Non-Destructive Inspection of Impact Damage in Composite Aircraft Panels by Ultrasonic Guided Waves and Statistical Processing.

ABSTRACT: This paper discusses a non-destructive evaluation (NDE) technique for the detection of damage in composite aircraft structures following high energy wide area blunt impact (HEWABI) from ground service equipment (GSE), such as heavy cargo loaders and other heavy equipment. The test structures typically include skin, co-cured stringers, and C-frames that are bolt-connected onto the skin with shear ties. The inspection exploits the waveguide geometry of these structures by utilizing ultrasonic guided waves and a line scan approach. Both a contact prototype and a non-contact prototype were developed and tested on realistic test panels subjected to impact in the laboratory. The results are presented in terms of receiver operating characteristic curves that show excellent probability of detection with low false alarm rates for defects located in the panel skin and stringers.

SUBMITTER: Capriotti M

PROVIDER: S-EPMC5553524 | biostudies-literature | 2017 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Non-Destructive Inspection of Impact Damage in Composite Aircraft Panels by Ultrasonic Guided Waves and Statistical Processing.

Capriotti Margherita M Kim Hyungsuk E HE Scalea Francesco Lanza di FLD Kim Hyonny H

Materials (Basel, Switzerland) 20170604 6

This paper discusses a non-destructive evaluation (NDE) technique for the detection of damage in composite aircraft structures following high energy wide area blunt impact (HEWABI) from ground service equipment (GSE), such as heavy cargo loaders and other heavy equipment. The test structures typically include skin, co-cured stringers, and C-frames that are bolt-connected onto the skin with shear ties. The inspection exploits the waveguide geometry of these structures by utilizing ultrasonic guid ...[more]

PMID: 28772976

Similar Datasets

Propagation of Ultrasonic Guided Waves in Composite Multi-Wire Ropes.

Project description:Multi-wire ropes are widely used as load-carrying constructional elements in bridges, cranes, elevators, etc. Structural integrity of such ropes can be inspected by using non-destructive ultrasonic techniques. The objective of this work was to investigate propagation of ultrasonic guided waves (UGW) along composite multi-wire ropes in the cases of various types of acoustic contacts between neighboring wires and the plastic core. The modes of UGW propagating along the multi-wire ropes were identified using modelling, the dispersion curves were calculated using analytical and semi-analytical finite element (SAFE) techniques. In order to investigate the effects of UGW propagation, the two types of the acoustic contact between neighboring wires were simulated using the 3D finite element method (FE) as well. The key question of investigation was estimation of the actual boundary conditions between neighboring wires (solid or slip) and the real depth of penetration of UGW into the overall cross-section of the rope. Therefore, in order to verify the results of FE modelling, the guided wave penetration into strands of multi-wire rope was investigated experimentally. The performed modelling and experimental investigation enabled us to select optimal parameters of UGW to be used for non-destructive testing.

| S-EPMC5456774 | biostudies-other

Application of Dual Focused Ultrasonic Phased Array Transducer in Two Orthogonal Cross-Sections for Inspection of Multi-Layered Composite Components of the Aircraft Fuselage.

Project description:Our previous studies have shown that the application of the proposed technique of a dual focused ultrasonic beam in two orthogonal cross-sections in passive (elevation) and active (azimuth) apertures of linear ultrasonic phased array transducer (ULPAT) enhances the 3D spatial resolution in the case of the inspection of conventional defects (flat bottom holes) or measurement of thickness of multi-layered metal composites. The objective of this work is to apply the proposed technique to enhance the spatial resolution of the ULPAT in the cases of detection and sizing demonstration of internal defects possessing spatially complex geometry, and during the inspection of defective multi-layered thin composite components (e.g., GLARE) of the aircraft fuselage. The specially prepared aluminium specimen possessing an internal defect of complicated geometry (crescent-shaped) was investigated. The simulation results and experiments demonstrate the resolution enhancement, higher amplitude of the reflections (e.g., 2.5 times or +8 dB) and spatial improvement in the defect detection even in the case of the non-perpendicular incidence of ultrasonic waves to the complex geometry surface of the internal defect. During the experiments, the multi-layered GFRP-metal based composite sample GLARE 3-3/2 was investigated in the case of the single-side access to the surface of the sample. The internal artificial delamination type defect of 25 mm was detected with a higher accuracy. Compared to the limitations of conventional ULPAT, the relative error (32%) (at the -6 dB level) of lateral defect dimensions estimation was completely reduced.

| S-EPMC7178666 | biostudies-literature

Predicting bone strength with ultrasonic guided waves.

Project description:Recent bone quantitative ultrasound approaches exploit the multimode waveguide response of long bones for assessing properties such as cortical thickness and stiffness. Clinical applications remain, however, challenging, as the impact of soft tissue on guided waves characteristics is not fully understood yet. In particular, it must be clarified whether soft tissue must be incorporated in waveguide models needed to infer reliable cortical bone properties. We hypothesize that an inverse procedure using a free plate model can be applied to retrieve the thickness and stiffness of cortical bone from experimental data. This approach is first validated on a series of laboratory-controlled measurements performed on assemblies of bone- and soft tissue mimicking phantoms and then on in vivo measurements. The accuracy of the estimates is evaluated by comparison with reference values. To further support our hypothesis, these estimates are subsequently inserted into a bilayer model to test its accuracy. Our results show that the free plate model allows retrieving reliable waveguide properties, despite the presence of soft tissue. They also suggest that the more sophisticated bilayer model, although it is more precise to predict experimental data in the forward problem, could turn out to be hardly manageable for solving the inverse problem.

| S-EPMC5335564 | biostudies-literature

Rainbow trapping of ultrasonic guided waves in chirped phononic crystal plates.

Project description:The rainbow trapping effect has been demonstrated in electromagnetic and acoustic waves. In this study, rainbow trapping of ultrasonic guided waves is achieved in chirped phononic crystal plates that spatially modulate the dispersion, group velocity, and stopband. The rainbow trapping is related to the progressively slowing group velocity, and the extremely low group velocity near the lower boundary of a stopband that gradually varies in chirped phononic crystal plates. As guided waves propagate along the phononic crystal plate, waves gradually slow down and finally stop forward propagating. The energy of guided waves is concentrated at the low velocity region near the stopband. Moreover, the guided wave energy of different frequencies is concentrated at different locations, which manifests as rainbow guided waves. We believe implementing the rainbow trapping will open new paradigms for guiding and focusing of guided waves. Moreover, the rainbow guided waves with energy concentration and spatial separation of frequencies may have potential applications in nondestructive evaluation, spatial wave filtering, energy harvesting, and acoustofluidics.

| S-EPMC5213308 | biostudies-literature

Dataset for structural health monitoring of pipelines using ultrasonic guided waves.

Project description:Ultrasonic guided waves (UGW) technique is widely used for nondestructive testing (NDT) of pipelines. In structural health monitoring (SHM), this technique can used to continuously assess the health of these kind of structures. However, environmental conditions can affect UGW propagation and result in false indication of defects. This article describes and provides a database of UGW signals that were acquired at different temperatures during a long period of time. This database could be used to test the efficiency of temperature compensation methods. Besides, a corrosion like defect was created at the end of the monitoring period. Therefore, damage detection methods in SHM could be tested as well.

| S-EPMC9747640 | biostudies-literature

Temperature affected guided wave propagation in a composite plate complementing the Open Guided Waves Platform.

Project description:The influence of temperature is regarded as particularly important for a structural health monitoring system based on ultrasonic guided waves. Since the temperature effect causes stronger signal changes than a typical defect, the former must be addressed and compensated for reliable damage assessment. Development of new temperature compensation techniques as well as the comparison of existing algorithms require high-quality benchmark measurements. This paper investigates a carbon fiber reinforced plastic (CFRP) plate that was fully characterized in previous research in terms of stiffness tensor and guided wave propagation. The same CFRP plate is used here for the analysis of the temperature effect for a wide range of ultrasound frequencies and temperatures. The measurement data are a contribution to the Open Guided Waves (OGW) platform: http://www.open-guided-waves.de . The technical validation includes initial results on the analysis of phase velocity variations with temperature and exemplary damage detection results using state-of-the-art signal processing methods that aim to suppress the temperature effect.

| S-EPMC6778066 | biostudies-literature

Peri-Elastodynamic Simulations of Guided Ultrasonic Waves in Plate-Like Structure with Surface Mounted PZT.

Project description:Peridynamic based elastodynamic computation tool named Peri-elastodynamics is proposed herein to simulate the three-dimensional (3D) Lamb wave modes in materials for the first time. Peri-elastodynamics is a nonlocal meshless approach which is a scale-independent generalized technique to visualize the acoustic and ultrasonic waves in plate-like structure, micro-electro-mechanical systems (MEMS) and nanodevices for their respective characterization. In this article, the characteristics of the fundamental Lamb wave modes are simulated in a sample plate-like structure. Lamb wave modes are generated using a surface mounted piezoelectric (PZT) transducer which is actuated from the top surface. The proposed generalized Peri-elastodynamics method is not only capable of simulating two dimensional (2D) in plane wave under plane strain condition formulated previously but also capable of accurately simulating the out of plane Symmetric and Antisymmetric Lamb wave modes in plate like structures in 3D. For structural health monitoring (SHM) of plate-like structures and nondestructive evaluation (NDE) of MEMS devices, it is necessary to simulate the 3D wave-damage interaction scenarios and visualize the different wave features due to damages. Hence, in addition, to simulating the guided ultrasonic wave modes in pristine material, Lamb waves were also simulated in a damaged plate. The accuracy of the proposed technique is verified by comparing the modes generated in the plate and the mode shapes across the thickness of the plate with theoretical wave analysis.

| S-EPMC5796372 | biostudies-literature

Numerical simulation of monitoring corrosion in reinforced concrete based on ultrasonic guided waves.

Project description:Numerical simulation based on finite element method is conducted to predict the location of pitting corrosion in reinforced concrete. Simulation results show that it is feasible to predict corrosion monitoring based on ultrasonic guided wave in reinforced concrete, and wavelet analysis can be used for the extremely weak signal of guided waves due to energy leaking into concrete. The characteristic of time-frequency localization of wavelet transform is adopted in the corrosion monitoring of reinforced concrete. Guided waves can be successfully used to identify corrosion defects in reinforced concrete with the analysis of suitable wavelet-based function and its scale.

| S-EPMC4075001 | biostudies-other

Non-destructive inspection of food and technical oils by terahertz spectroscopy.

Project description:Quality control and non-destructive monitoring are of notable interest of food and pharmaceutical industries. It relies on the ability of non-invasive inspection which can be employed for manufacturing process control. We hereby apply terahertz (THz) time-domain spectroscopy as non-destructive technique to monitor pure and degraded oils as well as hydrocarbon chemicals. Significant differences in the spectra of refractive index (RI) and absorption coefficient arising from the presence of ester linkages in the edible and technical oils were obtained. Explicit increase from 1.38 to 1.5 of the RI in all THz spectrum range was observed in hydrocarbons and mono-functional esters with the increase of molar mass. This fact is in contrast of RI dependence on molar mass in multi-functional esters, such as Adipate or vegetable oils, where it is around 1.54. Degradation products, Oleic Acid (OA) and water in particular, lead only to some changes in absorption coefficient and RI spectra of vegetable oils. We demonstrate that complex colloidal and supramolecular processes, such as dynamics of inverse micelles and oil hydrolysis, take part during oil degradation and are responsible for non-uniform dependence of optical properties on extent of degradation.

| S-EPMC6303405 | biostudies-literature

Dataset on reflection and transmission coefficients of ultrasonic shear horizontal guided waves in plates with wall thinning.

Project description:This data article reports the data for reflection and transmission coefficients of the SH0 and SH1 ultrasonic guided waves modes due to their interaction with tapered wall thinning in aluminium plates. Several thinning depths and edge taper angles were machined, at the total of 35 different samples. Periodic permanent magnet array electromagnet acoustic transducers were used to generate and receive the waves. Both modes were individually generated and separated in the received signal by means of effective post-processing technique. Reflection and transmission coefficients were calculated at both the leading and trailing edges of the thinning region for mode-converted and non-mode converted signals; therefore, eight coefficients were calculated for each generated mode, at the total of sixteen coefficients for each sample. Additional finite-element model was used in order to obtain numerical values for the coefficients. These data were used in order to analyze the interaction of the SH0 and SH1 modes with wall thinning and the capabilities of using them in non-destructive evaluation of corrosion-like defects in the research paper entitled "Interaction of SH guided waves with wall thinning" (Kubrusly et al., 2019).

| S-EPMC6265498 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data