Robust hierarchical 3D carbon foam electrode for efficient water electrolysis.

ABSTRACT: Herein we report a 3D heterostructure comprising a hierarchical macroporous carbon foam that incorporates mesoporous carbon nanotubes decorated with cobalt oxide nanoparticles as an unique and highly efficient electrode material for the oxygen evolution reaction (OER) in electrocatalytic water splitting. The best performing electrode material showed high stability after 10?h, at constant potential of 1.7?V vs. RHE (reversible hydrogen electrode) in a 0.1?M KOH solution and high electrocatalytic activity in OER with low overpotential (0.38?V vs RHE at 10?mA?cm-2). The excellent electrocatalytic performance of the electrode is rationalized by the overall 3D macroporous structure and with the firmly integrated CNTs directly grown on the foam, resulting in a large specific surface area, good electrical conductivity, as well as an efficient electrolyte transport into the whole electrode matrix concurrent with an ability to quickly dispose oxygen bubbles into the electrolyte. The eminent properties of the three-dimensional structured carbon matrix, which can be synthesized through a simple, scalable and cost effective pyrolysis process show that it has potential to be implemented in large-scale water electrolysis systems.

SUBMITTER: Pham TN

PROVIDER: S-EPMC5522430 | biostudies-literature | 2017 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Robust hierarchical 3D carbon foam electrode for efficient water electrolysis.

Pham Tung Ngoc TN Sharifi Tiva T Sandström Robin R Siljebo William W Shchukarev Andrey A Kordas Krisztian K Wågberg Thomas T Mikkola Jyri-Pekka JP

Scientific reports 20170721 1

Herein we report a 3D heterostructure comprising a hierarchical macroporous carbon foam that incorporates mesoporous carbon nanotubes decorated with cobalt oxide nanoparticles as an unique and highly efficient electrode material for the oxygen evolution reaction (OER) in electrocatalytic water splitting. The best performing electrode material showed high stability after 10 h, at constant potential of 1.7 V vs. RHE (reversible hydrogen electrode) in a 0.1 M KOH solution and high electrocatalytic ...[more]

PMID: 28733585

Similar Datasets

Project description:In electrochemical processes, gas bubbles on the electrode can cause an increase in both overpotential and ohmic voltage drop which leads to higher energy consumption. Applying power ultrasound during water electrolysis can help to reduce the overpotential, enhance mass transfer, and save energy. In this study, we investigated the effect of ultrasound (20 kHz) on the hydrogen evolution reaction (HER) on a stainless steel plate with varying concentrations of NaOH solutions at 298 K, using linear sweep voltammetry (LSV). We especially focused on understanding the bubble behavior on the stainless steel plate during HER using high-speed imaging in ultrasonic field. When ultrasound was applied to solutions with NaOH concentrations of 0.1, 0.5, 1 M, the current density increased by about 9.0, 5.9, 2.8 %, respectively. As the ultrasound irradiation began, the bubbles tended to hover around on the electrode surface, coalescing with other bubbles, rather than rising. When the size of the coalesced bubbles became too large to stay on the surface of the electrode, they were expelled from the ultrasonic field. The repeated collapse and coalescence of these bubbles was observed while they were rising. The velocity increased about 2 times when ultrasound irradiation began, and increased by more than 6 times in the ultrasonic field. More nucleation of bubbles was observed on the electrode in the ultrasonic field. Using ultrasound reduced the critical diameter of bubbles which detached from the electrode, from 58.0 to 15.9 μm, and the residence time of the bubbles, from 533 to 118 ms. Further, when the ultrasound was applied, the mean diameter of bubbles decreased from 71.8 to 17 μm. Hence, bubble coverage on the electrode surface decreased from 8.3 to 1 % despite an increase in the total number of bubbles. As a result, ultrasound was found to be effective for hydrogen production during water electrolysis, increasing current by the faster removal of gas from the stainless steel plate.

Dataset Information

Robust hierarchical 3D carbon foam electrode for efficient water electrolysis.

Publications

Robust hierarchical 3D carbon foam electrode for efficient water electrolysis.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets