Generating highly reflective and conductive metal layers through a light-assisted synthesis and assembling of silver nanoparticles in a polymer matrix.

ABSTRACT: The development of metalized surfaces exhibiting mirror properties and/or electric conductivity without heavy equipments and with low metal charge is a big challenge in view of many industrial applications. We report herein on the photo-assembling of silver nanoparticles (AgNPs) in a polymer matrix, carried out within minutes from an acrylate monomer and silver nitrate at room temperature, under air and without any solvents. The top surface of the material gets converted into a continuous silver thin film and a depthwise concentration gradient of AgNPs is created in the polymer, which images the absorption profile of the actinic UV light in the reactive formulation. This specific assembling of the silver@polymer coating induces excellent reflective and conductive properties. The conductance was observed to strongly increase with increasing the exposure from 3 to 30?min due to the formation of a more and more compact metal film. This coating strategy works with a variety of substrates (textile, paper, glass, wood, plastic and stainless steel). Moreover, on flexible surfaces such as textile, the flexibility was preserved. The possibility to use this kind of nanomaterial as a printing ink, with a much lower metal concentration (3 to 5 wt.%) than concurrent inks, was also demonstrated.

SUBMITTER: Zaier M

PROVIDER: S-EPMC5622138 | biostudies-literature | 2017 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Generating highly reflective and conductive metal layers through a light-assisted synthesis and assembling of silver nanoparticles in a polymer matrix.

Zaier Mohamed M Vidal Loïc L Hajjar-Garreau Samar S Balan Lavinia L

Scientific reports 20170929 1

The development of metalized surfaces exhibiting mirror properties and/or electric conductivity without heavy equipments and with low metal charge is a big challenge in view of many industrial applications. We report herein on the photo-assembling of silver nanoparticles (AgNPs) in a polymer matrix, carried out within minutes from an acrylate monomer and silver nitrate at room temperature, under air and without any solvents. The top surface of the material gets converted into a continuous silver ...[more]

PMID: 28963491

Similar Datasets

Project description:Despite efforts to mature human pluripotent stem cell-derived cardiomyocytes (hPSC-CMs) for disease modeling and high throughput screening, cells remain immature and may not reflect adult biology. Recent advancements utilize electro-mechanical and paracrine stimulation to functionally mature cardiomyocytes, but the resulting engineered constructs continue to lack a microenvironment conducive to electrical signal propagation and maturity. Conductive polymers are attractive candidates to facilitate electrical communication between gaps in sparse hPSC-CM clusters or between hPSC-CMs to repair conduction defects. To create a conductive polymer platform for improved electrical signal propagation between hPSC-CMs and achieve electrical maturity, we electrospun poly(3,4-ethylendioxythiophene):polystyrene sulfonate (PEDOT:PSS) blended with 8% (w/v) poly(vinyl alcohol) (PVA). Matrix fiber structure remained stable over 4 weeks in buffer, stiffness remains near cardiac stiffness in vivo, and electrical conductivity scaled with PEDOT:PSS concentration. When fibroblasts were added to fibers, cells had higher initial attachment to PEDOT:PSS compared to PVA-only scaffolds, and after 5 days, over 90% of fibroblasts remained viable on PEDOT:PSS scaffolds compared to PVA-only scaffolds. Electrically excitable hPSC-CMs cultured on conductive substrates exhibited an upregulation of cardiac and muscle-related genes as opposed to non-conductive substrates. These cells further displayed increased desmoplakin (DP) localization on conductive scaffolds, indicating an improvement in the mechanical stability of our hPSC-CMs. Sarcomere organization also scaled with increasing PEDOT:PSS concentration, even in sub-monolayer cell densities, suggesting that improved organization of the contractile machinery in these cells was due to the electrical condition of the matrix. Calcium handling indicated higher calcium flux with a shorter time to peak, further suggesting improved electrical maturity, even when sub-confluent. Taken together, these data suggest that PEDOT:PSS/PVA scaffolds are stable, of a stiffness relevant to cardiomyocytes, and supportive of electrical coupling even in the absence of a monolayer, which may improve cardiac disease modeling and drug development.

Project description:Printed electronics has advanced during the recent decades in applications such as organic photovoltaic cells and biosensors. However, the main limiting factors preventing the more widespread use of printing in flexible electronics manufacturing are (i) the poor attainable linewidths via conventional printing methods (≫10 μm), (ii) the limited availability of printable materials (e.g., low work function metals), and (iii) the inferior performance of many printed materials when compared to vacuum-processed materials (e.g., printed vs sputtered ITO). Here, we report a printing-based, low-temperature, low-cost, and scalable patterning method that can be used to fabricate high-resolution, high-performance patterned layers with linewidths down to ∼1 μm from various materials. The method is based on sequential steps of reverse-offset printing (ROP) of a sacrificial polymer resist, vacuum deposition, and lift-off. The sharp vertical sidewalls of the ROP resist layer allow the patterning of evaporated metals (Al) and dielectrics (SiO) as well as sputtered conductive oxides (ITO), where the list is expandable also to other vacuum-deposited materials. The resulting patterned layers have sharp sidewalls, low line-edge roughness, and uniform thickness and are free from imperfections such as edge ears occurring with other printed lift-off methods. The applicability of the method is demonstrated with highly conductive Al (∼5 × 10-8 Ωm resistivity) utilized as transparent metal mesh conductors with ∼35 Ω□ at 85% transparent area percentage and source/drain electrodes for solution-processed metal-oxide (In2O3) thin-film transistors with ∼1 cm2/(Vs) mobility. Moreover, the method is expected to be compatible with other printing methods and applicable in other flexible electronics applications, such as biosensors, resistive random access memories, touch screens, displays, photonics, and metamaterials, where the selection of current printable materials falls short.

Dataset Information

Generating highly reflective and conductive metal layers through a light-assisted synthesis and assembling of silver nanoparticles in a polymer matrix.

Publications

Generating highly reflective and conductive metal layers through a light-assisted synthesis and assembling of silver nanoparticles in a polymer matrix.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets