performed 4, 7 and 15 cycles by dosing a predefined amount of precursors, i.e., trimethyl aluminium and water. We obtained a growth per cycle of 0.14-0.15 nm determined by transmission electron microscopy (TEM), similar to atomic layer deposition (ALD) experiments at a few millibars and ~180 °C. We also increased the amount of precursors dosed by a factor of 2, 4 and 6 compared to the base case, maintaining the same purging time. The growth per cycle (GPC) increased, although not linearly, with the dosing time. In addition, we performed an experiment at 170 °C and 1 bar using the dosing times increased by factor 6, and obtained a growth per cycle of 0.16 nm. These results were verified with elemental analysis, which showed a good agreement with the results from TEM pictures. Thermal gravimetric analysis (TGA) showed a negligible amount of unreacted molecules inside the alumina films. Overall, the dosage of the precursors is crucial to control precisely the growth of the alumina films at atmospheric pressure and room temperature. Dosing excess of precursor provokes a chemical vapour deposition type of growth due to the physisorption of molecules on the particles, but this can be avoided by working at high temperatures.

SUBMITTER: Valdesueiro D

PROVIDER: S-EPMC5455438 | biostudies-literature | 2015 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Gas-Phase Deposition of Ultrathin Aluminium Oxide Films on Nanoparticles at Ambient Conditions.

Valdesueiro David D Meesters Gabrie M H GMH Kreutzer Michiel T MT van Ommen J Ruud JR

Materials (Basel, Switzerland) 20150319 3

We have deposited aluminium oxide films by atomic layer deposition on titanium oxide nanoparticles in a fluidized bed reactor at 27 ± 3 °C and atmospheric pressure. Working at room temperature allows coating heat-sensitive materials, while working at atmospheric pressure would simplify the scale-up of this process. We performed 4, 7 and 15 cycles by dosing a predefined amount of precursors, <i>i.e.</i>, trimethyl aluminium and water. We obtained a growth per cycle of 0.14-0.15 nm determined by t ...[more]

PMID: 28788000

Similar Datasets

Project description:In this paper, we report detailed experimental observations of unusual changes in the thickness of solid poly(N-isopropylacrylamide) (PNIPAM) ultrathin films, which are well known to have temperature-responsive hydrophilic-hydrophobic switching properties. To date, a number of studies have been carried out on the bulk and the brush forms of PNIPAM in contact with liquid water, as well as in highly humid environments, and, recently, these ultrathin films have been preliminarily shown to exhibit temperature responses even under low-humidity, ambient conditions. In this work, the thicknesses of ultrathin PNIPAM films in a temperature/moisture-controlled sample stage were monitored continuously using multichannel X-ray reflectometry. At room temperature, the sample thickness showed an unexpected increase after thermal treatment at 70 °C for 3 h. In the temperature cycle between 15 and 60 °C, heating and cooling resulted in some clear differences. During cooling, initially, the thickness was almost constant but began to increase when the temperature exceeded 33 °C, which corresponds to the lower critical solution temperature (LCST). This observation indicates that the PNIPAM ultrathin film is sensitive to the small amounts of water contained in the air, even under ambient, low-humidity conditions. On the other hand, during heating run from 15 to 60 °C, the humidity dependence was monotonic, and no specific changes in the PNIPAM films were observed at around the LCST. By studying the humidity dependence, we found that the hydrophilic and hydrophobic states of the PNIPAM ultrathin film exhibit different temperature dependence behaviors. In addition, we found that swelling takes place even under low-moisture conditions. To understand the difference in the thickness changes observed on cooling and heating further, some models considering the effect of the boundary conditions in the polymer ultrathin film system were considered. In the case of the ultrathin film, the hydrophilic/hydrophobic switching property occurred only in the surface layer, which dominated the absorption of water molecules from air. In contrast, the interface layer was time-stable and provided an escape route for water molecules during heating.

Dataset Information

Gas-Phase Deposition of Ultrathin Aluminium Oxide Films on Nanoparticles at Ambient Conditions.

Publications

Gas-Phase Deposition of Ultrathin Aluminium Oxide Films on Nanoparticles at Ambient Conditions.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets