Microplasma-assisted hydrogel fabrication: A novel method for gelatin-graphene oxide nano composite hydrogel synthesis for biomedical application.

ABSTRACT: Toxicity issues and biocompatibility concerns with traditional classical chemical cross-linking processes prevent them from being universal approaches for hydrogel fabrication for tissue engineering. Physical cross-linking methods are non-toxic and widely used to obtain cross-linked polymers in a tunable manner. Therefore, in the current study, argon micro-plasma was introduced as a neutral energy source for cross-linking in fabrication of the desired gelatin-graphene oxide (gel-GO) nanocomposite hydrogel scaffolds. Argon microplasma was used to treat purified gelatin (8% w/v) containing 0.1?1 wt% of high-functionality nano-graphene oxide (GO). Optimized plasma conditions (2,500 V and 8.7 mA) for 15 min with a gas flow rate of 100 standard cm³/min was found to be most suitable for producing the gel-GO nanocomposite hydrogels. The developed hydrogel was characterized by the degree of cross-linking, FTIR spectroscopy, SEM, confocal microscopy, swelling behavior, contact angle measurement, and rheology. The cell viability was examined by an MTT assay and a live/dead assay. The pore size of the hydrogel was found to be 287 ± 27 µm with a contact angle of 78° ± 3.7°. Rheological data revealed improved storage as well as a loss modulus of up to 50% with tunable viscoelasticity, gel strength, and mechanical properties at 37 °C temperature in the microplasma-treated groups. The swelling behavior demonstrated a better water-holding capacity of the gel-GO hydrogels for cell growth and proliferation. Results of the MTT assay, microscopy, and live/dead assay exhibited better cell viability at 1% (w/w) of high-functionality GO in gelatin. The highlight of the present study is the first successful attempt of microplasma-assisted gelatin-GO nano composite hydrogel fabrication that offers great promise and optimism for further biomedical tissue engineering applications.

SUBMITTER: Satapathy MK

PROVIDER: S-EPMC5490464 | biostudies-literature | 2017

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Microplasma-assisted hydrogel fabrication: A novel method for gelatin-graphene oxide nano composite hydrogel synthesis for biomedical application.

Satapathy Mantosh Kumar MK Chiang Wei-Hung WH Chuang Er-Yuan EY Chen Chih-Hwa CH Liao Jia-Liang JL Huang Huin-Ning HN

PeerJ 20170627

Toxicity issues and biocompatibility concerns with traditional classical chemical cross-linking processes prevent them from being universal approaches for hydrogel fabrication for tissue engineering. Physical cross-linking methods are non-toxic and widely used to obtain cross-linked polymers in a tunable manner. Therefore, in the current study, argon micro-plasma was introduced as a neutral energy source for cross-linking in fabrication of the desired gelatin-graphene oxide (gel-GO) nanocomposit ...[more]

PMID: 28663938

Similar Datasets

Project description:Regeneration of injured tendon and ligament (T&L) remains a clinical challenge due to their poor intrinsic healing capacity. Tissue engineering provides a promising alternative treatment approach to facilitate T&L healing and regeneration. Successful tendon tissue engineering requires the use of three-dimensional (3D) biomimetic scaffolds that possess the physical and biochemical features of native tendon tissue. We report here the development and characterization of a novel composite scaffold fabricated by co-electrospinning of poly-?-caprolactone (PCL) and methacrylated gelatin (mGLT). We found that photocrosslinking retained mGLT, resulted in a uniform distribution of mGLT throughout the depth of scaffold and also preserved scaffold mechanical strength. Moreover, photocrosslinking was able to integrate stacked scaffold sheets to form multilayered constructs that mimic the structure of native tendon tissues. Importantly, cells impregnated into the constructs remained responsive to topographical cues and exogenous tenogenic factors, such as TGF-?3. The excellent biocompatibility and highly integrated structure of the scaffold developed in this study will allow the creation of a more advanced tendon graft that possesses the architecture and cell phenotype of native tendon tissues.The clinical challenges in tendon repair have spurred the development of tendon tissue engineering approaches to create functional tissue replacements. In this study, we have developed a novel composite scaffold as a tendon graft consisting of aligned poly-?-caprolactone (PCL) microfibers and methacrylated gelatin (mGLT). Cell seeding and photocrosslinking between scaffold layers can be performed simultaneously to create cell impregnated multilayered constructs. This cell-scaffold construct combines the advantages of PCL nanofibrous scaffolds and photocrosslinked gelatin hydrogels to mimic the structure, mechanical anisotropy, and cell phenotype of native tendon tissue. The scaffold engineered here as a building block for multilayer constructs should have applications beyond tendon tissue engineering in the fabrication of tissue grafts that consist of both fibrous and hydrogel components.

Dataset Information

Microplasma-assisted hydrogel fabrication: A novel method for gelatin-graphene oxide nano composite hydrogel synthesis for biomedical application.

Publications

Microplasma-assisted hydrogel fabrication: A novel method for gelatin-graphene oxide nano composite hydrogel synthesis for biomedical application.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets