Microwaves effectively examine the extent and type of coking over acid zeolite catalysts.

ABSTRACT: Coking leads to the deactivation of solid acid catalyst. This phenomenon is a ubiquitous problem in the modern petrochemical and energy transformation industries. Here, we show a method based on microwave cavity perturbation analysis for an effective examination of both the amount and the chemical composition of cokes formed over acid zeolite catalysts. The employed microwave cavity can rapidly and non-intrusively measure the catalytically coked zeolites with sample full body penetration. The overall coke amount is reflected by the obtained dielectric loss (ε″) value, where different coke compositions lead to dramatically different absorption efficiencies (ε″/cokes' wt%). The deeper-dehydrogenated coke compounds (e.g., polyaromatics) lead to an apparently higher ε″/wt% value thus can be effectively separated from lightly coked compounds. The measurement is based on the nature of coke formation during catalytic reactions, from saturated status (e.g., aliphatic) to graphitized status (e.g., polyaromatics), with more delocalized electrons obtained for enhanced Maxwell-Wagner polarization.Catalyst deactivation by coke deposition is a major drawback in industrial processes. Here, the authors show a non-intrusive microwave cavity perturbation technique as a powerful tool to determine the nature and extent of coke accumulation in industrially-relevant zeolite catalysts.

SUBMITTER: Liu B

PROVIDER: S-EPMC5593951 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Stable complete methane oxidation over palladium based zeolite catalysts.

Project description:Increasing the use of natural gas engines is an important step to reduce the carbon footprint of mobility and power generation sectors. To avoid emissions of unburnt methane and the associated severe greenhouse effect of lean-burn engines, the stability of methane oxidation catalysts against steam-induced sintering at low temperatures (<500?°C) needs to be improved. Here we demonstrate how the combination of catalyst development and improved process control yields a highly efficient solution for complete methane oxidation. We design a material based on palladium and hierarchical zeolite with fully sodium-exchanged acid sites, which improves the support stability and prevents steam-induced palladium sintering under reaction conditions by confining the metal within the zeolite. Repeated short reducing pulses enable the use of a highly active transient state of the catalyst, which in combination with its high stability provides excellent performance without deactivation for over 90?h in the presence of steam.

| S-EPMC6026177 | biostudies-literature

Synthesis of novel perfluoroalkylglucosides on zeolite and non-zeolite catalysts.

Project description:Perfluoroalkylglucosides comprise a very important class of fluorine-containing surfactants. These compounds can be synthesized by using the Fisher reaction, starting directly from glucose and the required perfluoroalcohols. We wish to report on the use of zeolite catalysts of different structure and composition for the synthesis of perfluoroalkylglucosides when using glucose and 1-octafluoropentanol as substrates. Zeolites of different pore architecture have been chosen (ZSM-5, ZSM-12, MCM-22 and Beta). Zeolites were characterized by XRD, nitrogen sorption, scanning electron microscopy (SEM) and solid-state 27Al MAS NMR spectroscopy. The activity of the zeolite catalysts in the glycosidation reaction was studied in a batch reactor at 100 °C below atmospheric pressure. The performance of zeolites was compared to other catalysts, an ion-exchange resin (Purolite) and a montmorillonite-type layered aluminosilicate. The catalytic performance of zeolite Beta was the highest among the zeolites studied and the results were comparable to those obtained over Purolite and montmorillonite type catalysts.

| S-EPMC6272255 | biostudies-literature

DeNOx Abatement over Sonically Prepared Iron-Substituted Y, USY and MFI Zeolite Catalysts in Lean Exhaust Gas Conditions.

Project description:Iron-substituted MFI, Y and USY zeolites prepared by two preparation routes-classical ion exchange and the ultrasound modified ion-exchange method-were characterised by micro-Raman spectroscopy, X-ray diffraction (XRD), scanning electron microscopy (SEM), and ultraviolet (UV)/visible diffuse reflectance spectroscopy (UV/Vis DRS). Ultrasound irradiation, a new technique for the preparation of the metal salt suspension before incorporation to the zeolite structure, was employed. An experimental study of selective catalytic reduction (SCR) of NO with NH? on both iron-substituted reference zeolite catalysts and those prepared through the application of ultrasound conducted during an ion-exchange process is presented. The prepared zeolite catalysts show high activity and selectivity in SCR deNOx abatement. The MFI-based iron catalysts, especially those prepared via the sonochemical method, revealed superior activity in the deNOx process, with almost 100% selectivity towards N?. The hydrothermal stability test confirmed high stability and activity of MFI-based catalysts in water-rich conditions during the deNOx reaction at 450 °C.

| S-EPMC5791108 | biostudies-other

Coking-resistant dry reforming of methane over Ni/γ-Al<sub>2</sub>O<sub>3</sub> catalysts by rationally steering metal-support interaction.

Project description:The coking issue is the main challenge for dry reforming of methane (DRM) over Ni-based catalysts. Herein, we excavate the reasons for the enhanced coking resistance of the bounded Ni over the free state Ni in Ni/γ-Al2O3 catalysts for DRM. Rational metal-support interaction of the bounded Ni would facilitate desorption of CO, thus suppressing CO disproportionation and decreasing carbon deposition. The higher activity of the bounded Ni is ascribed to better methane cracking ability, stronger adsorption, and activation of CO2 by forming polydentate carbonate. The better activation of CO2 over the bounded Ni would also contribute to the gasification of formed coke. We gain an insight into the anti-coking mechanism of DRM determined by metal-support interaction in Ni/γ-Al2O3 catalysts through mechanistic studies. It is believed that our findings would enlighten the design of more efficient catalysts for DRM.

| S-EPMC8261659 | biostudies-literature

Catalytic Transfer Hydrogenation and Acid Reactions of Furfural and 5-(Hydroxymethyl)furfural over Hf-TUD-1 Type Catalysts.

Project description:Heterogeneous catalysis, which has served well the petrochemical industry, may valuably contribute towards a bio-based economy by sustainably enabling selective reactions to renewable chemicals. Carbohydrate-containing matter may be obtained from various widespread sources and selectively converted to furanic platform chemicals: furfural (Fur) and 5-(hydroxymethyl)furfural (Hmf). Valuable bioproducts may be obtained from these aldehydes via catalytic transfer hydrogenation (CTH) using alcohols as H-donors under relatively moderate reaction conditions. Hafnium-containing TUD-1 type catalysts were the first of ordered mesoporous silicates explored for the conversion of Fur and Hmf via CTH/alcohol strategies. The materials promoted CTH and acid reactions leading to the furanic ethers. The bioproducts spectrum was broader for the reaction of Fur than of Hmf. A Fur reaction mechanism based on literature data was discussed and supported by kinetic modelling. The influence of the Hf loading and reaction conditions (catalyst load, type of alcohol H-donor, temperature, initial substrate concentration) on the reaction kinetics was studied. The reaction conditions were optimized to maximize the yields of 2-(alkoxymethyl)furan ethers formed from Fur; up to 63% yield was reached at 88% Fur conversion, 4 h/150 °C, using Hf-TUD-1(75), which was a stable catalyst. The Hf-TUD-1(x) catalysts promoted the selective conversion of Hmf to bis(2-alkoxymethyl)furan; e.g., 96% selectivity at 98% Hmf conversion, 3 h/170 °C for Hf-TUD-1(50).

| S-EPMC8658772 | biostudies-literature

Hydrogenation of Lactic Acid to 1,2-Propanediol over Ru-Based Catalysts.

Project description:The catalytic hydrogenation of lactic acid to 1,2-propanediol with supported Ru catalysts in water was investigated. The influence of catalyst support (activated carbon, ?-Al2O3, SiO2, TiO2, and CeO2) and promoters (Pd, Au, Mo, Re, Sn) on the catalytic performance was evaluated. Catalytic tests revealed that TiO2 yields the best Ru catalysts. With a monometallic Ru/TiO2 catalyst, a 1,2-propanediol yield of 70?% at 79?% lactic acid conversion was achieved at 130?°C after 20?h reaction. Minor byproducts of the hydrogenation reaction were propionic acid, ethanol, 1-propanol, and 2-propanol. For the bimetallic catalysts, the addition of Pd and Au slightly enhanced the performance of Ru/TiO2, whereas the addition of common hydrogenation promoters such as Re, Mo, and Sn impaired the activity.

| S-EPMC5838540 | biostudies-literature

Universal holonomic quantum gates over geometric spin qubits with polarised microwaves.

Project description:A microwave shares a nonintuitive phase called the geometric phase with an interacting electron spin after an elastic scattering. The geometric phase, generally discarded as a global phase, allows universal holonomic gating of an ideal logical qubit, which we call a geometric spin qubit, defined in the degenerate subspace of the triplet spin qutrit. We here experimentally demonstrate nonadiabatic and non-abelian holonomic quantum gates over the geometric spin qubit on an electron or nitrogen nucleus. We manipulate purely the geometric phase with a polarised microwave in a nitrogen-vacancy centre in diamond under a zero-magnetic field at room temperature. We also demonstrate a two-qubit holonomic gate to show universality by manipulating the electron-nucleus entanglement. The universal holonomic gates enable fast and fault-tolerant manipulation for realising quantum repeaters interfacing between universal quantum computers and secure communication networks.

| S-EPMC6089953 | biostudies-literature

Conversion of Sucrose into Lactic Acid over Functionalized Sn-Beta Zeolite Catalyst by 3-Aminopropyltrimethoxysilane.

Project description:The utilization of sucrose, an easily accessible disaccharide, in the production of a versatile platform chemical lactic acid (LA), is more attractive than a monosaccharide. In this work, we report a modification approach by 3-aminopropyltrimethoxysilane to introduce an amino group onto the surface of the Sn-Beta Lewis acid catalyst. Using the modified catalyst, a maximum LA yield of 58% was achieved under optimal hydrothermal conditions (190 °C, 4 h) from sucrose, along with a complete conversion and a reduced 5-hydroxymethylfurfural (HMF) yield of 8% compared to Sn-Beta. To evaluate the role of the amino group, different substrates were used as the reactants to produce LA. The experimental results suggested that both fructose and glucose were crucial intermediates in the initial 2 h, whereas glucose is the sole reactant after 2 h. Upon modification, not only the hydrolysis of sucrose was promoted, but the side reaction of HMF formation was also suppressed.

| S-EPMC6643690 | biostudies-literature

Effect of Different Acid-Modified Coking Coals on Quinoline Adsorption.

Project description:The adsorption of quinoline from wastewater by coking coal (AC-1), HCl-modified coking coal (AC-2), HNO3-modified coking coal (AC-3), HF-modified coking coal (AC-4), and H2SO4-modified coking coals (AC-5) was investigated in this paper. The effects of acid-modified concentration, modification time, and adsorption time versus quinoline removal rate were studied by batch experiments. The quinoline concentration was measured by UV spectrophotometry, the average pore size and specific surface area of coking coal before and after modification were characterized through static nitrogen adsorption, the mineral composition of coking coal was tested by X-ray diffraction, the surface functional groups were tested by Fourier transform infrared spectroscopy, and the surface topography was tested using a scanning electron microscope. The experimental results showed that the adsorption capacity of coking coals was the best when both the modification time was 120 min and the acid-modified concentration was 0.1 mol·L-1 and the quinoline removal rate reaches the highest when the adsorption time was 120 min. The specific surface area of AC-2 increased from 2.898 to 3.637 m2·g-1, and the removal rate of quinoline increased from 77.64 to 90.61%. Acids reacted with inorganic mineral impurities within coking coal such as hydrogen vanadium phosphate hydrate, which caused an increase in the specific surface area. A new peak appeared in the Fourier transform infrared spectroscopy pattern at the wavenumber 2300 cm-1. The surface of coking coal modified by acids was rougher than that of AC-1. The adsorption capacity of coking coal was improved after modification, and modified coking coals have the highest potential as low-cost adsorbents for quinoline removal.

| S-EPMC6906776 | biostudies-literature

Nanoscale tomography reveals the deactivation of automotive copper-exchanged zeolite catalysts.

Project description:Copper-exchanged zeolite chabazite (Cu-SSZ-13) was recently commercialized for the selective catalytic reduction of NO X with ammonia in vehicle emissions as it exhibits superior reaction performance and stability compared to all other catalysts, notably Cu-ZSM-5. Herein, the 3D distributions of Cu as well as framework elements (Al, O, Si) in both fresh and aged Cu-SSZ-13 and Cu-ZSM-5 are determined with nanometer resolution using atom probe tomography (APT), and correlated with catalytic activity and other characterizations. Both fresh catalysts contain a heterogeneous Cu distribution, which is only identified due to the single atom sensitivity of APT. After the industry standard 135,000 mile simulation, Cu-SSZ-13 shows Cu and Al clustering, whereas Cu-ZSM-5 is characterized by severe Cu and Al aggregation into a copper aluminate phase (CuAl2O4 spinel). The application of APT as a sensitive and local characterization method provides identification of nanometer scale heterogeneities that lead to catalytic activity and material deactivation.

| S-EPMC5698465 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data