Zinc-modified Calcium Silicate Coatings Promote Osteogenic Differentiation through TGF-?/Smad Pathway and Osseointegration in Osteopenic Rabbits.

ABSTRACT: Surface-modified metal implants incorporating different ions have been employed in the biomedical field as bioactive dental implants with good osseointegration properties. However, the molecular mechanism through which surface coatings exert the biological activity is not fully understood, and the effects have been difficult to achieve, especially in the osteopenic bone. In this study, We examined the effect of zinc-modified calcium silicate coatings with two different Zn contents to induce osteogenic differentiation of rat bone marrow-derived pericytes (BM-PCs) and osteogenetic efficiency in ovariectomised rabbits. Ti-6Al-4V with zinc-modified calcium silicate coatings not only enhanced proliferation but also promoted osteogenic differentiation and mineralized matrix deposition of rat BM-PCs as the zinc content and culture time increased in vitro. The associated molecular mechanisms were investigated by Q-PCR and Western blotting, revealing that TGF-?/Smad signaling pathway plays a direct and significant role in regulating BM-PCs osteoblastic differentiation on Zn-modified coatings. Furthermore, in vivo results that revealed Zn-modified calcium silicate coatings significantly promoted new bone formation around the implant surface in osteopenic rabbits as the Zn content and exposure time increased. Therefore, Zn-modified calcium silicate coatings can improve implant osseointegration in the condition of osteopenia, which may be beneficial for patients suffering from osteoporosis-related fractures.

SUBMITTER: Yu J

PROVIDER: S-EPMC5469779 | biostudies-literature | 2017 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Zinc-modified Calcium Silicate Coatings Promote Osteogenic Differentiation through TGF-β/Smad Pathway and Osseointegration in Osteopenic Rabbits.

Yu Jiangming J Xu Lizhang L Li Kai K Xie Ning N Xi Yanhai Y Wang Yang Y Zheng Xuebin X Chen Xiongsheng X Wang Meiyan M Ye Xiaojian X

Scientific reports 20170613 1

Surface-modified metal implants incorporating different ions have been employed in the biomedical field as bioactive dental implants with good osseointegration properties. However, the molecular mechanism through which surface coatings exert the biological activity is not fully understood, and the effects have been difficult to achieve, especially in the osteopenic bone. In this study, We examined the effect of zinc-modified calcium silicate coatings with two different Zn contents to induce oste ...[more]

PMID: 28611362

Similar Datasets

Project description:The purpose of this study was to comparatively investigate the behavior of silicate and sol-silicate coatings non-modified or modified with an organosilane on wood and on wood pre-coated with silica-mineralized primers. Adhesion strength, morphology, and water permeability and related damages were studied to evaluate the possibility of utilizing such inorganic-based coating systems for durable protection of wood without or with relatively cheap and water-borne primers. Potassium silicate and potassium methylsiliconate aqueous solutions and a colloidal silica were used for the preparation of the coatings. The white coating paints were brushed on beech wood substrates at a rate of 220 g·m-2. The coatings exhibited good coverage ability. The pull-off adhesion strength values appeared to be related to pH following a polynomial law. The adhesion strength for the silicate coatings were adequate (above 3 MPa and up to 5 MPa) for wood, whereas the values for the sol-silicates were too low for practical applications. The adhesion values were in general higher for the samples cured in a climate room (23 ± 3 °C and 75 ± 2% relative humidity) than the samples cured in the ambient atmosphere of the laboratory (23 ± 3 °C and 25 ± 5% relative humidity). The presence of microdefects (cracks, holes) was revealed in the coating layers by optical and scanning electron microscopy. The surface roughness parameters assessed by confocal scanning laser microscopy were dependent on the magnification applied for their measurement. The arithmetic average roughness Sa was between 5 µm and 10 µm at magnification 5× and between 2.5 μm and 10 µm at magnification 20×. The maximum peak-to-valley height Sz confirmed the presence of open pores emerging through the coatings. The open pores constitute free pathways for water ingress through the coatings, and could explain the high water absorption of the coatings including the methysiliconate-containing silicate coating and despite the relatively high water contact angle and low wettability exhibited by this sample. The post-application of a hydrophobizing solution containing hexadecyltrimethoxysilane and dimethyloctadecyl[3-(trimethoxysilyl)propyl]ammonium chloride considerably reduced the water permeability, while application of nanosilica-containing organic primers increased the adhesion for the coatings. Silicate coatings with adhesion great enough and resistance against water damages can be generated on wood even without a primer using low silica-to-alkali ratio binders and an organosilane additive. The sol-silicate coatings appear to be applicable only with a primer. The improvement of the paint formulations to control the formation of microcracks and open pores could be useful to reduce the liquid water permeability and increase durability. Otherwise, the application of a hydrophobizing treatment can be used for this purpose.

Dataset Information

Zinc-modified Calcium Silicate Coatings Promote Osteogenic Differentiation through TGF-?/Smad Pathway and Osseointegration in Osteopenic Rabbits.

Publications

Zinc-modified Calcium Silicate Coatings Promote Osteogenic Differentiation through TGF-β/Smad Pathway and Osseointegration in Osteopenic Rabbits.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets