Preparation and Chemical/Microstructural Characterization of Azacrown Ether-Crosslinked Chitosan Films.

ABSTRACT: Chemically stable porous azacrown ether-crosslinked chitosan films were prepared by reacting varying molar amounts of N,N-diallyl-7,16-diaza-1,4,10,13-tetraoxa-dibenzo-18-crown-6 (molar equivalents ranging from 0, 0.125, 0.167, 0.25 and 0.5) with chitosan. Their chemical and structural properties were characterized by solid state-nuclear magnetic resonance (NMR), elemental, Fourier transform infrared (FTIR), microscopy, and X-ray analyses, as well as gel content. NMR and FTIR analyses of the reaction products suggested that new -CH₂- crosslink bridges were produced between the amine groups of chitosan (Ch) and the allyl groups of the azacrown (DAC). The crosslinking chemistry between allyl and amine groups of the reactants was further evidenced with solution NMR studies on model compound of glucosamine with the azacrown. X-ray diffraction analysis of the Ch/azacrown films using wide angle X-ray scattering (WAXS), including synchrotron-WAXS, revealed that the crystalline arrangement of chitosan (Ch) was partially destroyed with increasing grafting of azacrown ether proportion on the Ch polymer chain. Solubility and gel content determination confirmed network formation with a gel content as high as 84-95 wt %. Microstructural analysis revealed microporous morphology with high surface area. The morphology and structure of the azacrown ether-crosslinked chitosan films could be tailored by stoichiometry of the reacting species.

SUBMITTER: Toeri J

PROVIDER: S-EPMC5506952 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Preparation and Characterization of Chitosan-Agarose Composite Films.

Project description:Nowadays, there is a growing interest to develop biodegradable functional composite materials for food packaging and biomedicine applications from renewable sources. Some composite films were prepared by the casting method using chitosan (CS) and agarose (AG) in different mass ratios. The composite films were analyzed for physical-chemical-mechanical properties including tensile strength (TS), elongation-at-break (EB), water vapor transmission rate (WVTR), swelling ratio, Fourier-transform infrared spectroscopy, and morphology observations. The antibacterial properties of the composite films were also evaluated. The obtained results reveal that an addition of AG in varied proportions to a CS solution leads to an enhancement of the composite film's tensile strength, elongation-at-break, and water vapor transmission rate. The composite film with an agarose mass concentration of 60% was of the highest water uptake capacity. These improvements can be explained by the chemical structures of the new composite films, which contain hydrogen bonding interactions between the chitosan and agarose as shown by Fourier-transform infrared spectroscopy (FTIR) analysis and the micro-pore structures as observed with optical microscopes and scanning electron microscopy (SEM). The antibacterial results demonstrated that the films with agarose mass concentrations ranging from 0% to 60% possessed antibacterial properties. These results indicate that these composite films, especially the composite film with an agarose mass concentration of 60%, exhibit excellent potential to be used in food packaging and biomedical materials.

| S-EPMC5456607 | biostudies-other

Chitosan Films Functionalized with Different Hydroxycinnamic Acids: Preparation, Characterization and Application for Pork Preservation.

Project description:Hydroxycinnamic acids are one category of bioactive phenolic acids that are widely distributed in plants. In this study, chitosan (CS) was functionalized with three kinds of hydroxycinnamic acids (p-coumaric acid, caffeic acid and ferulic acid) through the carbodiimide-mediated grafting method. The obtained hydroxycinnamic-acid-grafted CSs (hydroxycinnamic acid-g-CSs) were further fabricated into food packaging films through solvent casting. For the first time, the functionalities of the different hydroxycinnamic acid-g-CS films were compared. Results showed the grafting ratio of p-coumaric acid-g-CS, caffeic acid-g-CS and ferulic acid-g-CS was 73.68, 129.42 and 91.75 mg/g, respectively. Instrumental analyses confirmed hydroxycinnamic acids conjugated with CS through amide and ester bonds. The functionalization of CS film with hydroxycinnamic acids produced a more compact microstructure and higher UV light barrier ability, mechanical strength, water vapor barrier ability, thermal stability and antioxidant and antimicrobial activities. Among the different hydroxycinnamic acid-g-CS films, caffeic acid-g-CS film presented the strongest barrier, mechanical, antioxidant and antimicrobial properties. Moreover, caffeic acid-g-CS film packaging effectively extended the shelf life of pork to 10 days at 4 °C. Our results suggest caffeic acid-g-CS film can be used in the active food packaging field.

| S-EPMC8000987 | biostudies-literature

Sodium Hydroxide-Free Soy Protein Isolate-Based Films Crosslinked by Pentaerythritol Glycidyl Ether.

Project description:The soy protein isolate (SPI), sodium dodecylbenzenesulfonate (SDBS) and pentaerythritol glycidyl ether (PEGE) were used to make biodegradable films in this study. Unlike the usual method that adding sodium hydroxide (NaOH) during the SPI-based film casting, SDBS was used as a surfactant playing the similar role as NaOH. Since NaOH is a chemical with corrosiveness and toxicity, the replacing of NaOH by SDBS might reduce the hazard threat during the utilization of SPI-based films in food packing application. Furthermore, the presentation of SDBS helped dispersing the hydrophobic PEGE into the hydrophilic SPI. PEGE is a crosslinking agent with multiple reactive epoxy groups. The chemical structures and micro morphologies of the fabricated films were investigated by means of FTIR, XRD, and SEM. The thermal stabilities of the films were examined by means of the thermo-gravimetric analysis. After the chemical crosslinking, the ultimate tensile strength of the film was significantly increased, meanwhile, the water absorption was dramatically decreased. It was concluded that the SPI-based film containing 4% PEGE achieved the optimal performance.

| S-EPMC6401677 | biostudies-other

Preparation and Characterization of Polyvinyl Alcohol-Chitosan Composite Films Reinforced with Cellulose Nanofiber.

Project description:In this study microcrystalline cellulose (MCC) was oxidized by 2,2,6,6-tetramethylpiperidine-1-oxyl radical (TEMPO)-mediated oxidation. The treated cellulose slurry was mechanically homogenized to form a transparent dispersion which consisted of individual cellulose nanofibers with uniform widths of 3-4 nm. Bio-nanocomposite films were then prepared from a polyvinyl alcohol (PVA)-chitosan (CS) polymeric blend with different TEMPO-oxidized cellulose nanofiber (TOCN) contents (0, 0.5, 1.0 and 1.5 wt %) via the solution casting method. The characterizations of pure PVA/CS and PVA/CS/TOCN films were performed in terms of field emission scanning electron microscopy (FESEM), tensile tests, thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), and X-ray diffraction (XRD). The results from FESEM analysis justified that low loading levels of TOCNs were dispersed uniformly and homogeneously in the PVA-CS blend matrix. The tensile strength and thermal stability of the films were increased with the increased loading levels of TOCNs to a maximum level. The thermal study indicated a slight improvement of the thermal stability upon the reinforcement of TOCNs. As evidenced by the FTIR and XRD, PVA and CS were considered miscible and compatible owing to hydrogen bonding interaction. These analyses also revealed the good dispersion of TOCNs within the PVA/CS polymer matrix. The improved properties due to the reinforcement of TOCNs can be highly beneficial in numerous applications.

| S-EPMC5509094 | biostudies-other

Preparation and Characterization of Films Extruded of Polyethylene/Chitosan Modified with Poly(lactic acid).

Project description:The use of mixtures of synthetic and natural polymers is a potential option to reduce the pollution by plastic waste. In this work, the method for the chemical modification of chitosan with poly(lactic acid) was developed; then, the preparation of films of blends of polyethylene and chitosan-poly(lactic acid) produced by an extrusion method using polyethylene-graft maleic anhydride as a compatibilizer. It was possible to obtain films with a maximum content of 20 wt% and 30 wt%, chitosan, with and without compatibilizer, respectively. Scanning electron microscope (SEM) analysis showed a homogeneous surface on all films. The addition of the compatibilizer had a significant effect on the mechanical properties of the films, such as an increase in Young's modulus and a decrease in the elongation at break; additionally, the compatibilizer promotes thermal degradation in a single step and gives the film a slight increase in thermal resistance. These results are attributed to an improved interaction in the interface of polyethylene and chitosan-poly(lactic acid), promoted by the compatibilizer.

| S-EPMC5455231 | biostudies-other

Preparation and Characterization of Electrostatically Crosslinked Polymer⁻Liposomes in Anticancer Therapy.

Project description:pH-sensitive polymer⁻liposomes can rapidly release their payloads. However, it is difficult to simultaneously achieve stability and pH-responsiveness in the polymer⁻liposomes. In this study, stable and pH-sensitive crosslinked polymer⁻liposomes were fabricated through electrostatic interactions. The pH-sensitive copolymer methoxy poly(ethylene glycol)-block-poly(methacrylic acid)-cholesterol (mPEG-b-P(MAAc)-chol) and crosslinking reagent poly(ethylene glycol) with end-capped with lysine (PEG-Lys2) were synthesized and characterized. At physiological conditions, the pH-sensitive copolymers were anionic and interacted electrostatically with the cationic crosslinker PEG-Lys2, forming the electrostatically-crosslinked polymer⁻liposomes and stabilizing the liposomal structure. At pH 5.0, the carboxylic groups in mPEG-b-P(MAAc)-chol were neutralized, and the liposomal structure was destroyed. The particle size of the crosslinked polymer⁻liposomes was approximately 140 nm and the polymer⁻liposomes were loaded with the anticancer drug doxorubicin. At pH 7.4, the crosslinked polymer⁻liposomes exhibited good stability with steady particle size and low drug leakage, even in the presence of fetal bovine serum. At pH 5.0, the architecture of the crosslinked polymer⁻liposomes was damaged following rapid drug release, as observed by using transmission electron microscopy and their apparent size variation. The crosslinked polymer⁻liposomes were pH-sensitive within the endosome and in the human breast cancer cells MDA-MB-231, as determined by using confocal laser scanning microscopy. The intracellular drug release profiles indicated cytotoxicity in cancer cells. These results indicated that the highly-stable and pH-sensitive electrostatically-crosslinked polymer⁻liposomes offered a potent drug-delivery system for use in anticancer therapies.

| S-EPMC6032249 | biostudies-literature

Preparation and Characterization of PHBV/PCL-Diol Blend Films.

Project description:Biodegradable thin films based on poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) and poly(caprolactone diol) (PCL-diol) blend were developed using the solution casting method. PHBV is biodegradable, biocompatible, and produced naturally by bacterial activity, but its use is restricted by high crystallinity and low resistance to thermal degradation with melting temperatures close to degradation thus narrowing the processing window. Solution casting was chosen as a cost-effective method reducing energy consumption and avoiding thermal degradation during processing. The increase in PCL-diol in blend composition (40-60 wt%) enhances the film-forming ability of PHBV and the wettability along with the decrease in the roughness of the resulting materials as revealed by contact angle measurements, scanning electron microscopy (SEM), and atomic force microscopy (AFM). Optimal composition in terms of filmogenity and surface structure has been achieved by the addition of PCL-diol in the amount of 60 wt%. FTIR confirmed the expected chemical structures with no evidence of chemical interactions between the two polymers.

| S-EPMC10747782 | biostudies-literature

A Slot-Die Technique for the Preparation of Continuous, High-Area, Chitosan-Based Thin Films.

Project description:Chitosan-based films have a diverse range of potential applications but are currently limited in terms of commercial use due to a lack of methods specifically designed to produce thin films in high volumes. To address this limitation directly, hydrogels prepared from chitosan, chitosan-tetraethoxy silane, also known as tetraethyl orthosilicate (TEOS) and chitosan-glutaraldehyde have been used to prepare continuous thin films using a slot-die technique which is described in detail. By way of preliminary analysis of the resulting films for comparison purposes with films made by other methods, the mechanical strength of the films produced was assessed. It was found that as expected, the hybrid films made with TEOS and glutaraldehyde both show a higher yield strength than the films made with chitosan alone. In all cases, the mechanical properties of the films were found to compare very favorably with similar measurements reported in the literature. In order to assess the possible influence of the direction in which the hydrogel passes through the slot-die on the mechanical properties of the films, testing was performed on plain chitosan samples cut in a direction parallel to the direction of travel and perpendicular to this direction. It was found that there was no evidence of any mechanical anisotropy induced by the slot die process. The examples presented here serve to illustrate how the slot-die approach may be used to create high-volume, high-area chitosan-based films cheaply and rapidly. It is suggested that an approach of the type described here may facilitate the use of chitosan-based films for a wide range of important applications.

| S-EPMC8153309 | biostudies-literature

Preparation, characterization, and modeling of α-zirconium phosphonates with ether-functional surfaces.

Project description:Layered α-zirconium(IV) phosphonates were prepared from novel ether-terminal alkyl phosphonic acids, providing nanoplatelets with brush-like polar surfaces. The precursor materials were characterized by NMR, mass spectrometry, and elemental analysis. The derived nanoparticles were examined by XRD, TEM, TGA, and elemental analysis. The experimental compositions were slightly rich in organophosphorus content. In general, the layered materials had good crystallinity, with layer reflections appearing up to (005) and d-spacings consistent with the anticipated α-phase structure. Computer simulations suggest that tailored surface chemistries, including ether functionalities, will offer favorable thermodynamic interactions with polyester polymer matrices.

| S-EPMC2808038 | biostudies-literature

Ultrasound-assisted preparation of chitosan/nano-silica aerogel/tea polyphenol biodegradable films: Physical and functional properties.

Project description:In this study, chitosan(CS), nano-silicon aerogels(nSA) and tea polyphenols(TP) were used as film-forming materials and processed with ultrasonication to form films using the tape-casting method. The effects of ultrasonication time, temperature and frequency on the properties of CS/nSA/TP film were explored via material property testing. The results of response surface showed that the maximum tensile strength of the film was 4.036 MPa at ultrasonication time(57.97 min), temperature(37.26 °C) and frequency(30 kHz). The maximum elongation at break of the film was 279.42 % at ultrasonication time(60.88 min), temperature(39.93 °C) and frequency(30 kHz). Due to cavitation and super-mixing effects, ultrasonication may make the surface of the film smoother and easier to degrade. After ultrasonication, TPs were protected by the 3D network structure composed of CS and nSA. Ultrasonication improved the antioxidant and antibacterial properties of the film. These results show that ultrasonication is an effective method to improve the properties of films.

| S-EPMC9168617 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data