Optimization of the Silver Nanoparticles PEALD Process on the Surface of 1-D Titania Coatings.

ABSTRACT: Plasma enhanced atomic layer deposition (PEALD) of silver nanoparticles on the surface of 1-D titania coatings, such as nanotubes (TNT) and nanoneedles (TNN), has been carried out. The formation of TNT and TNN layers enriched with dispersed silver particles of strictly defined sizes and the estimation of their bioactivity was the aim of our investigations. The structure and the morphology of produced materials were determined using X-ray photoelectron spectroscopy (XPS) and scanning electron miscroscopy (SEM). Their bioactivity and potential usefulness in the modification of implants surface have been estimated on the basis of the fibroblasts adhesion and proliferation assays, and on the basis of the determination of their antibacterial activity. The cumulative silver release profiles have been checked with the use of inductively coupled plasma-mass spectrometry (ICPMS), in order to exclude potential cytotoxicity of silver decorated systems. Among the studied nanocomposite samples, TNT coatings, prepared at 3, 10, 12 V and enriched with silver nanoparticles produced during 25 cycles of PEALD, revealed suitable biointegration properties and may actively counteract the formation of bacterial biofilm.

SUBMITTER: Radtke A

PROVIDER: S-EPMC5535259 | biostudies-literature | 2017 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Optimization of the Silver Nanoparticles PEALD Process on the Surface of 1-D Titania Coatings.

Radtke Aleksandra A Jędrzejewski Tomasz T Kozak Wiesław W Sadowska Beata B Więckowska-Szakiel Marzena M Talik Ewa E Mäkelä Maarit M Leskelä Markku M Piszczek Piotr P

Nanomaterials (Basel, Switzerland) 20170724 7

Plasma enhanced atomic layer deposition (PEALD) of silver nanoparticles on the surface of 1-D titania coatings, such as nanotubes (TNT) and nanoneedles (TNN), has been carried out. The formation of TNT and TNN layers enriched with dispersed silver particles of strictly defined sizes and the estimation of their bioactivity was the aim of our investigations. The structure and the morphology of produced materials were determined using X-ray photoelectron spectroscopy (XPS) and scanning electron mis ...[more]

PMID: 28737725

Similar Datasets

Project description:The present study was carried out to reduce the size of silver nanoparticles (AgNPs) by optimizing physico-chemical conditions of the Aspergillus fumigatus BTCB10 growth based on central composite design (CCD) through response surface methodology (RSM). Variables such as a concentration of silver nitrate (mM), NaCl (%) and the wet weight of biomass (g) were controlled to produce spherical, monodispersed particles of 33.23 nm size, observing 78.7% reduction in size as compared to the initially obtained size that was equal to 356 nm. The obtained AgNPs exhibited negative zeta potential of -9.91 mV with a peak at 420 nm in the UV-Vis range whereas Fourier Transform Infrared (FT-IR) analysis identified O-H, C = C, C ≡ C, C-Br and C-Cl groups attached as capping agents. After conducting RSM experiments, a high nitrate reductase activity value of 179.15 nmol/h/ml was obtained; thus indicating a likely correlation between enzyme production and AgNPs synthesis. The F-value (significant at 3.91), non-significant lack of fit and determination coefficient (R2 = 0.7786) is representative of the good relation between the predicted values of response. We conclude that CCD is an effective tool in obtaining significant results of high quality and efficiency.The present study was carried out to reduce the size of silver nanoparticles (AgNPs) by optimizing physico-chemical conditions of the Aspergillus fumigatus BTCB10 growth based on central composite design (CCD) through response surface methodology (RSM). Variables such as a concentration of silver nitrate (mM), NaCl (%) and the wet weight of biomass (g) were controlled to produce spherical, monodispersed particles of 33.23 nm size, observing 78.7% reduction in size as compared to the initially obtained size that was equal to 356 nm. The obtained AgNPs exhibited negative zeta potential of –9.91 mV with a peak at 420 nm in the UV-Vis range whereas Fourier Transform Infrared (FT-IR) analysis identified O–H, C = C, C ≡ C, C–Br and C–Cl groups attached as capping agents. After conducting RSM experiments, a high nitrate reductase activity value of 179.15 nmol/h/ml was obtained; thus indicating a likely correlation between enzyme production and AgNPs synthesis. The F-value (significant at 3.91), non-significant lack of fit and determination coefficient (R2 = 0.7786) is representative of the good relation between the predicted values of response. We conclude that CCD is an effective tool in obtaining significant results of high quality and efficiency.

Dataset Information

Optimization of the Silver Nanoparticles PEALD Process on the Surface of 1-D Titania Coatings.

Publications

Optimization of the Silver Nanoparticles PEALD Process on the Surface of 1-D Titania Coatings.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets